CN105505064A - White water-based alkali-resistant sealing primer and preparation method thereof - Google Patents
White water-based alkali-resistant sealing primer and preparation method thereof Download PDFInfo
- Publication number
- CN105505064A CN105505064A CN201610031975.XA CN201610031975A CN105505064A CN 105505064 A CN105505064 A CN 105505064A CN 201610031975 A CN201610031975 A CN 201610031975A CN 105505064 A CN105505064 A CN 105505064A
- Authority
- CN
- China
- Prior art keywords
- alkali
- resistant sealing
- parts
- water
- white water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a white water-based alkali-resistant sealing primer and a preparation method thereof. The sealing primer and the preparation method have the beneficial effects that after-tack can not be caused when boards made from magnesite materials are stacked after being brushed with the white water-based alkali-resistant sealing primer by adding cellulose ether, a thickening agent, a film-forming additive and other substances to alkali-resistant sealing emulsion and regulating the ratio; the white water-based alkali-resistant sealing primer is low in formula cost, has very strong after-tack resistance, alkali resistance, sealability and freeze-thaw stability, can achieve the waterproof and alkali resistant effects and avoids the problem of after-tack in the production processes of the boards made from magnesite materials; the preparation method of the white water-based alkali-resistant sealing primer is simple, is easy to implement and has very high practicability.
Description
Technical field
The present invention relates to magnesia cement board making field, particularly relate to a kind of white water-borne alkali-resistant sealing primer being applied to magnesia cement plate and preparation method thereof.
Background technology
Magnesia cement sheet material be with the light burnt powder of calcined magnesite stone gained or with the ashes of low temperature calcination rhombspar gained (main component is for MgO) for jointing compound, add the water-soluble magnesium salts such as magnesium chloride hexahydrate (MgCL26H2O), then add that water obtains.Generally need to be coated with one deck alkali-resistant sealing primer at magnesia cement plate outside surface, alkali-resistant sealing primer plays alkali resistant, closed effect, and it is closed the alkali resistant of magnesia cement sheet material and plays good effect.Alkali resistant primary coat kind is in the market many, but most of alkali-resistant primer is when being applied in magnesite material sheet material, and it can cause when carrying out well stacking after-tack in closed, maintenance, makes magnesia cement sheet material be bonded in one piece, does not reach desirable effect.
Therefore, prior art has yet to be improved and developed.
Summary of the invention
In view of above-mentioned the deficiencies in the prior art, the object of the present invention is to provide a kind of white water-borne alkali-resistant sealing primer and preparation method thereof, to be intended to solve in prior art after alkali-resistant sealing primer brushing is on magnesite material sheet material, can cause during windrow of going forward side by side buttress and after-tack, magnesia cement sheet material is made to be bonded in one piece, divide meeting to destroy paint film and sheet material by force, do not reach the problem of ideal effect.
Technical scheme of the present invention is as follows:
A kind of white water-borne alkali-resistant sealing primer, wherein, percentage, comprising:
Alkali resistant sealing emulsion 300-500 part;
Ether of cellulose 0.5-1 part;
Wetting agent 0.5-1 part;
Defoamer 0.5-1 part;
Thickening material 1-5 part;
Sterilant 0.5-1 part;
Frostproofer 10-50 part;
Film coalescence aid 0.5-12 part;
Water 475-645 part;
Described alkali resistant sealing emulsion is self-crosslinking acrylic emulsion; Described wetting agent is nonylphenol class wetting agent; Described defoamer is metal soap defoamer; Described thickening material is alkali swelling type thickening material; Described sterilant is Kathon CG series bactericidal agent; Described frostproofer is alcohols frostproofer; Described water is deionized water.
Described white water-borne alkali-resistant sealing primer, wherein, the model of described wetting agent is the CF-10 of Tao Shi; The model of described defoamer is the NXZ of Nuo Puke; The model of described thickening material is the TT935 of Tao Shi; The model of described sterilant is the LXE of Tao Shi; Described frostproofer is any one in ethylene glycol or propylene glycol.
