CN1237654A - 单晶二氧化钛纳米丝的制备方法 - Google Patents

单晶二氧化钛纳米丝的制备方法 Download PDF

Info

Publication number
CN1237654A
CN1237654A CN98111329.XA CN98111329A CN1237654A CN 1237654 A CN1237654 A CN 1237654A CN 98111329 A CN98111329 A CN 98111329A CN 1237654 A CN1237654 A CN 1237654A
Authority
CN
China
Prior art keywords
tio
micro emulsion
solution
nano thread
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN98111329.XA
Other languages
English (en)
Other versions
CN1077612C (zh
Inventor
李光来
王广厚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing University
Original Assignee
Nanjing University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing University filed Critical Nanjing University
Priority to CN98111329A priority Critical patent/CN1077612C/zh
Publication of CN1237654A publication Critical patent/CN1237654A/zh
Application granted granted Critical
Publication of CN1077612C publication Critical patent/CN1077612C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种获得微米量级的TiO2纳米丝，尤其是单晶TiO2纳米丝的方法，制备NaCl溶液的微乳和TiO2前驱物Ti(OH) 4微乳，将NaCl溶液与Ti(OH) 4两种微乳均匀混合并在一定温度下作热处理，经过热处理，再经过分离、烘干，即得单晶TiO2纳米丝。所用原料是普通的化学药品，制备过程简单，无特殊要求。所得纳米棒尺寸均匀，通过改变成分配比，可以方便地改变纳米晶丝尺寸。重复性好。

Description

单晶二氧化钛纳米丝的制备方法
本发明涉及纳米丝状材料的制备，尤其涉及单晶二氧化钛纳米丝的制备方法。
现有碳弧法、激光烧融、膜模法，气液固(vls)等方法分别制备出纳米碳管、纳米硅(Si)和锗(Ge)棒、GaN棒(纳米级)等长度是微米而直径为几至几十纳米的丝、棒或管。至今还未曾见过获得微米量级的TiO2纳米丝，尤其是单晶TiO2纳米丝的制备方法。
本发明的目的是提出一种获得微米量级的TiO2纳米丝、尤其是单晶TiO2纳米丝的方法。
本发明的目的是这样实现的：一种获得微米量级的TiO2纳米丝，尤其是单晶TiO2纳米丝的方法，其特征是制备NaCl溶液的微乳和TiO2前驱物Ti(OH)4微乳将NaCl溶液与Ti(OH)4两种微乳均匀混合并在一定温度下作热处理，经过热处理0。5-4小时，再经过分离、烘干，即得单晶TiO2纳米丝。
其技术关键是实现Ti(OH)4和NaCl两种微乳的充分均匀混合和控制温度制备过程简单、易重复实现。
本发明的特点是：能获得微米量级的TiO2纳米丝，尤其是单晶TiO2纳米丝，这种材料是微电子、光电器件中具有广泛的应用前景。所用原料是普通的化学药品，易买到。制备过程简单，无特殊要求。所得纳米棒尺寸均匀，通过改变成分配比，可以方便地改变纳米晶丝尺寸。重复性好。
以下结合附图和通过实施例对本发明作进一步说明：
图1为单晶TiO2纳米丝的形貌
图2为单晶TiO2纳米丝的高分辨率像，直径25nm，丝内无缺陷。
微乳法制备TiO2前驱物Ti(OH)4
实验所用微乳体系中，油相为环己烷；表面活性剂是壬基酚聚氧乙烯五醚和九醚分别NP5、NP9，亦可以为其它表面活性剂，其重量比为NP5∶NP9=1∶1的NP5/NP9混合物；水相分别是TiCl4溶液，氨水和NaCl溶液。
本方法主要包括两步，第一步实现NaCl微乳和TiO2的前驱物Ti(OH)4微乳的充分混合；第二步将上述混合物在一定的温度下热处理分离、烘干后即得到制品。具体过程如下：
1：制备TiO2前驱物Ti(OH)4微乳
实验所用微乳体系中，油相为C6-8的芳、烃族溶剂，如环己烷；表面活性剂是重量比NP5∶NP9=1∶1的NP5/NP9混合物；水相分别是TiCl4溶液，氨水和NaCl溶液。
将适量环己烷，NP5/NP9,0.5M TiCl4溶液在烧杯中混合制成TiCl4溶液的微乳；将适量环己烷，NP5/NP9,2M NH4OH溶液混合制成NH4OH溶液的微乳；再将适量上述两种微乳充分混合，反应得到Ti(OH)4的微乳。所有操作在10-25℃下进行。
2:NaCl溶液微乳的制备：
将适量环己烷，NP5/NP9,2M NaCl溶液在10-25℃下混合制成NaCl溶液的微乳。
3．Ti(OH)4和NaCl的充分均匀混合：
将适量Ti(OH)4微乳和NaCl微乳在10-25℃下充分混合，混合微乳中Ti和Na的原子比记作NT.NT一般取值20-2000。将混合微乳倒入足量丙酮中，沉淀生成。沉淀离心分离后，用丙酮清洗两遍，烘干后得到白色NaCl和Ti(OH)4混合粉末。
4热处理；
将上述粉末在适当温度热处理一段时间。产物用水溶解，除去其中NaCl。沉淀离心分离，用水再洗两遍，烘干。即制成具有金红石晶体结构的TiO2纳米晶丝。
表1给出了三组成分配比及所得TiO2纳米晶丝的尺寸。热处理为在750℃保温2小时。其中，环己烷，丙酮，NaCl和氨水为分析纯，TiCl4为化学纯，表面活性剂是直接从化工厂购买的工业原料，水是一次蒸馏水，热处理炉为管式定碳炉。表中TiCl4微乳成分是：0.2ml 0.5M TiCl4溶液+6.6ml环己烷+3.4mlNP5/NP9；NH4OH微乳的成分为0.2ml 2M氨水+6.6ml环己烷+3.4mlNP5/NP9；NaCl微乳的成分是0.2ml 2M NaCl溶液+6.6ml环己烷+3.4mlNP5/NP9。从表中可以看出，纳米TiO2晶丝的尺寸随NT的值变化，NT越大，品丝越细长。NT的值取20-2000。
本发明方法的关键是在微乳体系中实现Ti(OH)4和NaCl的充分均匀混合。对比实验表明，若二者混合不均匀，则棒较粗，粗细不均匀。
表1微乳体系的成分和TiO2纳米晶丝的尺寸
123   TiCl4微乳4ml2mllml  NH4OH微乳4ml2mllml NaCl微乳12ml24ml30ml  NT1004001000 晶须平均尺寸(长度直径)2μm、75nm2μm、30nm4μm、22nm

