CN108589291A - Antibacterial refuses the processing method of the face fabric for automobile seat of oil - Google Patents
Antibacterial refuses the processing method of the face fabric for automobile seat of oil Download PDFInfo
- Publication number
- CN108589291A CN108589291A CN201810348240.9A CN201810348240A CN108589291A CN 108589291 A CN108589291 A CN 108589291A CN 201810348240 A CN201810348240 A CN 201810348240A CN 108589291 A CN108589291 A CN 108589291A
- Authority
- CN
- China
- Prior art keywords
- oil
- antibacterial
- automobile seat
- repellent
- finishing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the processing methods that a kind of antibacterial refuses the face fabric for automobile seat of oil, refuse oily technological process in face fabric for automobile seat, increase antiseptic, is i.e. flow is followed successively by：The processing of oil-refusing finishing agent, addition antiseptic, two leachings two roll, preliminary drying and baking；Treatment method is simple, fabric after processing, while can achieve the effect that water and oil repellant and antibacterial, and has better wearability, gas permeability and penetrability.
Description
Technical Field
The invention relates to treatment of automobile seat fabric, in particular to a method for treating antibacterial and oil-repellent automobile seat fabric.
Background
The automobile seat fabric is generally divided into leather and cloth; the terylene accounts for a great proportion in the fiber raw materials of the automobile seat fabric, wherein the terylene accounts for 72 percent in Western Europe, 69 percent in Japan and 60 percent in America; because the terylene has good elasticity, has certain drapability and good wrinkle resistance, and exceeds other fibers; the high strength, excellent light resistance, corrosion resistance and wear resistance make the fabric popular in the application of the automobile seat fabric, and the fabric is stiff and smooth and durable. However, terylene is easy to stain, and can be easily stained by body contact, chemical reaction, static effect and the like. Automobile seats are not washed frequently along with the service life of automobiles, bacteria are more and more, and water-repellent and oil-repellent finishing and antibacterial finishing are needed in order to keep good appearance and cleanness of the seats.
Disclosure of Invention
Based on the problems, the invention discloses a method for processing the antibacterial and oil-repellent automobile seat fabric, which is simple, and the antibacterial finishing is also carried out during the oil-repellent finishing, and meanwhile, the wear resistance, the air permeability and the moisture permeability of the fabric are also enhanced.
The technical scheme adopted by the invention is as follows:
the processing method of the antibacterial and oil-repellent automobile seat fabric is characterized in that an antibacterial agent is added in the oil-repellent process flow of the automobile seat fabric, namely the flow sequentially comprises the following steps: treating an oil repellent finishing agent, adding an antibacterial agent, soaking and rolling twice, pre-drying and baking; wherein,
step 1, treating an oil-repellent finishing agent, wherein the used oil-repellent finishing agent is an organic fluorine FG-910 finishing agent, and the concentration is 40-70 g/L;
in the step 2, an antibacterial agent is added, the antibacterial agent is xylan, and the treatment process comprises the following steps: and (2) soaking the fabric obtained in the step (1) in a xylan solution for 24 hours, then soaking in a 0.85% NaCl solution, adjusting the pH value of the solution with a NaOH solution to 7.0-7.2, placing in a pressure steam sterilizer, after 30 minutes, soaking in a 75% ethanol solution for 1 minute, and then washing.
In step 1, the immersion time in the oil repellent finish was 2 minutes.
In the pre-drying process, the pre-drying temperature is 80-85 ℃, and the pre-drying time is 5-10 minutes.
In the baking process, the baking temperature is 110-120 ℃, and the baking time is 5 minutes.
