CN112593151A - 一种耐腐蚀无缝钢管及其制备工艺 - Google Patents

一种耐腐蚀无缝钢管及其制备工艺 Download PDF

Info

Publication number
CN112593151A
CN112593151A CN202011351161.7A CN202011351161A CN112593151A CN 112593151 A CN112593151 A CN 112593151A CN 202011351161 A CN202011351161 A CN 202011351161A CN 112593151 A CN112593151 A CN 112593151A
Authority
CN
China
Prior art keywords
steel pipe
pickling
corrosion
bar
lubricant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202011351161.7A
Other languages
English (en)
Inventor
唐俊杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hengyang Hongchang Mechanization Co ltd
Original Assignee
Hengyang Hongchang Mechanization Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hengyang Hongchang Mechanization Co ltd filed Critical Hengyang Hongchang Mechanization Co ltd
Priority to CN202011351161.7A priority Critical patent/CN112593151A/zh
Publication of CN112593151A publication Critical patent/CN112593151A/zh
Pending legal-status Critical Current

Abstract

本发明涉及无缝钢管技术领域，尤其是一种耐腐蚀无缝钢管及其制备工艺，首先将上述原料冶炼成棒胚，冶炼完成后棒胚冷却到700‑800℃，然后重新对棒胚加热、穿孔、第一次酸洗、冷轧、热处理、精整、第二次酸洗，在穿孔顶头设置喷射润滑剂的装置，保证在穿孔过程中不间断将润滑剂从顶头喷出喷射在顶头与钢管之间；第一次酸洗时，酸洗液选自浓度为5％‑8％的氢氟酸与浓度为10％‑12％的硝酸的混合液；酸洗需要对钢坯从常温加热到60℃～65℃，整个酸洗过程1‑2小时。通过润滑剂在钢管内表面形成一层保护膜，既起到了冷却作用、保护了钢管内壁不被划伤，避免空气进入管壁内，进一步保证钢管的质量，使得到的钢管表面更加光滑，提高钢管的耐腐蚀性。

