CN106555341A - A kind of preparation method of three prevention fabrics - Google Patents
A kind of preparation method of three prevention fabrics Download PDFInfo
- Publication number
- CN106555341A CN106555341A CN201611051981.8A CN201611051981A CN106555341A CN 106555341 A CN106555341 A CN 106555341A CN 201611051981 A CN201611051981 A CN 201611051981A CN 106555341 A CN106555341 A CN 106555341A
- Authority
- CN
- China
- Prior art keywords
- fabric
- preparation
- prevention
- mixed liquor
- gluing solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of three prevention fabrics, including following preparation process, step one：Fabric cleaning is clean, remove spot unnecessary on fabric；Step 2：Mixed liquor is obtained after three anti-auxiliary agents are mixed in proportion with gluing solution, in mixed liquor the quality accounting of three anti-auxiliary agents be 1%～10%, gluing solution quality accounting be 99%～90%, mixed liquor is uniformly applied to fabric face；Step 3：By fabric drying, drying temperature is 100～160 DEG C, and drying time is 1～3min；The three anti-auxiliary agent is perfluorocarboxylic acid ester, and the gluing solution is PU glue.Water repellent, waterproof efficacy can be used and be reached in the PU glue surfaces face of doing by the fabric that the preparation method of three prevention fabric of the present invention is obtained, and overcome traditional method and cannot accomplish that oil repellent reaches the deficiency of six grades of tests of standard AATCC118.
Description
Technical field
The present invention relates to a kind of processing method of fabric, specifically a kind of preparation method of three prevention fabrics.
Technical background
At present, existing case and bag surface with the preparation method of three prevention fabrics is：Fabric is impregnated in three anti-auxiliary agents,
Drying is then taken out, then fabric face carries out gluing (such as PVC glue or PU glue), dries again, obtains three prevention fabrics.This method
Fabric side can only be done face use by obtained three prevention fabric, and three anti-effects are unable to reach if it PU glue surfaces need to be done face.
The content of the invention
The invention provides a kind of preparation method of three prevention fabrics.
Present invention aim to address existing case and bag surface can only with three prevention fabrics obtained in the preparation method of three prevention fabrics
Fabric side is done into face use, the problem of three anti-effects is unable to reach if PU glue surfaces need to be done face.
The technical solution adopted for the present invention to solve the technical problems is：A kind of preparation method of three prevention fabrics, including with
Lower preparation process：
Step one：Fabric cleaning is clean, remove spot unnecessary on fabric；
Step 2：Mixed liquor is obtained after three anti-auxiliary agents are mixed in proportion with gluing solution, three anti-auxiliary agent in mixed liquor
Quality accounting be 1%～10%, gluing solution quality accounting be 99%～90%, mixed liquor is uniformly applied to fabric face；
Step 3：By fabric drying, drying temperature is 100～160 DEG C, and drying time is 1～3min..
Further, described three anti-auxiliary agents are perfluorocarboxylic acid ester.
Further, the gluing solution is PU glue.
The invention has the beneficial effects as follows：The fabric that the preparation method of three prevention fabric of the present invention is obtained can be by PU glue
Water repellent, waterproof efficacy are used and reached in the face face of doing, and overcomes traditional method and cannot accomplish that oil repellent reaches six grades of standard AATCC118
The deficiency of test.
Description of the drawings
Fig. 1 is the flow chart of the present invention.
Specific embodiment
The present invention is further described with reference to the accompanying drawings and examples：
As shown in the figure, there is provided the flow chart of the preparation method of three prevention fabric of the invention, including following preparation process：
Step one：Fabric cleaning is clean, remove spot unnecessary on fabric；
Step 2：Mixed liquor is obtained after three anti-auxiliary agents are mixed with gluing solution, the quality of three anti-auxiliary agents in mixed liquor
It is 95% that accounting is the quality accounting of 5%, gluing solution, and mixed liquor is uniformly applied to fabric face；
Step 3：It it is 130 DEG C by fabric drying, drying temperature, drying time is 2min.
The three anti-auxiliary agent is perfluorocarboxylic acid ester.
The gluing solution is PU glue.
The fabric that the preparation method of three prevention fabric of the present invention is obtained can by the PU glue surfaces face of doing use and reach water repellent,
Waterproof efficacy, overcomes traditional method and cannot accomplish that oil repellent reaches the deficiency of six grades of tests of standard AATCC118.
Claims (3)
1. a kind of preparation method of three prevention fabrics, it is characterised in that including following preparation process：
Step one：Fabric cleaning is clean, remove spot unnecessary on fabric；
Step 2：Mixed liquor is obtained after three anti-auxiliary agents are mixed in proportion with gluing solution, the matter of three anti-auxiliary agents in mixed liquor
It is 99%～90% that amount accounting is the quality accounting of 1%～10%, gluing solution, and mixed liquor is uniformly applied to fabric face；
Step 3：By fabric drying, drying temperature is 100～160 DEG C, and drying time is 1～3min.
2. the preparation method of three prevention fabric according to claim 1, it is characterised in that：The three anti-auxiliary agent is perfluorocarboxylic acid
Ester.
3. the preparation method of three prevention fabric according to claim 1, it is characterised in that：The gluing solution is PU glue.