Described white water-borne alkali-resistant sealing primer, wherein, percentage, comprising:
Alkali resistant sealing emulsion 300 parts;
Ether of cellulose 0.5 part;
Wetting agent 0.5 part;
Defoamer 0.5 part;
Thickening material 1 part;
0.5 part, sterilant;
Frostproofer 10 parts;
Film coalescence aid 0.5 part;
475 parts, water.
Described white water-borne alkali-resistant sealing primer, wherein, percentage, comprising:
Alkali resistant sealing emulsion 500 parts;
Ether of cellulose 1 part;
Wetting agent 1 part;
Defoamer 1 part;
Thickening material 5 parts;
1 part, sterilant;
Frostproofer 50 parts;
Film coalescence aid 12 parts;
645 parts, water.
Described white water-borne alkali-resistant sealing primer, wherein, percentage, comprising:
Alkali resistant sealing emulsion 400 parts;
Ether of cellulose 0.75 part;
Wetting agent 0.75 part;
Defoamer 0.75 part;
Thickening material 3 parts;
0.75 part, sterilant;
Frostproofer 30 parts;
Film coalescence aid 6 parts;
550 parts, water.
A making method for white water-borne alkali-resistant sealing primer described above, wherein, comprises the following steps:
First water and dispersion agent are joined in coating cylinder, and be under the condition of 500r/min at rotating speed, progressively add ether of cellulose, wetting agent, defoamer, thickening material and frostproofer, stir 10min; Add alkali resistant sealing emulsion again, and be stir 10min under the condition of 400r/min at rotating speed; Finally add sterilant and film coalescence aid again, and to remain on rotating speed be stir 5min under the condition of 400r/min, obtained described white water-borne alkali-resistant sealing primer.
Beneficial effect: a kind of white water-borne alkali-resistant sealing primer of the present invention and preparation method thereof, it by adding the materials such as ether of cellulose, thickening material and film coalescence aid in alkali resistant sealing emulsion, and adjust its proportioning, magnesite material sheet material can not be caused when brushing and going forward side by side windrow buttress after described white water-borne alkali-resistant sealing primer and after-tack.The formulation cost of white water-borne alkali-resistant sealing primer of the present invention is low, it has extremely strong anti-after tackiness, alkali-resistivity, closure and freeze-thaw stability, and can play waterproof and alkali resistant effect, that avoids again magnesite material production process of plate after-tacks problem; And the making method of white water-borne alkali-resistant sealing primer of the present invention is simple and easy to realize, and has high practicality.
Embodiment
The invention provides a kind of white water-borne alkali-resistant sealing primer and preparation method thereof, for making object of the present invention, technical scheme and effect clearly, clearly, the present invention is described in more detail below.Should be appreciated that specific embodiment described herein only in order to explain the present invention, be not intended to limit the present invention.
In prior art, common alkali-resistant sealing primer is not added with the material such as ether of cellulose and thickening material, and its brushing is on magnesite material sheet material, and magnesite material sheet material can cause when carrying out stacking and after-tack, and magnesite material sheet material namely can be caused to be bonded together.The invention provides a kind of white water-borne alkali-resistant sealing primer, it is in specialized application magnesite material sheet material, and effectively can solve its problem of after-tacking.Particularly, percentage, white water-borne alkali-resistant sealing primer of the present invention comprises: alkali resistant sealing emulsion 300-500 part; Ether of cellulose 0.5-1 part; Wetting agent 0.5-1 part; Defoamer 0.5-1 part; Thickening material 1-5 part; Sterilant 0.5-1 part; Frostproofer 10-50 part; Film coalescence aid 0.5-12 part; Water 475-645 part.
In the present invention, described alkali resistant sealing emulsion is self-crosslinking acrylic emulsion, and it has good alkali resistant and sealing process, and as the prime cost of described white water-borne alkali-resistant sealing primer, its parts by weight added in this component are 300-500 part.
