CN106947220A - 高耐热bmc复合材料 - Google Patents
高耐热bmc复合材料 Download PDFInfo
- Publication number
- CN106947220A CN106947220A CN201710281149.5A CN201710281149A CN106947220A CN 106947220 A CN106947220 A CN 106947220A CN 201710281149 A CN201710281149 A CN 201710281149A CN 106947220 A CN106947220 A CN 106947220A
- Authority
- CN
- China
- Prior art keywords
- resisting
- high heat
- bmc
- vinylite
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高耐热BMC复合材料，该复合材料采用短切玻璃纤维和碳纤维粉末乙烯基树脂复合而成的料状成型材料；主要解决耐高温、零收缩、低比重等功能性问题，提高材料的机械性能和稳定性。
Description
技术领域
本发明涉及一种高耐热BMC复合材料。
背景技术
BMC(Bulk Molding Compounds)是以特殊不饱和聚脂热固硬化性树脂，具有优良的电气绝缘特性、耐热性、耐燃性、高机械强度尺寸安定性、耐蚀性、耐水性、收缩稳定性等,各种热固硬化性成型材料中最高级品。
BMC射出成型又称团状模塑料注塑成型。英国称为DMC（料团状模塑料）射出成型。这种射出成型的基本材料是不饱和聚脂、苯乙烯树脂、再加上矿物填料、着色剂和10-30%（重量百分比）的玻璃纤维增强材料等组成的块状塑料。玻纤长度一般取6—12mm，长的可达25mm，对这种以不饱和聚脂为粘结剂的玻璃纤维增强的新型模塑材料命名为BMC和SMC（片状模塑料）；这些块状原料是属增强热固性塑料。其制品去有很高电阻值、耐湿性、有优良机械性能和较小的收缩率，因此可用来生产厚截面的制品，广泛应用在电子工业和家用电器方面，作各种壳体和小零件等等。
然而该材料在耐高温和抗收缩方面的性能还需要进一步优化，使其在无线电、精密仪器等设备仪表上使用时才能更适合。
发明内容
本发明旨在克服现有技术的不足，提供一种高耐热BMC复合材料，该BMC复合材料耐热，耐水、耐油、耐蚀性优良，适应各种成型工艺，可满足各种产品的性能要求。
本发明提供的一种高耐热BMC复合材料，该复合材料采用短切玻璃纤维和碳纤维粉末乙烯基树脂复合而成的料状成型材料。
所述复合材料包括碳纤维粉末乙烯基树脂、邻苯二甲酸二烯、丙脂、短切玻璃纤维、硬酯酸锌、滑石粉、氧化锌以及过氧化二苯甲。
其质量配比为：32-35%的碳纤维粉末乙烯基树脂，邻苯二甲酸二烯为聚酯树脂的20%-40%，1%-3%的丙脂，22-25%的短切玻璃纤维，1%-3%的硬酯酸锌，滑石粉为聚酯树脂的2%，其余为0.01%的氧化锌以及过氧化二苯甲。
所述丙脂的质量比重为2%。
所述硬酯酸锌的质量比重为2%。
本发明采用以上技术方案与现有技术相比，具有以下技术效果：
1.高耐热性：我公司研发的BMC复合材料新产品长期工作温度达到170℃.以上，热变形温度达到300℃
2.零收缩：制备模压复合材料的过程中用添加低收缩剂和超细填料来解决成型后收缩变形的问题，由于基体是收缩率较低的乙烯基树脂，选择低收缩较好的苯乙烯溶液作为低收缩剂，不同目数填料互相配制后的复合材料则可达到零收缩的特点。
3.低比重：由于碳纤维比重较低，调整配方，改变碳纤维与填料的比例，制备的复合材料。
具体实施方式
本发明的实施提供一种高耐热BMC复合材料，为使本领域技术人员更好地理解本发明的技术方案，下面结合附图和具体实施方式对本发明作进一步详细描述。通过参考附图描述的实施方式是示例性的，仅用于解释本发明，而不能解释为对本发明的限制。
本发明的目的在于提供一种高耐热BMC复合材料，该复合材料采用短切玻璃纤维和碳纤维粉末乙烯基树脂复合而成的料状成型材料。
实施例1
本实施例提供的高耐热BMC复合材料包括碳纤维粉末乙烯基树脂、邻苯二甲酸二烯、丙脂、短切玻璃纤维、硬酯酸锌、滑石粉、氧化锌以及过氧化二苯甲。
其质量配比为：32%的碳纤维粉末乙烯基树脂，邻苯二甲酸二烯为聚酯树脂的20%%，2%的丙脂，22%的短切玻璃纤维，2%的硬酯酸锌，滑石粉为聚酯树脂的2%，其余为0.01%的氧化锌以及过氧化二苯甲。
经上述配比制备方法制得的电池，通过实验，热变形温度达到300℃，密度1.6g/cm3，收缩率0，拉伸强度80MP。
实施例2
本实施例提供的复合材料包括碳纤维粉末乙烯基树脂、邻苯二甲酸二烯、丙脂、短切玻璃纤维、硬酯酸锌、滑石粉、氧化锌以及过氧化二苯甲。
其质量配比为：35%的碳纤维粉末乙烯基树脂，邻苯二甲酸二烯为聚酯树脂的40%，2%的丙脂， 25%的短切玻璃纤维，2%的硬酯酸锌，滑石粉为聚酯树脂的2%，其余为0.01%的氧化锌以及过氧化二苯甲。
经上述配比制备方法制得的电池，通过实验，热变形温度达到300℃，密度1.6g/cm3，收缩率0，拉伸强度80MP。
实施例3
本实施例提供的复合材料包括碳纤维粉末乙烯基树脂、邻苯二甲酸二烯、丙脂、短切玻璃纤维、硬酯酸锌、滑石粉、氧化锌以及过氧化二苯甲。
其质量配比为：33%的碳纤维粉末乙烯基树脂，邻苯二甲酸二烯为聚酯树脂的35%，2%的丙脂，24%的短切玻璃纤维，2%的硬酯酸锌，滑石粉为聚酯树脂的2%，其余为0.01%的氧化锌以及过氧化二苯甲。
所述丙脂的质量比重为2%。
所述硬酯酸锌的质量比重为2%。
经上述配比制备方法制得的电池，通过实验，热变形温度达到300℃，密度1.5g/cm3，收缩率0，拉伸强度70MP。
Claims (5)
1.一种高耐热BMC复合材料，其特征在于，该复合材料采用短切玻璃纤维和碳纤维粉末乙烯基树脂复合而成的料状成型材料。
2.根据权利要求1所述的一种高耐热BMC复合材料，其特征在于，所述复合材料包括碳纤维粉末乙烯基树脂、邻苯二甲酸二烯、丙脂、短切玻璃纤维、硬酯酸锌、滑石粉、氧化锌以及过氧化二苯甲。
3.根据权利要求1所述的一种高耐热BMC复合材料，其特征在于，其质量配比为：32-35%的碳纤维粉末乙烯基树脂，邻苯二甲酸二烯为聚酯树脂的20%-40%，1%-3%的丙脂，22-25%的短切玻璃纤维，1%-3%的硬酯酸锌，滑石粉为聚酯树脂的2%，其余为0.01%的氧化锌以及过氧化二苯甲。
4.根据权利要求3所述的一种高耐热BMC复合材料，其特征在于，所述丙脂的质量比重为2%。
5.根据权利要求3所述的一种高耐热BMC复合材料，其特征在于，所述硬酯酸锌的质量比重为2%。