CN109181476A - A kind of graphene anticorrosive paint and its application method - Google Patents
A kind of graphene anticorrosive paint and its application method Download PDFInfo
- Publication number
- CN109181476A CN109181476A CN201810957300.7A CN201810957300A CN109181476A CN 109181476 A CN109181476 A CN 109181476A CN 201810957300 A CN201810957300 A CN 201810957300A CN 109181476 A CN109181476 A CN 109181476A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- graphene
- anticorrosive paint
- preservative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of graphene anticorrosive paints, it is characterized in that, raw material including following parts by weight, epoxy resin part, deionization moisture content, graphene film part, graphene dispersing solution part, levelling agent part, wetting dispersing agent part, pigment part, alcohol solvent part, anionic acrylic lotion part, defoaming agent part, Rs preservative part, curing agent part, polyaniline part, coalescing agent part, different monooctyl ester part, thickener part, the sour two formicester parts of rich code, demoulding preservative part, toughener part, silane coupling agent part.The preparation method of the above raw material includes: 1, is mixed, 2, auxiliary material high-speed stirred is added into slurries, 3, slurries sand mill is added and is sanded, 4, put into and carry out high-speed stirred in tank of sizing mixing and form graphene anticorrosive paint, the present invention uses environment-friendly materials, greatly improves product quality；Labor and material saving is easy to use, scumbling, while having the various aspects of performance such as excellent waterproofness, heat resistance, anti-corrosive properties, weatherability, stability.
Description
Technical field
The present invention relates to the fields of graphene coating, more particularly, to a kind of graphene anticorrosive paint and its application method.
Background technique
Anticorrosive paint is generally divided into conventional anticorrosive paint and anticorrosive paint, is essential one kind in paint
Coating.Conventional anticorrosive paint is under general condition, to play the role of the longevity etch-proof, protection non-ferrous metal uses to metal etc.
Life；It for anticorrosive paint refers to relatively conventional anticorrosive paint, can be applied in relatively harsh corrosive environment, and have and can reach
A kind of anticorrosive paint of protection period longer than conventional anticorrosive paint.
However, existing anticorrosive paint has the disadvantage in that 1, pollutes to atmosphere；2, service life is short；3, price
Valuableness, it is both dangerous or not environmentally；4, volatile in work progress, so that the health to construction personnel impacts.
Therefore, a kind of environmentally friendly graphene anticorrosive paint is developed, the hardness, good of high paint film is made it have
Water resistance and weatherability are current urgent problems to be solved.
Summary of the invention
The present invention is to overcome above situation insufficient, it is desirable to provide a kind of technical solution that can solve the above problem.
A kind of graphene anticorrosive paint, the raw material including following parts by weight, 90-100 parts of epoxy resin, deionized water 15-
20 parts, 15-17 parts of graphene film, 10-20 parts of graphene dispersing solution, 3-5 parts of levelling agent, 5-7 parts of wetting dispersing agent, pigment 3-5
Part, 35-40 parts of alcohol solvent, 20-25 parts of anionic acrylic lotion, 30-50 parts of Rs preservative, is consolidated 16-18 parts of defoaming agent
8-16 parts of agent, 20-36 parts of polyaniline, 10-30 parts of coalescing agent, monooctyl ester 12-15 parts different, 5-8 parts of thickener, rich code acid diformazan
10-15 parts of rouge, demoulding preservative 10-15 parts, 5-10 parts of toughener, 15-20 parts of silane coupling agent.
