CS207591A3

CS207591A3 - Solid substance suspensions resistant to sedimentation, process for preparing such suspensions and their application

Info

Publication number: CS207591A3
Application number: CS912075A
Authority: CS
Inventors: Georg Ing Schuster; Hans-Hartwig Ing Kastle
Original assignee: Walhalla Kalk Entwicklungs Und
Priority date: 1990-07-06
Filing date: 1991-07-04
Publication date: 1992-04-15
Also published as: EP0467165B1; DE4021525C2; EP0467165A1; DE4021525A1; ATE129690T1

Abstract

The invention relates to aqueous solids suspensions which are stable to sedimentation and in particular milk of lime based on aqueous suspensions of calcium hydroxide Ca(OH)2, which contain, as sedimentation stabiliser, waterglass, preferably in an amount of 0.5 to 8% by weight, calculated as solid waterglass containing 17 to 20% by weight of water and based on the mass of the solid in the suspension, and processes for their preparation and their use and dry solids mixtures containing added stabilisers. In the case of the preparation of milk of lime, the waterglass may be added both before or during slaking of calcined lime and before or after calcium hydroxide is mixed into the preparation water. Suspensions stabilised according to the invention, such as milk of lime, are stable to sedimentation over a storage time of at least 5 weeks, even at low temperatures, not more than 5% of serum being formed. Even after a longer storage time without mechanical mixing, a corresponding milk of lime can be stirred up simply and rapidly for use. The invention accordingly has exceptional advantages in terms of process engineering and economics, since the investment costs for stirring or mixing apparatuses and mechanical mixing for stirring up are not required during the entire storage time. The invention leads in particular to high energy savings.

Description

í o < c. / \ *j.j o <c. / j.

Suspense pevné látky odolné vůči sedimentaci, způsobjejich výroby a jejich použitíSedimentation-resistant solids suspensions, their production and use

Oblast technikyTechnical field

Vynález se týká vodných suspensí pevné látky, oddol-ných vůči. sedimentaci, obzvláště hašeného vápna a vápen-ného mléka, způsobu jejich výroby a jejich použití, ja-kož i k tomu vhodných směsí pevných látek se stabilisační-mi.prostředky. . Dosavadní, stav'techniky L\’ i , e Γ i »! 1 jí < ,-Í^ r «· ' ·ς ' V; průmyslové /praxi, še'používají rozličně typy'čás-tic pevných látek z organických a anorganických,popřipa- d. dě minerálních látek, -v jemně dispersní formě ve vodnýchZ- - suspensích?‘: ?;Jako ^příklady je možno uvést suspense bento-nitu, ktere .móhou itake obsahovat 'vapnC/Vá které ;.s'ě've •' značném _rózsahu pouzívaj í obzvláště\ve vrtacích téchni- ů, ^kach,.úá3.é',Wspense pigmentů, "jako -jsou'-například anor- .\. 1 gáriické, ^popřípadě._mineralni pigmentyj ako j e. titanová .<běloba,z‘zinková'běloba, . oxid křemičitý, čerň zoxidůže-ttleza," ·.manganová ‘Čerň, "'-'saze,' -miniumA berlínská modř,: „ : nebo chromdioxidová zelen, a přírodní nebo synteticky ,•vyrobené organické pigmenty, jako je sepia, indigo, pig-J menty z kovových komplexů a podobně.’Takoveto suspensepigmentů se používají například pro barvy a laky, papír,textilie, cement nebo beton, jako nátěrové prostředky, . jakož i jako tlakové barvy. .. . Na základě vesměs, velmi, malé velikosti částeček v . t oblasti mikrometrů nebo méně podléhají vodné suspense ta-·kovýchto látek bez zvláštních opatření "chemického nebo ’ .fyzikálního"druhu, například míchání, více nebo méně sil-ně výrazné sedimentaci, přičemž v mnoha případech odpo- - vídající sedimenty již nejsou vůbec, nebo již ne úplněresusoendovatelné. - 2 - ‘f Lj.y - - '£ 1 . ·ιί. j·*·' Λ. V-BACKGROUND OF THE INVENTION The present invention relates to aqueous solid-phase suspensions of the invention. sedimentation, especially slaked lime and lime milk, a process for their production and their use, as well as suitable solids mixtures with stabilizing agents. . Existing, state-of-the-art technologies! 1 her <; In practice, the various types of solids particles from organic and inorganic and / or mineral substances are used in a finely dispersed form in aqueous suspensions. bentite which can be used in a wide range of applications especially in drilling rigs, as well as Wspense pigments. are, for example, anoric, garium, or mineral pigment such as titanium, white, zinc, silicon dioxide, black oxide, tungsten, yellow, black. or blue chromium, or chromium dioxide green, and naturally or synthetically produced organic pigments, such as sepia, indigo, pigment complexes from metal complexes, and the like. paints and varnishes, paper, textiles, cement or concrete, as coating compositions, j On the basis of all, very small particle sizes in the micrometer range or less, aqueous suspensions of such substances are subject to no "chemical or physical" type, for example mixing, more or less, by special measures. less severe sedimentation, and in many cases the corresponding sediments are no longer at all or no longer completely resettable. - 2 - Lj f Lj.y - - '£ 1. · Ιί. j · * · 'Λ. IN-

