CN202123720U - Holographic pattern film - Google Patents
Holographic pattern film Download PDFInfo
- Publication number
- CN202123720U CN202123720U CN2011202549585U CN201120254958U CN202123720U CN 202123720 U CN202123720 U CN 202123720U CN 2011202549585 U CN2011202549585 U CN 2011202549585U CN 201120254958 U CN201120254958 U CN 201120254958U CN 202123720 U CN202123720 U CN 202123720U
- Authority
- CN
- China
- Prior art keywords
- film
- holographic pattern
- information transfer
- transfer layer
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model relates to a holographic pattern film. An information transfer layer of the holographic pattern film has a holographic pattern groove structure of a copied base film. The structure of the holographic pattern film is as follows in sequence: a foil film, an adhesive layer and the information transfer layer, wherein the adhesive layer is one of acrylic resin or improved acrylic resin, polyurethane resin or improved polyurethane resin, and epoxy resin or improved epoxy resin; the information transfer layer has the groove structure of the surface of the copied base film. According to the holographic pattern film disclosed by the utility model, the information transfer layer has the holographic pattern groove structure of the copied base film, so that the holographic pattern of the base film can be copied accurately.
Description
Technical field
The utility model relates to a kind of holographic pattern film, and the information transfer layer of this holographic pattern film has the holographic pattern groove structure of the female film that duplicates.
Background technology
In the prior art; When making the holographic pattern film, employing be that technology is: in moulding press, directly on film, carry out the impression of holographic pattern; The holographic pattern film of making both can be the transfer membrane as intermediate products, also can be used as finished product holographic pattern film and sold or use.But in the prior art, the making of each reel all need repeat the mold pressing procedure of film surface hologram line obviously; Production efficiency is low; According to statistics, go up according to the manufacture craft of stating operation, with existing production capacity; A moulding press can only be produced 30000 meters films in one day, and the efficient of mold pressing procedure has only 1/3 of painting process.
But in fact, when carrying out the making of holographic pattern film, be exist to practice thrift cost, raise the efficiency possible.Reason is: so-called holographic pattern, be meant the employing mould pressing process, and holographic interference fringes is impressed into that base material (plastic sheeting, paper or other materials) is gone up and the hologram that obtains with the form of embossment structure.It from macroscopic view visually is presented as various hologram patterns, but from microcosmic, it is presented as groove, promptly has the interference fringe groove of certain depth; And the above-mentioned interference stripe groove can duplicate.
The applicant thinks that above-mentioned groove structure can be replicated from microcosmic fully after above-mentioned groove structure is researched and analysed between each layer.Therefore, can realize duplicating of holographic pattern, thereby reduce production costs greatly, and enhance productivity accurately the duplicating of holographic pattern information groove structure as long as can realize.
The utility model content
The purpose of the utility model is following:
A kind of holographic pattern film is provided, and this holographic pattern film utilizes coating process to make, and the information transfer layer has the groove structure of the female film surface hologram line that duplicates; Therefore realized accurately duplicating to holographic pattern on female film; Accuracy of repetition is high, and is effective, and production efficiency is high.
A kind of holographic pattern film of the utility model, said structure is following successively:
The paper tinsel film;
Adhesive layer, said adhesive layer are a kind of in acrylic resin or acrylic resin modified, polyurethane resin or modified polyurethane resin, epoxy resin or the modified epoxy;
The information transfer layer;
It is characterized in that: said information transfer layer has the groove structure on the female film surface that is replicated.The holographic pattern film of the utility model is with respect to holographic pattern film of the prior art; The holographic effect of the figure line that its surface has not is to be directly to form through holography impression, but through to holographic pattern groove structure on female film accurately duplicate and form.The holographic pattern groove structure that is about to female film surface is copied to the information transfer layer.The application's adhesive layer material all has thermosetting, makes in combination process, and information transfer layer and paper substrate adhesion-tight, easy to operate, and be industrial materials commonly used, provide cost savings.
Further, in the technique scheme, said paper tinsel film is selected from the composite membrane or the chemical films of PET film, PP film, PI film, PC film, PS film, PE film, PVC film, PVDC film, nylon membrane or metal forming or above-mentioned paper tinsel, film.