Description

一种耐腐蚀无缝钢管及其制备工艺
技术领域
本发明涉及无缝钢管技术领域，尤其涉及一种耐腐蚀无缝钢管及其制备工艺。
背景技术
随着时代的进步，人们对钢材的质量要求越来越高，特别是钢管的耐腐蚀性，钢管的耐腐蚀性如果不好，使用过程容易发生泄漏现象，而钢管的耐腐蚀性关键影响因素为钢管本身材质以及钢管加工的工艺。
发明内容
本发明的目的是为了解决现有技术中钢管耐腐蚀性不好的缺点，而提出的一种耐腐蚀无缝钢管及其制备工艺。
为了实现上述目的，本发明采用了如下技术方案：
一种耐腐蚀无缝钢管，钢的化学成份(质量％)为：C 0.05～0.08，Si 0.20～0.35，Mn≤0.50，P≤0.020，Al 0.40～0.80，Mo0.25～0.35，S≤0.030，Cr 20.00～22.00，Ce 0.02～0.06，其余为Fe。
一种耐腐蚀无缝钢管制备工艺，包括以下步骤：首先将上述原料冶炼成棒胚，冶炼完成后棒胚冷却到700-800℃，然后重新对棒胚加热、穿孔、第一次酸洗、冷轧、热处理、精整、第二次酸洗，将棒料加热穿孔，加热温度为1100-1200℃；加热时间30-50分钟；管坯加热两端部温差不大于20℃，且穿孔时，在穿孔顶头设置喷射润滑剂的装置，保证在穿孔过程中不间断将润滑剂从顶头喷出喷射在顶头与钢管之间；第一次酸洗时，酸洗液选自浓度为5％-8％的氢氟酸与浓度为10％-12％的硝酸的混合液；酸洗需要对钢坯从常温加热到60℃～65℃，整个酸洗过程1-2小时。
喷射的润滑剂重量百分比如下：工业牛油8-10％、石墨20-30％二甲基硅油0.05-0.1％、其余为玻璃粉。
棒胚加热、穿孔、酸洗冷轧、热处理均在真空条件下进行。
本发明提出的一种耐腐蚀无缝钢管及其制备工艺，有益效果在于：通过润滑剂在钢管内表面形成一层保护膜，既起到了冷却作用、保护了钢管内壁不被划伤，同时棒胚加热、穿孔、酸洗冷轧、热处理均在真空条件下进行，避免空气进入管壁内，进一步保证钢管的质量，使得到的钢管表面更加光滑，提高钢管的耐腐蚀性。
具体实施方式
下面本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
一种耐腐蚀无缝钢管，钢的化学成份(质量％)为：C 0.05～0.08，Si 0.20～0.35，Mn≤0.50，P≤0.020，Al 0.40～0.80，Mo0.25～0.35，S≤0.030，Cr 20.00～22.00，Ce 0.02～0.06，其余为Fe，CrMoAl钢的焊接性能良好，保证钢管与钢管之间连接更加牢靠，避免使用过程中泄漏。
一种耐腐蚀无缝钢管制备工艺，包括以下步骤：首先将上述原料冶炼成棒胚，冶炼完成后棒胚冷却到700-800℃，然后重新对棒胚加热、穿孔、第一次酸洗、冷轧、热处理、精整、第二次酸洗，将棒料加热穿孔，加热温度为1100-1200℃；加热时间30-50分钟；管坯加热两端部温差不大于20℃，且穿孔时，在穿孔顶头设置喷射润滑剂的装置，保证在穿孔过程中不间断将润滑剂从顶头喷出喷射在顶头与钢管之间；第一次酸洗时，酸洗液选自浓度为5％-8％的氢氟酸与浓度为10％-12％的硝酸的混合液；酸洗需要对钢坯从常温加热到60℃～65℃，整个酸洗过程1-2小时。
喷射的润滑剂重量百分比如下：工业牛油8-10％、石墨20-30％二甲基硅油0.05-0.1％、其余为玻璃粉。
棒胚加热、穿孔、酸洗冷轧、热处理均在真空条件下进行。
通过润滑剂在钢管内表面形成一层保护膜，既起到了冷却作用、保护了钢管内壁不被划伤，同时棒胚加热、穿孔、酸洗冷轧、热处理均在真空条件下进行，避免空气进入管壁内，进一步保证钢管的质量，使得到的钢管表面更加光滑，提高钢管的耐腐蚀性。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (4)

1.一种耐腐蚀无缝钢管，其特征在于，钢的化学成份(质量％)为：C 0.05～0.08，Si0.20～0.35，Mn≤0.50，P≤0.020，Al 0.40～0.80，Mo0.25～0.35，S≤0.030，Cr 20.00～22.00，Ce 0.02～0.06，其余为Fe。
2.一种耐腐蚀无缝钢管制备工艺，包括以下步骤：首先将上述原料冶炼成棒胚，冶炼完成后棒胚冷却到700-800℃，然后重新对棒胚加热、穿孔、第一次酸洗、冷轧、热处理、精整、第二次酸洗，其特征在于，将棒料加热穿孔，加热温度为1100-1200℃；加热时间30-50分钟；管坯加热两端部温差不大于20℃，且穿孔时，在穿孔顶头设置喷射润滑剂的装置，保证在穿孔过程中不间断将润滑剂从顶头喷出喷射在顶头与钢管之间；第一次酸洗时，酸洗液选自浓度为5％-8％的氢氟酸与浓度为10％-12％的硝酸的混合液；酸洗需要对钢坯从常温加热到60℃～65℃，整个酸洗过程1-2小时。
3.根据权利要求2所述的一种耐腐蚀无缝钢管制备工艺，其特征在于，喷射的润滑剂重量百分比如下：工业牛油8-10％、石墨20-30％二甲基硅油0.05-0.1％、其余为玻璃粉。
4.根据权利要求2所述的一种耐腐蚀无缝钢管制备工艺，其特征在于，棒胚加热、穿孔、酸洗冷轧、热处理均在真空条件下进行。
CN202011351161.7A 2020-11-26 2020-11-26 一种耐腐蚀无缝钢管及其制备工艺 Pending CN112593151A (zh)