CN106120366A - A kind of preparation technology of novel adhesion lining cloth - Google Patents
A kind of preparation technology of novel adhesion lining cloth Download PDFInfo
- Publication number
- CN106120366A CN106120366A CN201610507891.9A CN201610507891A CN106120366A CN 106120366 A CN106120366 A CN 106120366A CN 201610507891 A CN201610507891 A CN 201610507891A CN 106120366 A CN106120366 A CN 106120366A
- Authority
- CN
- China
- Prior art keywords
- cloth
- lining cloth
- preparation technology
- coating
- adhesion lining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the preparation technology of a kind of novel adhesion lining cloth, this preparation technology is configured by initial survey, slurry, powder point coating is processed, bake, cool down and rolling, product inspection and seven steps of packing prepare novel adhesion lining cloth.It is an advantage of the current invention that: the preparation technology of novel adhesion lining cloth of the present invention, by with dacron as raw material, use polyester filament water-jet weaving, with polyester filament as raw material, woven for base fabric, through water repellent resin aftershaping, there is the advantage that higher intensity, elastic recovery capability and mobility are strong, solve the conventional shortcomings such as water spraying intensity fault is many, cloth quality is unstable and of poor quality；And bakee operation by the hydrophilic treated of particular slurry, powder point and three times, make the adhesion lining cloth prepared have good bonding effect, after bonding with fabric, have soft, comfortable, well-pressed, shape-retaining ability is good, not modification after washing, and then the elastic force of adhesion lining cloth and intensity are all increased.
Description
Technical field
The invention belongs to textile technology field, particularly to the preparation technology of a kind of novel adhesion lining cloth.
Background technology
Lining cloth, with woven fabric, knitted fabric and non-weaving cloth as base fabric, carries out Special Finishing processing through special machinery, is used for
Clothing back boxing, trousers waist lining and medicated cap liner, play reinforcement, well-pressed grade acts on, is special garment accessories.
Along with the raising of people's living standard, the requirement to clothing is no longer limited only to attractive in appearance, but more focuses on clothes
The comfort of dress dress, especially adhesion lining cloth, although need not image planes material the most attractive in appearance, but, the performance of adhesion lining cloth own
Quality directly influence the quality of these clothing.
It is more generally to there is fabric defect in the common lining cloth that existing market is selected, as broken yarn, cotton knot, tear, three, intensity difference
Etc. factor, have a strong impact on the quality of lining cloth；This kind of lining cloth great majority use water repellent to process, and after gluing, viscosity effect is very poor no matter
Plain weave or twill are after water repellent processes, and regardless of water repellent grade, bonding effect is the most very poor.
Therefore, the preparation technology right and wrong of the novel adhesion lining cloth of a kind of bonding effect that can improve lining cloth and intensity are researched and developed
Often it is necessary.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of bonding effect that can improve lining cloth and the Novel sticky of intensity
Close the preparation technology of lining cloth.
For solving above-mentioned technical problem, the technical scheme is that the preparation technology of novel adhesion lining cloth, its innovative point
It is: comprise the following steps:
(1) initial survey: selection surface is without the dacron grey cloth of damaged spot, and tests, and is entered by grey cloth qualified for inspection
Next processes step；
(2) slurry configuration: use the polyenoic fatty compounds of group of polymerization to be configured to polyamide slurry；
(3) powder point coating processing: grey cloth qualified for initial survey is entered cloth with the speed of 15-25m/min, and is carried out slurry by coating machine
Powder point coating is processed, and described coating machine uses double roller and driven cloth-feeding device, and the painting of powder point processing coating by buncher
Amount of applying is for 24-27g/m2, and cloth surface temperature control during operation coating is at 130 DEG C-140 DEG C；
(4) bake: by after powder point coating grey cloth send into drying room bake, and described drying room be divided into three bakee districts: a district
Temperature is set as 154-158 DEG C, and two district's baking temperatures are 180-190 DEG C, and three district's baking temperatures are 190-200 DEG C, and bake
Time is as the criterion with the speed entering cloth；
(5) cooling, rolling: the grey cloth after baking uses chiller cooling to obtain lining cloth, and is rolled up by winding system
Take, and cut the diameter cut and be necessarily less than equal to 25cm, 100 meters of rolling or 50 meters of rolling；
(6) product inspection: take the sample of lining cloth, carries out instrument detection by national standard, surveys strong with YB090L type separation strength machine
Degree, peel strength controls in 15.16≤N≤27.79 by standard, and average strength is 21.56N；Survey with YGB201D formaldehyde tester
Content of formaldehyde, bioassay standard content of formaldehyde≤300mg/kg, pH value, between 4～9, makes lining cloth product quality reach country and use
The standard of family demand；
(7) packing: carry out being packed into lining cloth finished product by quality, product that outward appearance is the most qualified.