Further, in the technique scheme, said information transfer layer material is a kind of in metal or metal oxide or zinc sulphide or the silica, and thickness is the 50-1000 dust.The information transfer layer of above-mentioned material vapor deposition forms stable, even, fine and close adhering on female film groove structure; Therefore can duplicate the holographic pattern groove structure on female film surface accurately; And more be applicable to the vapor deposition of high speed reel, therefore can obtain better vapor deposition effect.
Further; In the technique scheme; Also comprise second protective layer, be positioned on the information transfer layer that said second protective layer material is a kind of in acrylic resin or acrylic resin modified, polyurethane resin or modified polyurethane resin, epoxy resin or the modified epoxy.And second protective layer material of above-mentioned selection can form fine and close structure on new holographic figure line film surface, forms protection thereby can fill and lead up its surperficial groove structure uniformly, and can both be applicable to the intaglio plate coating.
The beneficial effect of the utility model is following: the utility model is creationary utilized holographic pattern groove structure that female film surface has can be by accurate replicability; When making the holographic pattern film in the prior art; The operation that need repeat is holographic pattern impression operation particularly; Be improved to the duplicating of female film surface hologram groove groove structure, utilize painting process to carry out the making of holographic pattern film, thereby can reduce production costs greatly; Enhance productivity, saved particularly that repeat mold pressing this is the most loaded down with trivial details, influence production efficiency most, increased the link of production cost most.According to statistics, realizing impression is improved under the situation of coating, production efficiency will be than improving at least more than 3 times originally.The holographic pattern film of the utility model, its information transfer layer has the holographic pattern groove structure of the female film that duplicates, and can realize accurately duplicating female film holographic pattern.
Description of drawings
Fig. 1 is the microstructure sketch map of holographic pattern film of the present invention.
Fig. 2 is the microstructure sketch map of another preferred embodiment of holographic pattern film of the present invention.
Fig. 3 is a process flow diagram of the present invention.
In the above-mentioned sketch map, the female film of 1-; The groove structure of the female film surface hologram of 2-line; 4-information transfer layer; The 5-adhesive layer; 6-paper tinsel film; 7-second protective layer.
The specific embodiment
The manufacture craft of a kind of holographic pattern film of the present invention; Its principle is: the characteristic of utilizing holographic pattern microcosmic groove structure accurately to be duplicated; Utilize the information transfer layer to duplicate the holographic pattern groove structure on female film surface; Formation has the transfer membrane of the microcosmic groove structure of the holographic pattern that is replicated, and utilizes this transfer membrane to make the holographic pattern film again.The holographic pattern of female film then is retained in female film.On technology, when making the holographic pattern film, realized having substituted imprint process of the prior art with coating process, improved production efficiency greatly, provide cost savings.
Accurately duplicate requirement for what reach the holographic pattern groove structure; The application is in manufacture craft; The selection of layers of material and the technological parameter of layers of material are all optimized, both improved production efficiency, what is more important is in follow-up technology; Guaranteed the accuracy that the holographic pattern groove structure duplicates between each layer; Well arranged, the Stability Analysis of Structures of the groove structure that duplicates under the above-mentioned technological parameter, accuracy of repetition is high, thereby visually is presented as the high accuracy of female film holographic pattern is duplicated.
Specifically, as shown in Figure 3, the surface of female film 1 has holographic pattern groove structure 2, and vapor deposition information transfer layer 4 on female film surface, and evaporation process is following: in vacuum evaporation plating machine, vacuum is lower than 10-2 millibar, speed 60-1000m/min.Utilize the characteristic that can accurately be duplicated between structure sheaf of holographic pattern microcosmic groove structure, above-mentioned groove structure 2 is copied to information transfer layer 4 accurately.Having this kind layer constructed products and can be referred to as transfer membrane, is the basis of carrying out subsequent technique of the present invention.
