CN106192403A - A kind of natural mixed textile whole dye Antibacterial accessory ingredient - Google Patents

A kind of natural mixed textile whole dye Antibacterial accessory ingredient Download PDF

Info

Publication number
CN106192403A
CN106192403A CN201610536036.0A CN201610536036A CN106192403A CN 106192403 A CN106192403 A CN 106192403A CN 201610536036 A CN201610536036 A CN 201610536036A CN 106192403 A CN106192403 A CN 106192403A
Authority
CN
China
Prior art keywords
parts
oxide powder
natural
agent
accessory ingredient
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610536036.0A
Other languages
Chinese (zh)
Inventor
夏战利
崔颖
崔浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongshan Lyulang Additives Co Ltd
Original Assignee
Zhongshan Lyulang Additives Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongshan Lyulang Additives Co Ltd filed Critical Zhongshan Lyulang Additives Co Ltd
Priority to CN201610536036.0A priority Critical patent/CN106192403A/en
Publication of CN106192403A publication Critical patent/CN106192403A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a kind of natural mixed textile whole dye Antibacterial accessory ingredient, it is made up of the component of following mass fraction: corn starch solution 50 260 parts, nano-zinc oxide powder or cupric oxide powder 25 40 parts, pigment 10 18 parts, aqueous initiator 36 parts, natural antibacterial agent and 12 16 parts of the mixture of organic antibacterial agent, dispersant 37 parts, styrene-acrylic emulsion 14 18 parts, emulsifying agent 48 parts, the particle diameter of nano-zinc oxide powder or cupric oxide powder is 160 180nm.Dispersant is preferably disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate salt.Emulsifying agent is preferably dodecyl sodium sulfate.Product prepared by the present invention has the most superior anti-microbial property, is suitable for using at field of textiles, improves properties of product, advantageously reduce carrying capacity of environment, improve production efficiency, advantageously reduce production cost.