In preferred embodiment; the present invention is by adding ether of cellulose; after it dissolves in water; as a kind of protective colloid; " parcel " lives the particles such as kaolin of the present invention, titanium dioxide; and form one deck lubricant film at its outside surface, and can stable existence, also improve the slipping of material described in the present invention in the mobility and painting process of whipping process.Preferably, that ether of cellulose of the present invention adopts is Natvosol (HEC), it is a kind of white or faint yellow, tasteless, nontoxic threadiness or pulverulent solids, be prepared from through etherification reaction by alkali cellulose and oxyethane (or chloroethanol), it can form a lubricant film at material surfaces such as kaolin, can stable existence.
Wetting agent is by reducing its surface tension or interfacial tension, makes water or other substance be deployed in solid materials on the surface, or penetrates its surface, and material wetting for solid materials.Wetting agent described in the present invention is preferably nonylphenol class wetting agent, and more preferably, the present invention's wetting agent used is the CF-10 of Tao Shi.
Defoamer is also known as foam killer, and it is applied in processes process, produces or eliminate to produce foam for suppressing foam, maintains the stability of production technique.In preferred embodiment, defoamer of the present invention is metal soap defoamer.Preferably, the model of described defoamer is the NXZ of Nuo Puke.
Thickening material is a kind of auxiliary rheological agents, not only can make coating thickening, prevents from occurring sagging phenomenon in construction, and can give mechanical property and the package stability of coating excellence.Because in the present invention to add the parts by weight of water many, so add the problem that thickening material effectively can improve its differences in viscosity.Preferably, described thickening material is alkali swelling type thickening material, and more specifically, the model of described thickening material is the TT935 of Tao Shi.
Sterilant can effectively suppress or eliminate the materials such as the fungus and bacterium in white water-borne alkali-resistant sealing primer of the present invention, prevents it from going bad.In the present embodiment, described sterilant is Kathon CG series bactericidal agent; Preferably, the model of described sterilant is the LXE of Tao Shi.
The material that frostproofer can prevent the moisture in material from freezing at low temperatures, the white water-borne alkali-resistant sealing primer in the present invention is added with more water, and therefore adding frostproofer can effectively prevent it from freezing into block at low temperatures, the problem that cannot brush.Particularly, described frostproofer is alcohols frostproofer, and preferably, it can be any one in ethylene glycol or propylene glycol.
Preferably, the water added in the present invention is deionized water.
In addition, the present invention also provides a kind of making method of white water-borne alkali-resistant sealing primer described above, wherein, comprises the following steps:
First water and dispersion agent are joined in coating cylinder, and be under the condition of 500r/min at rotating speed, progressively add ether of cellulose, wetting agent, defoamer, thickening material and frostproofer, stir 10min; Add alkali resistant sealing emulsion again, and be stir 10min under the condition of 400r/min at rotating speed; Finally add sterilant and film coalescence aid again, and to remain on rotating speed be stir 5min under the condition of 400r/min, obtained described white water-borne alkali-resistant sealing primer.Certainly, the material added shows situation and determines, such as, when not adding defoamer in component, then without the need to being added by defoamer.
Below by several specific embodiment, the present invention program is further elaborated:
Embodiment one
In the present embodiment, described white water-borne alkali-resistant sealing primer, wherein percentage, comprising: alkali resistant sealing emulsion 300 parts; Ether of cellulose 0.5 part; Wetting agent 0.5 part; Defoamer 0.5 part; Thickening material 1 part; 0.5 part, sterilant; Frostproofer 10 parts; Film coalescence aid 0.5 part; 475 parts, water.Described wetting agent is nonylphenol class wetting agent; The model of described titanium dioxide is Du Pont R706; Described frostproofer is ethylene glycol.
