CN108754816A - A kind of preparation method of the polyester knitting wick fabric of waterproof - Google Patents
A kind of preparation method of the polyester knitting wick fabric of waterproof Download PDFInfo
- Publication number
- CN108754816A CN108754816A CN201810567688.XA CN201810567688A CN108754816A CN 108754816 A CN108754816 A CN 108754816A CN 201810567688 A CN201810567688 A CN 201810567688A CN 108754816 A CN108754816 A CN 108754816A
- Authority
- CN
- China
- Prior art keywords
- dacron thread
- epoxy resin
- polyester knitting
- waterproof
- wick fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of the polyester knitting wick fabric of waterproof, include the following steps：S1, at 20-25 DEG C, the dacron thread of stretching is impregnated into 1h in the epoxy, is taken out, stops stretching dacron thread, after placing 10min, cures 1h in 100-120 DEG C；S2, the dacron thread after solidification is woven using the weaving manner of variation double rib, extracts a needle every 15-20 wales, forms polyester knitting wick fabric.Utilize the high-elastic property of dacron thread, it is impregnated by stretching, epoxy resin is set fully to soak dacron thread, in normal state, extra epoxy resin is lost on restorable dacron thread, film layer is formed on dacron thread surface after epoxy resin cure, to improve the water resistance of dacron thread, is finally knitted to form dacron thread knitting wick fabric.
Description
Technical field
The present invention relates to garment industries, and in particular to a kind of preparation method of the polyester knitting wick fabric of waterproof.
Background technology
Polyester knitting wick fabric is to make raw material with low-elasticity terylene fibre, is woven using variation interlock, to
Keep cloth cover presentation wealthy narrow not equal, rough directly to striped.The thickness of striped can as required depending on.This fabric bumps point
Bright, feel is thick and solid plentiful, and elasticity and warmth retention property are good.
But due to dacron thread and weaving manner, polyester knitting wick fabric has stronger absorbability, as clothes
When cloth, get that drying time is longer wet accidentally, the overall weight of clothes has been further aggravated after thick and solid cloth water suction itself, has worn
It is stronger heavy burden sense.
In conclusion there is an urgent need for a kind of polyester knitting wick fabrics of waterproof.
Invention content
For overcome the deficiencies in the prior art, the purpose of the present invention is to provide a kind of polyester knitting wick faces of waterproof
Material.
To solve the above problems, the technical solution adopted in the present invention is as follows：
A kind of preparation method of the polyester knitting wick fabric of waterproof, includes the following steps：
S1, at 20-25 DEG C, the dacron thread of stretching is impregnated into 1h in the epoxy, is taken out, stops stretching dacron thread, put
After setting 10min, cure 1h in 100-120 DEG C；
S2, the dacron thread after solidification is woven using the weaving manner of variation double rib, is extracted every 15-20 wales
One needle forms polyester knitting wick fabric.
Preferably, the epoxy resin is alicyclic based epoxy resin.
Alicyclic based epoxy resin molecule carries cyclic structure, has preferable hydrophobic performance.
Preferably, which is characterized in that the epoxide number of the alicyclic based epoxy resin is 0.5-0.6mol/100g.
Epoxide number is the modest viscosity of 0.5-0.6mol/100g, can be sufficiently humidified so as to and be attached to dacron thread.
Preferably, it is mixed with breaking-down agent in the epoxy resin, the mass ratio of the epoxy resin and the breaking-down agent is 11:
(1-5)。
Breaking-down agent is conducive to reinforce the binding force of dacron thread and epoxy resin, to enhance the polyester knitting wick item of waterproof
The water resistance of fabric.
Preferably, the mass ratio of the epoxy resin and the breaking-down agent is 11:5.
Beneficial effects of the present invention：Using the high-elastic property of dacron thread, is impregnated by stretching, epoxy resin is made fully to soak
Dacron thread, in normal state, extra epoxy resin is lost on restorable dacron thread, in terylene after epoxy resin cure
Silk table face forms film layer, to improve the water resistance of dacron thread, is finally knitted to form dacron thread knitting wick fabric.
Specific implementation mode
Invention is further described in detail With reference to embodiment.
Embodiment 1
A kind of preparation method of the polyester knitting wick fabric of waterproof, includes the following steps：
S1, at 20-25 DEG C, the dacron thread of stretching is immersed in 1h in bisphenol A epoxide resin, take out, stop stretch terylene
Silk after placing 10min, cures 1h in 100-120 DEG C；
S2, the dacron thread after solidification is woven using the weaving manner of variation double rib, is extracted every 15-20 wales
One needle forms polyester knitting wick fabric.
