CN106414823A - Fabric for a table linen textile - Google Patents

Fabric for a table linen textile Download PDF

Info

Publication number
CN106414823A
CN106414823A CN201580019276.7A CN201580019276A CN106414823A CN 106414823 A CN106414823 A CN 106414823A CN 201580019276 A CN201580019276 A CN 201580019276A CN 106414823 A CN106414823 A CN 106414823A
Authority
CN
China
Prior art keywords
fabric
yarns
warp
yarn
polyester
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201580019276.7A
Other languages
Chinese (zh)
Inventor
O·阿拉内恩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Textile Finland Co
Original Assignee
Textile Finland Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Textile Finland Co filed Critical Textile Finland Co
Publication of CN106414823A publication Critical patent/CN106414823A/en
Pending legal-status Critical Current

Abstract

The application relates to a fabric for a table linen textile. The fabric comprising warp yarns configured to form a warp, the warp yarns comprising polyester, and filling yarns configured to form a filling. The warp and filling being woven according to a twill or satin weave, where each filling yarn repeats a sequence by passing under at least one warp yarn and passing over at least one warp yarn sequentially. The warp yarns comprising twisted filament polyester yarns in the twill weave, or twisted polyester staple fiber yarns or twisted polyester low pilling staple fiber yarns in the satin weave for increasing a durability of the fabric.

