CN105504438A - Anticorrosive and antibacterial fishing net - Google Patents
Anticorrosive and antibacterial fishing net Download PDFInfo
- Publication number
- CN105504438A CN105504438A CN201510978612.2A CN201510978612A CN105504438A CN 105504438 A CN105504438 A CN 105504438A CN 201510978612 A CN201510978612 A CN 201510978612A CN 105504438 A CN105504438 A CN 105504438A
- Authority
- CN
- China
- Prior art keywords
- fishing net
- minutes
- powder
- epoxy resin
- corrosive antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosive and antibacterial fishing net. The anticorrosive and antibacterial fishing net is prepared from following components: polyethylene fibers, bamboo powder, waste PCB powder, an epoxy resin adhesive film, calcium carbonate powder, dibutyl phthalate and calcium stearate. According to the prepared fishing net, a processing technology is simple, the polyethylene fibers are taken as the raw material for processing, the cost of the fishing net is reduced greatly, the performance of the prepared fishing net is improved greatly through modification processing performed on the polyethylene fibers in advance, the anticorrosive and antibacterial capacity of the fishing net can be improved greatly through adoption of the waste PCB powder and the bamboo powder, and the service life of the fishing net is prolonged accordingly; with addition of the processed epoxy resin adhesive film, the compatibility of the components can be improved, and the combination property of the fishing net can be enhanced; the fishing net has excellent tensile strength and wear resistance.
Description
Technical field
The present invention relates to fishing gear field, particularly relate to a kind of anti-corrosive antibacterial fishing net.
Background technology
Fishing lines refers to the line that braiding mesh sheet and the diameter tying net fishing gear are less than 4 millimeters, is the main raw making fishing net.Present fishing lines mainly uses nylon raw material to prepare, but nylon complete processing is complicated, and to temperature, humidity requirement harshness, yield rate is low, and nylon cost is higher, and water-intake rate is also higher, causes fishing net perishable; The fishing net of other materials existing, anti-corrosive antibacterial ability, the life-span is low.
Summary of the invention
The object of this invention is to provide a kind of anti-corrosive antibacterial fishing net, be achieved through the following technical solutions:
A kind of anti-corrosive antibacterial fishing net, is made up of following composition: polyethylene fibre 80 parts, 1 part, bamboo powder, waste PCB powder 0.5 part, 15 parts, epoxy resin glued membrane, calcium carbonate powders 0.5 part, dibutyl phthalate 5 parts, calcium stearate 1 part by weight.
Further, described polyethylene fibre is through modification in advance: by the mixed in hydrochloric acid of the phenylformic acid of 1% concentration and 10% concentration, then put in above-mentioned mixing solutions by polyethylene fibre, be heated to 65-70 DEG C, continue after 15 minutes, filter, dry.
Further, described waste PCB powder is through pre-treatment: put into by PCB powder after boiling 30 minutes in the sodium hydroxide solution of 1.5% concentration, filters, is washed to neutrality, dry.
Further, described epoxy resin glued membrane is through pre-treatment: the dodecyltrimethoxysilane Homogeneous phase mixing under alkaline environment by epoxy resin glued membrane and weight part being 0.1 part, be heated to 260 DEG C, continuing after 15 minutes, starting Slow cooling, when being cooled to 155 DEG C, be incubated 15 minutes, continue to be cooled to 128 DEG C, be incubated 30 minutes, till last cool to room temperature.
Further, the methyl methacrylate being 0.2 part by described bamboo powder and weight part carries out Hybrid Heating process 10 minutes.
Further, described calcium carbonate powders first adopts 1.5% concentration carboxylic acid washing outside surface, then carries out drying.
The invention has the beneficial effects as follows: the fishing net complete processing that the present invention makes is simple, polyethylene fibre is adopted to process as raw material, greatly reduce the price of fishing net, by carrying out modification in advance to polyethylene fibre, greatly improve the performance of the fishing net produced, by adopting treated waste and old pcb board powder to coordinate with bamboo powder, the anti-corrosive antibacterial ability of fishing net can greatly be improved, thus extend the work-ing life of fishing net; By adding treated epoxy resin glued membrane, the consistency between each composition can be improved, increasing the over-all properties of fishing net; Fishing net of the present invention has excellent tensile strength and wear resistance.
