CN106833289A - A kind of double-component aqueous epoxy primer and its production technology - Google Patents
A kind of double-component aqueous epoxy primer and its production technology Download PDFInfo
- Publication number
- CN106833289A CN106833289A CN201710142184.9A CN201710142184A CN106833289A CN 106833289 A CN106833289 A CN 106833289A CN 201710142184 A CN201710142184 A CN 201710142184A CN 106833289 A CN106833289 A CN 106833289A
- Authority
- CN
- China
- Prior art keywords
- component
- double
- deionized water
- epoxy primer
- aqueous epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of double-component aqueous epoxy primer and production technology, it is characterised in that by Ricinate, 3/5 defoamer, titanium dioxide, talcum powder, barium sulfate, rust resisting pigment, carbon black with a certain amount of deionized water mixed grinding to 40 μm；Epoxy emulsion, remaining defoamer, thickener and deionized water are added, dispersion stirs, and obtains component A；Curing agent and deionized water are mixed in proportion, component B is obtained；When using, by component A and component B according to amine and epoxy equivalent proportion 3:4 are used in mixed way.With water-based emulsion as film forming matter, pigment and filler provide decoration and barrier propterty to the present invention, and deionized water embodies the feature of environmental protection；The double-component system of use makes priming paint have good adhesive force, toughness and water resistance, antiseptic property is excellent, adding various aqueous promoters makes the storage stability of priming paint and workability good, it is possible to achieve normal temperature cure and moisturecuring so that the range of application of epoxy primer broadens.
Description
Technical field
The present invention relates to coating material production field, and in particular to water-base epoxy priming paint, a kind of especially aqueous ring of double-component
Oxygen priming paint and its production technology.
Background technology
Epoxy resin has adhesive strength high, and dielectric properties are good, and hardness is high, and deformation retract rate is small, to chemical solvent stabilization
The characteristics of, it is widely used in the industries such as base coat, intermediate coat, adhesive and composite.It is divided into list in coating application
Component System and double-component system, it is double-component system to apply at present most.
Common epoxy primer protective coating has strict requirements to the surface treatment of steel and coagulation soil's water content, if
Treatment does not reach requirement can reduce the long-effective protection effect of coating, or even the breakoff phenomenons such as disbonding, cracking prematurely occurs.
And the solidification temperature of common epoxy primer is higher, it is impossible to realize cold curing, harbour, harbour and bridge etc. in construction or
Need to carry out protective coating or Painting in Maintenance after use, and treatment is carried out on the basis of these building structure will reach requirement almost
It is impossible.
The content of the invention
Regarding to the issue above, it is an object of the invention to provide a kind of double-component aqueous epoxy primer, with normal temperature, moisturecuring
The characteristics of, and using water as solvent, composite environmental-friendly requirement will not produce VOC.
The present invention solves the technical scheme that is used of above-mentioned technical problem：A kind of double-component aqueous epoxy primer, it is special
Levy and be, including following components in percentage by weight：
Component A：Epoxy emulsion 35-40%
Pigment 18-20%
Rust resisting pigment 8-10%
Filler 15-20%
Ricinate 0.5-1.2%
Defoamer 0.2-1.0%
Thickener 0.5-0.8%
Deionized water polishing is very；
B component：Curing agent 12-18%
Deionized water 5-8%, amounts to 20%.
Further, the pigment includes titanium dioxide and carbon black, and its mass ratio is 18:0.02.
Further, the rust resisting pigment is HEUCOPHOS ZAM+ and Heucorin RZ, and mass ratio is 10:1.
Further, described filler is talcum powder, barium sulfate, and mass ratio is 1:1-1.5.
Further, the epoxy emulsion is Beckopox EP 2384w/57WA.
Further, the curing agent is Beckopox VEH 2188w/55WA amine hardeners.
A kind of production technology of double-component aqueous epoxy primer, it is characterised in that comprise the following steps：
(1) by Ricinate, 3/5 defoamer, titanium dioxide, talcum powder, barium sulfate, rust resisting pigment, carbon black with it is a certain amount of
Deionized water mixed grinding to 40 μm；
(2) epoxy emulsion, remaining defoamer, thickener and deionized water are added, dispersion stirs, and obtains component A；
(3) curing agent and deionized water are mixed in proportion, obtains component B；
(4) when using, by component A and component B according to amine and epoxy equivalent proportion 3:4 are used in mixed way.
