CN108297226A - A kind of processing method for improving willow-plaited process product and using quality - Google Patents
A kind of processing method for improving willow-plaited process product and using quality Download PDFInfo
- Publication number
- CN108297226A CN108297226A CN201710815455.2A CN201710815455A CN108297226A CN 108297226 A CN108297226 A CN 108297226A CN 201710815455 A CN201710815455 A CN 201710815455A CN 108297226 A CN108297226 A CN 108297226A
- Authority
- CN
- China
- Prior art keywords
- willow
- process product
- plaited process
- plaited
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the processing methods that a kind of improvement willow-plaited process product use quality, include the following steps：（1）Surface preparation,（2）Coating coating processing,（3）Laser treatment,（4）It is cooling to be dried.The present invention has carried out special Optimal improvements to the surface treatment method of willow-plaited process product and has handled, under the common mating reaction of each step, the present invention treated willow-plaited process product have good surface characteristic, its wearability can promote 20% or more, mould proof corrosion resistant duration can promote 25% or more, service life can extend 30% or so, have good value for applications.
Description
Technical field
The invention belongs to wicker plaiting article processing technique fields, and in particular to a kind of processing side for improving willow-plaited process product and using quality
Method.
Background technology
Wicker plaiting article is a kind of traditional technology in China, and present wicker products are popular on the market, and the type of wicker products is numerous
It is more, there are the multiple types such as seat, basket, basket, dustpan, round-bottomed basket, crate, shallow basket made of wicker or thin bamboo strips, the gaily decorated basket, bamboo strainer, food dish at domestic aspect.Export trade side
Face has formed buck basket, flower pot coat, picnic tableware basket, hanging basket, lampshade, kennel, cat litter, Bird's Nest, ornamental by opening up and designing
Craftwork etc. is a variety of, and the appreciation effect that low-grade goods become high-grade is formed in foreign trade, very popular.Wicker products with
Wicker, bamboo cane, rattan etc. are raw material, but above-mentioned raw materials ingredient causes when in use because of the characteristic of its own by worm, mould
Deng erosion, the problem of causing appearance, performance losses, thereby reduce service life.In order to improve this problem, now mostly by right
Its surface coating paint improves this problem, but coating for willow-plaited process product performance improvement still not persistently.
Invention content
The purpose of the present invention is for existing problem, provide a kind of processing side for improving willow-plaited process product and using quality
Method.
The present invention is achieved by the following technical solutions：
A kind of processing method for improving willow-plaited process product and using quality, includes the following steps：
（1）Surface preparation：
With clear water to woven willow-plaited process product surface carry out cleaning impurity elimination processing after, then it is dried processing it is spare；
（2）Coating coating processing：
Pre-prepared coating is evenly applied to step（1）Treated willow-plaited process product surface, dries in the air after the completion to surface drying
It is spare afterwards；Each ingredient and its corresponding parts by weight are in the coating：8 ~ 10 parts of nano-titanium dioxides, 2 ~ 4 parts of urea, 1 ~ 2 part
Potassium nitrate, 2 ~ 4 parts of potassium dihydrogen phosphates, 0.5 ~ 1 part of trialkyl phosphates, 1 ~ 1.5 part of polyvinyl alcohol, 1 ~ 2 part of methyl methacrylate
Ester, 15 ~ 20 parts of ethyl alcohol, 150 ~ 160 parts of water；
（3）Laser treatment：
By step（2）Treated, and willow-plaited process product are put into laser treatment instrument, are carried out at surface laser to willow-plaited process product
Reason, takes out spare after the completion；
（4）It is cooling to be dried：
With clear water to step（3）Treated, and willow-plaited process product are rinsed is cooled to room temperature, and then it are dried again place
After reason is not more than 8% to whole water content.
Further, step（1）Described in drying process temperature be 80 ~ 85 DEG C.
Further, step（2）Described in nano-titanium dioxide granular size be 10 ~ 40nm.
Further, step（3）Described in the power of laser treatment be 400 ~ 500W, the speed of laser scanning is 450 ~
500mm/min。
Further, step（4）Described in drying process temperature be 90 ~ 95 DEG C.
