CN111455493A - Antibacterial and antiviral fabric and preparation method and application thereof - Google Patents
Antibacterial and antiviral fabric and preparation method and application thereof Download PDFInfo
- Publication number
- CN111455493A CN111455493A CN202010324451.6A CN202010324451A CN111455493A CN 111455493 A CN111455493 A CN 111455493A CN 202010324451 A CN202010324451 A CN 202010324451A CN 111455493 A CN111455493 A CN 111455493A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- antiviral
- fabric
- finishing agent
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial and antiviral fabric and a preparation method and application thereof, wherein the antibacterial and antiviral fabric is prepared by spinning 10-15% of nano-silver antibacterial master batch and 85-90% of polyamide, polypropylene PP or polyester PET in percentage by mass, making the spinning yarn into a yarn, weaving the yarn into a fabric through a weaving machine, and impregnating the fabric with an antiviral and antibacterial finishing agent to form the antibacterial and antiviral fabric. The antibacterial and antiviral fabric can be used for resisting bacteria and viruses for a long time, and is suitable for curtain curtains, throw pillows, linings, bedding, wall paper and wall cloth, sofa cloth and clothes cloth.
Description
The technical field is as follows:
the invention relates to the field of textile fabrics, in particular to an antibacterial and antiviral fabric and a preparation method and application thereof.
Background art:
the existing living environment has the defects that bacteria and viruses are everywhere and fabric fabrics are inseparable demand articles, clothes, curtain curtains, throw pillows, sofas, bedding, wall cloth and the like are required to be in direct contact with human everyday, after the surfaces of the products are frequently contacted with people, the products are easy to carry the bacteria and viruses, and how to prepare the fabric with long-term antibacterial and antiviral properties becomes a problem to be solved urgently.
The invention content is as follows:
the invention aims to solve the technical problem of providing an antibacterial and antiviral fabric with long-acting antibacterial and antiviral functions.
The technical scheme provided by the invention is that the antibacterial and antiviral fabric is prepared by spinning 10-15% of nano-silver antibacterial master batch and 85-90% of polyamide, polypropylene PP or polyester PET in percentage by mass, manufacturing the spinning yarn into a fabric, weaving the fabric into a woven fabric, and impregnating the woven fabric with an antiviral and antibacterial finishing agent to form the antibacterial and antiviral fabric.
Preferably, the antibacterial and antiviral finishing agent is REV316 antiviral antibacterial finishing agent.
Further, the invention also provides a preparation method of the antibacterial and antiviral fabric, which comprises the following steps,
step one, spinning is made of 10-15% of nano-silver antibacterial master batch, 85-90% of polyamide, polypropylene PP or polyester PET according to mass percentage, and the spinning is made into yarn and then woven into fabric;
step two, preparing a finishing agent, namely adding water into a melting barrel, then adding 45 g/L g of antiviral and antibacterial finishing agent A, stirring uniformly, then adding 15 g/L g of antiviral and antibacterial finishing agent B, and then stirring and adding 40 g/L g of antiviral and antibacterial finishing agent C;
and step three, adding the finishing agent into the fabric woven in the step one in any one of padding, dipping, spraying and brushing, drying and shaping, wherein the drying temperature is 80-110 ℃, the shaping temperature is 120-130 ℃, the drying time is 3-5 min or 150-160 ℃, and the drying time is 30-60 s.
Preferably, the method comprises the following steps,
step one, spinning is made of 12% of nano-silver antibacterial master batches and 88% of polyester PET according to the mass percentage, and the spinning is made into yarns which are woven into fabrics;
step two, preparing a finishing agent, namely adding water into a melting barrel, then adding 45 g/L g of antiviral and antibacterial finishing agent A, stirring uniformly, then adding 15 g/L g of antiviral and antibacterial finishing agent B, and then stirring and adding 40 g/L g of antiviral and antibacterial finishing agent C;
and step three, adding the finishing agent into the fabric woven in the step one in any one of padding, dipping, spraying and brushing, drying and shaping, wherein the drying temperature is 100 ℃, the shaping temperature is 125 ℃, and the drying time is 3 min.
