CS203631B1 - Sanitary liquid adhesive agent

Info

Publication number: CS203631B1
Application number: CS891278A
Authority: CS
Inventors: Milan Bares; Stanislav Husnik; Jindrich Tippman
Original assignee: Milan Bares; Stanislav Husnik; Jindrich Tippman
Priority date: 1978-12-27
Filing date: 1978-12-27
Publication date: 1981-03-31

Description

Vynález se týká sanitačního kapalného adhezního prostředku na bázi anionaktivních a neionogenních tenzidů, určeného pro účinné odstraňování nečistoty spolu s desinfekčním a deodoračním účinkem při čištění hygienických a sanitačních zařízení.The present invention relates to a sanitizing liquid adhesive composition based on anionic and non-ionic surfactants for the effective removal of dirt along with a disinfecting and deodorizing effect in the cleaning of sanitary and sanitation equipment.

Dosud známé kapalné prostředky k odstraňování nečistoty na bázi povrchově aktivních látek a anorganických přísad mají zejména práškovou nebo kompaktní pevnou a v omezených případech i kapalnou formu. Práškové typy prostředků jsou obyčejně kombinací anionaktivních typů tenzidů sulfátového nebo sulfonanového typu, křemičitanů, sody a fosforečnanů. Pro dosaženídezinfekčního účinku jsou tyto čisticí prostředky kombinovány s přísadami na bázi anorganických a organických sloučenin, uvolňujících aktivní chlor. Kombinace neionogenních tenzidů na bázi aduktů etylénoxidu s mastnými alkoholy, .alkylfenoly, polypropylenglykoly a podobně, organických nebo anorganických sekvestračních látek a případně kationaktivnlch tenzidů jako antimikrobiálních složek je podstatou některých dosud známých kapalných čisticích a dezinfekčních prostředků. Další známé kapalné čisticí a desinfekční prostředky jsou tvořeny kombinací tenzidů na bázi nonylfenolpolyetylénglykdléteru s 8 až 10 moly naváza2 něho· etylénoxidu, alfaolefinsulfonanu sodného· a desinfekční složky na bázi 2-benzyl-4-chlorfenolu. Nevýhodou popsaných práškových a kapalných prostředků .je skutečnost, že jsou obyčejně používány jednorázově a krátkodobě a žádaný účinek se dosahuje za přispění mechanické síly. Fyzikální vlastnosti těchto· dosud známých prostředků neumožňují však dlouhodobější působení při čištění a desinfekci hygienických a sanitačních zařízení. Jiné známé prostředky tvoří kompaktní pevnou hmotu, obyčejně ve tvaru tablet, nebo· jsou jinak tvarované, většinou komprimované, případně líté a vyznačují se omezenou rozpustností ve vodě. Tyto prostředky jsou složeny z neionogenních tenzidů na bázi aduktů etylénoxidu s alkylfenoly, mastnými alkoholy, mastnými kyselinami, .polypropylenglykoly, anionaktivními tenzidy na bázi alkylbenzensulfonanu a alkalického· mýdla, desinfekčními látkami na bázi kvartérních amoniových solí, orto-benzyl-para-chlorfenolu, dichloro-meta-xylenolu, hexachlorofenu a podobně, hydrofobními složkami, jako· jsou vosky, parafinické uhlovodíky, vyšší nasycené mastné kyseliny a alkoholy, estery vyšších nasycených mastných kyselin a podobně, barvivý a parfémovými kompozicemi. Ve .srovnání s. kapalnými a práškovými prostředky, lze tyto pro203631 středky využívat delší dobu; danou v podstatě rychlostí jejích rozpouštění ve vodě. Jejich nevýhodou· však je to, že množství látky s detergenčními účinky uvolněné do vody, nedosahuje koncentrace, které je třeba k účinnému odstraňování nečistoty. Další nevýhodou je, že používané hydrofobní látky, omezující rozpustnost prostředku ve vodě, přechází účinkem povrchově aktivních látek do roztoku, což- znamená, že už v samotné fázi rozpouštění prostředku ve vodě působí jako nečistota a snižují detergenční účinnost procesu čištění s tímto· prostředkem.The prior art liquid soil removal compositions based on surfactants and inorganic additives have in particular a powder or compact solid and, in limited cases, liquid form. Powder types of compositions are generally a combination of anionic types of sulfate or sulfonate surfactants, silicates, soda and phosphates. In order to achieve a disinfectant effect, these cleaning agents are combined with additives based on inorganic and organic compounds releasing active chlorine. The combination of nonionic surfactants based on adducts of ethylene oxide with fatty alcohols, alkylphenols, polypropylene glycols and the like, organic or inorganic sequestering agents and optionally cationic surfactants as antimicrobial components is the essence of some of the liquid cleaning and disinfecting agents known hitherto. Other known liquid cleaners and disinfectants are the combination of surfactants based on nonylphenolpolyethylene glycol ether with 8 to 10 moles of bound ethylene oxide, sodium alpha-olefin sulfonate and a disinfectant based on 2-benzyl-4-chlorophenol. A disadvantage of the powder and liquid compositions described is the fact that they are normally used in one-time and short-term applications and the desired effect is achieved by the contribution of mechanical force. However, the physical properties of these prior art compositions do not allow long-term action in the cleaning and disinfection of sanitary and sanitation equipment. Other known formulations form a compact solid, usually in the form of tablets, or are otherwise shaped, usually compressed or possibly lithe, and are characterized by limited solubility in water. These compositions are composed of nonionic surfactants based on ethylene oxide adducts with alkylphenols, fatty alcohols, fatty acids, polypropylene glycols, anionic surfactants based on alkylbenzenesulfonate and alkaline soap, disinfectants based on quaternary ammonium salts, ortho-benzol-dichloro-para-chloro-phenol methyl-xylenol, hexachlorophene and the like, hydrophobic components such as waxes, paraffinic hydrocarbons, higher saturated fatty acids and alcohols, esters of higher saturated fatty acids and the like, colorants and perfume compositions. Compared to liquid and powder formulations, these agents can be used for extended periods of time; given essentially by its dissolution rate in water. However, their disadvantage is that the amount of detergent substance released into the water does not reach the concentration required to effectively remove the soil. A further disadvantage is that the hydrophobic agents used to limit the solubility of the composition in water pass into the solution by the action of surfactants, which means that they already act as an impurity in the water solubility phase and reduce the detergency of the cleaning process with the composition.

