CN109251663A - A kind of Al-alloy metal profile paint - Google Patents
A kind of Al-alloy metal profile paint Download PDFInfo
- Publication number
- CN109251663A CN109251663A CN201810844406.6A CN201810844406A CN109251663A CN 109251663 A CN109251663 A CN 109251663A CN 201810844406 A CN201810844406 A CN 201810844406A CN 109251663 A CN109251663 A CN 109251663A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- alumina silicate
- powder
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Al-alloy metal profile paint, it is made of according to parts by weight following raw material: 5~10 parts of alumina silicate, 12~18 parts of linseed oil, 0.2~0.5 part of zinc oxide, 12~16 parts of carbon black, 1.5~2.5 parts of cellulose, 17~25 parts of tea-seed oil, 9~12 parts of mica powder, 20~30 parts of water, 5~8 parts of zeolite powder, 1.3~1.5 parts of zinc chloride, 7~12 parts of tung oil, 2.4~2.8 parts of silica, 7~9 parts of titanium dioxide, 1.3~1.8 parts of alumina silicate, 2.5~4.5 parts of plant essence, 7~15 parts of kaolin, 16~22 parts of turpentine oil, 5~9 parts of coupling agent, 5~10 parts of graphite powder, 5~15 parts of aluminium oxide, 3~7 parts and 4~7 parts of adhesive of antioxidant.The advantages that metallic paint of the invention can effectively improve the fire resistance of paint, and raw material economics, use scope is extensive, can effectively prevent the destruction of fire source dope layer.
Description
Technical field
The present invention relates to metal casting correlative technology fields more particularly to a kind of Al-alloy metal profile to paint.
Background technique
Paint, whether it is traditional using natural materials as in the coating products of raw material or modern development to close
It is the coating products of raw material at chemical products, belongs to organic chemical industry's macromolecular material, be formed by film and belong to producing high-molecular
Polymer type, according to the classification of modern times current chemical products, coating belongs to fine chemical product, and modern coating is gradually
It is an important industry in chemical industry as a kind of multi-functional engineering material.Paint is very wide in routine use
General, the fire-fighting of building construction must be qualified, and whether the fire protecting performance of paint preferably also becomes an important problem naturally.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of Al-alloy metal profile proposed
With paint.
To achieve the goals above, present invention employs following technical solutions:
A kind of Al-alloy metal profile paint, is made of according to parts by weight following raw material: 5~10 parts of alumina silicate, linseed oil 12
~18 parts, 0.2~0.5 part of zinc oxide, 12~16 parts of carbon black, 1.5~2.5 parts of cellulose, 17~25 parts of tea-seed oil, mica powder 9
~12 parts, 20~30 parts of water, 5~8 parts of zeolite powder, 1.3~1.5 parts of zinc chloride, 7~12 parts of tung oil, silica 2.4~2.8
Part, 7~9 parts of titanium dioxide, 1.3~1.8 parts of alumina silicate, 2.5~4.5 parts of plant essence, 7~15 parts of kaolin, turpentine oil 16~
22 parts, 5~9 parts of coupling agent, 5~10 parts of graphite powder, 5~15 parts of aluminium oxide, 3~7 parts of antioxidant and 4~7 parts of adhesive.
A kind of above-mentioned Al-alloy metal profile paint, is made of according to parts by weight following raw material: 5~9 parts of alumina silicate,
12~17 parts of linseed oil, 0.2~0.4 part of zinc oxide, 12~15 parts of carbon black, 1.5~2.4 parts of cellulose, 17~24 parts of tea-seed oil,
9~11 parts of mica powder, 20~29 parts of water, 5~7 parts of zeolite powder, 1.3~1.49 parts of zinc chloride, 7~11 parts of tung oil, silica
2.4~2.7 parts, 7~8.9 parts of titanium dioxide, 1.3~1.7 parts of alumina silicate, 2.5~4.4 parts of plant essence, 7~14 parts of kaolin,
16~21 parts of turpentine oil, 5~8 parts of coupling agent, 5~9 parts of graphite powder, 5~14 parts of aluminium oxide, 3~6 parts of antioxidant and adhesive
4~6 parts.