The willow-plaited process product generally use coating coating after braiding is come to performances such as its Vermins-proof mildew-proofs in existing method
It is improved, although playing good effect, it, which improves protection persistence, cannot still reach the growing performance of people
Demand, there is an urgent need for further improve；To this present invention employs a kind of special processing method, willow-plaited process product are effectively improved
Integrated quality, it is different from traditional coating ingredient wherein first uniqueness has prepared a kind of coating, mainly coordinate subsequent laser
Processing is used, and a laser treatment has been carried out after coating is half-dried, this laser produces 400 on the surface of wicker products
DEG C or so high temperature, in advance the coating after coating effectively reduce the initial temperature of laser, in wicker plaiting article after the isolation of coating
Temperature on product surface is 300 DEG C or so, this temperature carries out carbonization treatment to the wood fibre of wicker products, in its surface shape
At the carburization zone of a suitable thickness, while the nano-titanium dioxide ingredient added in coating can effectively be consolidated under the high temperature conditions
It is fixed to combine on carburization zone, the characteristics such as its wear-resisting, heatproof, corrosion resistant are improved, the nitrogen phosphorus in urea, potassium nitrate, potassium dihydrogen phosphate
Element at high temperature penetrates into carburization zone, improves the chemical combination complexity and compactness of carburization zone, further improves willow
The surface characteristic of establishment product.
The present invention has the following advantages compared with prior art：
The present invention has carried out special Optimal improvements to the surface treatment method of willow-plaited process product and has handled, in matching jointly for each step
Under cooperation is used, there is the present invention treated willow-plaited process product good surface characteristic, wearability can promote 20% or more, prevent
Mould corrosion resistant duration can promote 25% or more, and service life can extend 30% or so, have good value for applications.
Specific implementation mode
Embodiment 1
A kind of processing method for improving willow-plaited process product and using quality, includes the following steps：
（1）Surface preparation：
With clear water to woven willow-plaited process product surface carry out cleaning impurity elimination processing after, then it is dried processing it is spare；
（2）Coating coating processing：
Pre-prepared coating is evenly applied to step（1）Treated willow-plaited process product surface, dries in the air after the completion to surface drying
It is spare afterwards；Each ingredient and its corresponding parts by weight are in the coating：8 parts of nano-titanium dioxides, 2 parts of urea, 1 part of potassium nitrate, 2
Part potassium dihydrogen phosphate, 0.5 part of trialkyl phosphates, 1 part of polyvinyl alcohol, 1 part of methyl methacrylate, 15 parts of ethyl alcohol, 150 parts
Water；
（3）Laser treatment：
By step（2）Treated, and willow-plaited process product are put into laser treatment instrument, are carried out at surface laser to willow-plaited process product
Reason, takes out spare after the completion；
（4）It is cooling to be dried：
With clear water to step（3）Treated, and willow-plaited process product are rinsed is cooled to room temperature, and then it are dried again place
After reason is not more than 8% to whole water content.
Further, step（1）Described in drying process temperature be 80 DEG C.
Further, step（2）Described in nano-titanium dioxide granular size be 10 ~ 40nm.
Further, step（3）Described in the power of laser treatment be 400W, the speed of laser scanning is 450mm/
min。
Further, step（4）Described in drying process temperature be 90 DEG C.
Embodiment 2
A kind of processing method for improving willow-plaited process product and using quality, includes the following steps：
（1）Surface preparation：
With clear water to woven willow-plaited process product surface carry out cleaning impurity elimination processing after, then it is dried processing it is spare；
（2）Coating coating processing：
Pre-prepared coating is evenly applied to step（1）Treated willow-plaited process product surface, dries in the air after the completion to surface drying
It is spare afterwards；Each ingredient and its corresponding parts by weight are in the coating：9 parts of nano-titanium dioxides, 3 parts of urea, 1.5 parts of nitric acid
Potassium, 3 parts of potassium dihydrogen phosphates, 0.8 part of trialkyl phosphates, 1.2 parts of polyvinyl alcohol, 1.5 parts of methyl methacrylates, 18 parts of second
Alcohol, 155 parts of water；
（3）Laser treatment：
By step（2）Treated, and willow-plaited process product are put into laser treatment instrument, are carried out at surface laser to willow-plaited process product
Reason, takes out spare after the completion；
（4）It is cooling to be dried：
With clear water to step（3）Treated, and willow-plaited process product are rinsed is cooled to room temperature, and then it are dried again place
After reason is not more than 8% to whole water content.
Further, step（1）Described in drying process temperature be 83 DEG C.