The advantage of the invention is that：1st, with water-based emulsion as film forming matter, pigment and filler provide decoration and barrier propterty,
Deionized water embodies the feature of environmental protection.2nd, the double-component system that the present invention is used makes priming paint have good adhesive force, toughness and water-fast
Property, antiseptic property is excellent, adds various aqueous promoters to make the storage stability of priming paint and workability good.3rd, the present invention is used
Raw material it is most of be home made article, with cost advantage, added emulsion master grind process is simple, it is easy to operate.4th, the present invention
Normal temperature cure and moisturecuring can be realized so that the range of application of epoxy primer broadens.
Specific embodiment
Below by specific embodiment, the invention will be further described, and following examples are descriptive, is not limit
Qualitatively, it is impossible to which protection scope of the present invention is limited with this.
Embodiment 1
Each raw material weight percentage of component A
The percentage by weight of each raw material of B component
| Beckopox VEH 2188w/55WA amine hardeners | 15.00 |
| Di-water deionized waters | 5.00 |
| Total is amounted to | 20.00 |
| P/B pigments | 1.32 |
| Crosslinking ratio equivalent proportions (amine/epoxy) | 75% |
A kind of production technology of double-component aqueous epoxy primer, it is characterised in that comprise the following steps：
(1) by Ricinate, 3/5 defoamer, titanium dioxide, talcum powder, barium sulfate, rust resisting pigment, carbon black with it is a certain amount of
Deionized water mixed grinding to 40 μm；
(2) epoxy emulsion, remaining defoamer, thickener and deionized water are added, dispersion stirs, and obtains component A；
(3) curing agent and deionized water are mixed in proportion, obtains component B；
(4) when using, by component A and component B according to amine and epoxy equivalent proportion 3:4 are used in mixed way.
Finally it should be noted that：Various embodiments above is merely illustrative of the technical solution of the present invention, rather than its limitations；To the greatest extent
Pipe has been described in detail with reference to foregoing embodiments to the present invention, it will be understood by those within the art that：Its according to
The technical scheme described in foregoing embodiments can so be modified, or which part or all technical characteristic are entered
Row equivalent；And these modifications or replacement, the essence of appropriate technical solution is departed from various embodiments of the present invention technology
The scope of scheme.
Claims (7)
1. a kind of double-component aqueous epoxy primer, it is characterised in that including following components in percentage by weight：
Component A：Epoxy emulsion 35-40%
Pigment 18-20%
Rust resisting pigment 8-10%
Filler 15-20%
Ricinate 0.5-1.2%
Defoamer 0.2-1.0%
Thickener 0.5-0.8%
Deionized water polishing is very；
B component：Curing agent 12-18%
Deionized water 5-8%, amounts to 20%.
2. a kind of double-component aqueous epoxy primer according to claim 1, it is characterised in that the pigment includes titanium dioxide
And carbon black, its mass ratio is 18:0.02.
3. a kind of double-component aqueous epoxy primer according to claim 1, it is characterised in that the rust resisting pigment is
HEUCOPHOS ZAM+ and Heucorin RZ, mass ratio is 10:1.
4. a kind of double-component aqueous epoxy primer according to claim 1, it is characterised in that described filler be talcum powder,
Barium sulfate, mass ratio is 1:1-1.5.
5. a kind of double-component aqueous epoxy primer according to claim 1, it is characterised in that the epoxy emulsion for
Beckopox EP 2384w/57WA。
6. a kind of double-component aqueous epoxy primer according to claim 1, it is characterised in that the curing agent is
Beckopox VEH 2188w/55WA amine hardeners.
7. a kind of technique for producing double-component aqueous epoxy primer as described in claim 1-6, it is characterised in that including following
Step：
(1) Ricinate, 3/5 defoamer, titanium dioxide, talcum powder, barium sulfate, rust resisting pigment, carbon black are gone with a certain amount of
Ionized water mixed grinding is to 40 μm；
(2) epoxy emulsion, remaining defoamer, thickener and deionized water are added, dispersion stirs, and obtains component A；
(3) curing agent and deionized water are mixed in proportion, obtains component B；
(4) when using, by component A and component B according to amine and epoxy equivalent proportion 3:4 are used in mixed way.