Coating adhesive adhesion coating 5 on the information transfer layer 4 of transfer membrane, also coating adhesive adhesion coating 5 on the paper tinsel film earlier carries out transfer membrane and paper tinsel film compound again; Combination process is following: in compounding machine; 80-150 ℃ of oven dry, be 10-60 second drying time, operating speed is 20-150m/min.Female film is peeled off, can be obtained the holographic pattern film.After peeling off, attached on the paper tinsel film, because information transfer layer 4 is the holographic pattern groove structures 2 on the female film that duplicates, therefore, this holographic pattern film has also promptly been realized duplicating holographic pattern on female film to information transfer layer 4 with adhesive layer.And female film of this moment still also remains with complete holographic pattern, can continue to use and carry out follow-up technology.When carrying out combination process, can dry earlier again adhesive layer compound, also can be earlier compound oven dry again, among the application this is not done the qualification of order.
As a kind of improvement, can apply a transfer layer between female film 1 and the information transfer layer 4, thereby make that duplicating with transfer effect of female film surface hologram groove groove structure is more superior.Transfer layer adopts coating machine to be applied to wet amount 1-20 gram/m
2,, 80-200 ℃ of oven dry, be 10-60 second drying time, operating speed is 20-150m/min.
Improve as another kind; On the basis that makes above-mentioned holographic pattern film, above-mentioned can also further being improved to: surface-coated second protective layer at the holographic pattern film, carry out itself and film compound again; After compound film is peeled off the holographic pattern film that is improved.Because it is not through multiple membrane process, so its surface do not have minute surface (face) effect that traditional transfer membrane technology is had, and this is a weak point of utilizing the holographic pattern film that this technology makes.So the information transfer layer not only has the holographic pattern groove structure identical with female film; And grating is just full; Groove structure is stable, well arranged, and this new holographic figure line film can reach face (minute surface) effect after the same transfer of the holographic pattern film that makes with traditional transfer membrane technology.
Female film among the present invention adopts female film commonly used on the market to get final product; Preferred surface has the roll type film of holographic pattern groove structure or the composite membrane of metal forming or film and metal forming; Because its surface grating is full, groove structure is more stable, more helps realizing accurately duplicating of groove structure.And the female film of roll type is applicable to and the continuity production application of large molded machine, coating machine, compounding machine can improves efficiency of operation greatly.Female film commonly used on the market mainly contains following two kinds of structures.A kind of is the female film with double-layer structure, promptly comprises paper tinsel rete, Information Level, and wherein the information layer surface impression has holographic pattern.Therefore, from microcosmic, female film surface promptly has the groove structure of holographic pattern, thereby can realize duplicating this groove structure.And another kind has three-decker, i.e. paper tinsel rete, Information Level, information protection layer, and wherein the information layer surface impression has holographic pattern.Above-mentioned paper tinsel rete; Can be selected from the composite membrane of PET film, PP film, PI film, PC film, PS film, PE film, PVC film, PVDC film, nylon membrane or metal forming or above-mentioned paper tinsel, film; Metal forming wherein; Then can be all kinds of common metal paper tinsels of aluminium foil, Copper Foil or the like, as long as processing requests such as Information Level adhesion-tight, the follow-up heatproof stretch-proof of adaptation all can.For carrying out compound paper tinsel film,, can also select to use chemical films except selecting for use the above-mentioned material with female film.Chemical films described here is meant with plastics to be that substrate surface is through chemically treated plastic sheeting.
First group of embodiment (1-3)
It is that medium carries out vapor deposition that the information transfer layer adopts metallic copper; Adhesive layer adopts polyurethane resin; Second protective layer adopts acrylic resin; Holographic pattern membrane structure: paper tinsel film, urethane resin layer, metal copper layer, acrylate resin layer.
Information transfer layer vapor deposition thickness 50 dusts, evaporation process: vacuum 10-2 millibar, speed 60m/min; The adhesive layer combination process: 80 ℃ of oven dry, be 10 seconds drying time, operating speed is 20m/min; Acrylic resin adopts coating machine to be applied to wet amount 1 gram/m
2, 80 ℃ of oven dry, 10 seconds drying times, operating speed 20m/min.