Uvedené nedostatky odstraňuje sanitační kapalný adhezní prostředek na bázi anionaktivních a neionogenních tenzidů, jehož podstata spočívá v tom, že obsahuje 6 až 15 % hmot. .anionaktivních tenzidů na bázi alkalických solí esterů vícesytných minerálních kyselin s alkylpolyetylénglykolétery a·/ /nebo neionogenních tenzidů na bázi alkylfenolpolyetylénglykoléterů, s výhodou sodné soli kyseliny alkylpolyetylénglykolétersírové a alkylpolyetylénglykoíéterfosfor.ečné s 12 až 18 uhlíkovými atomy v alkylu a 3 až 6 moly navázaného etylénoxidu a/nebo nonylfenalpolyetylénglykoléter s 8 až 12 moly navázaného· etylénoxidu, ve vzájemném hmot. poměru 0,5 až 2:1, dále 0,5 až 3 % hmot. desinfekčních látek, 0,1 až 20 % hmot. zahušťovacích přísad, s 'výhodou polyetylénglykol o molekulové hmotnosti 3000 až 6000 a/nebo polyvinylalkohol a/nebo amorfní hydratovaný kysličník křemičitý, ve vzájemném hmot. poměru 90 až 100:1 a 62 až 92 % hmot. vody. Dále obsahuje 0,01 až 0,05 .% hmot. barviva a 0,1 až 1,0 % hmot. parfému.These drawbacks are overcome by a sanitizing liquid adhesive composition based on anionic and non-ionic surfactants, which comprises 6 to 15 wt. anionic surfactants based on the alkali metal salts of esters of polyhydric mineral acids with alkylpolyethylene glycol ethers and / or / or nonionic surfactants based on alkylphenolpolyethylene glycol ethers, preferably sodium salts of alkylpolyethylene glycol ether sulphate and alkylpolyethylene glycol ether of C12 to C18 to C12-18alkylene ether / or nonylphenalpolyethylene glycol ether with 8 to 12 moles of ethylene oxide bound, in a relative mass. a ratio of 0.5 to 2: 1, further 0.5 to 3 wt. % disinfectants, 0.1 to 20 wt. thickening agents, preferably polyethylene glycol having a molecular weight of 3,000 to 6,000 and / or polyvinyl alcohol and / or amorphous hydrated silica, relative to each other. a ratio of 90 to 100: 1 and 62 to 92 wt. water. It further contains 0.01 to 0.05 wt. % dye and 0.1 to 1.0 wt. perfume.

