CN105178564A - Integrated terrazzo floor and production method thereof - Google Patents
Integrated terrazzo floor and production method thereof Download PDFInfo
- Publication number
- CN105178564A CN105178564A CN201510497295.2A CN201510497295A CN105178564A CN 105178564 A CN105178564 A CN 105178564A CN 201510497295 A CN201510497295 A CN 201510497295A CN 105178564 A CN105178564 A CN 105178564A
- Authority
- CN
- China
- Prior art keywords
- concrete
- terrace
- carry out
- terrazzo
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of building construction, and particularly relates to an integrated terrazzo floor and a production method thereof. The production method comprises the steps of uniformly scattering a Yuhua stone aggregate on a primarily solidified concrete base 3-5 h after concrete pouring; and then, carrying out sleeking and levelling. The concrete comprises the following raw materials: cement, waste residues of glass, emery, marble powder, epoxy resin and water, wherein the weight ratio of cement to waste residues of glass to emery to marble powder to epoxy resin to water is 35 to 80 to 75 to 50 to 10 to 17. Construction of the floor is simple, the cost is low, and the obtained floor is abrasion-resistant and environment-friendly, and is long in service life.
Description
Technical field
The invention belongs to the realm of building construction, be specifically related to one terrazzo concrete terrace and manufacture method thereof.
Background technology
Terrace is the material be layed on ground, requires to have certain strength and stiffness, and has warming, wear-resisting performance.It is maximum that concrete has become current application quantity, and the building structural materials that the scope of application is the widest, according to statistics, China's concrete output in 2012, up to 12-13 hundred million m3, accounts for about 40% of Gross World Product.But its ubiquitous easy-weathering cracking, dusting, the defect such as not wear-resisting are also perplex a people's difficult problem, and receive common concern all the time.Although cause the reason of this phenomenon to be many-sided, in fact affect and reduce result of use and the life-span of terrazzo concrete terrace.
Summary of the invention
The object of the present invention is to provide one terrazzo concrete terrace and manufacture method thereof, solve current traditional wash floor construction cost high, easily ftractureed drum equivalent risk, makes terrazzo concrete short for application life.
For achieving the above object, the present invention adopts following technical scheme:
The manufacture method of one terrazzo concrete terrace, described terrace is 3-5h after concreting, is evenly shed by Yuhuatai colorful pebble aggregate in the concrete foundation of initial set, and it is floating then to carry out receipts light.
Described method concrete steps comprise as follows:
(1) after substrate surface being cleaned out, by basic unit's element ground grinding process, make that it is smooth, not ghost, bubble-free;
(2) at substrate surface coating interleaving agent;
(3) by concreting in basic unit, with watering with floating, shake simultaneously slurry even to concrete water bleeding;
(4) 3-5h after concreting, pin steps on sunken 4-5mm, and when the Yuhuatai colorful pebble aggregate chosen, is evenly shed in concrete foundation after becoming initial set state without bleeding by surface, then carry out receipts light with finisher floating, wait aquation is complete;
(5) complete in 6-12h at terrace and carry out maintenance with maintenance wax, carry out sanding and polishing process again after 1 week, make ground present mirror effect.
Described concrete comprises following raw material: cement, glass waste residue, diamond dust, marble powder, epoxy resin, water; Each raw material weight ratio is: 35:80:75:50:10:17.
Described interleaving agent comprises following parts by weight raw material: Yellow Fructus Gardeniae juice 15-26 part, silicone oil 20-25 part, French chalk 16-19 part, emulsifier 10-15 part.
The invention has the advantages that: traditional terrazzo concrete terrace is after concreting completes, operation is carried out in the above again after curing time reaches, construction forms ink terrace, which not only adds floor construction cost, also making concrete become secondary builds shaping, considerably increase concrete cracking, play the risk of drum, finally cause terrazzo concrete short for application life, and the construction method that the present invention adopts is simple, construction costs is low, obtain terrace can not ftracture, play drum, application life than traditional ground plateau length 2-3 doubly.
Detailed description of the invention
embodiment 1
(1) after substrate surface being cleaned out, by basic unit's element ground grinding process, make that it is smooth, not ghost, bubble-free;
(2) at substrate surface coating interleaving agent;
(3) by concreting in basic unit, with watering with floating, shake simultaneously slurry even to concrete water bleeding;
(4) 4h after concreting, pin steps on sunken 4mm, and when the Yuhuatai colorful pebble aggregate chosen, is evenly shed in concrete foundation after becoming initial set state without bleeding by surface, then carry out receipts light with finisher floating, wait aquation is complete;
(5) complete in 8h at terrace and carry out maintenance with maintenance wax, carry out sanding and polishing process again after 1 week, make ground present mirror effect.
