CN103952946A - Scratch-resistant wallpaper and production method thereof - Google Patents
Scratch-resistant wallpaper and production method thereof Download PDFInfo
- Publication number
- CN103952946A CN103952946A CN201410212843.8A CN201410212843A CN103952946A CN 103952946 A CN103952946 A CN 103952946A CN 201410212843 A CN201410212843 A CN 201410212843A CN 103952946 A CN103952946 A CN 103952946A
- Authority
- CN
- China
- Prior art keywords
- wallpaper
- layer
- scratch resistant
- plasticizer
- scratch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses scratch-resistant wallpaper and a preparation method thereof. The scratch-resistant wallpaper has a layered structure and consists of a bottom wallpaper layer, a middle adhesive layer and a top scratch-resistant layer in sequence from bottom to top, wherein the wallpaper layer is made of pure wallpaper, non-woven wallpaper or PVC (polyvinyl chloride) wallpaper; the adhesive layer is formed by coating the bottom wallpaper layer with transparent slurry consisting of a plasticizer, polyvinyl chloride resin, a viscosity reducer, an external lubricating agent and a stabilizing agent, and then drying at 180-200 DEG C; the top scratch-resistant layer is formed by coating the adhesive layer with homogenate consisting of 25 percent of plasticizer, 60 percent of polyvinyl chloride, 7 percent of viscosity reducer, 7 percent of external lubricating agent and 1 percent of stabilizing agent through a photogravure roller or a rotary screen printing roller, and drying at 180-200 DEG C. Under the action of outer force, the scratch-resistant wallpaper disclosed by the invention can effectively buffer the outer force to achieve a scratch resisting effect; furthermore, under outer force friction, the scratch-resistant wallpaper still can keep the original attractiveness.
Description
Technical field
The present invention relates to a kind of scratch resistant wallpaper and production method thereof, belong to wallpaper production field.
Background technology
Wallpaper is in the extensive use of the public place such as megastore, hotel, will inevitably cause and the friction of other objects in the application in these places, in the attractive in appearance and life-span that can affect wallpaper in friction process, the scratch resistant performance that how effectively to improve wallpaper is called the focus of wallpaper manufacturer extensive concern.By the scratch resistant wallpaper of independent research, effective processing is carried out in wallpaper surface and can improve its scratch resistant performance, the scratch resistant wallpaper the present invention relates to, scratch resistant performance that can fine raising wallpaper, and after long-term use, still keep the attractive in appearance and combination property of wallpaper.
Summary of the invention
One of object of the present invention is in order to solve the technical problem that wallpaper easily scratches wallpaper in the time running into external force and to have proposed a kind of scratch resistant wallpaper.
Two of object of the present invention is the production method of a kind of scratch resistant wallpaper that provides above-mentioned.
Technical scheme of the present invention
A kind of scratch resistant wallpaper, is layer structure, is made up of successively from top to bottom wallpaper layer, the adhesion coating in intermediate layer and the scratch resistant layer of top layer of bottom;
Described wallpaper layer is pure paper wallpaper, nonwoven wallpaper or PVC wallpaper;
Described adhesion coating is served as reasons and is counted by weight percentage, i.e. 25% plasticizer, 60% molecular weight is the Corvic of 50000-120000,7% thinner, the transparent slurry of 7% external lubricant and 10% stabilizing agent composition is coated on bottom wallpaper layer, then controlling temperature is that 180-200 DEG C of oven dry forms, and its thickness is 10-30 silk;
Plasticizer in above-mentioned adhesion coating is DINP, and thinner is BYK4040, and external lubricant is the compound ester of multi-functional aliphatic acid, and stabilizing agent is potassium zinc stabilizer;
Described top layer scratch resistant layer is served as reasons and is counted by weight percentage, i.e. 25% plasticizer, 60% polyvinyl chloride, 7% thinner, the homogenate of 7% external lubricant and 1% stabilizing agent mixing gained is coated on sticky adhesion coating by gravure printing wheel or cylinder print wheel, and coating quality is 70g/M
2, then controlling temperature is that 180-200 DEG C of oven dry forms, its thickness is 10-30 silk;
Plasticizer in above-mentioned top layer scratch resistant layer is DINP, and thinner is BYK4040, and external lubricant is the compound ester of multi-functional aliphatic acid, and stabilizing agent is potassium zinc stabilizer.