Description

Fabric for table flax textile
Invention field
Present application relates generally to a kind of fabric for table flax textile.
Background of invention
Table flax textile, such as tablecloth and shield, are in order at covering dining table surface and other tables of covering are spun with Caulis et Folium Lini The actual reason of fabric and use.Additionally, sordid table flax textile clean table is sub- can only taken away When linen textile is placed on dining table, table flax textile is easy to and is accelerated with the cleaning of dining table after the meal and turn over table.
Additionally, table flax textile is used for creating the individual outward appearance of dining table by different types of design and color.
The table that cotton has been very universal flax textile material, but the table flax textile of cotton has poor dirt Repellency.
In order to improve dirt repellency, have been developed for a kind of table sodolin, using poly- wherein in its warp and latitude Ester.
However, the polyester table sodolin of i.e. toilet exploitation has the dirt repellency of improvement, thus plant polyester table and use The availability of table flax textile that sodolin is obtained and the suitability are also bad, and it during normal use loses it quickly Profile.
Aforementioned drawback significantly limit the availability of existing table sodolin.
Content of the invention
It is an object of the present invention to avoiding drawbacks described above and providing a kind of row of the dirt for table flax textile Scolding property fabric, it can be benefited can with quick print and by the distinctive pattern of client and color, meets the need of industrial washing Ask, and increased to the ruggedness using chemistry and mechanical mottle present in neutralization industrial washing.
One object of the present invention is by the fabric of offer claim 1 and the table flax textile of claim 5 It is satisfied.
According to an embodiment of the invention, the fabric for table flax textile includes：Warp thread, it is configured to Form warp, described warp thread comprises polyester；And weft yarn, it is configured to form latitude.Described warp and latitude are according to twill weave or satin weave Weave and be braided, each of which weft yarn passes through sequentially to pass through and at least one warp thread below at least one warp thread Top passes through and repetitive sequence.Described warp thread includes twisted filaments polyester yarn in described twill weave, or in described satin weave Braiding includes twisting polyester staple fiber yarn or twisting polyester low balling-up staple yarn, to increase the ruggedness of described fabric.
According to an embodiment of the invention, table flax textile comprises fabric, and described fabric includes：Warp thread, its It is configured to form through described warp thread comprises polyester；And weft yarn, it is configured to form latitude.Described warp and latitude are compiled according to twill Knit or satin weave and be braided, each of which weft yarn pass through sequentially below at least one warp thread pass through and at least One warp yarns passes through and repetitive sequence.Described warp thread includes twisted filaments polyester yarn in described twill weave, or Described satin weave includes twisting polyester staple fiber yarn or twisting polyester low balling-up staple yarn, to increase the resistance to of described fabric The property used.
The further embodiment of the present invention is clear and definite in the dependent claims.
Verb "comprising" is used herein as open restriction, and it had both been not excluded for and had not required the other feature do not recorded Presence.Verb " comprising " and " having " is defined as comprising.
It is defined as one as not usage quantity word herein or using term " at least one " or more than one, and And term " multiple " is defined as two or more than two.
Term " another " is defined as at least two or more as used in this article.
Meaning that term "or" comprises "and/or" according to it in general manner and use, except non-content separately clear stipulaties.
For verb defined above and term, unless given difference in claim or in elsewhere in this specification Definition, these definition should be suitable for.
Finally, the feature recorded in the dependent claims can free of one another combine, unless separately clearly stated.
Brief description
Embodiments of the present invention will be described with reference to the drawings, wherein
Accompanying drawing 1a illustrates schematic diagram and the cross section of twill weave, and
Accompanying drawing 1b illustrates schematic diagram and the cross section of satin weave.
Specific embodiment
Accompanying drawing 1a illustrates principle and the cross-sectional view of the twill weave of fabric 100, and it can be used for table linen textile Product, such as tablecloth, shield, long band cloth (runner) or napkin.Fabric 100 can be such as Tefi Oy's Wizard Twill- fabric, it passes through twill weave and is obtained.
Fabric 100 includes twisted filaments polyester yarn 112, and for 100% polyester and it is twisted at least 250 twist m, such as it 250th, 300,350,400,450 or 500 twist m.Filament yarn 112 forms through 110 and makes it possible to provide thickness and the light of fabric 100 Sliding surface, it mainly comprises polyester so that the distinctive pattern of the desired user of sublimation print technology print and color can be passed through Color.Additionally, the cleaning on surface is easy on the intensive surface of polyester.
Fabric 100 also includes weft yarn 122, for example：Comprise as the Revolving cup spinning (rotor of 35,50,55,65 or 80% cotton Spun) twist polyester-cotton yarn, comprise the Revolving cup spinning twisting cotton yarn of 100% cotton, or some other yarn that can absorb dampness.As Fruit weft yarn 122 comprises such as 35% cotton, then overall fabric 100 comprises 10-20% cotton, and such as 10,12,14,16,18 or 20%, It is used for preventing when fabric 100 in use when, electrostatic during mangling for the fabric 100.Weft yarn 122 forms latitude 120.
It is braided according to twill weave through 110 and latitude 120, wherein each weft yarn 122 passes through sequentially in 4 filament yarns Pass through, then 1 filament yarn 112 above as an alternative below 112 or below such as 2,3 or 5 filament yarns 112 Or pass through and repetitive sequence above such as 2 or 3 filament yarns 112 as an alternative, such as can from accompanying drawing fabric 100 Cross section seen as.Then weft yarn 122 repeats identical sequence, but to the mobile filament yarn 112 in side from And produce twill pattern.
The dirt repellency of fabric 100 is passed through to process filament yarn 112 and weft yarn by least one ptfe compounds 122 providing.Generally, dirt repellency processes the friction reducing between warp thread 112 and weft yarn 122, and it easily causes fabric 100 damages during operation and maintenance.
However, filament yarn 112 provide enough mechanical friction between the weft yarn 122 of filament yarn 112 and latitude 120 so that The ruggedness of fabric 100 increases when the ruggedness of its such as industrial washing improves.
Additionally, the friction between filament yarn 112 and weft yarn 122 makes fabric 100 be easy to add in charging and folding device Work, does not therefore interfere and produces pause.
The weight of fabric 100 is such as 220-280 gram/m.In fabric 100, the density of filament yarn 122 is for example extremely Few 30 yarns/centimetre, such as 30,35,40,45 or 50 yarns/centimetre, the density of weft yarn 122 be e.g., from about 20 yarns/centimetre, such as 16,18, 20th, 22 or 24 yarns/centimetre.
Accompanying drawing 1b illustrates principle and the cross-sectional view of the satin weave of fabric 102, and it can be used for such as tablecloth, pad Cloth, long band cloth or napkin.Fabric 102 can be such as Tefi Oy's Stella Satine- fabric, and it is compiled by satin weave Knit prepared.
Fabric 102 includes warp thread 132, such as twisting polyester staple fiber yarn or twisting polyester low balling-up staple yarn, and it is 100% polyester.Silvalin 132 forms through 130 and makes it possible to provide the surface of fabric 102, and it mainly comprises polyester so that can With using sublimation print technology and surface is easy to clean.
Silvalin 132 provides fabric 102 to be similar to cotton and covers quality and the outward appearance of frosted face, and it realizes exquisite printing Effect.Additionally, low balling-up silvalin 132 prevents fabric 102 surface balling-up.
Fabric 102 also includes weft yarn 122, for example：Comprise as 35,50,55,65 or 80% cotton Revolving cup spinning twist polyester- Cotton yarn, comprises the Revolving cup spinning twisting cotton yarn of 100% cotton, or some other yarn that can absorb dampness.Weft yarn 122 forms latitude 120.
It is braided according to satin weave through 130 and latitude 120, wherein each weft yarn 122 passes through sequentially in 4 silvalins Pass through, then 1 silvalin 132 above as an alternative below 132 or below such as 2,3 or 5 silvalins 132 Or pass through and repetitive sequence above such as 2 or 3 silvalins 132 as an alternative, such as can from accompanying drawing fabric 102 Cross section seen as.Then weft yarn 122 repeats identical sequence, but to mobile 2 silvalins 132 in side and produces Raw twill pattern.
The dirt repellency of fabric 102 is provided by least one ptfe compounds, but silvalin 132 is in fiber Enough mechanical friction is provided so that the ruggedness of fabric 102 increases between yarn 132 and weft yarn 122.Additionally, because friction, knitting Thing 102 is easy to process.
The weight of fabric 102 is such as 240-280 gram/m.The density of silvalin 132 be for example, at least 30 yarns/li Rice, such as 30,35,40,45 or 50 yarns/centimetre, the density of weft yarn 122 be e.g., from about 20 yarns/centimetre, such as 16,18,20,22 or 24 Yarn/centimetre.
The ratio through density and weft density being used is determined by the thickness of the warp thread 112,132 being used and weft yarn 122. Suitable ratio through density and weft density makes it possible to provide through intensive front and the filling density collection back side in fabric 100,102, this Mean outstanding printing effect, dirt repellency and ruggedness.
Filling density integrates the back side as providing enough dampnesss in fabric 100,102 so that preventing from drawing in charging and folding apparatus Rise produce pause electrostatic, prevent fabric 100,102 mangle and folding apparatus in slip, and keep fabric 100,102 endure Directly.
Additionally, fabric 100,102 can be used for working clothing, such as overcoat and apron.
The present invention has carried out above description with reference to aforementioned embodiments, and has illustrated the multiple excellent of the present invention Point.It is apparent that the present invention is not limited these embodiments, and it is included in the spirit of inventive concept and appended claims With all possible embodiments in scope.