Further, the dacron in described step (1), use polyester filament water-jet weaving, be former with polyester filament
Material, woven for base fabric, through water repellent resin aftershaping；And the door width of selection grey cloth is 150-160cm or 125-130cm, terylene is long
The density of silk reaches required grammes per square metre according to the requirement of client and is as the criterion.
Further, in described step (2), the polyenoic fatty compounds of group of polymerization is ethylenediamine or diethylenetriamines.
It is an advantage of the current invention that: the preparation technology of novel adhesion lining cloth of the present invention, by with dacron as raw material, adopt
Use polyester filament water-jet weaving, with polyester filament as raw material, woven for base fabric, through water repellent resin aftershaping, have higher strong
Degree, elastic recovery capability and the strong advantage of mobility, solve that conventional water spraying intensity fault is many, cloth quality unstable and quality
The shortcomings such as difference；And bakee operation by the hydrophilic treated of particular slurry, powder point and three times, make the adhesion lining cloth prepared have
Well bonding effect, after bonding with fabric, has softness, comfortable, well-pressed, and shape-retaining ability is good, not modification after washing, and then makes to glue
Elastic force and the intensity of closing lining cloth all increase.
Detailed description of the invention
The following examples can make professional and technical personnel that the present invention is more fully understood, but the most therefore by this
Bright it is limited among described scope of embodiments.
Embodiment 1
The preparation technology of the present embodiment novel adhesion lining cloth, this preparation technology comprises the steps:
(1) initial survey: selecting surface without the dacron grey cloth of damaged spot, this dacron grey cloth uses polyester filament water spray to knit
Make, with polyester filament as raw material, woven for base fabric, through water repellent resin aftershaping；And the door width of selection grey cloth is 155cm, terylene
The density of long filament reaches required grammes per square metre according to the requirement of client and is as the criterion；And test, under grey cloth qualified for inspection is entered
One processes step；
(2) slurry configuration: use diethylenetriamines to be configured to polyamide slurry；
(3) powder point coating processing: grey cloth qualified for initial survey is entered cloth with the speed of 15m/min, and is carried out slurry powder by coating machine
Point coating processing, described coating machine uses double roller and is driven cloth-feeding device, and the coating of powder point processing coating by buncher
Amount is 27g/m2, and cloth surface temperature control during operation coating is at 140 DEG C；
(4) bake: by after powder point coating grey cloth send into drying room bake, and described drying room be divided into three bakee districts: a district
Temperature is set as 154 DEG C, and two district's baking temperatures are 180 DEG C, and three district's baking temperatures are 190 DEG C, and the time baked is to enter cloth
Speed is as the criterion；
(5) cooling, rolling: the grey cloth after baking uses chiller cooling to obtain lining cloth, and is rolled up by winding system
Take, and cut the diameter cut and be necessarily less than equal to 25cm, 100 meters of rolling；
(6) product inspection: take the sample of lining cloth, carries out instrument detection by national standard, surveys strong with YB090L type separation strength machine
Degree, peel strength controls in 15.16≤N≤27.79 by standard, and average strength is 21.56N；Survey with YGB201D formaldehyde tester
Content of formaldehyde, bioassay standard content of formaldehyde≤300mg/kg, pH value, between 4～9, makes lining cloth product quality reach country and use
The standard of family demand；
(7) packing: carry out being packed into lining cloth finished product by quality, product that outward appearance is the most qualified.