Making step: first water and dispersion agent are joined in coating cylinder, and be under the condition of 500r/min at rotating speed, progressively add frostproofer, titanium dioxide and thickening material, stir 10min; Add alkali resistant sealing emulsion again, and be stir 10min under the condition of 400r/min at rotating speed; Finally add sterilant and film coalescence aid again, and to remain on rotating speed be stir 5min under the condition of 400r/min, obtained described white water-borne alkali-resistant sealing primer.
By the white water-borne alkali-resistant sealing primer that the present embodiment is obtained, it has extremely strong anti-after tackiness, alkali-resistivity, closure, freeze-thaw stability, can play waterproof and alkali resistant effect, and that avoids again producing in stacking procedure after-tacks problem, the production process of making method of the present invention is simple, successful.
Embodiment two
In the present embodiment, described white water-borne alkali-resistant sealing primer, its percentage, comprising: alkali resistant sealing emulsion 500 parts; Ether of cellulose 1 part; Wetting agent 1 part; Defoamer 1 part; Thickening material 5 parts; 1 part, sterilant; Frostproofer 50 parts; Film coalescence aid 12 parts; 645 parts, water.Described alkali resistant sealing emulsion is self-crosslinking acrylic emulsion; Described ether of cellulose is hydroxyethyl ether cellulose; Described wetting agent is nonylphenol class wetting agent; Described defoamer is metal soap defoamer; Described thickening material is alkali swelling type thickening material; Described sterilant is Kathon CG series bactericidal agent; Described frostproofer is alcohols frostproofer; Described water is deionized water.
Making step: first water and dispersion agent are joined in coating cylinder, and be under the condition of 500r/min at rotating speed, progressively add ether of cellulose, wetting agent, defoamer, thickening material and frostproofer, stir 10min; Add alkali resistant sealing emulsion again, and be stir 10min under the condition of 400r/min at rotating speed; Finally add sterilant and film coalescence aid again, and to remain on rotating speed be stir 5min under the condition of 400r/min, obtained described white water-borne alkali-resistant sealing primer.
By the white water-borne alkali-resistant sealing primer that the present embodiment is obtained, it has extremely strong anti-after tackiness, alkali-resistivity, closure, freeze-thaw stability, can play waterproof and alkali resistant effect, and that avoids again producing in stacking procedure after-tacks problem, the production process of making method of the present invention is simple, successful.
Embodiment three
In the present embodiment, described white water-borne alkali-resistant sealing primer, its percentage, comprising: alkali resistant sealing emulsion 400 parts; Ether of cellulose 0.75 part; Wetting agent 0.75 part; Defoamer 0.75 part; Thickening material 3 parts; 0.75 part, sterilant; Frostproofer 30 parts; Film coalescence aid 6 parts; 550 parts, water.Described alkali resistant sealing emulsion is self-crosslinking acrylic emulsion; Described ether of cellulose is hydroxyethyl ether cellulose; Described wetting agent is nonylphenol class wetting agent; Described defoamer is metal soap defoamer; Described thickening material is alkali swelling type thickening material; Described sterilant is Kathon CG series bactericidal agent; Described frostproofer is alcohols frostproofer; Described water is deionized water.
Making step: first water and dispersion agent are joined in coating cylinder, and be under the condition of 500r/min at rotating speed, progressively add ether of cellulose, wetting agent, defoamer, thickening material and frostproofer, stir 10min; Add alkali resistant sealing emulsion again, and be stir 10min under the condition of 400r/min at rotating speed; Finally add sterilant and film coalescence aid again, and to remain on rotating speed be stir 5min under the condition of 400r/min, obtained described white water-borne alkali-resistant sealing primer.
By the white water-borne alkali-resistant sealing primer that the present embodiment is obtained, it has extremely strong anti-after tackiness, alkali-resistivity, closure, freeze-thaw stability, can play waterproof and alkali resistant effect, and that avoids again producing in stacking procedure after-tacks problem, the production process of making method of the present invention is simple, successful.
