CN1676745A - Multi-layer coating fabric - Google Patents
Multi-layer coating fabric Download PDFInfo
- Publication number
- CN1676745A CN1676745A CN 200410017318 CN200410017318A CN1676745A CN 1676745 A CN1676745 A CN 1676745A CN 200410017318 CN200410017318 CN 200410017318 CN 200410017318 A CN200410017318 A CN 200410017318A CN 1676745 A CN1676745 A CN 1676745A
- Authority
- CN
- China
- Prior art keywords
- fabric
- coating fabric
- laminated coating
- layer
- polyurethane resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention discloses a kind of multi-layer-pasting fabric, made with the method of pasting at least 2 layers of different slurries on one layer of base cloth. The components of the slurry-pasting surface layer is (by weight): polyurethane resinI30-60%, polyurethane resin II 30-50%, cross linkerI1-5%, cross linker II 0.5-3.5%, accelerator I 0.5-10%, accelerator II 0.5-5%, fire retardant 2-5%, antiseptic and mildew preventive 1-2%, dimethyl formamide 0-2%, toluene 3-5% and methyl ethyl ketone 1-2%. The components of the slurry-pasting bottom layer is (by weight): polyurethane adhesive 80-100% and dimethyl formamide 0-20%. The coldness resistance of this invention is nice, and even at -60deg.C the paintcoat will not turn fragile, crack, get deformed or become hard. At the same time, it has the merits of aeration, fire resistance and antisepsis, with the air permeability of over 1000g/square meter, antisepsis of 1 level and the fire resistance reaching the nation standard. In a word, it is more fit to be used in cold.
Description
Technical field
The present invention relates to a kind of functional textile, particularly a kind of have a textiles cold-resistant, ventilative, fire-retardant, antibacterial functions.
Background technology
In the prior art, in extreme climate environment, work, live at people, textiles is had further functional demand, has developed some respectively and had textiles cold-resistant, ventilative, fire resistance, make fabric have windproof, DOWN PROOF gets out, cold-resistant performance such as warming.
91218732), " research and development of military function textile material " (" china academia collection of thesis " the time of meeting: functional windproof coated fabric May 10 calendar year 2001) in disclosed domestic patent (application number is 88101574.1) and " cold-resistant and permeable coating windbreaker cloth " (Chinese science and technology achievement storehouse numbering:, its performance incompatibility is lower than under-20 ℃ of temperature to be used, otherwise embrittlement, breaking strain will harden, thereby lost cold-resistant warming effect, therefore incompatible in the South Pole, dark cold fields such as high-altitude, deep-sea use.
Summary of the invention
The objective of the invention is to be to provide a kind of laminated coating textiles cold-resistant, ventilative, fire-retardant, antibacterial functions that has simultaneously.Overcome functional windproof coated fabric and be lower than under-20 ℃ of temperature and use, can harden embrittlement, breaking strain have lost the defective of cold-resistant thermal effect, also have fire-retardant, anti-microbial property simultaneously.
A kind of laminated coating fabric of the present invention is characterized in that it is different slurry coatings and constituting more than coating on one deck base cloth is two-layer at least or two-layer.
Aforesaid laminated coating fabric is characterized in that the percentage by weight of coating paste surface layer component is: polyurethane resin I 30-60%, polyurethane resin II 30-50%, crosslinking agent I 1-5%, crosslinking agent II 0.5-3.5%, promoter I 0.5-10%, promoter II0.5-5%, fire retardant 2-5%, antibacterial mildew inhibitor 1-2%, dimethylformamide 0-2%, toluene 3-5%, methyl ethyl ketone 1-2%.
Aforesaid laminated coating fabric is characterized in that the percentage by weight of coating paste bottom component is: polyurethane adhesive 80-100%, dimethylformamide 0-20%.
Aforesaid laminated coating fabric is characterized in that described polyurethane resin I is the two-liquid type fragrance same clan (UD-8310LP), and polyurethane resin II is hydrophilic aliphatic category (Y-208).
Aforesaid laminated coating fabric is characterized in that described crosslinking agent I is a no xanthochromia isocyanates (NE), and crosslinking agent II is the two-liquid type fragrance same clan (UD).
Aforesaid laminated coating fabric is characterized in that described promoter I solidifies isocyanates (HI-215) at a high speed for no xanthochromia, and promoter II is two-liquid type general category (UD-102).
Aforesaid laminated coating fabric is characterized in that described polyurethane adhesive is the hydrophilic class of atresia (Y-147).
The advantage of coated fabric of the present invention is that its cold tolerance is better, have in temperature when reaching-60 ℃ fabric coating not crisp, do not split, indeformable, characteristics such as do not harden, also have ventilative, fire-retardant, antibiotic multiple function simultaneously, its gas permeability is greater than 1000g/m
2, antibacterial and mouldproof can reach 1 grade, fire-retardantly also be up to state standards, so it is more suitable in using at ice box.