The preparation method of above-mentioned a kind of scratch resistant wallpaper, specifically comprises the steps:
(1), first will be by counting by weight percentage, i.e. 25% plasticizer, 60% molecular weight is the Corvic of 50000-120000,7% thinner, the transparent slurry of 7% external lubricant and 1% stabilizing agent composition is coated on the wallpaper layer of bottom, then controlling temperature is 180-200 DEG C of oven dry, obtains the adhesion coating that thickness is 10-30 silk;
(2), will be by counting by weight percentage, i.e. 25% plasticizer, 60% polyvinyl chloride, 7% thinner, the homogenate of 7% external lubricant and 1% stabilizing agent mixing gained is coated by gravure printing wheel or cylinder print wheel on the adhesion coating of step (1) gained, and coating quality is 70g/M
2, then control temperature and be 180-200 DEG C and dry, obtaining thickness is the scratch resistant wallpaper of 10-30 silk.
Beneficial effect of the present invention
The scratch resistant wallpaper of one of the present invention, owing to having adopted plasticizer and external lubricant in scratch resistant layer, makes the scratch resistant wallpaper of final gained can effectively cushion external force under external force and play scratch resistant effect, and still keeps original attractive in appearance after running into external force friction.
Detailed description of the invention
Be described in further detail of the present invention below by embodiment, but be not used for limiting the scope of the invention.
The various raw materials that the present invention is used, plasticizer DINP is purchased from Guangzhou Kai Feng Chemical trade Co., Ltd;
Thinner BYK4040 is purchased from Hebei Shen Mei chemical building material Co., Ltd;
External lubricant, the compound ester of multi-functional aliphatic acid is purchased from Shanghai Di Run Chemical Co., Ltd.;
Stabilizing agent is that potassium zinc stabilizer is purchased from Shanghai Yong Yan Chemical Industry Science Co., Ltd.
embodiment 1
A kind of scratch resistant wallpaper, is layer structure, is made up of the scratch resistant layer of bottom wallpaper layer, the sticky adhesion coating in intermediate layer and top layer;
Described wallpaper layer is goldleaf wallpaper;
Described adhesion coating is served as reasons and is counted by weight percentage, i.e. 25% plasticizer, 60% molecular weight is the Corvic of 50000-120000,7% thinner, and the transparent slurry of 7% external lubricant and 1% stabilizing agent composition is coated on the wallpaper layer of bottom and is formed;
Plasticizer in above-mentioned adhesion coating is DINP, and thinner is BYK4040, and external lubricant is the compound ester of multi-functional aliphatic acid, and stabilizing agent is potassium zinc stabilizer;
Described scratch resistant layer is served as reasons and is counted by weight percentage, by 25% plasticizer, and 60% polyvinyl chloride, 7% thinner, the homogenate of 7% external lubricant and 1% stabilizing agent mixing gained is coated on sticky adhesion coating and is dried by gravure printing wheel or cylinder print wheel and forms;
Plasticizer in above-mentioned top layer scratch resistant layer is DINP, and thinner is BYK4040, and external lubricant is the compound ester of multi-functional aliphatic acid, and stabilizing agent is potassium zinc stabilizer.