Obzvláště důležitým příkladem auspense pevné látky,ohrožené sedimentací, je vápenné mléko, které se vyrábív průmyslovém měřítku z páleného vápna /oxid vápenatý/nebo dolomitového vápna hašením s vodou, popřípadě sus-pendováním hašeného vápna, které je také označováno jakovápenný hydrát, bílý vápenný hydrát, popřípadě jako hy-drát oxidu vápenatého, nebo hydrátu dolomitového vápnave vodě. Vápenné mléko tedy· představuje vodnou suspensi,která v podstatě sestává z hydroxidu vápenatého/ Ca/OH/^ / · Jako běžné vedlejší součásti je možnouvést hydroxid horečnatý /Mg/0H/2/ , oxid křemičitý/ SiO2 f , oxid železitý / Pe^O^ / a oxid .'hlinitý/Al^O^ / , které se obvykle vyskytují v množství pod 1 %hmotnostní, vz_tažéno na, sušinu hašeného vápna. Vápennémléko se používá obzvláště pro neutralizační-a srážecí . -.reakce. 7 ; ‘ . ^Hašené'.-vápno, popřípadě vápenné mlékoj.;jsou; těchnic--;^ky/důle žité ^produkty,/ které se využívají y .rozličných ap- ,.sílikačních oblastech ve velikých množstvích',."hápříkiaď ja- \ .::ko/;hnojíva,/pojivá prd nátěrové pigmenty, pro barvení ky- ,'poyým-i barvivý, pro zpracování odpadních vod, pro úpravupitné.vody, pro čištění spalin, jakož i pro výrobu malty. K tomu se vápenné mléko vyrábí na místě ze suchých .vápenných produktů hašením' a/nebů - suspendováním, nebo . " -* ' -i .se používá.jako spotřební produkt ve formě 20 ;až 40%suspense. ./Vápenné suspense se většinou používají po zře-dění jako 3% až 20% suspense. ~A particularly important example of auspension of a solid which is at risk of sedimentation is lime milk, which is produced on an industrial scale from burnt lime / calcium oxide / or dolomite lime by quenching with water, optionally by slaking lime, also referred to as lime hydrate, white lime hydrate. , optionally as a calcium oxide hydride or dolomite calcium hydrate with water. Thus, lime milk is an aqueous suspension which essentially consists of calcium hydroxide (Ca (OH) 2). Magnesium hydroxide (Mg (OH) 2), silica (SiO 2), iron oxide (Pe 2), can be used as a conventional by-product. And the aluminum oxide (Al2 O3), which is usually present in amounts below 1% by weight, based on the slaked lime. Lime is particularly used for neutralizing and precipitating. -.reaction. 7; . Slaked lime or lime milk; important products that are utilized in different ap- plication regions in large quantities, such as fertilizers, bonding pigments, for dyeing dyeing, dyeing, wastewater treatment, water treatment, flue gas cleaning and mortar production. Lime milk is produced locally from dry lime products by extinguishing and / or by suspending or using as a consumable product in the form of a 20 to 40% suspension. Lime suspensions are generally used as a 3% to 20% suspension after dilution. ~