The mass ratio of bisphenol A epoxide resin and breaking-down agent is 11:1.
The epoxide number of bisphenol A epoxide resin is 0.5-0.6mol/100g.
Embodiment 2
A kind of preparation method of the polyester knitting wick fabric of waterproof, includes the following steps：
S1, at 20-25 DEG C, the dacron thread of stretching is immersed in 1h in bisphenol F epoxy resin, take out, stop stretch terylene
Silk after placing 10min, cures 1h in 100-120 DEG C；
S2, the dacron thread after solidification is woven using the weaving manner of variation double rib, is extracted every 15-20 wales
One needle forms polyester knitting wick fabric.
The mass ratio of bisphenol F epoxy resin and breaking-down agent is 11:5.
The epoxide number of bisphenol F epoxy resin is 0.5-0.6mol/100g.
Embodiment 3
A kind of preparation method of the polyester knitting wick fabric of waterproof, includes the following steps：
S1, at 20-25 DEG C, the dacron thread of stretching is immersed in 1h in 206 resin of epoxy, take out, stop stretch terylene
Silk after placing 10min, cures 1h in 100-120 DEG C；
S2, the dacron thread after solidification is woven using the weaving manner of variation double rib, is extracted every 15-20 wales
One needle forms polyester knitting wick fabric.
The mass ratio of 206 resin of epoxy and breaking-down agent is 11:3.
The epoxide number of 206 resin of epoxy is 0.5-0.6mol/100g.
206 resin of epoxy is a kind of alicyclic based epoxy resin of the prior art.
Embodiment 4
A kind of preparation method of the polyester knitting wick fabric of waterproof, includes the following steps：
S1, at 20-25 DEG C, the dacron thread of stretching is immersed in 1h in 269 resin of epoxy, take out, stop stretch terylene
Silk after placing 10min, cures 1h in 100-120 DEG C；
S2, the dacron thread after solidification is woven using the weaving manner of variation double rib, is extracted every 15-20 wales
One needle forms polyester knitting wick fabric.
The mass ratio of 269 resin of epoxy and breaking-down agent is 11:5.
The epoxide number of 269 resin of epoxy is 0.5-0.6mol/100g.
269 resin of epoxy is a kind of alicyclic based epoxy resin of the prior art.
Comparative example
By dacron thread using the weaving manner braiding of variation double rib, a needle is extracted every 15-20 wales, formation is washed
Synthetic fibre is knitted wick fabric.
It is that 130g polyester knitting wick fabrics are placed in water immersion 3h by weight in embodiment 1-4 and comparative example, takes out
It weighs immediately afterwards；Polyester knitting wick fabric after weighing is weighed after hanging 1h in the same space, and calculated weight variation is surveyed
Test result is as shown in table 1.
Table 1
| Project | Weigh weight/g after taking-up | Weight/g after suspension 1h |
| Embodiment 1 | 167 | 139 |
| Embodiment 2 | 165 | 143 |
| Embodiment 3 | 137 | 131 |
| Embodiment 4 | 147 | 134 |
| Comparative example | 208 | 176 |
The above embodiment is only the certain preferred embodiments of the present invention, cannot limit the model protected of the present invention with this
It encloses, the variation and replacement of any unsubstantiality that those skilled in the art is done on the basis of the present invention belong to the present invention
Range claimed.
Claims (5)
1. a kind of preparation method of the polyester knitting wick fabric of waterproof, includes the following steps：
S1, at 20-25 DEG C, the dacron thread of stretching is impregnated into 1h in the epoxy, is taken out, stops stretching dacron thread, place
After 10min, cure 1h in 100-120 DEG C；
S2, the dacron thread after solidification is woven using the weaving manner of variation double rib, one is extracted every 15-20 wales
Needle forms polyester knitting wick fabric.
2. the preparation method of the polyester knitting wick fabric of waterproof according to claim 1, which is characterized in that the epoxy
Resin is alicyclic based epoxy resin.
3. the preparation method of the polyester knitting wick fabric of waterproof according to claim 2, which is characterized in that the alicyclic ring
The epoxide number of same clan's epoxy resin is 0.5-0.6mol/100g.
4. according to the preparation method of the polyester knitting wick fabric of waterproof described in claim 1-3 any one claims,
It is characterized in that, being mixed with breaking-down agent in the epoxy resin, the mass ratio of the epoxy resin and the breaking-down agent is 11:(1-
5)。
5. the preparation method of the polyester knitting wick fabric of waterproof according to claim 4, which is characterized in that the epoxy
The mass ratio of resin and the breaking-down agent is 11:5.