Embodiment 2
The preparation technology of the present embodiment novel adhesion lining cloth, this preparation technology comprises the steps:
(1) initial survey: selecting surface without the dacron grey cloth of damaged spot, this dacron grey cloth uses polyester filament water spray to knit
Make, with polyester filament as raw material, woven for base fabric, through water repellent resin aftershaping；And the door width of selection grey cloth is 127cm, terylene
The density of long filament reaches required grammes per square metre according to the requirement of client and is as the criterion；And test, under grey cloth qualified for inspection is entered
One processes step；
(2) slurry configuration: use ethylenediamine or diethylenetriamines to be configured to polyamide slurry；
(3) powder point coating processing: grey cloth qualified for initial survey is entered cloth with the speed of 25m/min, and is carried out slurry powder by coating machine
Point coating processing, described coating machine uses double roller and is driven cloth-feeding device, and the coating of powder point processing coating by buncher
Amount is 24g/m2, and cloth surface temperature control during operation coating is at 130 DEG C DEG C；
(4) bake: by after powder point coating grey cloth send into drying room bake, and described drying room be divided into three bakee districts: a district
Temperature is set as 158 DEG C, and two district's baking temperatures are 190 DEG C, and three district's baking temperatures are 200 DEG C, and the time baked is to enter cloth
Speed is as the criterion；
(5) cooling, rolling: the grey cloth after baking uses chiller cooling to obtain lining cloth, and is rolled up by winding system
Take, and cut the diameter cut and be necessarily less than equal to 25cm, 50 meters of rolling；
(6) product inspection: take the sample of lining cloth, carries out instrument detection by national standard, surveys strong with YB090L type separation strength machine
Degree, peel strength controls in 15.16≤N≤27.79 by standard, and average strength is 21.56N；Survey with YGB201D formaldehyde tester
Content of formaldehyde, bioassay standard content of formaldehyde≤300mg/kg, pH value, between 4～9, makes lining cloth product quality reach country and use
The standard of family demand；
(7) packing: carry out being packed into lining cloth finished product by quality, product that outward appearance is the most qualified.
Embodiment 3
The preparation technology of the present embodiment novel adhesion lining cloth, this preparation technology comprises the steps:
(1) initial survey: selecting surface without the dacron grey cloth of damaged spot, this dacron grey cloth uses polyester filament water spray to knit
Make, with polyester filament as raw material, woven for base fabric, through water repellent resin aftershaping；And the door width of selection grey cloth is 127cm, terylene
The density of long filament reaches required grammes per square metre according to the requirement of client and is as the criterion；And test, under grey cloth qualified for inspection is entered
One processes step；
(2) slurry configuration: use ethylenediamine or diethylenetriamines to be configured to polyamide slurry；
(3) powder point coating processing: grey cloth qualified for initial survey is entered cloth with the speed of 20m/min, and is carried out slurry powder by coating machine
Point coating processing, described coating machine uses double roller and is driven cloth-feeding device, and the coating of powder point processing coating by buncher
Amount is 25g/m2, and cloth surface temperature control during operation coating is at 135 DEG C；
(4) bake: by after powder point coating grey cloth send into drying room bake, and described drying room be divided into three bakee districts: a district
Temperature is set as 156 DEG C, and two district's baking temperatures are 185 DEG C, and three district's baking temperatures are 195 DEG C, and the time baked is to enter cloth
Speed is as the criterion；
(5) cooling, rolling: the grey cloth after baking uses chiller cooling to obtain lining cloth, and is rolled up by winding system
Take, and cut the diameter cut and be necessarily less than equal to 25cm, 50 meters of rolling；
(6) product inspection: take the sample of lining cloth, carries out instrument detection by national standard, surveys strong with YB090L type separation strength machine
Degree, peel strength controls in 15.16≤N≤27.79 by standard, and average strength is 21.56N；Survey with YGB201D formaldehyde tester
Content of formaldehyde, bioassay standard content of formaldehyde≤300mg/kg, pH value, between 4～9, makes lining cloth product quality reach country and use
The standard of family demand；
(7) packing: carry out being packed into lining cloth finished product by quality, product that outward appearance is the most qualified.