A kind of application method of graphene anticorrosive paint, comprising the following steps:
S1, the epoxy resin of equivalent ingredient, deionized water, graphene dispersing solution, different monooctyl ester and sour two formicesters of rich code are put
Into being stirred under vacuum in dissolving machine, carries out vacuum stirring and be uniformly dissolved, form mixed liquor；
S2, after raw material vacuum stirring is uniformly dissolved to form mixed liquor, Rs preservative, the demoulding that equivalent ingredient is added are anti-
Then rotten agent, thickener and silane coupling agent are put into vacuum screw stirring differentiation machine, carry out 30-50 points of high-speed stirred differentiation
Clock forms uniform mixed serum；
It is S3, uniform mixed serum is micro- from sand mill by the inspiration of vacuum drawn machine, it is micro- micro- to fineness≤15 from being sanded
Rice；
S4, it is poured into micro- in vacuum screw stirring differentiation machine again from qualified mixed serum is sanded, stir at low speed point
Change, when mixed serum is stirred to regulation viscosity, graphene anticorrosive paint is made.
As a further solution of the present invention: needing glass bar to be stirred in the S1.
As a further solution of the present invention: the mixing speed of the S2 high speed stirring is 1300r/min.
As a further solution of the present invention: the mixing speed stirred at low speed in the S4 is 450r/min.
Compared with prior art, the beneficial effects of the present invention are: being obviously improved the production efficiency of graphene anticorrosive paint；Greatly
The sales volume of width raising graphene anticorrosive paint；Graphene anticorrosive paint has excellent waterproofness, cheats corruption, is heat-resisting simultaneously
The various aspects of performance such as property, weatherability, stability.It is embodied in following:
1, graphene anticorrosive paint has good waterproofness and hole corruption is because of the stable sp2 hybrid structure of graphene
Physical barriers can be formed between smeared material and active medium, prevent the progress of scattering and permeating, special lamella
Shape structure acts on the good physical shielding that is diffused with of water, oxygen and ion, can increase the infiltration of corrosive medium in the coating
Saturating distance, to reach the corrosion proof function to smeared material.Graphene also has good thermal stability and chemical stabilization
Property, it is able to maintain under 600 DEG C of hot conditions and in corrosive environment relatively stable, ensure that coating in extreme circumstances
Still there is preferable protective action, anti-corruption of the coating in wet environment also can be enhanced in the lipophilic-hydrophobic property itself having
Corrosion energy.
2, graphene anticorrosive paint has outstanding insulating properties, the anionic anionic type propylene in graphene anticorrosive paint
Anion in yogurt liquid can be complementary with the positive and negative attraction of the electron ion in atmosphere, so that electron ion be made to lose electric conductivity；
3, the construction technology of graphene anticorrosive paint is simple, convenient and efficient, only needs Typical spray in required corrosion-resistant object
On surface, so that it may carry out anti-corrosion in time, and the investment of production equipment of graphene anticorrosive paint is small；
4, graphene anticorrosive paint is environmental type product (being detected by Europe superscript SGS), no pollution to the environment, energy conservation
Emission reduction, nonirritant toxic gas distributes during smearing, the safe handling that can be trusted.
Additional aspect and advantage of the invention will be set forth in part in the description, and will partially become from the following description
Obviously, or practice through the invention is recognized.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment one
A kind of graphene anticorrosive paint, the raw material including following parts by weight, 90-100 parts of epoxy resin, deionized water 15-
20 parts, 15-17 parts of graphene film, 10-20 parts of graphene dispersing solution, 3-5 parts of levelling agent, 5-7 parts of wetting dispersing agent, pigment 3-5
Part, 35-40 parts of alcohol solvent, 20-25 parts of anionic acrylic lotion, 30-50 parts of Rs preservative, is consolidated 16-18 parts of defoaming agent
8-16 parts of agent, 20-36 parts of polyaniline, 10-30 parts of coalescing agent, monooctyl ester 12-15 parts different, 5-8 parts of thickener, rich code acid diformazan
10-15 parts of rouge, demoulding preservative 10-15 parts, 5-10 parts of toughener, 15-20 parts of silane coupling agent.