Described concrete comprises following raw material: cement, glass waste residue, diamond dust, marble powder, epoxy resin, water; Each raw material weight ratio is: 35:80:75:50:10:17.
Described interleaving agent contains following parts by weight raw material: 20 parts, Yellow Fructus Gardeniae juice, silicone oil 23 parts, French chalk 17 parts, emulsifier 13 parts.
embodiment 2
(1) after substrate surface being cleaned out, by basic unit's element ground grinding process, make that it is smooth, not ghost, bubble-free;
(2) at substrate surface coating interleaving agent;
(3) by concreting in basic unit, with watering with floating, shake simultaneously slurry even to concrete water bleeding;
(4) 3h after concreting, pin steps on sunken 5mm, and when the Yuhuatai colorful pebble aggregate chosen, is evenly shed in concrete foundation after becoming initial set state without bleeding by surface, then carry out receipts light with finisher floating, wait aquation is complete;
(5) complete in 6h at terrace and carry out maintenance with maintenance wax, carry out sanding and polishing process again after 1 week, make ground present mirror effect.
Described concrete comprises following raw material: cement, glass waste residue, diamond dust, marble powder, epoxy resin, water; Each raw material weight ratio is: 35:80:75:50:10:17.
Described interleaving agent comprises following parts by weight raw material: 15 parts, Yellow Fructus Gardeniae juice, silicone oil 20 parts, French chalk 16 parts, emulsifier 10 parts.
embodiment 3
(1) after substrate surface being cleaned out, by basic unit's element ground grinding process, make that it is smooth, not ghost, bubble-free;
(2) at substrate surface coating interleaving agent;
(3) by concreting in basic unit, with watering with floating, shake simultaneously slurry even to concrete water bleeding;
(4) 5h after concreting, pin steps on sunken 5mm, and when the Yuhuatai colorful pebble aggregate chosen, is evenly shed in concrete foundation after becoming initial set state without bleeding by surface, then carry out receipts light with finisher floating, wait aquation is complete;
(5) complete in 12h at terrace and carry out maintenance with maintenance wax, carry out sanding and polishing process again after 1 week, make ground present mirror effect.
Described concrete comprises following raw material: cement, glass waste residue, diamond dust, marble powder, epoxy resin, water; Each raw material weight ratio is: 35:80:75:50:10:17.
Described interleaving agent comprises following parts by weight raw material: 26 parts, Yellow Fructus Gardeniae juice, silicone oil 25 parts, French chalk 19 parts, emulsifier 15 parts.
The foregoing is only preferred embodiment of the present invention, all equalizations done according to the present patent application the scope of the claims change and modify, and all should belong to covering scope of the present invention.
Claims (4)
1. the manufacture method of one terrazzo concrete terrace, is characterized in that: described terrace is 3-5h after concreting, is evenly shed by Yuhuatai colorful pebble aggregate in the concrete foundation of initial set, and it is floating then to carry out receipts light.
2. the manufacture method of one terrazzo concrete terrace according to claim 1, is characterized in that: described method concrete steps comprise as follows:
(1) after substrate surface being cleaned out, by basic unit's element ground grinding process, make that it is smooth, not ghost, bubble-free;
At substrate surface coating interleaving agent;
(2) by concreting in basic unit, with watering with floating, shake simultaneously slurry even to concrete water bleeding;
(3) 3-5h after concreting, pin steps on sunken 4-5mm, and when the Yuhuatai colorful pebble aggregate chosen, is evenly shed in concrete foundation after becoming initial set state without bleeding by surface, then carry out receipts light with finisher floating, wait aquation is complete;
(4) complete in 6-12h at terrace and carry out maintenance with maintenance wax, carry out sanding and polishing process again after 1 week, make ground present mirror effect.
3. the manufacture method of one terrazzo concrete terrace according to claim 1, is characterized in that: described concrete comprises following raw material: cement, glass waste residue, diamond dust, marble powder, epoxy resin, water; Each raw material weight ratio is: 35:80:75:50:10:17.
4. the manufacture method of one terrazzo concrete terrace according to claim 1, is characterized in that: described interleaving agent comprises following parts by weight raw material: Yellow Fructus Gardeniae juice 15-26 part, silicone oil 20-25 part, French chalk 16-19 part, emulsifier 10-15 part.