Description

A kind of natural mixed textile whole dye Antibacterial accessory ingredient
Technical field
The present invention relates to a kind of natural mixed textile whole dye Antibacterial accessory ingredient.
Background technology
Slurry makes sliver surface be coated with serous coat that is smooth, wear-resisting, pliable and tough and that have some strength, makes twining of sliver surface It is close to the trunk of sliver around fiber, reduces the coefficient of friction on sliver surface, make fraction slurries penetrate into yarn interior simultaneously, increase fibre Adhesion between dimension, improves the tensile strength of yarn, to adapt to the hightension in weaving process, middle beating, reduces broken end and carries High efficiency.
Spinning sizing agent develops into even to this day, can not meet wanting of various yarn variety and slashing technique Ask, traditional three big slurry system PVA, polyacrylic acid, modified starch, all there is various no defect.PVA is due in desizing After be present in serosity and be difficult to degrade, current employer's organization the most clearly proposes to lack in sizing technique with or without PVA, because of During the yarn sizing highly dense at high-grade ramuscule, the congenital high-tenacity of PVA becomes a kind of restraining factors on the contrary, many times Reduce loom efficiency.Acrylic size serous coat is too soft, and there is the risk that moisture absorption is glued again, and price is relatively costly.Degeneration is formed sediment Powder is brittle due to serous coat, limited to yarn adhesion so that it is although having environment-friendly advantage, but cannot individually make in starching With.
Textile auxiliary has indispensable important function to the product quality and surcharge that improve textile, and it is not only The various specific function of textile and style can be given, such as soft, wrinkle resistant, shrinkproof, waterproof, antibacterial, antistatic, fire-retardant etc., also may be used To improve dyeing and finishing technology, play and save the energy and reduce the effect of processing cost.The textile auxiliary entirety to promoting textile industry Level and the effect in Textile Chain it is critical that, but at present, natural mixed textile of the prior art is whole The antibacterial effect of dye Antibacterial accessory ingredient is unsatisfactory, and action time is shorter.
Summary of the invention
The problem existed for above-mentioned prior art, the invention provides a kind of natural mixed textile whole dye Antibacterial accessory ingredient, Prepared product has the most superior anti-microbial property, is suitable for using at field of textiles, improves properties of product, advantageously reduce Carrying capacity of environment, improves production efficiency, advantageously reduces production cost.
To achieve these goals, the technical solution used in the present invention is:
A kind of natural mixed textile whole dye Antibacterial accessory ingredient, is made up of the component of following mass fraction: corn starch solution 50-260 Part, nano-zinc oxide powder or cupric oxide powder 25-40 part, pigment 10-18 part, aqueous initiator 3-6 part, natural antibacterial agent with Mixture 12-16 part of organic antibacterial agent, dispersant 3-7 part, styrene-acrylic emulsion 14-18 part, emulsifying agent 4-8 part.
Preferably, it is made up of the component of following mass fraction: corn starch solution 80-200 part, nano-zinc oxide powder Or the mixing of cupric oxide powder 28-36 part, pigment 12-16 part, aqueous initiator 4-6 part, natural antibacterial agent and organic antibacterial agent Thing 13-15 part, dispersant 4-6 part, styrene-acrylic emulsion 15-17 part, emulsifying agent 5-7 part.
Any of the above-described scheme preferably, is made up of the component of following mass fraction: corn starch solution 140 parts, nanometer Zinc oxide powder or cupric oxide powder 32 parts, pigment 14 parts, aqueous initiator 5 parts, natural antibacterial agent are mixed with organic antibacterial agent Compound 14 parts, dispersant 5 parts, styrene-acrylic emulsion 16 parts, emulsifying agent 6 parts.
Preferably, described aqueous initiator is hydrogen peroxide, peracetic acid, sodium pyrosulfite, mistake to any of the above-described scheme At least one in sodium sulfate or Ammonium persulfate..
Preferably, the particle diameter of described nano-zinc oxide powder or cupric oxide powder is 160-180nm to any of the above-described scheme.
Preferably, described dispersant is disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate salt to any of the above-described scheme.
Preferably, described emulsifying agent is dodecyl sodium sulfate to any of the above-described scheme.Dodecyl sodium sulfate makes nanometer Zinc oxide powder or cupric oxide powder granule are uniformly dispersed.
Preferably, described organic antibacterial agent is sodium cocoate, TCC, methacrylic acid to any of the above-described scheme At least one in diethylamino ethyl ester or Lupenyl palmitate.
Any of the above-described scheme preferably, described natural antibacterial agent be in chitin, mustard, Oleum Ricini, Wasabia japonic (Euterma Wasabi) at least A kind of.
Nano-zinc oxide powder in the sun, especially under ultraviolet irradiation, can decomposite in water and air voluntarily The electronegative electronics (e-) moved freely, leaves the hole (h+) of positively charged simultaneously.This hole can be activated in air Oxygen becomes active oxygen, has extremely strong chemism, can with gas chromatography generation oxidation reaction (including the Organic substance in antibacterial), Thus most germs and virus are killed.Relevant quantitative test shows: in 5 minutes, nano oxidized zinc concentration is 1% Time, the sterilizing rate of staphylococcus aureus is 98.86%, and colibacillary sterilizing rate is 99.93%.
Sodium cocoate: there is washing, moistening, emulsifying and the dispersibility of excellence.Low irritant, and other surface can be reduced The zest of activating agent.