Further, the application of the antibacterial and antiviral fabric is also provided, and the antibacterial and antiviral fabric is used for curtains, door curtains, throw pillows, curtain linings, bedding, wall paper and wall cloth, sofa cloth and clothes cloth.
Compared with the prior art, the invention has the following advantages after adopting the scheme: the fabric can be applied to curtain curtains, throw pillows, linings, bedding, wall paper and wall cloth, sofa cloth, clothes and the like, has wide application range, can play an effective antibacterial and antiviral role, has good washing fastness, forms a firm antiviral and antibacterial drug film on the surface of the fabric, has good antiviral activity and antibacterial effect, has good safety performance, is safe to human skin, and meets a plurality of environmental protection standard requirements at home and abroad.
The specific implementation mode is as follows:
the invention is further illustrated with respect to specific embodiments below:
example 1
An antibacterial and antiviral fabric is characterized in that spinning is made of 12% of nano-silver antibacterial master batches and 88% of polyester PET (polyethylene terephthalate) in percentage by mass, yarns are made and woven into a fabric through a weaving machine, and the fabric is impregnated with an antiviral and antibacterial finishing agent to form the antibacterial and antiviral fabric.
The preparation method of the antibacterial and antiviral fabric comprises the following steps,
step one, spinning is made of 12% of nano-silver antibacterial master batches and 88% of polyester PET according to the mass percentage, and the spinning is made into yarns which are woven into fabrics;
step two, preparing a finishing agent, namely adding water into a melting barrel, then adding 45 g/L g of antiviral and antibacterial finishing agent A, stirring uniformly, then adding 15 g/L g of antiviral and antibacterial finishing agent B, and then stirring and adding 40 g/L g of antiviral and antibacterial finishing agent C;
step three, adding the finishing agent into the fabric woven in the step one in any one mode of padding, dipping, spraying and brushing, drying and sizing, wherein the drying temperature is 100 ℃, the sizing temperature is 125 ℃, and the drying time is 3min
The antibacterial and antiviral fabric prepared by the method can be used for curtains, door curtains, throw pillows, curtain linings, bedding, wallpaper, wall cloth, sofa cloth and clothes cloth.
Tests and applications of a plurality of authoritative units such as ITS, SGS, Chinese disease prevention and control center and the like prove that: the nano-silver antibacterial master batch has excellent antibacterial action on MRSA, staphylococcus aureus, pneumonia bacillus, escherichia coli, pseudomonas aeruginosa and candida albicans, and the nano-silver antibacterial master batch fiber has broad-spectrum and efficient antibacterial and deodorant effects and is highly resistant to dry cleaning and water washing; has no irritation to skin, no anaphylactic reaction, no toxicity, no teratogenicity, no mutagenicity, no potential carcinogenicity, no harmful substances such as formaldehyde and the like, meets the requirement of environmental protection, and meets the standard of Oeko-Tex stand 100.
The nano silver antibacterial master batch acts on the cell membrane of bacteria, so that the cell membrane is damaged, the permeability is increased, intracellular plasma is leaked out, the synthesis of bacterial protein can be hindered, the consumption of thallus endoproteosome is caused, and the bacteria are killed. Tests prove that the nano-silver antibacterial master batch can be synthesized with fibers, has high-efficiency and durable antibacterial property, and has broad-spectrum antibacterial activity on gram-negative bacteria, gram-positive bacteria and fungi; can be dispersed in synthetic fiber slice and plastic; can reduce the odor caused by the reproduction of microorganisms, and has lasting freshness; the fabric is non-toxic and safe, has no irritation to skin, and meets the requirements of ecological textiles; has no adverse effect on the whiteness, color light, strength, hand feeling and vapor permeability of the fiber.
The anti-virus antibacterial finishing agent is REV316 anti-virus antibacterial finishing agent produced by Herst International Group company, and consists of A, B, C, the appearance of the finishing agent is liquid, and the pH value is 6-7 at the use concentration; weak cationic; the relative density (20 ℃) is 1.01 to 1.1g/cm 3. Is non-toxic, non-explosive and safe to human body, and conforms to GB18401-2010 national textile product basic safety technical Specification, European Union REACH regulation, ROHS Standard and Oeko-Tex Standard 100 Standard.
