CN108504902A - 一种电阻合金丝 - Google Patents

一种电阻合金丝 Download PDF

Info

Publication number
CN108504902A
CN108504902A CN201810478014.2A CN201810478014A CN108504902A CN 108504902 A CN108504902 A CN 108504902A CN 201810478014 A CN201810478014 A CN 201810478014A CN 108504902 A CN108504902 A CN 108504902A
Authority
CN
China
Prior art keywords
alloy wire
resistance alloy
yttrium
manganese
nickel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810478014.2A
Other languages
English (en)
Inventor
汪杨重子
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Tianhong Electronics Co ltd
Original Assignee
Suzhou Tianhong Electronics Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Tianhong Electronics Co ltd filed Critical Suzhou Tianhong Electronics Co ltd
Priority to CN201810478014.2A priority Critical patent/CN108504902A/zh
Publication of CN108504902A publication Critical patent/CN108504902A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种电阻合金丝，所述电阻合金丝由镍、硅、锰、钇、铜、混合稀土和铁组成。通过上述方式，本发明提供的电阻合金丝，在保证电阻率的情况下，高温寿命得到明显提高。

Description

一种电阻合金丝
技术领域
本发明涉及电阻材料领域，特别是涉及一种电阻合金丝。
背景技术
电阻合金丝应用于生产过热保护和精准控制电流过载的过热保护元件，有效地防止( 电机、变压器... 等) 因电流过大而产生过热。现有的电阻合金丝在高温使用时，寿命较低。
发明内容
本发明主要解决的技术问题是提供一种电阻合金丝，在保证电阻率的情况下，高温寿命得到明显提高。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种电阻合金丝，所述电阻合金丝由镍、硅、锰、钇、铜、混合稀土和铁组成，所述电阻合金丝中各组分的质量百分比含量为：
镍：80%~90%；
硅：0.7%~1.5%；
锰：0.35%~0.42%；
钇：0.05%~0.12%；
铜：1.1%~1.9%；
铁：余量。
在本发明一个较佳实施例中，所述电阻合金丝中各组分的质量百分比含量为：镍：80%；硅：0.7%；锰：0.35%；钇：0.05%；铜：1.1%；铁：余量。
在本发明一个较佳实施例中，所述电阻合金丝中各组分的质量百分比含量为：镍：81%；硅：0.8%；锰：0.36%；钇：0.06%；铜：1.2%；铁：余量。
在本发明一个较佳实施例中，所述电阻合金丝中各组分的质量百分比含量为：镍：82%；硅：0.9%；锰：0.37%；钇：0.08%；铜：1.4%；铁：余量。
在本发明一个较佳实施例中，所述电阻合金丝中各组分的质量百分比含量为：镍：86%；硅：1.2%；锰：0.39%；钇：0.09%；铜：1.5%；铁：余量。
在本发明一个较佳实施例中，所述电阻合金丝的电阻率为（0.31~0.35）±0.01μΩ·m。
本发明的有益效果是：本发明指出的一种电阻合金丝，在保证电阻率的情况下，高温寿命得到明显提高。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例1：所述电阻合金丝中各组分的质量百分比含量为：镍：80%；硅：0.7%；锰：0.35%；钇：0.05%；铜：1.1%；铁：余量。
实施例2：所述电阻合金丝中各组分的质量百分比含量为：镍：81%；硅：0.8%；锰：0.36%；钇：0.06%；铜：1.2%；铁：余量。
实施例3：所述电阻合金丝中各组分的质量百分比含量为：镍：82%；硅：0.9%；锰：0.37%；钇：0.08%；铜：1.4%；铁：余量。
实施例4：所述电阻合金丝中各组分的质量百分比含量为：镍：86%；硅：1.2%；锰：0.39%；钇：0.09%；铜：1.5%；铁：余量。
测试例：对实施例1-4中的电阻合金丝进行性能测试，测试方法参照相应的国家标准，测试结果见表1。
表1：
综上所述，本发明指出的一种电阻合金丝，在保证电阻率的情况下，高温寿命得到明显提高。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (6)

1.一种电阻合金丝，其特征在于，所述电阻合金丝由镍、硅、锰、钇、铜、混合稀土和铁组成，所述电阻合金丝中各组分的质量百分比含量为：
镍：80%~90%；
硅：0.7%~1.5%；
锰：0.35%~0.42%；
钇：0.05%~0.12%；
铜：1.1%~1.9%；
铁：余量。
2.根据权利要求1所述的电阻合金丝，其特征在于，所述电阻合金丝中各组分的质量百分比含量为：镍：80%；硅：0.7%；锰：0.35%；钇：0.05%；铜：1.1%；铁：余量。
3.根据权利要求1所述的电阻合金丝，其特征在于，所述电阻合金丝中各组分的质量百分比含量为：镍：81%；硅：0.8%；锰：0.36%；钇：0.06%；铜：1.2%；铁：余量。
4.根据权利要求1所述的电阻合金丝，其特征在于，所述电阻合金丝中各组分的质量百分比含量为：镍：82%；硅：0.9%；锰：0.37%；钇：0.08%；铜：1.4%；铁：余量。
5.根据权利要求1所述的电阻合金丝，其特征在于，所述电阻合金丝中各组分的质量百分比含量为：镍：86%；硅：1.2%；锰：0.39%；钇：0.09%；铜：1.5%；铁：余量。
6.根据权利要求1所述的电阻合金丝，其特征在于，所述电阻合金丝的电阻率为（0.31~0.35）±0.01μΩ·m。
CN201810478014.2A 2018-05-18 2018-05-18 一种电阻合金丝 Pending CN108504902A (zh)