TCC: a kind of efficient, broad spectrum antimicrobicide, it possesses lasting, safe and stable sterilization feature, with skin Skin has a fabulous compatibility, and all has gram positive bacteria, gram negative bacteria, fungus, yeast, virus and efficiently press down Kill effect.Outstanding advantages be stability and compatibility fabulous, there is no niff, and consumption be few, lasting medicine.It is added In fancy soap, shampoo, bath gel, handwashing liquid, cleansing milk, beautifying liquid, acne removing frost, detergent, liquid detergent, trauma agent/ointment, beauty and make-up Product, palpus foam cream, toothpaste, collutory, antibacterial dish washing detergent, wound disinfection agent, fabric antimicrobial finishing agent, medical disinfecting Agent, fiber textile and except sterilizing in bromhidrosis and tinea pedis series products, antibacterial and deodorization.
Diethyl aminoethyl methacrylate: colourless transparent liquid.By methacrylic acid and diethylaminoethanol effect And obtain.These product have reactive amino and polymerizable vinyl, can increase cohesive, thermosetting, due to the effect of ionic bond, and can Improve bridging property and dyestuff and the tinctorial property of pigment, can be used for preparing thermohardening lacquer, antistatic additive, dyeing assistant, lubrication Oil additive, binding agent, leather processing inorganic agent, combustion adjuvant etc..
Lupenyl palmitate: a kind of good fibrous raw material, has that good permeability, hygroscopicity be strong, soft, antibacterial, the winter The features such as warm Xia Liang.
The invention has the beneficial effects as follows: prepared product has the most superior anti-microbial property, be suitable for making at field of textiles With, improve properties of product, advantageously reduce carrying capacity of environment, improve production efficiency, advantageously reduce production cost.
Detailed description of the invention
Embodiment one,
A kind of natural mixed textile whole dye Antibacterial accessory ingredient, it is characterised in that be made up of the component of following mass fraction: corn starch Solution 50 parts, nano-zinc oxide powder or cupric oxide powder 25 parts, pigment 10 parts, aqueous initiator 3 parts, natural antibacterial agent and have 12 parts of the mixture of machine antibacterial, dispersant 3 parts, styrene-acrylic emulsion 14 parts, emulsifying agent 4 parts.
Aqueous initiator be the particle diameter of sodium pyrosulfite, nano-zinc oxide powder or cupric oxide powder be 160nm.Powder is Disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate salt.Emulsifying agent is dodecyl sodium sulfate.Nanometer seed grain is made to be uniformly dispersed.Organic anti- Microbial inoculum is sodium cocoate.Natural antibacterial agent is Wasabia japonic (Euterma Wasabi).
Embodiment two,
A kind of natural mixed textile whole dye Antibacterial accessory ingredient, it is characterised in that be made up of the component of following mass fraction: Semen Maydis forms sediment Powder solution 140 parts, nano-zinc oxide powder or cupric oxide powder 32 parts, pigment 14 parts, aqueous initiator 5 parts, natural antibacterial agent With 14 parts of the mixture of organic antibacterial agent, dispersant 5 parts, styrene-acrylic emulsion 16 parts, emulsifying agent 6 parts.
Aqueous initiator is in sodium peroxydisulfate or Ammonium persulfate..The particle diameter of nano-zinc oxide powder or cupric oxide powder is 180nm.Dispersant is disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate salt.Emulsifying agent is dodecyl sodium sulfate.Organic antibacterial agent is plumage Fan alcohol cetylate.Natural antibacterial agent is Oleum Ricini.
Embodiment three,
A kind of natural mixed textile whole dye Antibacterial accessory ingredient, it is characterised in that be made up of the component of following mass fraction: corn starch Solution 260 parts, nano-zinc oxide powder or cupric oxide powder 40 parts, pigment 18 parts, aqueous initiator 6 parts, natural antibacterial agent with 16 parts of the mixture of organic antibacterial agent, dispersant 7 parts, styrene-acrylic emulsion 18 parts, emulsifying agent 8 parts.
Aqueous initiator is hydrogen peroxide or peracetic acid.The particle diameter of nano-zinc oxide powder or cupric oxide powder is 180nm。
Dispersant is disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate salt.Emulsifying agent is dodecyl sodium sulfate.Make nanometer seed Grain be uniformly dispersed organic antibacterial agent be TCC natural antibacterial agent be mustard, Oleum Ricini.
Embodiment four,
As different from Example 1, natural mixed textile whole dye Antibacterial accessory ingredient, it is made up of the component of following mass fraction: Semen Maydis Starch solution 60 parts, nano-zinc oxide powder or cupric oxide powder 30 parts, pigment 13 parts, aqueous initiator 4 parts, natural antibacterial agent With 13 parts of the mixture of organic antibacterial agent, dispersant 4 parts, styrene-acrylic emulsion 15 parts, emulsifying agent 5 parts.
Embodiment five,
As different from Example 1, natural mixed textile whole dye Antibacterial accessory ingredient, it is made up of the component of following mass fraction: Semen Maydis Starch solution 80 parts, nano-zinc oxide powder or cupric oxide powder 32 parts, pigment 115 parts, aqueous initiator 5 parts, natural antibacterial Agent and 143 parts of the mixture of organic antibacterial agent, dispersant 5 parts, styrene-acrylic emulsion 16 parts, emulsifying agent 6 parts.
The technical scheme provided the embodiment of the present invention above is described in detail, specific case used herein Principle and embodiment to the embodiment of the present invention are set forth, and the explanation of above example is only applicable to help to understand this The principle of inventive embodiments；Simultaneously for one of ordinary skill in the art, according to the embodiment of the present invention, in specific embodiment party All will change in formula and range of application, in sum, this specification content should not be construed as limitation of the present invention.

