CN104562235A - Forming technology of fishing net threads suitable for fresh water - Google Patents
Forming technology of fishing net threads suitable for fresh water Download PDFInfo
- Publication number
- CN104562235A CN104562235A CN201410300160.8A CN201410300160A CN104562235A CN 104562235 A CN104562235 A CN 104562235A CN 201410300160 A CN201410300160 A CN 201410300160A CN 104562235 A CN104562235 A CN 104562235A
- Authority
- CN
- China
- Prior art keywords
- rotating speed
- temperature
- fishing net
- drawing roller
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a forming technology of fishing net threads suitable for fresh water. The forming technology comprises the steps of carrying out melt mixing on high-strength polyethylene, polypropylene, titanium dioxide, chlorinated polyethylene, calcium stearate, graphite and antioxidant RD, spinning, forming, and obtaining the fishing net threads. The forming technology of the fishing net threads is simple; the spinning uniformity is high; the rate of finished products is high and is up to 99.6%; the tensile strength of the fishing net threads is up to 45.3MPa; the requirement on the fishing net threads in the fresh water can be met; the water absorption rate of the fishing net threads is smaller than 0.8%; the corrosion resistance of the fishing net threads is good, and a fishing net has good wear resistance.
Description
Technical field
The invention belongs to fishing gear rapidoprint field, be specifically related to the moulding process of the fishing lines used in a kind of applicable fresh water.
Background technology
Fishing lines refers to the line that braiding mesh sheet and the diameter tying net fishing gear are less than 4 millimeters, is the main material making fishing net.Present fishing lines mainly uses nylon raw material to prepare, but nylon processing technology is complicated, to temperature, humidity requirement harshness, yield rate is low, and nylon cost is higher, water absorption rate is also higher, because impurities in water is many, easy fibre structure to be damaged after fishing lines water suction, cause fishing net perishable.
Summary of the invention
The object of this invention is to provide the processing technology of the fishing lines used in a kind of applicable fresh water, improve the decay resistance of fishing lines.
The present invention is achieved through the following technical solutions:
The moulding process of the fishing lines used in a kind of applicable fresh water, get high-strength polyethylene 60-72 part by weight, polypropylene 10-15 part, titanium dioxide 0.5-2 part, haloflex 5-10 part, calcium stearate 0.1-0.5 part, graphite 2-5 part, above-mentioned raw materials uses extruder to carry out granulation by anti-aging agent RD 0.5-2 part, extruder front-end temperature is 175 DEG C, stage casing temperature is 180 DEG C, terminal temperature is 178 DEG C, the raw material extruded is added spray silk case, keep spray silk case temperature at 180-185 DEG C, then spinnerets spinning is used through measuring pump, measuring pump is by the spinning head UNICOM of many passages uniformly and on spinnerets, measuring pump rotating speed is 9-12r/min, before pump, pressure is 56bar, after pump, pressure is 115bar, the length of spinning head is 2-10mm, spinning head internal diameter is 0.2-0.8mm, after spinning, drawing roller is used to carry out wound draw, first drawing roller rotating speed is 3600m/mim, second drawing roller rotating speed is 4000m/min, 3rd deflector roll rotating speed is 4200m/min, electric heater unit is provided with between drawing roller, heating-up temperature is 95-108 DEG C, then deflector roll winding is used, above-mentioned roller rotating speed is the linear velocity of roller external diameter, cross air blowing device is provided with between spinning head and drawing roller, wind speed is 0.5m/s, air temperature is 20 DEG C.
Described electric heater unit uses each 12 resistance wires up and down, and resistance wire is horizontally disposed with, two resistance wire spacing 3-5cm, improves the efficiency of drying.
Beneficial effect of the present invention: the moulding technique of fishing lines provided by the invention is simple, spinning uniformity is high, finished product rate is high, reach 99.6%, the TENSILE STRENGTH of fishing lines reaches 45.3MPa, can meet the requirement of fresh water fishing lines, and fishing lines water absorption rate is less than 0.8%, the corrosion resistance and good of fishing lines, and fishing net has good anti-wear performance.
Detailed description of the invention
Embodiment 1
The moulding process of the fishing lines used in a kind of applicable fresh water, get high-strength polyethylene 62 parts by weight, polypropylene 13 parts, titanium dioxide 1 part, haloflex 6.5 parts, calcium stearate 0.2 part, 3.5 parts, graphite, above-mentioned raw materials uses extruder to carry out granulation by anti-aging agent RD 0.5 part, extruder front-end temperature is 175 DEG C, stage casing temperature is 180 DEG C, terminal temperature is 178 DEG C, the raw material extruded is added spray silk case, keep spray silk case temperature at 180 DEG C, then spinnerets spinning is used through measuring pump, measuring pump is by the spinning head UNICOM of many passages uniformly and on spinnerets, measuring pump rotating speed is 10r/min, before pump, pressure is 56bar, after pump, pressure is 115bar, the length of spinning head is 3mm, spinning head internal diameter is 0.25mm, after spinning, drawing roller is used to carry out wound draw, first drawing roller rotating speed is 3600m/mim, second drawing roller rotating speed is 4000m/min, 3rd deflector roll rotating speed is 4200m/min, electric heater unit is provided with between drawing roller, heating-up temperature is 100 DEG C, then deflector roll winding is used, above-mentioned roller rotating speed is the linear velocity of roller external diameter, cross air blowing device is provided with between spinning head and drawing roller, wind speed is 0.5m/s, air temperature is 20 DEG C.