Claims (6)

1.一种用于桌用亚麻纺织品的织物(100，102)，其包括1. A fabric (100, 102) for table linen comprising 经纱(112，132)，其被配置以形成经(110，130)，所述经纱包含聚酯，和warp yarns (112, 132) configured to form warp yarns (110, 130), said warp yarns comprising polyester, and 纬纱(122)，其被配置以形成纬(120)，a weft yarn (122) configured to form a weft (120), 所述经和纬根据斜纹编织或缎纹编织而被编织，其中每个纬纱(122)通过循序地在至少一个经纱(112，132)下方穿过以及在至少一个经纱(112，132)上方穿过而重复序列，The warp and weft are woven according to a twill weave or a satin weave, wherein each weft yarn (122) passes sequentially under at least one warp yarn (112, 132) and over at least one warp yarn (112, 132) repeat the sequence over and over, 其特征在于It is characterized by 所述经纱在所述斜纹编织中包括加捻长丝聚酯纱(112)，或者在所述缎纹编织中包括加捻聚酯短纤维纱(132)或加捻聚酯低起球短纤维纱(132)，以增加所述织物的耐用性。The warp yarns comprise twisted filament polyester yarns (112) in the twill weave, or twisted polyester staple yarns (132) or twisted polyester low-pilling staple fibers in the satin weave Yarn (132) to increase the durability of the fabric. 2.权利要求1所述的织物，其中所述纬纱包括转杯纺加捻聚酯-棉纱，其包含棉以防止所述织物的静电。2. The fabric of claim 1, wherein the weft yarns comprise rotor spun twisted polyester-cotton yarns comprising cotton to prevent static electricity of the fabric. 3.前述权利要求中任一项所述的织物，其中所述经纱和纬纱通过至少一种聚四氟乙烯化合物处理以提高所述织物的污物排斥性。3. The fabric of any one of the preceding claims, wherein the warp and weft yarns are treated with at least one polytetrafluoroethylene compound to improve the soil repellency of the fabric. 4.前述权利要求中任一项所述的织物，其中所述经纱的密度为至少30纱/厘米且所述纬纱的密度为约20纱/厘米。4. The fabric of any one of the preceding claims, wherein the warp yarns have a density of at least 30 yarns/cm and the weft yarns have a density of about 20 yarns/cm. 5.一种桌用亚麻纺织品，其包括根据权利要求1-4中任一项所述的织物(100)。5. A table linen textile comprising the fabric (100) according to any one of claims 1-4. 6.权利要求5所述的桌用亚麻纺织品，其是桌布、垫布、长条饰布或餐巾。6. The table linen textile product according to claim 5, which is a tablecloth, a doily, a strip or a napkin.
CN201580019276.7A 2014-03-18 2015-03-18 Fabric for a table linen textile Pending CN106414823A (en)