Following table is the preparation technology contrast with the preparation technology of tradition lining cloth of embodiment 1～3 novel adhesion lining cloth:
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Traditional handicraft | |
| Peel strength (N) | 18.92 | 24.79 | 27.72 | 15.16 |
| Content of formaldehyde (mg/kg) | 286 | 292 | 276 | 302 |
| Bond properties | Scrubbed bubble-free phenomenon | Scrubbed bubble-free phenomenon | Scrubbed bubble-free phenomenon | Scrubbed easily there is bubble phenomenon |
As can be seen from the above table, the preparation technology of embodiment 1-3 Novel lapping cloth is compared with traditional handicraft, and the adhesion lining cloth prepared has
Having good bonding effect, after bonding with fabric, have softness, comfortable, well-pressed, shape-retaining ability is good, not modification after washing, and then makes
Elastic force and the intensity of adhesion lining cloth all increase；And three embodiments are compared to each other, the adhesive lining that embodiment 3 is prepared into
The each performance parameter of cloth is optimal, thus embodiment 3 is most preferred embodiment.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The skill of the industry
The art personnel simply explanation it should be appreciated that the present invention is not restricted to the described embodiments, described in above-described embodiment and description
The principle of the present invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these
Changes and improvements both fall within scope of the claimed invention.Claimed scope by appending claims and
Its equivalent defines.
Claims (3)
1. the preparation technology of a novel adhesion lining cloth, it is characterised in that: comprise the following steps:
(1) initial survey: selection surface is without the dacron grey cloth of damaged spot, and tests, and is entered by grey cloth qualified for inspection
Next processes step；
(2) slurry configuration: use the polyenoic fatty compounds of group of polymerization to be configured to polyamide slurry；
(3) powder point coating processing: grey cloth qualified for initial survey is entered cloth with the speed of 15-25m/min, and is carried out slurry by coating machine
Powder point coating is processed, and described coating machine uses double roller and driven cloth-feeding device, and the painting of powder point processing coating by buncher
Amount of applying is for 24-27g/m2, and cloth surface temperature control during operation coating is at 130 DEG C-140 DEG C；
(4) bake: by after powder point coating grey cloth send into drying room bake, and described drying room be divided into three bakee districts: a district
Temperature is set as 154-158 DEG C, and two district's baking temperatures are 180-190 DEG C, and three district's baking temperatures are 190-200 DEG C, and bake
Time is as the criterion with the speed entering cloth；
(5) cooling, rolling: the grey cloth after baking uses chiller cooling to obtain lining cloth, and is rolled up by winding system
Take, and cut the diameter cut and be necessarily less than equal to 25cm, 100 meters of rolling or 50 meters of rolling；
(6) product inspection: take the sample of lining cloth, carries out instrument detection by national standard, surveys strong with YB090L type separation strength machine
Degree, peel strength controls in 15.16≤N≤27.79 by standard, and average strength is 21.56N；Survey with YGB201D formaldehyde tester
Content of formaldehyde, bioassay standard content of formaldehyde≤300mg/kg, pH value, between 4～9, makes lining cloth product quality reach country and use
The standard of family demand；
(7) packing: carry out being packed into lining cloth finished product by quality, product that outward appearance is the most qualified.
The preparation technology of novel adhesion lining cloth the most according to claim 1, it is characterised in that: washing in described step (1)
Synthetic fibre fabric, uses polyester filament water-jet weaving, with polyester filament as raw material, woven for base fabric, through water repellent resin aftershaping；And choosing
Being 150-160cm or 125-130cm with the door width of grey cloth, the density of polyester filament reaches required grammes per square metre according to the requirement of client
It is as the criterion.
The preparation technology of novel adhesion lining cloth the most according to claim 1, it is characterised in that: polymerization in described step (2)
Polyenoic fatty compounds of group be ethylenediamine or diethylenetriamines.