CN110948962A - Preparation method of antibacterial blended apocynum venetum fabric - Google Patents

Preparation method of antibacterial blended apocynum venetum fabric Download PDF

Info

Publication number
CN110948962A
CN110948962A CN201811129176.1A CN201811129176A CN110948962A CN 110948962 A CN110948962 A CN 110948962A CN 201811129176 A CN201811129176 A CN 201811129176A CN 110948962 A CN110948962 A CN 110948962A
Authority
CN
China
Prior art keywords
fabric
fibers
layer
antibacterial
blended
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811129176.1A
Other languages
Chinese (zh)
Inventor
周建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Xiangfei Fashion Co Ltd
Original Assignee
Jiangyin Xiangfei Fashion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Xiangfei Fashion Co Ltd filed Critical Jiangyin Xiangfei Fashion Co Ltd
Priority to CN201811129176.1A priority Critical patent/CN110948962A/en
Publication of CN110948962A publication Critical patent/CN110948962A/en
Pending legal-status Critical Current

Abstract

The invention particularly relates to a preparation method of an apocynum venetum antibacterial blended fabric, which comprises the following steps: manufacturing a surface layer: the surface layer is made of apocynum venetum antibacterial fabric, the apocynum venetum antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of apocynum venetum fibers and cotton fibers, and the wefts are blended yarns of hemp fibers and cotton fibers; manufacturing the intermediate layer: the hemp fibers and the cotton fibers in the first fabric layer and the third fabric layer are firstly blended, then blended with the apocynum venetum fibers, and woven into cloth, the second fabric layer is manufactured by spinning cotton fibers, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode; manufacturing an inner layer; and (6) attaching the components into a whole. According to the preparation method of the antibacterial blended apocynum fabric, the prepared apocynum fabric has a good antibacterial function, and the preparation process is simple and easy to operate.

Description

Preparation method of antibacterial blended apocynum venetum fabric
Technical Field
The invention belongs to the technical field of fabrics, and particularly relates to a preparation method of an antibacterial apocynum venetum blended fabric.
Background
With the increasing awareness of environmental protection and health care, more and more people are paying attention to natural fibers, and cotton fibers are widely applied to the production of various textiles as the most common natural fibers. At present, yarns on the market come out endlessly, are different in material structure, and are widely applied to the living fields of weaving, rope making, thread making and the like. Xinjiang cotton fiber is well known in the textile industry due to its flexibility and is known as a cotton top grade product by people, and has the advantages of less frequent combing, uniform and smooth evenness and high dyeability. However, the elasticity and the heat retention of the cotton fiber blended yarn on the market at present are not good, so that the woven fabric has the defects of poor heat retention effect and poor elasticity.
Preventing bacteria from harming human body is being paid more and more attention by consumers. Apocynum venetum fiber is a protective fiber for human body to avoid bacterial invasion.
In view of the above, a method for preparing an antibacterial blended fabric of apocynum venetum is needed to be developed.
Disclosure of Invention
The invention aims to provide a preparation method of an antibacterial apocynum venetum blended fabric, which comprises the following steps:
a, manufacturing a surface layer: the surface layer is made of apocynum venetum antibacterial fabric, the apocynum venetum antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of apocynum venetum fibers and cotton fibers, and the wefts are blended yarns of hemp fibers and cotton fibers;
b, manufacturing an intermediate layer: the hemp fibers and the cotton fibers in the first fabric layer and the third fabric layer are firstly blended, then blended with the apocynum venetum fibers, and woven into cloth, the second fabric layer is manufactured by spinning cotton fibers, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode;
c, manufacturing of the inner layer: uniformly mixing apocynum venetum fibers, hemp fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain lining fabric;
d, integrating lamination: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
Preferably, in the step a, the antibacterial apocynum venetum fabric is added with an antibacterial finishing agent for treatment for 30-40 minutes and then baked at the temperature of 55 ℃ for 20-30 minutes.
Preferably, after the step c, adding 2% of detergent and 8% of softener into the lining fabric for water washing treatment, and controlling the water temperature to be 30-40 ℃ and washing for 20-30 minutes.
Preferably, the time for the cooking and processing in the step d is 10-50h, the temperature is 20-70 ℃, and the humidity is 40-85%.
Preferably, in the step d, the calendering temperature is 60-100 ℃, and the pressure is 50-100Kg/cm2The speed is 15-30 m/min.
Due to the adoption of the technical scheme, the invention has the following advantages and beneficial effects:
according to the preparation method of the antibacterial blended apocynum fabric, the prepared apocynum fabric has a good antibacterial function, and the preparation process is simple and easy to operate.
Detailed Description
In order to more clearly illustrate the invention, the invention is further described below in connection with preferred embodiments. It is to be understood by persons skilled in the art that the following detailed description is illustrative and not restrictive, and is not to be taken as limiting the scope of the invention.
Example 1
A preparation method of an apocynum venetum antibacterial blended fabric comprises the following steps:
a, manufacturing a surface layer: the surface layer is made of apocynum venetum antibacterial fabric, the apocynum venetum antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of apocynum venetum fibers and cotton fibers, and the wefts are blended yarns of hemp fibers and cotton fibers;
b, manufacturing an intermediate layer: the hemp fibers and the cotton fibers in the first fabric layer and the third fabric layer are firstly blended, then blended with the apocynum venetum fibers, and woven into cloth, the second fabric layer is manufactured by spinning cotton fibers, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode;
c, manufacturing of the inner layer: uniformly mixing apocynum venetum fibers, hemp fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain lining fabric;
d, integrating lamination: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
In the step a, the antibacterial apocynum venetum fabric is added with an antibacterial finishing agent for treatment for 30 minutes and then is baked at the temperature of 55 ℃ for 20 minutes. And c, adding 2% of detergent and 8% of softening agent into the inner fabric for washing after the step c, controlling the water temperature at 30 ℃ and washing for 20 minutes. The time for curing and processing in the step d is 10 hours, the temperature is 20 ℃, and the humidity is 40%. In the step d, the calendering temperature is 60 ℃ and the pressure is 50Kg/cm2The speed was 15 m/min.
Example 2
A preparation method of an apocynum venetum antibacterial blended fabric comprises the following steps:
a, manufacturing a surface layer: the surface layer is made of apocynum venetum antibacterial fabric, the apocynum venetum antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of apocynum venetum fibers and cotton fibers, and the wefts are blended yarns of hemp fibers and cotton fibers;
b, manufacturing an intermediate layer: the hemp fibers and the cotton fibers in the first fabric layer and the third fabric layer are firstly blended, then blended with the apocynum venetum fibers, and woven into cloth, the second fabric layer is manufactured by spinning cotton fibers, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode;
c, manufacturing of the inner layer: uniformly mixing apocynum venetum fibers, hemp fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain lining fabric;
d, integrating lamination: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
In the step a, the apocynum venetum antibacterial fabric is addedThe antibacterial finishing agent is treated for 30-40 minutes and then baked for 30 minutes at 55 ℃. And c, after the step c, adding 2% of detergent and 8% of softening agent into the fabric on the inner layer for washing, controlling the water temperature at 40 ℃, and washing for 30 minutes. The time for curing and processing in the step d is 10-50h, the temperature is 70 ℃, and the humidity is 85%. In the step d, the calendering temperature is 100 ℃ and the pressure is 100Kg/cm2The speed was 30 m/min.
Through detection, all indexes of the apocynum venetum antibacterial spun yarn prepared by the two embodiments are shown in the following table
Breaking Strength N (warp direction) Breaking Strength N (weft) Antibacterial rate/percentage of Apocynum venetum Ultraviolet transmittance/%)
Example 1 250N 220N 94 3.3-4.2
Example 2 250N 215N 95.6 3.1-4.5
The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, which are given by way of illustration of the principles of the present invention, and that various changes and modifications may be made without departing from the spirit and scope of the invention as defined by the appended claims. The scope of the invention is defined by the appended claims and equivalents thereof.