Information transfer layer vapor deposition thickness 500 dusts, evaporation process: vacuum 10
-3Millibar, speed 500m/min; The adhesive layer combination process: 120 ℃ of oven dry, be 30 seconds drying time, operating speed is 100m/min; Acrylic resin adopts coating machine to be applied to wet amount 10 gram/m
2, 150 ℃ of oven dry, 30 seconds drying times, operating speed 100m/min.
Embodiment 3
Information transfer layer vapor deposition thickness 1000 dusts, evaporation process: vacuum 10
-3Millibar, speed 1000m/min; The adhesive layer combination process: 150 ℃ of oven dry, be 60 seconds drying time, operating speed is 150m/min; Acrylic resin adopts coating machine to be applied to wet amount 20 gram/m
2, 200 ℃ of oven dry, 60 seconds drying times, operating speed 150m/min.
Second group of embodiment (4-6)
Different with first group of embodiment is that the information transfer layer adopts metallic aluminium; Adhesive layer adopts acrylic resin; Second protective layer adopts polyurethane resin; Holographic pattern membrane structure: paper tinsel film, acrylate resin layer, aluminium lamination, urethane resin layer.
The 3rd group of embodiment (7-9)
Different with first group of embodiment is that the information transfer layer adopts silica; Adhesive layer adopts acrylic resin modified; Second protective layer adopts epoxy resin; Holographic pattern membrane structure: paper tinsel film, acrylic resin modified layer, silicon oxide layer, epoxy resin layer.
The 4th group of embodiment (10-12)
Different with first group of embodiment is that the information transfer layer adopts zinc sulphide; Adhesive layer adopts epoxy resin; Second protective layer adopts acrylic resin modified; Holographic pattern membrane structure: paper tinsel film, epoxy resin layer, zinc sulfide layer, acrylic resin modified layer.
The 5th group of embodiment (13-15)
Different with first group of embodiment is that the information transfer layer adopts metallic zinc; Adhesive layer adopts modified epoxy; Second protective layer adopts modified polyurethane resin; Holographic pattern membrane structure: paper tinsel film, modified epoxy layer, metallic zinc layer, modified polyurethane resin layer.
The 6th group of embodiment (16-18)
Different with first group of embodiment is that the information transfer layer adopts zinc sulphide; Adhesive layer adopts modified polyurethane resin; Second protective layer adopts modified epoxy; Holographic pattern membrane structure: paper tinsel film, modified polyurethane resin layer, zinc sulfide layer, modified epoxy layer.
In embodiment 1-18, apply a transfer layer, vapor deposition information transfer layer more earlier on female film surface.Transfer layer adopts celluosic resin, acrylic resin, polyurethane resin, epoxy resin, modified cellulose resin, acrylic resin modified, modified polyurethane resin, modified epoxy, wax class successively; Process conditions such as 1-18 are said, recycle above-mentioned transfer layer material and get embodiment 19-36.
The foregoing description product is through detecting, and the holographic pattern film is to the accuracy that accurately reaches more than 90% of duplicating of female film holographic pattern groove structure, from contrast visually, the holographic pattern indifference on the holographic pattern on the holographic pattern film and the female film.
Claims (4)
1. holographic pattern film, said structure is following successively:
The paper tinsel film;
Adhesive layer, said adhesive layer are a kind of in acrylic resin or acrylic resin modified, polyurethane resin or modified polyurethane resin, epoxy resin or the modified epoxy;
The information transfer layer;
It is characterized in that: said information transfer layer has the groove structure on the female film surface that is replicated.
2. a kind of holographic pattern film according to claim 1 is characterized in that: said paper tinsel film is selected from the composite membrane or the chemical films of PET film, PP film, PI film, PC film, PS film, PE film, PVC film, PVDC film, nylon membrane or metal forming or above-mentioned paper tinsel, film.
3. a kind of holographic pattern film according to claim 1 and 2 is characterized in that: said information transfer layer material is a kind of in metal or metal oxide or zinc sulphide or the silica, and thickness is the 50-1000 dust.
4. a kind of holographic pattern film according to claim 1 and 2; It is characterized in that: also comprise second protective layer; Be positioned on the information transfer layer, said second protective layer material is a kind of in acrylic resin or acrylic resin modified, polyurethane resin or modified polyurethane resin, epoxy resin or the modified epoxy.