A kind of application method of graphene anticorrosive paint, comprising the following steps:
S1, the epoxy resin of equivalent ingredient, deionized water, graphene dispersing solution, different monooctyl ester and sour two formicesters of rich code are put
Into being stirred under vacuum in dissolving machine, carries out vacuum stirring and be uniformly dissolved, form mixed liquor；
S2, after raw material vacuum stirring is uniformly dissolved to form mixed liquor, Rs preservative, the demoulding that equivalent ingredient is added are anti-
Then rotten agent, thickener and silane coupling agent are put into vacuum screw stirring differentiation machine, carry out 30-50 points of high-speed stirred differentiation
Clock forms uniform mixed serum；
It is S3, uniform mixed serum is micro- from sand mill by the inspiration of vacuum drawn machine, it is micro- micro- to fineness≤15 from being sanded
Rice；
S4, it is poured into micro- in vacuum screw stirring differentiation machine again from qualified mixed serum is sanded, stir at low speed point
Change, when mixed serum is stirred to regulation viscosity, graphene anticorrosive paint is made.
Embodiment two
A kind of graphene anticorrosive paint, the raw material including following parts by weight, 90 parts of epoxy resin, 15 parts of deionized water, stone
15 parts of black alkene piece, 10 parts of graphene dispersing solution, 3 parts of levelling agent, 5 parts of wetting dispersing agent, 3 parts of pigment, 35 parts of alcohol solvent, yin from
20 parts of subtype acrylic emulsion, 16 parts of defoaming agent, 30 parts of Rs preservative, 8 parts of curing agent, 20 parts of polyaniline, 10 parts of coalescing agent,
12 parts of different monooctyl ester, 5 parts of thickener, sour 10 parts of two formicester of rich code, demoulding 10 parts of preservative, 5 parts of toughener, silane coupling agent 15
Part.
Embodiment three
A kind of graphene anticorrosive paint, the raw material including following parts by weight, 90 parts of epoxy resin, 15 parts of deionized water, stone
15 parts of black alkene piece, 10 parts of graphene dispersing solution, 3 parts of levelling agent, 5 parts of wetting dispersing agent, 3 parts of pigment, 35 parts of alcohol solvent, yin from
20 parts of subtype acrylic emulsion, 16 parts of defoaming agent, 30 parts of Rs preservative, 8 parts of curing agent, 20 parts of polyaniline, 10 parts of coalescing agent,
12 parts of different monooctyl ester, 5 parts of thickener, sour 10 parts of two formicester of rich code, demoulding 10 parts of preservative, 5 parts of toughener, silane coupling agent 15
Part.
Example IV
A kind of graphene anticorrosive paint, the raw material including following parts by weight, 100 parts of epoxy resin, 20 parts of deionized water, stone
17 parts of black alkene piece, 20 parts of graphene dispersing solution, 5 parts of levelling agent, 7 parts of wetting dispersing agent, 5 parts of pigment, 40 parts of alcohol solvent, yin from
25 parts of subtype acrylic emulsion, 18 parts of defoaming agent, 50 parts of Rs preservative, 16 parts of curing agent, 36 parts of polyaniline, coalescing agent 30
Part, 15 parts of different monooctyl ester, 8 parts of thickener, sour 15 parts of two formicester of rich code, demoulding 15 parts of preservative, 10 parts of toughener, silane coupling agent
20 parts.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
Claims (9)
1. a kind of graphene anticorrosive paint, which is characterized in that the raw material including following parts by weight, 90-100 parts of epoxy resin are gone
15-20 parts of ionized water, 15-17 parts of graphene film, 10-20 parts of graphene dispersing solution, 3-5 parts of levelling agent, wetting dispersing agent 5-7
Part, 3-5 parts of pigment, 35-40 parts of alcohol solvent, 20-25 parts of anionic acrylic lotion, 16-18 parts of defoaming agent, Rs preservative
30-50 parts, 8-16 parts of curing agent, 20-36 parts of polyaniline, 10-30 parts of coalescing agent, monooctyl ester 12-15 parts different, 5-8 parts of thickener,
Sour 10-15 parts of two formicester of rich code, demoulding preservative 10-15 parts, 5-10 parts of toughener, 15-20 parts of silane coupling agent.