Claims (5)

1. A preparation method of an antibacterial blended apocynum fabric is characterized by comprising the following steps:
a, manufacturing a surface layer: the surface layer is made of apocynum venetum antibacterial fabric, the apocynum venetum antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of apocynum venetum fibers and cotton fibers, and the wefts are blended yarns of hemp fibers and cotton fibers;
b, manufacturing an intermediate layer: the hemp fibers and the cotton fibers in the first fabric layer and the third fabric layer are firstly blended, then blended with the apocynum venetum fibers, and woven into cloth, the second fabric layer is manufactured by spinning cotton fibers, and the first fabric layer, the second fabric layer and the third fabric layer are sequentially attached together in a dispensing or needle and thread sewing mode;
c, manufacturing of the inner layer: uniformly mixing apocynum venetum fibers, hemp fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and weaving to obtain lining fabric;
d, integrating lamination: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
2. The preparation method of the apocynum venetum antibacterial blended fabric according to claim 4, characterized by comprising the following steps: in the step a, the antibacterial apocynum venetum fabric is added with an antibacterial finishing agent for treatment for 30-40 minutes and then baked at the temperature of 55 ℃ for 20-30 minutes.
3. The preparation method of the apocynum venetum antibacterial blended fabric according to any one of claim 2, characterized by comprising the following steps: and c, adding 2% of detergent and 8% of softening agent into the inner fabric for washing treatment, wherein the water temperature is controlled at 30-40 ℃, and the washing treatment is carried out for 20-30 minutes.
4. The preparation method of the apocynum venetum antibacterial blended fabric according to claim 3, characterized by comprising the following steps: the curing and processing time in the step d is 10-50h, the temperature is 20-70 ℃, and the humidity is 40-85%.
5. The preparation method of the apocynum venetum antibacterial blended fabric according to claim 4, which is characterized by comprising the following steps of: in the step d, the calendering temperature is 60-100 ℃, and the pressure is 50-100Kg/cm2The speed is 15-30 m/min.
CN201811129176.1A 2018-09-27 2018-09-27 Preparation method of antibacterial blended apocynum venetum fabric Pending CN110948962A (en)