The treatment method is simple, the oil-repellent finishing agent is treated firstly, the organic fluorine FG-910 finishing agent with the concentration of 40-70g/L is adopted, the surface of the fiber can be effectively and fully covered, the film on the surface of the fiber can be in a fully and fully covered state, and meanwhile, the finishing agent with the concentration can also achieve a good water-repellent effect; the dipping time in the oil-repellent finishing agent is 2 minutes, the dipping time cannot be too long, and the dipping time is too long, so that the oil-repellent and water-repellent performance of the fabric is reduced; xylan is selected as the antibacterial agent, and-NH 3 ions in xylan molecules are adsorbed on the surfaces of bacterial cells to generate a new macromolecular membrane structure, so that transportation of nutrients in the cells is hindered, positive charges and negative charges in cell walls and cell membranes are unevenly distributed, the cell walls are damaged, and the effect of inhibiting the growth of harmful bacteria is further achieved; the xylan permeates into harmful bacteria cells to cause the physiological activity disorder of the harmful bacteria cells, so that the aim of sterilization is fulfilled; the pre-drying temperature is 80-85 ℃, so that the finishing agent and the antibacterial agent can completely react on the surface of the fiber and can be better crosslinked into chains; the baking temperature is 110-120 ℃, the finishing agent and the antibacterial agent form a protective film on the fiber surface, and the organic fluorine polymer is ensured to be subjected to crosslinking and curing reaction, so that the fabric achieves the optimal water-repellent, oil-repellent and antibacterial effects.
Detailed Description
The technical solution of the present invention is described in detail below. The embodiments of the present invention are provided only for illustrating a specific structure, and the scale of the structure is not limited by the embodiments.
The processing method of the antibacterial and oil-repellent automobile seat fabric is characterized in that an antibacterial agent is added in the oil-repellent process flow of the automobile seat fabric, namely the flow sequentially comprises the following steps: treating an oil repellent finishing agent, adding an antibacterial agent, soaking and rolling twice, pre-drying and baking;
step 1, treating an oil-repellent finishing agent, wherein the used oil-repellent finishing agent is an organic fluorine FG-910 finishing agent with the concentration of 40-70 g/L; the dipping time is 2 minutes;
step 2, adding an antibacterial agent, wherein the antibacterial agent is xylan, and the treatment process comprises the following steps: soaking the fabric obtained in the step 1 in a xylan solution for 24 hours, then soaking the fabric in a 0.85% NaCl solution, adjusting the pH value of the solution with a NaOH solution to 7.0-7.2, placing the fabric in a pressure steam sterilizer, after 30 minutes, soaking the fabric in a 75% ethanol solution for 1 minute, and then washing the fabric;
and step 3: conventional two-dipping and two-rolling;
and 4, step 4: pre-drying at 80-85 deg.C for 5-10 min;
and 5: baking at 110-120 deg.C for 5 min.
Claims (4)
1. The processing method of the antibacterial and oil-repellent automobile seat fabric is characterized by comprising the following steps of: in the oil-repellent process flow of the automobile seat fabric, an antibacterial agent is added, namely the flow sequentially comprises the following steps: treating an oil repellent finishing agent, adding an antibacterial agent, soaking and rolling twice, pre-drying and baking; wherein,
step 1, treating an oil-repellent finishing agent, wherein the used oil-repellent finishing agent is an organic fluorine FG-910 finishing agent, and the concentration is 40-70 g/L;
in the step 2, an antibacterial agent is added, the antibacterial agent is xylan, and the treatment process comprises the following steps: and (2) soaking the fabric obtained in the step (1) in a xylan solution for 24 hours, then soaking in a 0.85% NaCl solution, adjusting the pH value of the solution with a NaOH solution to 7.0-7.2, placing in a pressure steam sterilizer, after 30 minutes, soaking in a 75% ethanol solution for 1 minute, and then washing.
2. The method for treating an antibacterial and oil repellent automobile seat fabric according to claim 1, wherein in the step 1, the immersion time in the oil repellent finishing agent is 2 minutes.
3. The method for processing the antibacterial and oil repellent automobile seat fabric according to claim 1, characterized in that in the pre-drying, the pre-drying temperature is 80-85 ℃, and the pre-drying time is 5-10 minutes.
4. The method for treating the antibacterial and oil repellent automobile seat fabric according to claim 1, wherein in the baking, the baking temperature is 110-120 ℃ and the baking time is 5 minutes.