CN104087129A - Primer composition for bicycles - Google Patents
Primer composition for bicycles Download PDFInfo
- Publication number
- CN104087129A CN104087129A CN201410358850.9A CN201410358850A CN104087129A CN 104087129 A CN104087129 A CN 104087129A CN 201410358850 A CN201410358850 A CN 201410358850A CN 104087129 A CN104087129 A CN 104087129A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- ethanol
- silicone oil
- polyurethane dispersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a primer composition for bicycles, belonging to the technical field of coatings. The primer composition is prepared by using 55-65 parts of water-based epoxy acrylic resin, 20-30 parts of water-based polyurethane dispersion, 8-12 parts of water-soluble amino resin, 10-15 parts of hexamethylene diisocyanate, 5-8 parts of ethanol, 0.1-1 part of glycerin, 1-2 parts of propanediol butyl ether, 0.01-0.1 part of sodium carboxymethylcellulose, 5-30 parts of pigments, 0.2-0.5 part of silicone oil and 50-65 parts of deionized water by weight as raw materials. The primer composition is environment-friendly.
Description
Technical field
The invention belongs to technical field of coatings, relate in particular to a kind of bicycle use paint base composition.
Background technology
Priming paint is the first layer of paint system, for improve finish paint sticking power, increase finish paint fullness ratio, alkali-resistivity is provided, anti-corrosion function etc. is provided, can ensure the even absorption of finish paint simultaneously, be paint system performance best effect.
Traditional bicycle use priming paint is generally solvent bottom paint, contains a large amount of hazardous solvents, and these solvents, in construction and use procedure, can cause certain injury to workmen and contactee.
Summary of the invention
The technical problem that the present invention solves is to provide a kind of bicycle use paint base composition of environment-friendly type.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is:
It is made up of the raw material of following parts by weight:
55 parts～65 parts of water-based epoxy acrylic resins, 20 parts～30 parts of aqueous polyurethane dispersion, 8 parts～12 parts of water soluble amino resins, 10 parts～15 parts of hexamethylene diisocyanates, 5 parts～8 parts of ethanol, 0.1 part～1 part of glycerine, 1 part～2 parts of propandiol butyl ethers, 0.01 part～0.1 part of Xylo-Mucine, 5 parts～30 parts of pigment, 50 parts～65 parts of 0.2 part～0.5 part of silicone oil and deionized waters;
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put into reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, for subsequent use;
B, by above-mentioned water-based epoxy acrylic resin, aqueous polyurethane dispersion, water soluble amino resin, glycerine, propandiol butyl ether, Xylo-Mucine, pigment, silicone oil, the intermediate product I that deionized water and A step make is put into high speed dispersor, disperses 4 hours～6 hours with the rotating speeds of 900 revs/min～1000 revs/min, makes.
Owing to adopting technique scheme, the beneficial effect that the present invention obtains is:
1, over-all properties of the present invention is good.
2, the present invention is a kind of bicycle use paint base composition of environment-friendly type, does not all have the volatilization of hazardous solvent in construction process and use procedure.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described, and protection scope of the present invention is not only confined to following examples.
Embodiment 1
The raw materials of this bicycle use paint base composition is: water-based epoxy acrylic resin 5.5kg, aqueous polyurethane dispersion 2.0kg, water soluble amino resin 1.2kg, hexamethylene diisocyanate 1.5kg, ethanol 0.8kg, glycerine 0.1kg, propandiol butyl ether 0.2kg, Xylo-Mucine 0.01kg, pigment 3.0kg, silicone oil 0.05kg and deionized water 6.5kg;
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put into reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, for subsequent use;
B, by above-mentioned water-based epoxy acrylic resin, aqueous polyurethane dispersion, water soluble amino resin, glycerine, propandiol butyl ether, Xylo-Mucine, pigment, silicone oil, the intermediate product I that deionized water and A step make is put into high speed dispersor, disperses 6 hours with the rotating speeds of 900 revs/min, makes.
Embodiment 2
The raw materials of this bicycle use paint base composition is: water-based epoxy acrylic resin 6.0kg, aqueous polyurethane dispersion 2.5kg, water soluble amino resin 1.0kg, hexamethylene diisocyanate 1.2kg, ethanol 0.7kg, glycerine 0.05kg, propandiol butyl ether 0.15kg, Xylo-Mucine 0.005kg, pigment 2.0kg, silicone oil 0.04kg and deionized water 6.0kg;
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put into reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, for subsequent use;
B, by above-mentioned water-based epoxy acrylic resin, aqueous polyurethane dispersion, water soluble amino resin, glycerine, propandiol butyl ether, Xylo-Mucine, pigment, silicone oil, the intermediate product I that deionized water and A step make is put into high speed dispersor, disperses 4 hours with the rotating speeds of 1000 revs/min, makes.
Embodiment 3
The raw materials of this bicycle use paint base composition is: water-based epoxy acrylic resin 6.5kg, aqueous polyurethane dispersion 3.0kg, water soluble amino resin 0.8kg, hexamethylene diisocyanate 1.0kg, ethanol 0.5kg, glycerine 0.01kg, propandiol butyl ether 0.1kg, Xylo-Mucine 0.001kg, pigment 0.5kg, silicone oil 0.02kg and deionized water 5.0kg;
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put into reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, for subsequent use;
B, by above-mentioned water-based epoxy acrylic resin, aqueous polyurethane dispersion, water soluble amino resin, glycerine, propandiol butyl ether, Xylo-Mucine, pigment, silicone oil, the intermediate product I that deionized water and A step make is put into high speed dispersor, disperses 5 hours with the rotating speeds of 950 revs/min, makes.
The bicycle use paint base composition that embodiment 1～3 is made carries out Performance Detection, and its result is as shown in table 1.
Table 1
Claims (1)
1. a bicycle use paint base composition, is characterized in that being made up of the raw material of following parts by weight:
55 parts～65 parts of water-based epoxy acrylic resins, 20 parts～30 parts of aqueous polyurethane dispersion, 8 parts～12 parts of water soluble amino resins, 10 parts～15 parts of hexamethylene diisocyanates, 5 parts～8 parts of ethanol, 0.1 part～1 part of glycerine, 1 part～2 parts of propandiol butyl ethers, 0.01 part～0.1 part of Xylo-Mucine, 5 parts～30 parts of pigment, 50 parts～65 parts of 0.2 part～0.5 part of silicone oil and deionized waters;
Its preparation method comprises the following steps:
A, above-mentioned hexamethylene diisocyanate and ethanol are put into reactor mix, react, until nco value is less than 0.5, obtain intermediate product I, for subsequent use;
B, by above-mentioned water-based epoxy acrylic resin, aqueous polyurethane dispersion, water soluble amino resin, glycerine, propandiol butyl ether, Xylo-Mucine, pigment, silicone oil, the intermediate product I that deionized water and A step make is put into high speed dispersor, disperses 4 hours～6 hours with the rotating speeds of 900 revs/min～1000 revs/min, makes.