Further, step（2）Described in nano-titanium dioxide granular size be 10 ~ 40nm.
Further, step（3）Described in the power of laser treatment be 450W, the speed of laser scanning is 480mm/
min。
Further, step（4）Described in drying process temperature be 93 DEG C.
Embodiment 3
A kind of processing method for improving willow-plaited process product and using quality, includes the following steps：
（1）Surface preparation：
With clear water to woven willow-plaited process product surface carry out cleaning impurity elimination processing after, then it is dried processing it is spare；
（2）Coating coating processing：
Pre-prepared coating is evenly applied to step（1）Treated willow-plaited process product surface, dries in the air after the completion to surface drying
It is spare afterwards；Each ingredient and its corresponding parts by weight are in the coating：10 parts of nano-titanium dioxides, 4 parts of urea, 2 parts of potassium nitrate,
4 parts of potassium dihydrogen phosphates, 1 part of trialkyl phosphates, 1.5 parts of polyvinyl alcohol, 2 parts of methyl methacrylates, 20 parts of ethyl alcohol, 160 parts
Water；
（3）Laser treatment：
By step（2）Treated, and willow-plaited process product are put into laser treatment instrument, are carried out at surface laser to willow-plaited process product
Reason, takes out spare after the completion；
（4）It is cooling to be dried：
With clear water to step（3）Treated, and willow-plaited process product are rinsed is cooled to room temperature, and then it are dried again place
After reason is not more than 8% to whole water content.
Further, step（1）Described in drying process temperature be 85 DEG C.
Further, step（2）Described in nano-titanium dioxide granular size be 10 ~ 40nm.
Further, step（3）Described in the power of laser treatment be 500W, the speed of laser scanning is 500mm/
min。
Further, step（4）Described in drying process temperature be 95 DEG C.
Using the willow-plaited process product of wicker braiding as experimental subjects, it is handled respectively with above-mentioned three kinds of methods, finally
It was found that the present invention treated willow-plaited process product are promoted compared with the surface abrasion resistance of the willow-plaited process product after traditional coating coating processing
23% or so, it is mould proof（Using Trichoderma as experimental strain）Duration improves 28% or so, and service life extends 32% or so,
Integrated quality is good, has good promotional value and the market competitiveness.
Claims (5)
1. a kind of processing method for improving willow-plaited process product and using quality, which is characterized in that include the following steps：
（1）Surface preparation：
With clear water to woven willow-plaited process product surface carry out cleaning impurity elimination processing after, then it is dried processing it is spare；
（2）Coating coating processing：
Pre-prepared coating is evenly applied to step（1）Treated willow-plaited process product surface, dries in the air after the completion to surface drying
It is spare afterwards；Each ingredient and its corresponding parts by weight are in the coating：8 ~ 10 parts of nano-titanium dioxides, 2 ~ 4 parts of urea, 1 ~ 2 part
Potassium nitrate, 2 ~ 4 parts of potassium dihydrogen phosphates, 0.5 ~ 1 part of trialkyl phosphates, 1 ~ 1.5 part of polyvinyl alcohol, 1 ~ 2 part of methyl methacrylate
Ester, 15 ~ 20 parts of ethyl alcohol, 150 ~ 160 parts of water；
（3）Laser treatment：
By step（2）Treated, and willow-plaited process product are put into laser treatment instrument, are carried out at surface laser to willow-plaited process product
Reason, takes out spare after the completion；
（4）It is cooling to be dried：
With clear water to step（3）Treated, and willow-plaited process product are rinsed is cooled to room temperature, and then it are dried again place
After reason is not more than 8% to whole water content.
2. a kind of processing method for improving willow-plaited process product and using quality according to claim 1, which is characterized in that step
（1）Described in drying process temperature be 80 ~ 85 DEG C.
3. a kind of processing method for improving willow-plaited process product and using quality according to claim 1, which is characterized in that step
（2）Described in nano-titanium dioxide granular size be 10 ~ 40nm.
4. a kind of processing method for improving willow-plaited process product and using quality according to claim 1, which is characterized in that step
（3）Described in the power of laser treatment be 400 ~ 500W, the speed of laser scanning is 450 ~ 500mm/min.
5. a kind of processing method for improving willow-plaited process product and using quality according to claim 1, which is characterized in that step
（4）Described in drying process temperature be 90 ~ 95 DEG C.