2. a kind of graphene anticorrosive paint according to claim 1, which is characterized in that the raw material including following parts by weight,
90 parts of epoxy resin, 15 parts of deionized water, 15 parts of graphene film, 10 parts of graphene dispersing solution, 3 parts of levelling agent, wetting dispersing agent 5
Part, 3 parts of pigment, 35 parts of alcohol solvent, 20 parts of anionic acrylic lotion, 16 parts of defoaming agent, 30 parts of Rs preservative, curing agent
8 parts, 20 parts of polyaniline, 10 parts of coalescing agent, 12 parts of different monooctyl ester, 5 parts of thickener, sour 10 parts of two formicester of rich code, demoulding preservative
10 parts, 5 parts of toughener, 15 parts of silane coupling agent.
3. a kind of graphene anticorrosive paint according to claim 1, which is characterized in that the raw material including following parts by weight,
95 parts of epoxy resin, 17 parts of deionized water, 16 parts of graphene film, 15 parts of graphene dispersing solution, 4 parts of levelling agent, wetting dispersing agent 6
Part, 4 parts of pigment, 37 parts of alcohol solvent, 23 parts of anionic acrylic lotion, 17 parts of defoaming agent, 40 parts of Rs preservative, curing agent
11 parts, 30 parts of polyaniline, 15 parts of coalescing agent, 14 parts of different monooctyl ester, 7 parts of thickener, sour 13 parts of two formicester of rich code, demoulding preservative
13 parts, 8 parts of toughener, 17 parts of silane coupling agent.
4. a kind of graphene anticorrosive paint according to claim 1, which is characterized in that the raw material including following parts by weight,
100 parts of epoxy resin, 20 parts of deionized water, 17 parts of graphene film, 20 parts of graphene dispersing solution, 5 parts of levelling agent, wetting dispersing agent
7 parts, 5 parts of pigment, 40 parts of alcohol solvent, 25 parts of anionic acrylic lotion, 18 parts of defoaming agent, 50 parts of Rs preservative, solidification
16 parts of agent, 36 parts of polyaniline, 30 parts of coalescing agent, 15 parts of different monooctyl ester, 8 parts of thickener, sour 15 parts of two formicester of rich code, demoulding anti-corrosion
15 parts of agent, 10 parts of toughener, 20 parts of silane coupling agent.
5. a kind of graphene anticorrosive paint according to claim 1, which is characterized in that the thickener is cellulose family increasing
Thick dose.
6. a kind of application method of graphene anticorrosive paint, which comprises the following steps:
S1, the epoxy resin of equivalent ingredient, deionized water, graphene dispersing solution, different monooctyl ester and sour two formicesters of rich code are put into very
In empty stirring and dissolving machine, carries out vacuum stirring and be uniformly dissolved, form mixed liquor；
S2, when raw material vacuum stirring be uniformly dissolved to form mixed liquor after, be added equivalent ingredient Rs preservative, demoulding anti-corrosion
Then agent, thickener and silane coupling agent are put into vacuum screw stirring differentiation machine, carry out high-speed stirred and break up 30-50 minutes,
Form uniform mixed serum；
It is S3, uniform mixed serum is micro- from sand mill by the inspiration of vacuum drawn machine, it is micro- from being sanded to fineness≤15 micron；
S4, it is poured into micro- in vacuum screw stirring differentiation machine again from the mixed serum that qualification is sanded, carries out stirring at low speed differentiation, when
Mixed serum is stirred to regulation viscosity, and graphene anticorrosive paint is made.
7. a kind of application method of graphene anticorrosive paint according to claim 6, which is characterized in that needed in the S1
Glass bar is stirred.
8. a kind of application method of graphene anticorrosive paint according to claim 6, which is characterized in that the S2 high speed
The mixing speed of stirring is 1300r/min.
9. a kind of application method of graphene anticorrosive paint according to claim 6, which is characterized in that low speed in the S4
The mixing speed of stirring is 450r/min.