CN1844226A - Color plastic floor made of waste PVC and manufacturing method thereof - Google Patents
Color plastic floor made of waste PVC and manufacturing method thereof Download PDFInfo
- Publication number
- CN1844226A CN1844226A CN 200610043514 CN200610043514A CN1844226A CN 1844226 A CN1844226 A CN 1844226A CN 200610043514 CN200610043514 CN 200610043514 CN 200610043514 A CN200610043514 A CN 200610043514A CN 1844226 A CN1844226 A CN 1844226A
- Authority
- CN
- China
- Prior art keywords
- plastic floor
- color plastic
- pvc
- useless pvc
- produces
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a process for making colored plastic rubber flooring from waste PVC, wherein the flooring comprises (by weight ratio) waste PVC 100, CPE 10-50, plasticizer 10-50, filling material 50-350, stabilizing agent 1-10, lubricating agent 0.1-3, and combustion inhibitor 5-15. The making process comprises the steps of waste PVC disintegrating, cleaning, drying, mixing, squeezing, coloring, embossing, cooling down and cutting.
Description
(1) technical field under
The present invention relates to a kind of plastic floor, particularly a kind of color plastic floor that utilizes useless PVC production and preparation method thereof.
(2) background technology
Existing pavement mainly contains following several: sintering ceramic tile, lithotome, bamboo-wood floor, fabric carpet.They have exposed all weak points gradually in daily use: the sintering ceramic tile: hard, sliding, from great, occupy cultivated land (clay), high energy consumption, classified as the restriction project by country; Lithotome: shortage of resources, from great, radiation arranged; Wood, bamboo floor: do not prevent fires, moistureproof, the introducing that in the production installation process, can not avoid objectionable impurities; Fabric carpet: do not set fire, moistureproof, easily breed bacteria, biology, non-easy cleaning etc.The birth of plastic floor has overcome numerous deficiencies of above ground material, and have sound-absorbing, suitable elasticity is arranged, from heavy and light, abundant, the energy-conserving and environment-protective of pattern, fire-retardant, antibiotic chemically-resistant material, easy cleaning, the easy advantage of maintenance, but because of it involves great expense, can not penetration and promotion.
(3) summary of the invention
The present invention is in order to remedy the deficiencies in the prior art, and a kind of color plastic floor that cost, the useless PVC of utilization easy to utilize produce and preparation method thereof that reduces greatly is provided.
The present invention is achieved through the following technical solutions:
A kind of color plastic floor that utilizes useless PVC to produce, its special character is: the raw material and the auxiliary material that comprise following parts by weight:
Useless PVC 100 CPE 10-50 softening agent 10-50
Filler 50-350 stablizer 1-10 lubricant 0.1-3
Fire retardant 5-15.
Color plastic floor of the present invention, other comprises the Sodium dodecylbenzene sulfonate as 2-15 part surface treatment agent.
Color plastic floor of the present invention, other comprises an amount of pattern piece that spreads.The described pattern piece that spreads is in versicolor PVC, the PU of 0.1-2mm, PE, EPDM, the CPE particle one or more for size.
Described softening agent is DOP or DBP.
Described filler is one or more in light calcium carbonate, water-ground limestone, calcium sulfate, flyash, talcum powder, cement, the red mud.
Described surface treatment agent is a Sodium dodecylbenzene sulfonate.
Described stablizer is one or both in tribasic lead sulfate, the dibasic lead phosphite.
Described lubricant is stearic acid or stearate.
Described floor is sheet material or coiled material.
The making method of the color plastic floor that the useless PVC of utilization of the present invention produces comprises the steps:
(1) useless PVC pulverizing, cleaning, the drying that classification is reclaimed;
(2) choose 100 parts of useless PVC material, the filler after adding 50-350 part drying treatment adds CPE, softening agent, surface treatment agent, stablizer, lubricant, fire retardant, then 70-140 ℃ of following high-speed mixing;
(3) mixed raw materials and auxiliary material feeding screw rod are extruded agent, under 100-185 ℃, extrude;
(4) evenly spread at screw extrusion press head place handle well spread pattern piece or mill base;
(5) with rolling press press polish or use the embossing machine embossing;
(6) cooling, the cutting, finished product.
Because this floor added CPE, make this floor when possessing plastic nature, possess the character of rubber again, anti-skidding, eliminate the noise, suitable elasticity and snappiness are arranged, light and sliding, hard and not crisp.Simultaneously, this floor is homogeneous penetrating, and is not stratified, thickness 2-8mm; Pattern is various monochromes and marbleize, and the surface is plane, salient point surface and hammering line face.
The present invention has kept the excellent properties of existing plastic floor, greatly reduce production cost (for the currently available products production cost 50%).Simultaneously, utilize useless PVC because of a large amount of, and eliminated " white garbage " pollution environment.
(4) embodiment
Embodiment 1:
Useless PVC pulverizing, cleaning, drying to the classification recovery; Choose the useless PVC material of 100kg, add CPE 40kg, DOP 40kg, tribasic lead sulfate 3kg, dibasic lead phosphite 2kg stearic acid 2.5kg, lime carbonate 150kg, aluminium hydroxide 10kg, then 70 ℃ of following high-speed mixing; Mixed raw materials and auxiliary material feeding screw rod are extruded agent, under 100 ℃, extrude; Evenly spread size at screw extrusion press head place and spread the pattern piece for the versicolor PU of 0.1-2mm; Use the rolling press press polish; The cooling, the cutting, finished product.