Účinek sanitačního kapalného adhezního prostředku podle vynálezu spočívá v tom, že se jím dosahuje podstatně vyššího čisticího a^: desinfekčního účinku při odstraňování nečistoty a eliminace nežádoucích, zejména patogenních mikroorganismů. Zahušťovací přísady umožňují zvýšení viskosity prostředku a adhezních vlastností, čímž se vzhledem k jeho časově: dostatečně dlouhému^-působení na čištěném povrchu zvyšuje jeho účinek ve srovnání s běžnými a dosud známými kapalnými čisticími prostředky. Maximálně se využijí nejen detergenční vlastnosti- účinných látek, ale zejména mikrúbicidní účinky desinfekční přísady, např. hexachlorfenu, kvartérních amoníových' solí, derivátů, chlorxylenolu a zejména 2-benzyl-4-chlorfenolu. Při časově velmi krátké expozici sanitačního kapalného adhezního prostředku podle vynálezu se projevuje význačný mikrobicidní účinek uvedených desinfekčních látek v kombinaci s ostatními složkami prostředku na nežádoucí patogenní mikroorganismy, jako jsou Escherichia coli, Pseudomonas aeruginosa, Staphylococcuís aureus, .Gandida albičans, Aspergillus niger a podobně. Viskozitní a adhezní vlastnosti prostředku se dále projeví v tom, že^- prostředek setrvává delší dobu na čištěném povrchu i při;, opakovaném splachování vodou, 3 až 5násobném. Toto omezené, avšak regulované uvolňování, naneseného prostředku z čištěného povrchu rozpouštěním do vody vede· k prodlužování jeho účinku a k dosažení příznivé pěnící charakteristiky.Effect of sanitizing liquid adhesive composition of the invention is that it achieves a considerably higher cleaning ^and: a disinfecting effect in removing impurities and the elimination of undesirable, notably pathogenic microorganisms. Thickening agents increase the viscosity of the composition allow the adhesion properties and, thus due to its time: sufficiently long ^- acting on the cleaned surface enhances its effect compared to conventional and prior art liquid detergents. Not only do the detergent properties of the active ingredients be utilized, but especially the microbicidal effects of a disinfectant, such as hexachlorophene, quaternary ammonium salts, derivatives, chlorxylenol and especially 2-benzyl-4-chlorophenol. The very short exposure of the sanitizing liquid adhesive composition of the present invention exhibits a remarkable microbicidal effect of the disinfectants in combination with the other ingredients of the composition on undesirable pathogenic microorganisms such as Escherichia coli, Pseudomonas aeruginosa, Staphylococcus aureus, Gandida albicans, Aspergillus niger. The viscosity and adhesion properties of the composition will further result in that ^- the composition stays longer on the surface being cleaned even when ;, Repeated flushing water 3 to 5 times. This limited but controlled release of the deposited composition from the surface to be cleaned by dissolution into water leads to a prolonged action and a favorable foaming characteristic.

Sanitační kapalný adhezní prostředek podle vynálezu je určen zejména pro- klozetové mísy a podobná hygienická zařízení a sanitační zařízení, včetně koupelnových van, umyvadel, obkladů a podlah.The sanitary liquid adhesive composition according to the invention is particularly intended for toilet bowl and similar sanitary facilities and sanitary facilities, including bathtubs, washbasins, tiles and floors.

Sanitační kapalný adhezní prostředek podle vynálezu je, blíže popsán na několika následujících příkladech:The sanitizing liquid adhesive composition of the invention is described in more detail in the following examples:

PřikladlHe did

18,46 % hmot. 30% hmot. roztoku alkylpolyetylénglykolétersíranu sodného s 12 až 16 uhlíkovými atomy v alkylu a 3 až 4-moly navázaného etylénoxidu se rozpustilo v 22,89 proč. hmot. vody a po zamíchání se přidalo 9,2'3 % hmot. 10% roztoku 2-be^,nzyl-4-chlorfenolu ve vodě, obsahující 40 % hmot. alfaolefinsulfonanu sodného. Po dokonalém rozmíchání' a rozpuštění jednotlivých složek na čirý roztok se do takto· připravené směsi postupně dávkovalo za míchání 48,92 % hmot. 15% hmot. roztoku polyvinylalkoholu i ve vodě. Do homogenní čiré viskózní směsi se přidalo 0,28 % hmot. parfému a 0,22 % hmot. barviva. Vytvořil se homogenní, čirý, zbarvený prostředek o vysokých adhezních vlastnostech. Viskozita, stanovená metodou podle Forda, CSN 673 013, při teplotě 20 °C a průměru trysky 4 mm činila 70 s. Připravený prostředek měl ve Srovnání s komerčně vyráběným desinfekčním, prostředkem, obsahujícím 2-benzyl-4-chlorfenal, o 30· %· vyšší mikrobicidní účinek na· patogenní mikroorganismy v expozicích do 1 min. Příklad. 218.46% wt. 30% wt. of a solution of C 12 -C 16 alkylpolyethylene glycol ether sulphate and 3 to 4 moles of bound ethylene oxide were dissolved in 22.89 why. wt. water and, after stirring, 9.2 wt. 10% solution of ^2-BE Benzyl-4-chlorophenol in water containing 40% by weight. sodium alpha-olefin sulfonate. After thorough mixing and dissolution of the components to form a clear solution, 48.92% by weight were gradually added to the mixture. 15 wt. solution of polyvinyl alcohol also in water. 0.28 wt.% Was added to the homogeneous clear viscous mixture. % perfume and 0.22 wt. dyes. A homogeneous, clear, colored composition having high adhesion properties was formed. The viscosity, determined by the Ford method, CSN 673 013, at 70 ° F and a nozzle diameter of 4 mm was 70 sec. The composition was 30% by comparison with a commercially available disinfectant composition containing 2-benzyl-4-chlorophenal. · Higher microbicidal effect on · pathogenic microorganisms at exposures up to 1 min. Example. 2

10· % hmot. 30% hmot. roztoku alkylpolyetylénglykolétersíranu sodného s 12 až 16 uhlíkovými atomy v alkylu a 3 až 4 moly navázaného etylénoxidu se rozpustilo, v 34-,9-7 proč. hmot. vody a za míchání se přidalo 5 % hmot. nonylfenolpolyetylénglykoléteru s 9 moly navázaného etylénoxidu a 1Ό % hmot. 10%. hmot: roztoku 2-benzyl-4-chlorfenolu ve vodě, obsahujícího· 40 %. hmot; alfaolefinsulfonanu sodného. Do takto připraveného· roztoku, se přidala směs: látek, připravená z 15 % hmot: polyetylénglykolu o molekulové hmotnosti 60QO a 4,5 % hmot. alkylpolyetylénglykoléterfosforečnanu sodného s alkylem obsahujícím· 12 až 18 vodíkových atomů a 4 moly navázaného· etylénoxidu. Směs se připravila., tak, že- se obě' složky roztavily na čirou taveninu pří teplotě 75 °C a po roztavení. se přidalo 20 % hmot. vody, zahřáté na stejnou; teplotu. Do takto· připraveného roztoku se přidalo; 0,0.310 · wt. 30% wt. of a solution of C 12 -C 16 alkylpolyethylene glycol ether sulphate and 3 to 4 moles of bound ethylene oxide was dissolved in 34-, 9-7 why. wt. water and 5% wt. % nonylphenolpolyethylene glycol ether with 9 moles of attached ethylene oxide and 1Ό wt. 10%. % of a solution of 2-benzyl-4-chlorophenol in water containing · 40%. wt; sodium alpha-olefin sulfonate. To the solution thus prepared was added a mixture of substances prepared from 15% by weight: polyethylene glycol having a molecular weight of 60% and 4.5% by weight. sodium alkylpolyethylene glycol ether phosphate with an alkyl of 12 to 18 hydrogen atoms and 4 moles of bound ethylene oxide. The mixture was prepared by melting both components to a clear melt at 75 ° C and after melting. 20 wt. water heated to the same; temperature. To the solution thus prepared was added; 0,0.3

8 hmot. barviva a 0,5 % Óiínot. parfému. Po zamíchání se získal čirý a homogenní barevný roztok, mající silné adhezní vlastnosti a viekozitu stanovenou jako v příkladu 1,. 50 s. Připravený prostředek měl obdobný účinek jako v příkladu 1 s tím, že v dané době expozice se dosáhlo odstranění i více odolných mikroorganismů.8 wt. dyes and 0.5% O. perfume. After mixing, a clear and homogeneous color solution having strong adhesive properties and a viscosity determined as in Example 1 was obtained. The prepared composition had an effect similar to that of Example 1 except that more resistant microorganisms were removed at any given time of exposure.