Embodiment
A kind of anti-corrosive antibacterial fishing net, is made up of following composition: polyethylene fibre 80 parts, 1 part, bamboo powder, waste PCB powder 0.5 part, 15 parts, epoxy resin glued membrane, calcium carbonate powders 0.5 part, dibutyl phthalate 5 parts, calcium stearate 1 part by weight.
Further, described polyethylene fibre is through modification in advance: by the mixed in hydrochloric acid of the phenylformic acid of 1% concentration and 10% concentration, then put in above-mentioned mixing solutions by polyethylene fibre, be heated to 65-70 DEG C, continue after 15 minutes, filter, dry.
Further, described waste PCB powder is through pre-treatment: put into by PCB powder after boiling 30 minutes in the sodium hydroxide solution of 1.5% concentration, filters, is washed to neutrality, dry.
Further, described epoxy resin glued membrane is through pre-treatment: the dodecyltrimethoxysilane Homogeneous phase mixing under alkaline environment by epoxy resin glued membrane and weight part being 0.1 part, be heated to 260 DEG C, continuing after 15 minutes, starting Slow cooling, when being cooled to 155 DEG C, be incubated 15 minutes, continue to be cooled to 128 DEG C, be incubated 30 minutes, till last cool to room temperature.
Further, the methyl methacrylate being 0.2 part by described bamboo powder and weight part carries out Hybrid Heating process 10 minutes.
Further, described calcium carbonate powders first adopts 1.5% concentration carboxylic acid washing outside surface, then carries out drying.
A kind of making method of anti-corrosive antibacterial fishing net is:
1) following composition is taken by weight: polyethylene fibre 80 parts, 1 part, bamboo powder, waste PCB powder 0.5 part, 15 parts, epoxy resin glued membrane, calcium carbonate powders 0.5 part, dibutyl phthalate 5 parts, calcium stearate 1 part;
2) mixed after treatment by above-mentioned raw materials and add in forcing machine, forcing machine one section of temperature is 200 DEG C, and two sections of temperature are 220 DEG C, and three sections of temperature are 225 DEG C, and latter end temperature is 230 DEG C; 3) by 2) Raw adds in spray silk case, uses spinning appts to carry out wire drawing, then carry out drawing-off, then dry at 85-90 DEG C, then uses wind up roll to carry out winding collection.
Claims (6)
1. an anti-corrosive antibacterial fishing net, it is characterized in that, be made up of following composition by weight: polyethylene fibre 80 parts, 1 part, bamboo powder, waste PCB powder 0.5 part, 15 parts, epoxy resin glued membrane, calcium carbonate powders 0.5 part, dibutyl phthalate 5 parts, calcium stearate 1 part.
2. a kind of anti-corrosive antibacterial fishing net according to claim 1, it is characterized in that, described polyethylene fibre is through modification in advance: by the mixed in hydrochloric acid of the phenylformic acid of 1% concentration and 10% concentration, again polyethylene fibre is put in above-mentioned mixing solutions, be heated to 65-70 DEG C, continue after 15 minutes, filter, dry.
3. a kind of anti-corrosive antibacterial fishing net according to claim 1, it is characterized in that, described waste PCB powder is through pre-treatment: put into by PCB powder after boiling 30 minutes in the sodium hydroxide solution of 1.5% concentration, filters, is washed to neutrality, dry.
4. a kind of anti-corrosive antibacterial fishing net according to claim 1, it is characterized in that, described epoxy resin glued membrane is through pre-treatment: the dodecyltrimethoxysilane Homogeneous phase mixing under alkaline environment by epoxy resin glued membrane and weight part being 0.1 part, is heated to 260 DEG C, continues after 15 minutes, start Slow cooling, when being cooled to 155 DEG C, being incubated 15 minutes, continuing to be cooled to 128 DEG C, be incubated 30 minutes, till last cool to room temperature.
5. a kind of anti-corrosive antibacterial fishing net according to claim 1, is characterized in that, the methyl methacrylate being 0.2 part by described bamboo powder and weight part carries out Hybrid Heating process 10 minutes.
6. a kind of anti-corrosive antibacterial fishing net according to claim 1, is characterized in that, described calcium carbonate powders first adopts 1.5% concentration carboxylic acid washing outside surface, then carries out drying.