The preparation method of above-mentioned a kind of scratch resistant wallpaper, specifically comprises the steps:
(1), first will be by counting by weight percentage, i.e. 25% plasticizer, 60% molecular weight is the Corvic of 50000-120000,7% thinner, the transparent slurry of 7% external lubricant and 1% stabilizing agent composition is coated on the wallpaper layer of bottom, then controlling temperature is 190 DEG C of oven dry, obtains the adhesion coating that thickness is 10-30 silk;
(2), will be by counting by weight percentage, i.e. 25% plasticizer, 60% polyvinyl chloride, 7% thinner, the homogenate of 7% external lubricant and 1% stabilizing agent mixing gained is coated by gravure printing wheel or cylinder print wheel on the adhesion coating of step (1) gained, and coating quality is 70g/M
2, the wallpaper printing streamline that then Negotiation speed is 30M/min is sent into baking oven, and control temperature is 190 DEG C dries, and obtaining thickness is the scratch resistant wallpaper of 10-30 silk.
The scratch resistant wallpaper of above-mentioned gained adopts and with the brush of little steel wire, it is carried out to the method that equivalent scrapes for several times back and forth and detect, whether it leaves the technical indicator number that sharp trace reflects that it is scratch resistant, keep wallpaper appearance property constant, scrape maximum times and weigh its scratch resistant performance.From the result scraping, can find out, scratch resistant wallpaper of the present invention has the effect of the scraping of the external force of preventing, is particularly suitable for being applied to the public place such as hotel, market.
The above is only giving an example of embodiments of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvement and modification, these improve and modification also should be considered as protection scope of the present invention.
Claims (2)
1. a scratch resistant wallpaper, is layer structure, it is characterized in that described scratch resistant wallpaper, is made up of successively from top to bottom wallpaper layer, the adhesion coating in intermediate layer and the scratch resistant layer of top layer of bottom;
Described wallpaper layer is pure paper wallpaper, nonwoven wallpaper or PVC wallpaper;
Described adhesion coating is served as reasons and is counted by weight percentage, i.e. 25% plasticizer, 60% molecular weight is the Corvic of 50000-120000,7% thinner, the transparent slurry of 7% external lubricant and 1% stabilizing agent composition is coated on bottom wallpaper layer, then controlling temperature is that 180-200 DEG C of oven dry forms, and its thickness is 10-30 silk;
Plasticizer in above-mentioned adhesion coating is DINP, and thinner is BYK4040, and external lubricant is the compound ester of multi-functional aliphatic acid, and stabilizing agent is potassium zinc stabilizer;
Described top layer scratch resistant layer is served as reasons and is counted by weight percentage, i.e. 25% plasticizer, 60% molecular weight is the polyvinyl chloride of 50000-120000,7% thinner, the homogenate of 7% external lubricant and 1% stabilizing agent mixing gained is coated on sticky adhesion coating and controlled temperature by gravure printing wheel or cylinder print wheel is that 180-200 DEG C of oven dry forms, and its thickness is 10-30 silk;
Plasticizer in above-mentioned top layer scratch resistant layer is DINP, and thinner is BYK4040, and external lubricant is the compound ester of multi-functional aliphatic acid, and stabilizing agent is potassium zinc stabilizer.
2. the production method of a kind of scratch resistant wallpaper as claimed in claim 1, is characterized in that specifically comprising the steps:
(1), first will be by counting by weight percentage, i.e. 25% plasticizer, 60% molecular weight is the Corvic of 50000-120000,7% thinner, the transparent slurry of 7% external lubricant and 10% stabilizing agent composition is coated on bottom wallpaper layer, then controlling temperature is 180-200 DEG C of oven dry, obtains the adhesion coating that thickness is 10-30 silk;
(2), will be by counting by weight percentage, i.e. 25% plasticizer, 60% polyvinyl chloride, 7% thinner, the homogenate of 7% external lubricant and 1% stabilizing agent mixing gained is coated by gravure printing wheel or cylinder print wheel on the adhesion coating of step (1) gained, and coating quality is 70g/M
2, then control temperature and be 180-200 DEG C and dry, obtaining thickness is the scratch resistant wallpaper of 10-30 silk.