CN105802410A - Waterproof acrylate coating and preparation method thereof - Google Patents
Waterproof acrylate coating and preparation method thereof Download PDFInfo
- Publication number
- CN105802410A CN105802410A CN201410847703.8A CN201410847703A CN105802410A CN 105802410 A CN105802410 A CN 105802410A CN 201410847703 A CN201410847703 A CN 201410847703A CN 105802410 A CN105802410 A CN 105802410A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- dispersant
- calcium carbonate
- titanium dioxide
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to a waterproof acrylate coating and a preparation method thereof. The waterproof acrylate coating is prepared through adding proper amounts of a high quality filler and assistants to a pure acrylate copolymer or a pure acrylate emulsion, and is a synthetic resin mono-component waterproof coating. The waterproof acrylate coating comprises, by weight, 10-20 parts of titanium dioxide, 20-30 parts of talcum powder, 20-30 parts of heavy calcium carbonate, 1-2 parts of a dispersant, 50-70 parts of an emulsion, and 10-20 parts of distilled water. The waterproof acrylate coating and the preparation method thereof are disclosed in the invention.
Description
Technical field:
The present invention relates to a kind of acrylate water-repellent paint and preparation method.
Background technology:
Acrylate waterproof paint is with pure acrylic acid ester copolymer or pure propionic ester emulsion, add appropriate high quality filler, auxiliary agent configuration form, belong to synthetic resin single-component waterproof coating material.Suitable in the buildings waterproof under the non-long-term Soaking environments such as roofing, metope, toilet bath room, basement, seepage control project；It is particularly well-suited to the roof waterproof engineering of light and thin shell structure, it is possible to be used as binding agent or exterior wall decorating coating.
Summary of the invention:
It is an object of the invention to provide a kind of acrylate water-repellent paint and preparation method.
Above-mentioned purpose is realized by following technical scheme:
OnePlant acrylate water-repellent paint, its composition includes: titanium dioxide, Pulvis Talci, ground calcium carbonate, dispersant, emulsion, distilled water, ratio of weight and number: titanium dioxide 10-20, Pulvis Talci 20-30, ground calcium carbonate 20-30, dispersant 1-2, emulsion 50-70, distilled water 10-20.
Described acrylate water-repellent paint, ratio of weight and number: titanium dioxide 10, Pulvis Talci 20, ground calcium carbonate 20, dispersant 1, emulsion 50, distilled water 10.
Described acrylate water-repellent paint, ratio of weight and number: titanium dioxide 20, Pulvis Talci 30, ground calcium carbonate 30, dispersant 2, emulsion 70, distilled water 20.
Described acrylate water-repellent paint, ratio of weight and number: percentage by weight: titanium dioxide 15, Pulvis Talci 15, ground calcium carbonate 15, dispersant 1.5, emulsion 60, distilled water 15.
A kind of preparation method of described acrylate water-repellent paint, by the titanium dioxide 10-20 of parts by weight, Pulvis Talci 20-30, ground calcium carbonate 20-30, dispersant 1-2, emulsion 50-70, distilled water 10-20 and surfactant carry out suction head tank after emulsifying, add initiator, to be triggered dose with another head tank of suction after water dissolution, both enter reactor in the way of dropping simultaneously and carry out polyreaction, reaction temperature controls at 70-85 degree, control rate of addition, its component reaction material is made to drip off at 3-3.5 hour, last insulation reaction 1-1.5h, make to react completely, then cool down, with ammonia, reactant liquor PH is modulated 7-8.
Beneficial effect:
1. the present invention has excellent weatherability, thermostability and ultra-violet resistance, and within the scope of-30 DEG C to 80 DEG C, performance is substantially unchanged, and good extending performance adapts to the craze and transfiguration of basal plane certain amplitude.Can allocating various color according to needs, waterproof layer has decoration and effect of heat insulation concurrently.Environmental protection, nonpoisonous and tasteless, free from environmental pollution, to person fanout free region.Easy construction, the duration is short, easy to maintenance.Can construct at moisture substrate, there is certain breathability.