P ř í k 1 a d 3Example 1 a d 3

14,85 % hmot. 30% alkylpolyetylénglykolétersíranu sodného s 12 až 18 uhlíkovými atomy v alkylu a 3 až 4 moly navázaného etylénoxidu se rozpustilo v 29,5 % hmot. vody. Přidalo se 4,95 % hmot. nonylfenolpolyetylénglykoléteru s 10 moly navázaného etylénoxidu a po zamíchání se ve vytvořené směsi dispergovalo 0,5 % hmot. hexa- < chlororenu. Do takto připravené směsi látek se postupně za míchání přidalo 49,5 % hmot. 15% hmot. rožtoku polyvinylalkoholu ve vodě. Do homogenní viskózní směsi se dále přidalo· 0,5 % hmot. parfému a 0,2 % hmot. barviva. Získal sé čirý a homogenní barevný prostředek s vysokou adhezitou a viskozitou stanovenou jako v příkladu 1,14.85% wt. 30% of C12-18 alkyl alkyl polyethylene glycol ether sulphate and 3 to 4 moles of bound ethylene oxide were dissolved in 29.5 wt. water. 4.95 wt. % of nonylphenolpolyethylene glycol ether with 10 moles of bound ethylene oxide and after stirring, 0.5 wt. hexane chlororene. 49.5 wt. 15 wt. polyvinyl alcohol solution in water. To the homogeneous viscous mixture was further added 0.5 wt. % perfume and 0.2 wt. dyes. It obtained a clear and homogeneous color composition with high adhesion and viscosity determined as in Example 1,

s. Prostředek měl stejné mikřobicidní účinky, jako prostředky připravené podle příkladů 1 a 2.The composition had the same microbicidal effects as the compositions prepared according to Examples 1 and 2.

Příklad 4Example 4

10,0 % hmot. alkylpolyetylénglykolétersíranu sodného s 12 až 18 uhlíkovými atomy v alkylu a 3 až 4 moly navázaného, etyloxidu se rozpustilo v 21,27 % hmot. vody, přidalo· se 5 % hmot. nonylfenolpolyetylénglykoléteru s 9 moly navázaného etylénoxidu a 10 % hmot. 10°/o hmot. roztoku 2-benzyl-4-chlorfenolu ve vodě, obsahujícího 40 % hmot. alfaolefinsulfonanu sodného·. Do takto připraveného roztoku se přidal roztok, jehož teplota byla 60 až 65 °C, připravený z 18 % hmot. polyetylénglykůlu o molekulové hmotnosti 3000 a 35 ·% hmot. vody při teplotě 75 °C. Dále se přidalo 0,2 % hmot. hydratovaného amorfního· kysličníku křemičitého, 0,5 % hmot. parfému a 0,03 % hmot. barviva, a takto připravená směs se dokonale promíchala. Získal se prostředek stejných vlastností jako v příkladu 2 a viskozitě, stanovené jako v příkladu 1, 40 s.10.0 wt. sodium alkylpolyethylene glycol ether sulfate of 12 to 18 carbon atoms in alkyl and 3 to 4 moles of bound ethyloxide was dissolved in 21.27 wt. % water, 5 wt. % nonylphenolpolyethylene glycol ether with 9 moles of attached ethylene oxide and 10 wt. 10% w / w % solution of 2-benzyl-4-chlorophenol in water containing 40 wt. Sodium alpha - olefin sulfonate. To this solution was added a solution at a temperature of 60-65 ° C, prepared from 18 wt. % of polyethylene glycol having a molecular weight of 3000 and 35% by weight; water at 75 ° C. 0.2 wt. % hydrated amorphous silica, 0.5 wt. % perfume and 0.03 wt. dye, and the mixture thus prepared was thoroughly mixed. A composition having the same properties as in Example 2 and the viscosity determined as in Example 1, 40 s was obtained.

PŘEDMĚTSUBJECT

Claims

SUBJECT

What is claimed is: 1. An anionic and nonionic surfactant-based anionic liquid adhesive composition comprising 6 to 15 wt. anionic surfactants based on the alkali metal salts of polyesters of polyhydric mineral acids with alkylpolyethylene glycol ethers and / or nonionic surfactants based on alkylphenol polyethylene glycol ethers, preferably sodium salts of an alkylpolyethylene glycol ether ether or an alkylpolyethylene glycol ether of n-polyol; 8 to 12 moles of the invented ethylene oxide in mutual mass. a ratio of 0.5 to 2: 1, further 0.5 to 3 wt. disinfectants, 0.1 to 20 wt. thickening agents, preferably polyethylene glycol having a molecular weight of 3,000 to 6,000 and / or polyvinyl alcohol and / or amorphous hydrated silica, relative to each other. a ratio of 90 to 100: 1 and 62 to 92 wt. water.

2. A sanitizing liquid adhesive composition as claimed in claim 1 comprising from 0.01% to 0.05% by weight of said composition. % dye and 0.1 to 1.0 wt. perfume.