A kind of above-mentioned Al-alloy metal profile paint, is made of according to parts by weight following raw material: 6~9 parts of alumina silicate,
13~17 parts of linseed oil, 0.3~0.4 part of zinc oxide, 13~15 parts of carbon black, 1.6~2.4 parts of cellulose, 18~24 parts of tea-seed oil,
10~11 parts of mica powder, 21~29 parts of water, 6~7 parts of zeolite powder, 1.4~1.49 parts of zinc chloride, 8~11 parts of tung oil, silica
2.5~2.7 parts, 8~8.9 parts of titanium dioxide, 1.4~1.7 parts of alumina silicate, 2.6~4.4 parts of plant essence, 8~14 parts of kaolin,
17~21 parts of turpentine oil, 6~8 parts of coupling agent, 6~9 parts of graphite powder, 6~14 parts of aluminium oxide, 4~6 parts of antioxidant and adhesive
5~6 parts.
A kind of above-mentioned Al-alloy metal profile paint, is made of according to parts by weight following raw material: 7.5 parts of alumina silicate,
15 parts of linseed oil, 0.35 part of zinc oxide, 14 parts of carbon black, 2 parts of cellulose, 21 parts of tea-seed oil, 10.5 parts of mica powder, 25 parts of water, boiling
6.5 parts of mountain flour, 1.4 parts of zinc chloride, 9.5 parts of tung oil, 2.6 parts of silica, 8 parts of titanium dioxide, 1.55 parts of alumina silicate, plant essence
3.5 parts, 11 parts of kaolin, 19 parts of turpentine oil, 7 parts of coupling agent, 7.5 parts of graphite powder, 10 parts of aluminium oxide, 5 parts of antioxidant and viscous
5.5 parts of mixture.
Compared with prior art, the invention has the benefit that
A kind of Al-alloy metal profile paint of the invention can effectively improve the fire resistance of paint, and raw material economics uses model
It encloses extensively, can effectively prevent the beneficial effects such as the destruction of fire source dope layer.
Specific embodiment
Embodiment 1
A kind of Al-alloy metal profile paint, is made of according to parts by weight following raw material: 5 parts of alumina silicate, 12 parts of linseed oil, oxygen
Change 0.2 part of zinc, 12 parts of carbon black, 1.5 parts of cellulose, 17 parts of tea-seed oil, 9 parts of mica powder, 20 parts of water, 5 parts of zeolite powder, zinc chloride
1.3 parts, 7 parts of tung oil, 2.4 parts of silica, 7 parts of titanium dioxide, 1.3 parts of alumina silicate, 2.5 parts of plant essence, 7 parts of kaolin, pine
16 parts of fuel-economizing, 5 parts of coupling agent, 5 parts of graphite powder, aluminium oxide 5,3 parts of antioxidant and 4 parts of adhesive.
Embodiment 2
A kind of above-mentioned Al-alloy metal profile paint, is made of according to parts by weight following raw material: 10 parts of alumina silicate, linseed oil
18 parts, 0.5 part of zinc oxide, 16 parts of carbon black, 2.5 parts of cellulose, 25 parts of tea-seed oil, 12 parts of mica powder, 30 parts of water, 8 parts of zeolite powder,
1.5 parts of zinc chloride, 12 parts of tung oil, 2.8 parts of silica, 9 parts of titanium dioxide, 1.8 parts of alumina silicate, 4.5 parts of plant essence, kaolin
15 parts, 22 parts of turpentine oil, 9 parts of coupling agent, 10 parts of graphite powder, 15 parts of aluminium oxide, 7 parts of antioxidant and 7 parts of adhesive.