Claims (5)

1．一种获得微米量级的TiO2纳米丝，尤其是单晶TiO2纳米丝的方法，其特征是制备NaCl溶液的微乳和TiO2前驱物Ti(OH)4微乳将NaCl溶液与Ti(OH)4两种微乳均匀混合并在一定温度下作热处理，经过热处理，再经过分离、烘干，即得单晶TiO2纳米丝。
2．由权利要求1所述的制备微米量级的TiO2纳米丝的方法，其特征是微乳体系中，油相为C6nC8-的芳、烃族溶液，如环己烷；水相分别是TiCl4溶液，氨水和NaCl溶液，再加上表面活性剂使微乳充分均匀。
3．由权利要求1、2所述的制备微米量级的TiO2纳米丝的方法，其特征是表面活性剂为NP5/NP9，以0.5M TiCl4溶液混合制成TiCl4溶液的微乳；将适量环己烷，NP5/NP9,2M NH4OH溶液混合制成NH4OH溶液的微乳；再将适量上述两种微乳充分混合，反应得到Ti(OH)4的微乳，所有操作在10-25℃下进行。
4．由权利要求1、2所述的制备微米量级的TiO2纳米丝的方法，其特征是过热处理时间为0。5-4小时。
5由权利要求1、2所述的制备微米量级的TiO2纳米丝的方法，其特征是混合微乳中Ti和Na的原子比取值20-2000。
CN98111329A 1998-06-02 1998-06-02 单晶二氧化钛纳米丝的制备方法 Expired - Fee Related CN1077612C (zh)