CN108440858A - The special harness of environmentally friendly vehicle wraps up PVC film - Google Patents
The special harness of environmentally friendly vehicle wraps up PVC film Download PDFInfo
- Publication number
- CN108440858A CN108440858A CN201810111785.8A CN201810111785A CN108440858A CN 108440858 A CN108440858 A CN 108440858A CN 201810111785 A CN201810111785 A CN 201810111785A CN 108440858 A CN108440858 A CN 108440858A
- Authority
- CN
- China
- Prior art keywords
- pvc film
- environmentally friendly
- friendly vehicle
- special harness
- wraps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of special harness of environmentally friendly vehicle to wrap up PVC film, and raw material weight percent is as follows：Corvic 58 60%, dioctyl terephthalate 24 26%, epoxidized soybean oil 2%, filler 8%, calcium zinc stabilizer 1%, antioxidant 2 2.5%, colorant 2%, antimony oxide 2 2.5%.By using ethylene process resin, fire retardant and antioxidant are combined, and greatly improve the tension intensity of the PVC film, and improve fire-resistant, anti-oxidant, anti-aging property.
Description
Technical field
The invention belongs to environmentally friendly vehicle special harness package PVC film fields, more specifically more particularly to a kind of environmentally friendly vapour
The special harness of vehicle wraps up PVC film.
Background technology
PVC built up membranes are in extensive use, but the existing PVC film intensity for automotive wire bundle package is poor, easy
Combustion, oxidizable, when use, is easy to bring security risk, and usage time is short, and aging is fast.
Invention content
The purpose of the present invention is to provide a kind of special harness of environmentally friendly vehicle to wrap up PVC film, to solve above-mentioned background technology
The problem of middle proposition.
To achieve the above object, the present invention provides the following technical solutions：
A kind of special harness package PVC film of environmentally friendly vehicle, raw material weight percent are as follows：Corvic 58-60%,
Dioctyl terephthalate 24-26%, epoxidized soybean oil 2%, filler 8%, calcium zinc stabilizer 1%, antioxidant 2-2.5%, colorant
2%, antimony oxide 2-2.5%.
Preferably, the epoxide number of the epoxidized soybean oil is not less than 6.5%.
Preferably, the filler is the mixture of calcium carbonate, barium sulfate and fire retardant.
Compared with prior art, the beneficial effects of the invention are as follows：By using ethylene process resin, fire retardant and antioxidant
It is combined, greatly improves the tension intensity of the PVC film, and improve fire-resistant, anti-oxidant, anti-aging property.
Specific implementation mode
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
A kind of special harness package PVC film of environmentally friendly vehicle, raw material weight percent are as follows：Corvic 58-
60%, dioctyl terephthalate 24-26%, epoxidized soybean oil 2%, filler 8%, calcium zinc stabilizer 1%, antioxidant 2-2.5%,
Colorant 2%, antimony oxide 2-2.5%.
Specifically, the epoxide number of the epoxidized soybean oil is not less than 6.5%.
Specifically, the filler is the mixture of calcium carbonate, barium sulfate and fire retardant.
The present invention also provides the preparation processes that a kind of special harness of environmentally friendly vehicle wraps up PVC film, by the weight hundred of raw material
Score numerical value is input in automatic metering equipment, and automatic metering equipment measures material, and material is added in high-speed mixer
20-30min is mixed, mixing 30-40min in ten thousand horsepowers of mixers is then fed into, rolling turbine using gelatinization carries out continuous pressure rolling, leads to
Five roll calendar calendering formations are sent into after crossing filter filtering, and decorative pattern is suppressed in the position for needing to be embossed, are rolled up after cooling and shaping
Take packaging.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (3)
1. a kind of special harness of environmentally friendly vehicle wraps up PVC film, which is characterized in that its raw material weight percent is as follows：Polychlorostyrene second
Olefine resin 58-60%, dioctyl terephthalate 24-26%, epoxidized soybean oil 2%, filler 8%, calcium zinc stabilizer 1% are anti-oxidant
Agent 2-2.5%, colorant 2%, antimony oxide 2-2.5%.
2. the special harness of a kind of environmentally friendly vehicle according to claim 1 wraps up PVC film, it is characterised in that：The epoxy is big
The epoxide number of soya-bean oil is not less than 6.5%.
3. the special harness of a kind of environmentally friendly vehicle according to claim 1 wraps up PVC film, it is characterised in that：The filler
For the mixture of calcium carbonate, barium sulfate and fire retardant.