Embodiment 3
A kind of above-mentioned Al-alloy metal profile paint, is made of according to parts by weight following raw material: 7.5 parts of alumina silicate, flax
Oily 15 parts, 0.35 part of zinc oxide, 14 parts of carbon black, 2 parts of cellulose, 21 parts of tea-seed oil, 10.5 parts of mica powder, 25 parts of water, zeolite powder
6.5 parts, 1.4 parts of zinc chloride, 9.5 parts of tung oil, 2.6 parts of silica, 8 parts of titanium dioxide, 1.55 parts of alumina silicate, plant essence 3.5
Part, 11 parts of kaolin, 19 parts of turpentine oil, 7 parts of coupling agent, 7.5 parts of graphite powder, 10 parts of aluminium oxide, 5 parts of antioxidant and adhesive
5.5 part.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of Al-alloy metal profile paint, which is characterized in that be made of according to parts by weight following raw material: alumina silicate 5~
10 parts, 12~18 parts of linseed oil, 0.2~0.5 part of zinc oxide, 12~16 parts of carbon black, 1.5~2.5 parts of cellulose, tea-seed oil 17~
25 parts, 9~12 parts of mica powder, 20~30 parts of water, 5~8 parts of zeolite powder, 1.3~1.5 parts of zinc chloride, 7~12 parts of tung oil, dioxy
2.4~2.8 parts of SiClx, 7~9 parts of titanium dioxide, 1.3~1.8 parts of alumina silicate, 2.5~4.5 parts of plant essence, kaolin 7~15
Part, 16~22 parts of turpentine oil, 5~9 parts of coupling agent, 5~10 parts of graphite powder, 5~15 parts of aluminium oxide, 3~7 parts of antioxidant and viscous
4~7 parts of mixture.
2. a kind of Al-alloy metal profile paint according to claim 1, which is characterized in that have according to parts by weight following
Raw material composition: 5~9 parts of alumina silicate, 12~17 parts of linseed oil, 0.2~0.4 part of zinc oxide, 12~15 parts of carbon black, cellulose 1.5
~2.4 parts, 17~24 parts of tea-seed oil, 9~11 parts of mica powder, 20~29 parts of water, 5~7 parts of zeolite powder, zinc chloride 1.3~1.49
Part, 7~11 parts of tung oil, 2.4~2.7 parts of silica, 7~8.9 parts of titanium dioxide, 1.3~1.7 parts of alumina silicate, plant essence 2.5
~4.4 parts, 7~14 parts of kaolin, 16~21 parts of turpentine oil, 5~8 parts of coupling agent, 5~9 parts of graphite powder, 5~14 parts of aluminium oxide,
3~6 parts and 4~6 parts of adhesive of antioxidant.
3. a kind of Al-alloy metal profile paint according to claim 1, which is characterized in that have according to parts by weight following
Raw material composition: 6~9 parts of alumina silicate, 13~17 parts of linseed oil, 0.3~0.4 part of zinc oxide, 13~15 parts of carbon black, cellulose 1.6
~2.4 parts, 18~24 parts of tea-seed oil, 10~11 parts of mica powder, 21~29 parts of water, 6~7 parts of zeolite powder, zinc chloride 1.4~1.49
Part, 8~11 parts of tung oil, 2.5~2.7 parts of silica, 8~8.9 parts of titanium dioxide, 1.4~1.7 parts of alumina silicate, plant essence 2.6
~4.4 parts, 8~14 parts of kaolin, 17~21 parts of turpentine oil, 6~8 parts of coupling agent, 6~9 parts of graphite powder, 6~14 parts of aluminium oxide,
4~6 parts and 5~6 parts of adhesive of antioxidant.
4. a kind of Al-alloy metal profile paint according to claim 1, which is characterized in that have according to parts by weight following
Raw material composition: 7.5 parts of alumina silicate, 15 parts of linseed oil, 0.35 part of zinc oxide, 14 parts of carbon black, 2 parts of cellulose, 21 parts of tea-seed oil, cloud
10.5 parts of female powder, 25 parts of water, 6.5 parts of zeolite powder, 1.4 parts of zinc chloride, 9.5 parts of tung oil, 2.6 parts of silica, 8 parts of titanium dioxide,
1.55 parts of alumina silicate, 3.5 parts of plant essence, 11 parts of kaolin, 19 parts of turpentine oil, 7 parts of coupling agent, 7.5 parts of graphite powder, aluminium oxide
10 parts, 5 parts of antioxidant and 5.5 parts of adhesive.