Claims (9)

1. a natural mixed textile whole dye Antibacterial accessory ingredient, it is characterised in that be made up of the component of following mass fraction: Semen Maydis forms sediment Powder solution 50-260 part, nano-zinc oxide powder or cupric oxide powder 25-40 part, pigment 10-18 part, aqueous initiator 3-6 part, Natural antibacterial agent and mixture 12-16 part of organic antibacterial agent, dispersant 3-7 part, styrene-acrylic emulsion 14-18 part, emulsifying agent 4-8 Part.
The natural mixed textile of one the most according to claim 1 whole dye Antibacterial accessory ingredient, it is characterised in that by following mass parts The component composition of number: corn starch solution 80-200 part, nano-zinc oxide powder or cupric oxide powder 28-36 part, pigment 12-16 Part, aqueous initiator 4-6 part, natural antibacterial agent and mixture 13-15 part of organic antibacterial agent, dispersant 4-6 part, phenylpropyl alcohol breast Liquid 15-17 part, emulsifying agent 5-7 part.
The natural mixed textile of one the most according to claim 1 whole dye Antibacterial accessory ingredient, it is characterised in that by following mass parts The component composition of number: corn starch solution 140 parts, nano-zinc oxide powder or cupric oxide powder 32 parts, pigment 14 parts, aqueous are drawn Send out agent 5 parts, natural antibacterial agent and 14 parts of the mixture of organic antibacterial agent, dispersant 5 parts, styrene-acrylic emulsion 16 parts, emulsifying agent 6 parts.
The natural mixed textile of one the most according to claim 1 whole dye Antibacterial accessory ingredient, it is characterised in that described aqueous causes Agent is at least one in hydrogen peroxide, peracetic acid, sodium pyrosulfite, sodium peroxydisulfate or Ammonium persulfate..
The natural mixed textile of one the most according to claim 1 whole dye Antibacterial accessory ingredient, it is characterised in that described nano oxygen The particle diameter changing zinc powder or cupric oxide powder is 160-180nm.
The natural mixed textile of one the most according to claim 1 whole dye Antibacterial accessory ingredient, it is characterised in that described dispersant For disodium 4-dodecyl-2,4 '-oxydibenzenesulfonate salt.
The natural mixed textile of one the most according to claim 1 whole dye Antibacterial accessory ingredient, it is characterised in that described emulsifying agent For dodecyl sodium sulfate, nanometer seed grain is made to be uniformly dispersed.
The natural mixed textile of one the most according to claim 1 whole dye Antibacterial accessory ingredient, it is characterised in that described organic anti- Microbial inoculum be in sodium cocoate, TCC, diethyl aminoethyl methacrylate or Lupenyl palmitate at least A kind of.
The natural mixed textile of one the most according to claim 1 whole dye Antibacterial accessory ingredient, it is characterised in that described natural anti- Microbial inoculum is at least one in chitin, mustard, Oleum Ricini, Wasabia japonic (Euterma Wasabi).
CN201610536036.0A 2016-07-10 2016-07-10 A kind of natural mixed textile whole dye Antibacterial accessory ingredient Pending CN106192403A (en)