Tests show that the antiviral and antibacterial finishing agent reacts with the fabric at high temperature and is crosslinked to form a water-insoluble compound which does not run off in water, achieves the long-term non-dissolving antiviral and antibacterial effect through contact type antibacterial and antiviral, and is suitable for fabrics such as cotton, hemp, silk, wool, polyester cotton, chinlon, viscose fiber and the like.
The testing of the national third-party detection mechanism proves that: the antiviral activity rate of the antiviral and antibacterial finishing fabric on H3N2 influenza virus and H1N1 influenza A virus can reach 99%. The standard washing is carried out for 50 times under the laboratory condition, and the bacteriostasis rate of the antibacterial agent to staphylococcus aureus, escherichia coli, klebsiella pneumoniae and candida albicans can reach 99 percent.
The antibacterial and antiviral fabric product relates to curtain curtains, throw pillows, lining cloth, bedding, wall paper and wall cloth, sofa cloth, clothes cloth and the like, has a wide application range, has obvious effects of effectively playing a role in resisting bacteria and viruses, has good washing fastness, forms a firm antiviral and antibacterial drug film on the surface of a fabric, has good antiviral activity and antibacterial effect, has good safety performance, is safe to human skin, and meets a plurality of environmental protection standard requirements at home and abroad.
The foregoing is illustrative of the preferred embodiments of the present invention only and is not to be construed as limiting the claims. All the equivalent structures or equivalent process changes made by the description of the invention are included in the scope of the patent protection of the invention.
Claims (5)
1. An antibacterial and antiviral fabric is characterized in that: according to the mass percentage, 10-15% of nano-silver antibacterial master batch, 85-90% of polyamide, polypropylene PP or polyester PET are prepared into spinning, the spinning is made into yarn, the weaving is carried out to obtain fabric, and the fabric is impregnated with antiviral antibacterial finishing agent to form the antibacterial and antiviral fabric.
2. The antibacterial and antiviral fabric according to claim 1, wherein: the antibacterial and antiviral finishing agent is REV316 antiviral antibacterial finishing agent.
3. The preparation method of the antibacterial and antiviral fabric is characterized by comprising the following steps: comprises the following steps of (a) carrying out,
step one, spinning is made of 10-15% of nano-silver antibacterial master batch, 85-90% of polyamide, polypropylene PP or polyester PET according to mass percentage, and the spinning is made into yarn and then woven into fabric;
step two, preparing a finishing agent, namely adding water into a melting barrel, then adding 45 g/L g of antiviral and antibacterial finishing agent A, stirring uniformly, then adding 15 g/L g of antiviral and antibacterial finishing agent B, and then stirring and adding 40 g/L g of antiviral and antibacterial finishing agent C;
and step three, adding the finishing agent into the fabric woven in the step one in any one of padding, dipping, spraying and brushing, drying and shaping, wherein the drying temperature is 80-110 ℃, the shaping temperature is 120-130 ℃, the drying time is 3-5 min or 150-160 ℃, and the drying time is 30-60 s.
4. The preparation method of the antibacterial and antiviral fabric according to claim 1, characterized by comprising the following steps: comprises the following steps of (a) carrying out,
step one, spinning is made of 12% of nano-silver antibacterial master batches and 88% of polyester PET according to the mass percentage, and the spinning is made into yarns which are woven into fabrics;
step two, preparing a finishing agent, namely adding water into a melting barrel, then adding 45 g/L g of antiviral and antibacterial finishing agent A, stirring uniformly, then adding 15 g/L g of antiviral and antibacterial finishing agent B, and then stirring and adding 40 g/L g of antiviral and antibacterial finishing agent C;
and step three, adding the finishing agent into the fabric woven in the step one in any one of padding, dipping, spraying and brushing, drying and shaping, wherein the drying temperature is 100 ℃, the shaping temperature is 125 ℃, and the drying time is 3 min.
5. The use of the antibacterial and antiviral fabric according to claim 1, wherein the antibacterial and antiviral fabric is used for curtains, door curtains, throw pillows, curtain linings, bedding, wall paper and wall coverings, sofa fabrics and clothes.