Described electric heater unit uses each 12 resistance wires up and down, and resistance wire is horizontally disposed with, two resistance wire spacing 4cm, improves the efficiency of drying.
Embodiment 2
The moulding process of the fishing lines used in a kind of applicable fresh water, get high-strength polyethylene 68 parts by weight, polypropylene 12 parts, titanium dioxide 1.5 parts, haloflex 8 parts, calcium stearate 0.3 part, 3 parts, graphite, above-mentioned raw materials uses extruder to carry out granulation by anti-aging agent RD 0.6 part, extruder front-end temperature is 175 DEG C, stage casing temperature is 180 DEG C, terminal temperature is 178 DEG C, the raw material extruded is added spray silk case, keep spray silk case temperature at 182 DEG C, then spinnerets spinning is used through measuring pump, measuring pump is by the spinning head UNICOM of many passages uniformly and on spinnerets, measuring pump rotating speed is 10r/min, before pump, pressure is 56bar, after pump, pressure is 115bar, the length of spinning head is 5mm, spinning head internal diameter is 0.2mm, after spinning, drawing roller is used to carry out wound draw, first drawing roller rotating speed is 3600m/mim, second drawing roller rotating speed is 4000m/min, 3rd deflector roll rotating speed is 4200m/min, electric heater unit is provided with between drawing roller, heating-up temperature is 95 DEG C, then deflector roll winding is used, above-mentioned roller rotating speed is the linear velocity of roller external diameter, cross air blowing device is provided with between spinning head and drawing roller, wind speed is 0.5m/s, air temperature is 20 DEG C.
Embodiment 3
The moulding process of the fishing lines used in a kind of applicable fresh water, get high-strength polyethylene 72 parts by weight, polypropylene 14 parts, titanium dioxide 1.2 parts, haloflex 6 parts, calcium stearate 0.2 part, 4 parts, graphite, above-mentioned raw materials uses extruder to carry out granulation by anti-aging agent RD 1.2 parts, extruder front-end temperature is 175 DEG C, stage casing temperature is 180 DEG C, terminal temperature is 178 DEG C, the raw material extruded is added spray silk case, keep spray silk case temperature at 182 DEG C, then spinnerets spinning is used through measuring pump, measuring pump is by the spinning head UNICOM of many passages uniformly and on spinnerets, measuring pump rotating speed is 11r/min, before pump, pressure is 56bar, after pump, pressure is 115bar, the length of spinning head is 4mm, spinning head internal diameter is 0.3mm, after spinning, drawing roller is used to carry out wound draw, first drawing roller rotating speed is 3600m/mim, second drawing roller rotating speed is 4000m/min, 3rd deflector roll rotating speed is 4200m/min, electric heater unit is provided with between drawing roller, heating-up temperature is 105 DEG C, then deflector roll winding is used, above-mentioned roller rotating speed is the linear velocity of roller external diameter, cross air blowing device is provided with between spinning head and drawing roller, wind speed is 0.5m/s, air temperature is 20 DEG C.
Claims (2)
1. the moulding process of the fishing lines used in an applicable fresh water, it is characterized in that, get high-strength polyethylene 60-72 part by weight, polypropylene 10-15 part, titanium dioxide 0.5-2 part, haloflex 5-10 part, calcium stearate 0.1-0.5 part, graphite 2-5 part, above-mentioned raw materials uses extruder to carry out granulation by anti-aging agent RD 0.5-2 part, extruder front-end temperature is 175 DEG C, stage casing temperature is 180 DEG C, terminal temperature is 178 DEG C, the raw material extruded is added spray silk case, keep spray silk case temperature at 180-185 DEG C, then spinnerets spinning is used through measuring pump, measuring pump is by the spinning head UNICOM of many passages uniformly and on spinnerets, measuring pump rotating speed is 9-12r/min, before pump, pressure is 56bar, after pump, pressure is 115bar, the length of spinning head is 2-10mm, spinning head internal diameter is 0.2-0.8mm, after spinning, drawing roller is used to carry out wound draw, first drawing roller rotating speed is 3600m/mim, second drawing roller rotating speed is 4000m/min, 3rd deflector roll rotating speed is 4200m/min, electric heater unit is provided with between drawing roller, heating-up temperature is 95-108 DEG C, then deflector roll winding is used, above-mentioned roller rotating speed is the linear velocity of roller external diameter, cross air blowing device is provided with between spinning head and drawing roller, wind speed is 0.5m/s, air temperature is 20 DEG C.
2. the processing technology of the fishing lines used in a kind of applicable fresh water according to claim 1, is characterized in that, described electric heater unit uses each 12 resistance wires up and down, and resistance wire is horizontally disposed with, two resistance wire spacing 3-5cm.