Embodiment 2:
Useless PVC pulverizing, cleaning, drying to the classification recovery; Choose the useless PVC material of 100kg, add CPE 10kg, DBP 10kg, tribasic lead sulfate 1kg, dibasic lead phosphite 1kg stearic acid 0.5kg, lime carbonate 50kg, aluminium hydroxide 5kg, then 140 ℃ of following high-speed mixing; Mixed raw materials and auxiliary material feeding screw rod are extruded agent, extrude at 185 times; Evenly spread 20kg size at screw extrusion press head place and spread the pattern piece for the versicolor EPDM of 0.1-2mm; Use the embossing machine embossing; The cooling, the cutting, finished product.
Embodiment 3:
Useless PVC pulverizing, cleaning, drying to the classification recovery; Choose the useless PVC material of 100kg, add CPE 50kg, DOP 50kg, tribasic lead sulfate 4kg, dibasic lead phosphite 5kg stearic acid 3kg, flyash 350kg, aluminium hydroxide 15kg, then 100 ℃ of following high-speed mixing; Mixed raw materials and auxiliary material feeding screw rod are extruded agent, under 140 ℃, extrude; Mill base is evenly spread at the place at the screw extrusion press head; Use the rolling press press polish; The cooling, the cutting, finished product.
Embodiment 4:
Useless PVC pulverizing, cleaning, drying to the classification recovery; Choose the useless PVC material of 100kg, add CPE 35kg, DBP 30kg, tribasic lead sulfate 8kg, Sodium dodecylbenzene sulfonate 15kg, sodium stearate 1kg, cement 100, red mud 150kg, aluminium hydroxide 15kg, then 100 ℃ of following high-speed mixing; Mixed raw materials and auxiliary material feeding screw rod are extruded agent, under 150 ℃, extrude; Mill base is evenly spread at the place at the screw extrusion press head; Use the rolling press press polish; The cooling, the cutting, finished product.
Embodiment 5:
Useless PVC pulverizing, cleaning, drying to the classification recovery; Choose the useless PVC material of 100kg, add CPE 35kg, DBP 30kg, dibasic lead phosphite 8kg, Sodium dodecylbenzene sulfonate 2kg, sodium stearate 1kg, talcum powder 150kg, aluminium hydroxide 8kg, then 90 ℃ of following high-speed mixing; Mixed raw materials and auxiliary material feeding screw rod are extruded agent, under 170 ℃, extrude; Evenly spread 10kg size at screw extrusion press head place and spread the pattern piece for the versicolor PVC of 0.1-2mm; Use the rolling press press polish; The cooling, the cutting, finished product.
Claims (10)
1. color plastic floor that utilizes useless PVC to produce is characterized in that: the raw material and the auxiliary material that comprise following parts by weight:
Useless PVC 100 CPE 10-50 softening agent 10-50
Filler 50-350 stablizer 1-10 lubricant 0.1-3
Fire retardant 5-15.
2. the color plastic floor that the useless PVC of utilization according to claim 1 produces, it is characterized in that: other comprises the Sodium dodecylbenzene sulfonate as 2-15 part surface treatment agent.
3. the color plastic floor that the useless PVC of utilization according to claim 1 produces is characterized in that: other comprises an amount of pattern piece that spreads.
4. the color plastic floor that the useless PVC of utilization according to claim 1 produces, it is characterized in that: described softening agent is DOP or DBP.
5. the color plastic floor that the useless PVC of utilization according to claim 1 produces, it is characterized in that: described filler is one or more in light calcium carbonate, water-ground limestone, calcium sulfate, flyash, talcum powder, cement, the red mud.
6. the color plastic floor that the useless PVC of utilization according to claim 1 produces, it is characterized in that: described stablizer is one or both in tribasic lead sulfate, the dibasic lead phosphite.
7. the color plastic floor that the useless PVC of utilization according to claim 1 produces, it is characterized in that: described lubricant is stearic acid or stearate.
8. the color plastic floor that the useless PVC of utilization according to claim 1 produces is characterized in that: the described pattern piece that spreads is in versicolor PVC, the PU of 0.1-2mm, PE, EPDM, the CPE particle one or more for size.
9. according to the color plastic floor of the useless PVC production of each described utilization of claim 1 to 8, it is characterized in that: described floor is sheet material or coiled material.
10. the making method of the color plastic floor that the useless PVC of utilization according to claim 1 produces is characterized in that: comprise the steps:
(1) useless PVC pulverizing, cleaning, the drying that classification is reclaimed;
(2) choose 100 parts of useless PVC material, the filler after adding 50-350 part drying treatment adds CPE, softening agent, surface treatment agent, stablizer, lubricant, fire retardant, then 70-140 ℃ of following high-speed mixing;
(3) mixed raw materials and auxiliary material feeding screw rod are extruded agent, under 100-185 ℃, extrude;
(4) evenly spread at screw extrusion press head place handle well spread pattern piece or mill base;
(5) with rolling press press polish or use the embossing machine embossing;
(6) cooling, the cutting, finished product.