Description of drawings
Accompanying drawing 1 coated fabric structural representation.
Accompanying drawing 2 coated fabric coating process schematic diagrames.
Specific embodiments
Below in conjunction with accompanying drawing coated fabric of the present invention is described further.
The present invention has adopted the transfer coated technology of release liners dry method, and product structure is two layers of coating and one deck base fabric.Its procedure of processing is as follows:
1. base cloth 3: COTTON FABRIC or islands-in-sea type fibre fabric are handled through fire-retardant, mildew-resistant, as the base cloth of coated fabric.
2. slurry is prepared:
(1) base pastes 2: polyurethane adhesive Y-147, dimethyl formyl are mixed, and the percentage by weight of its component is 85: 15, stirs with agitator, and is stand-by.
(2) surface layer slurry 1: polyurethane resin I UD-8310LP, polyurethane resin IIY-208, crosslinking agent I NE, crosslinking agent II UD, promoter I HI-215, promoter II UD-102, fire retardant TCPP, antibacterial mildew inhibitor SCJ-892, dimethylformamide, toluene, methyl ethyl ketone are mixed, and the percentage by weight of its component is
44: 32: 5: 3.3: 2.2: 1.5: 3: 2: 2: the usefulness agitator stirred in 3.5: 1.5, made stand-by.
3. the transfer coated technology of release liners dry method:
Release liners unreels → and surface layer slurry coating → drying → surface layer slurry coating → drying → base pastes coating → drying → heat posted closes → rolls → and slaking → paper film peels off → finished product
Concrete operations are as follows:
(1) release liners is after live-roller 4 unreels, and is coated with on paper by surface layer slurry scraper 5 for the first time and scrapes the 0.01-0.02mm surface layer slurry, dryer 6 inner dryings of setting 80-130 ℃ of inclination temperature 3 minutes.
(2) be coated with on paper by surface layer slurry scraper 7 more for the second time and scrape the 0.01-0.02mm surface layer slurry, dryer 8 inner dryings of setting 80-130 ℃ of inclination temperature 3 minutes.
(3) be coated with on paper by base pastes scraper 9 for the third time and scrape the 0.02-0.03mm base pastes, dryer 10 inner dryings of setting 100-120 ℃ of inclination temperature 3 minutes.
(4) base cloth of handling well in advance and is coated with the release liners of having scraped three layers of slurry after 100 ℃ hot-rolling 12 is bonding after base cloth let off roll 11 unreels, rolled by wind-up roll 13.
That (5) will roll was coated under 50 ℃ of conditions slaking 48 hours, then the paper film was peeled off, and oven dry makes finished product fully.
The advantage of coated fabric of the present invention is: cold tolerance is better, can reach in temperature-In the time of 60 ℃ fabric coating not crisp, do not split, indeformable, do not harden; Simultaneously it also have ventilative, The characteristic of fire-retardant, antibacterial and mouldproof, its gas permeability is greater than 1000g/m2, antibacterial and mouldproof can reach 1 Level fire-retardantly also is up to state standards, so it is more suitable in using at ice box.
Claims (7)
1. laminated coating fabric is characterized in that it is different slurry coatings and constituting more than coating on one deck base cloth is two-layer at least or two-layer.
2. laminated coating fabric as claimed in claim 1 is characterized in that the percentage by weight of coating paste surface layer component is: polyurethane resin I 30-60%, polyurethane resin II 30-50%, crosslinking agent I 1-5%, crosslinking agent II 0.5-3.5%, promoter I 0.5-10%, promoter II 0.5-5%, fire retardant 2-5%, antibacterial mildew inhibitor 1-2%, dimethylformamide 0-2%, toluene 3-5%, methyl ethyl ketone 1-2%.
3. laminated coating fabric as claimed in claim 1 is characterized in that the percentage by weight of coating paste bottom component is: polyurethane adhesive 80-100%, dimethylformamide 0-20%.
4. laminated coating fabric as claimed in claim 2 is characterized in that described polyurethane resin I is a two-liquid type aromatic series, and polyurethane resin II is hydrophilic aliphatic category.
5. laminated coating fabric as claimed in claim 2 is characterized in that described crosslinking agent I is no xanthochromia isocyanates, and crosslinking agent II is the two-liquid type fragrance same clan.
6. laminated coating fabric as claimed in claim 2 is characterized in that described promoter I solidifies isocyanates at a high speed for no xanthochromia, and promoter II is the two-liquid type general category.
7. laminated coating fabric as claimed in claim 3 is characterized in that described polyurethane adhesive is the hydrophilic class of atresia.