Detailed description of the invention:
Embodiment 1:
A kind of acrylate water-repellent paint, its composition includes: titanium dioxide, Pulvis Talci, ground calcium carbonate, dispersant, emulsion, distilled water percentage by weight: titanium dioxide 10-20, Pulvis Talci 20-30, ground calcium carbonate 20-30, dispersant 1-2, emulsion 50-70, distilled water 10-20.
Embodiment 2:
Acrylate water-repellent paint percentage by weight according to embodiment 1: titanium dioxide 10, Pulvis Talci 20, ground calcium carbonate 20, dispersant 1, emulsion 50, distilled water 10.
Embodiment 3:
Acrylate water-repellent paint according to embodiment 1 or 2, percentage by weight: titanium dioxide 20, Pulvis Talci 30, ground calcium carbonate 30, dispersant 2, emulsion 70, distilled water 20.
Embodiment 4:
According to the acrylate water-repellent paint described in embodiment 1 or 2 or 3, percentage by weight: percentage by weight: titanium dioxide 15, Pulvis Talci 15, ground calcium carbonate 15, dispersant 1.5, emulsion 60, distilled water 15.
Embodiment 5:
The preparation method of the acrylate water-repellent paint according to embodiment 1 or 2 or 3 or 4, by titanium dioxide 10-20, Pulvis Talci 20-30, ground calcium carbonate 20-30, dispersant 1-2, emulsion 50-70, distilled water 10-20 and surfactant carry out suction head tank after emulsifying, add initiator, to be triggered dose with another head tank of suction after water dissolution, both enter reactor in the way of dropping simultaneously and carry out polyreaction, reaction temperature controls at 70-85 degree, control rate of addition, its component reaction material is made to drip off at 3-3.5 hour, last insulation reaction 1-1.5h, make to react completely, then cool down, with ammonia, reactant liquor PH is modulated 7-8.
Claims (5)
1. an acrylate water-repellent paint, its composition includes: titanium dioxide, Pulvis Talci, ground calcium carbonate, dispersant, emulsion, distilled water, it is characterized in that: ratio of weight and number: titanium dioxide 10-20, Pulvis Talci 20-30, ground calcium carbonate 20-30, dispersant 1-2, emulsion 50-70, distilled water 10-20.
2. acrylate water-repellent paint according to claim 1, is characterized in that: ratio of weight and number: titanium dioxide 10, Pulvis Talci 20, ground calcium carbonate 20, dispersant 1, emulsion 50, distilled water 10.
3. acrylate water-repellent paint according to claim 1, is characterized in that: ratio of weight and number: titanium dioxide 20, Pulvis Talci 30, ground calcium carbonate 30, dispersant 2, emulsion 70, distilled water 20.
4. acrylate water-repellent paint according to claim 1, is characterized in that: ratio of weight and number: percentage by weight: titanium dioxide 15, Pulvis Talci 15, ground calcium carbonate 15, dispersant 1.5, emulsion 60, distilled water 15.
5. the preparation method of the acrylate water-repellent paint that one of claim 1 or 2 or 3 or 4 is described, it is characterized in that: by the titanium dioxide 10-20 of parts by weight, Pulvis Talci 20-30, ground calcium carbonate 20-30, dispersant 1-2, emulsion 50-70, distilled water 10-20 and surfactant carry out suction head tank after emulsifying, add initiator, to be triggered dose with another head tank of suction after water dissolution, both enter reactor in the way of dropping simultaneously and carry out polyreaction, reaction temperature controls at 70-85 degree, control rate of addition, its component reaction material is made to drip off at 3-3.5 hour, last insulation reaction 1-1.5h, make to react completely, then cool down, with ammonia, reactant liquor PH is modulated 7-8.