In sum, a kind of white water-borne alkali-resistant sealing primer of the present invention and preparation method thereof, it by adding the materials such as ether of cellulose, thickening material and film coalescence aid in alkali resistant sealing emulsion, and adjust its proportioning, magnesite material sheet material can not be caused when brushing and going forward side by side windrow buttress after described white water-borne alkali-resistant sealing primer and after-tack.The formulation cost of white water-borne alkali-resistant sealing primer of the present invention is low, it has extremely strong anti-after tackiness, alkali-resistivity, closure and freeze-thaw stability, and can play waterproof and alkali resistant effect, that avoids again magnesite material production process of plate after-tacks problem; And the making method of white water-borne alkali-resistant sealing primer of the present invention is simple and easy to realize, and has high practicality.
Should be understood that, application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be improved according to the above description or convert, and all these improve and convert the protection domain that all should belong to claims of the present invention.
Claims (6)
1. a white water-borne alkali-resistant sealing primer, is characterized in that, percentage comprises:
Alkali resistant sealing emulsion 300-500 part;
Ether of cellulose 0.5-1 part;
Wetting agent 0.5-1 part;
Defoamer 0.5-1 part;
Thickening material 1-5 part;
Sterilant 0.5-1 part;
Frostproofer 10-50 part;
Film coalescence aid 0.5-12 part;
Water 475-645 part;
Described alkali resistant sealing emulsion is self-crosslinking acrylic emulsion; Described wetting agent is nonylphenol class wetting agent; Described defoamer is metal soap defoamer; Described thickening material is alkali swelling type thickening material; Described sterilant is Kathon CG series bactericidal agent; Described frostproofer is alcohols frostproofer; Described water is deionized water.
2. white water-borne alkali-resistant sealing primer according to claim 1, it is characterized in that, the model of described wetting agent is the CF-10 of Tao Shi; The model of described defoamer is the NXZ of Nuo Puke; The model of described thickening material is the TT935 of Tao Shi; The model of described sterilant is the LXE of Tao Shi; Described frostproofer is any one in ethylene glycol or propylene glycol.
3. white water-borne alkali-resistant sealing primer according to claim 2, is characterized in that percentage comprises:
Alkali resistant sealing emulsion 300 parts;
Ether of cellulose 0.5 part;
Wetting agent 0.5 part;
Defoamer 0.5 part;
Thickening material 1 part;
0.5 part, sterilant;
Frostproofer 10 parts;
Film coalescence aid 0.5 part;
475 parts, water.
4. white water-borne alkali-resistant sealing primer according to claim 2, is characterized in that percentage comprises:
Alkali resistant sealing emulsion 500 parts;
Ether of cellulose 1 part;
Wetting agent 1 part;
Defoamer 1 part;
Thickening material 5 parts;
1 part, sterilant;
Frostproofer 50 parts;
Film coalescence aid 12 parts;
645 parts, water.
5. white water-borne alkali-resistant sealing primer according to claim 2, is characterized in that percentage comprises:
Alkali resistant sealing emulsion 400 parts;
Ether of cellulose 0.75 part;
Wetting agent 0.75 part;
Defoamer 0.75 part;
Thickening material 3 parts;
0.75 part, sterilant;
Frostproofer 30 parts;
Film coalescence aid 6 parts;
550 parts, water.
6. the making method of white water-borne alkali-resistant sealing primer as described in any one of claim 1-2, is characterized in that, comprise the following steps:
First water and dispersion agent are joined in coating cylinder, and be under the condition of 500r/min at rotating speed, progressively add ether of cellulose, wetting agent, defoamer, thickening material and frostproofer, stir 10min; Add alkali resistant sealing emulsion again, and be stir 10min under the condition of 400r/min at rotating speed; Finally add sterilant and film coalescence aid again, and to remain on rotating speed be stir 5min under the condition of 400r/min, obtained described white water-borne alkali-resistant sealing primer.