Vzhledem k tomu, že pálené vápno je před hašenímjemně rozemleto, vyskytuje se také hašené vápno ve forměvelmi jemného prášku, jehož hlavní podíl velikosti částe-ček je obvykle v rozmezí asi 1 .až·. asi 35 /ňm. Odpo- 'vídající- suspense vápenného mléka.podléhají proto velmisilné sedimentaci, přičemž vytvořené sedimenty nejsou povíce dnech již úplně resuspendovatelné ani silným mísícím,popřípadě míchacím zpracováním. 2 tohoto důvodu jsou ná-drže na vápenné mléko ve vápenkách, ve kterých se vyrábí - 3 - vápenné suspense, zásadně vybaveny míchadly, nebo jinými-mísí.c.ími_saří zeními, .která jsou v dlouhodobém provozu. U nádrží, ve kterých je skladováno vápenné mléko schop-né spotřeby, o koncentraci 20 až 40 % hmotnostních,pracují míchadla, popřípadě mísící zařízení, přerušovaně.Doba recirkulace však činí ještě alespoň 4 až 6 hodinza den.· Když se neuvažují investiční náklady na míchad-la, jsou s tímto procesem spojené náklady na energiiznačné. Například je pro míchanou nádrž o objemů g mpotřebné míchadlo o příkonu 0,3 až 1,2 kN v trvalémprovozu. Pro nádrž na vápenné mléko o objemů 20 m jepotřebné míchadlo o příkonu asi 7 aŽ 10 kw , což odpo- vídá roční spotřebě energie více než- 60 MWh . To. 2načí,že také při přerušovaném provozu se ročně spotřebuje vír - ce než 10 MWh energie; ... j.?o tlačení sedimentace mícháním tedy představujeyhpo’dstatný cenový faktor, který ve'veliké míře zvyšuje ·. cenu vápenného mléka, především proporcionelne: době skla^ •'ýdování." ' '·· ·-' ' < " ' ·’ '·' 3 · /' '< · ?V.· “λ’Χ// A '·’ V ' ’ . ' ' · , ·,·*.- ' y 1.//1 1 , ' 1 ' · / ' ' .·ř-řý' ,;Jé’ známé, že mokrým mletím vápenného hydrátu se raů- ' zé'vyrobit vápenná suspense, stabilní vůči sedimentaci..Since quicklime is finely ground before slaking, slaked lime is also present in the form of a very fine powder, the main proportion of the size of the particles usually being about 1 to about. about 35 µm. The corresponding slurry of lime milk is therefore subject to high sedimentation, whereby the sediments formed are no longer completely resuspended by the thick mixing or agitating processes. For this reason, lime milk containers in lime kilns in which 3-lime suspensions are produced are essentially equipped with agitators or other mixers which are in long-term operation. For tanks in which consumption-able lime milk is stored at a concentration of 20 to 40% by weight, the agitators or mixing equipment operate intermittently. However, the recirculation period is still at least 4 to 6 hours per day. agitators, the cost of energy is associated with this process. For example, an agitator of 0.3 to 1.2 kN in continuous operation is required for a stirred tank of g volume. For a 20 m lime tank, an agitator with a power consumption of about 7 to 10 kw is needed, which corresponds to an annual energy consumption of more than 60 MWh. It. 2 indicates that more than 10 MWh of energy is also consumed annually in intermittent operation; So, to push the sedimentation by mixing, it represents a significant price factor that greatly increases. the price of lime milk, especially proportionally: the time of glass ^ • '...' '· ·' '<"' · '' · '3 · /' '<·? V. ·“ λ'Χ // A' 'V' '. It is known that the wet milling of lime hydrate is carried out by the following processes: 1.//1 1, 1 ''. lime suspension, sedimentation stable.

Tento pracovní postup však má obzvláště dvě' význačné ne-’ výhody' : , ‘ 1. Mokré mletí vyžaduje značný příkon energie'; 2. Mokrým.mletím je možno docílit pouze koncentrace' maximálně do 20 % hmotnostních .However, this workflow has in particular two 'significant' advantages: ‘1. Wet milling requires considerable energy input '; 2. Wet concentration can only achieve a concentration of up to 20% by weight.

Vzhledem k tomu, Že se známé vápenné suspense vyrá-bějí a transportují o koncentraci až 40 % hmotnostních,-značí to pro takovéto vápenné mléko oddolné vůči sedimen-taci zdvojnásobení přepravních nákladů a nákladů na nádr-že. K tomu přichází, že mokrým mletím na základě podstat-ného zozmšlnění částic sé mění velikost zrn a jejichrozdělení. póry Výsledné velikosti částic jsouvzájemnými interakcemi částic, že za pod- prakticky tak malé, nenastává žádná sedimentace.Since the known lime suspensions are produced and transported at a concentration of up to 40% by weight, this doubles the cost of transportation and the cost of storage for such sedimentated lime milk. In addition to this, wet grinding, due to a substantial refinement of the particles, changes the grain size and division. pores The resulting particle sizes are mutual interactions of particles that, under virtually no small, no sedimentation occurs.

Další možnost výroby’vápenného mléka oddolného vůči sedimentaci spočívá v aplikaci vysokých míchacích energií, například pomocí disolveru. Takto vyrobené vápenné mlé-ko je zatíženo stejnými, výše uvedenými nevýhodami, nebottaké při tomto způsobu dochází ke značnému rozmělněníčástic, takže také zde nelze mluvit o stabilisaci vůčisedimentaci v pravém slova smyslu.Another possibility of producing sedimentation-resistant lime milk is to apply high mixing energies, for example by means of a dissolver. The lime milk produced in this way is burdened with the same disadvantages mentioned above, and in this method considerable particle comminution occurs, so that it is not possible to talk about stabilization of the sedimentation in the true sense of the word.

Podobné problémy se vyskytují také u jiných vodnýchsuspensí pevných látek, vyráběných a používaných v prů-myslovém měřítku. .Similar problems also occur with other aqueous solids suspensions produced and used on an industrial scale. .

Podstata vynálezuSUMMARY OF THE INVENTION

. .. Velkou potřebou tedy je odstranění výše uváděných ne-',· výhod a nalezení prostředku/ pomocí něhož by se. sedimenta-ce ce vodných suspensí pevných látek a obzvláště vápenného• ý.mléka zamezila,, popřípadě podstatně potlačila. "; :ý.j, C Předložený vynález tedy řeší úkol _dát k disposici ;alespoň dostatečně ;vůci sedimentaci stabilní vodné sus-.pěnse pevných látek, obzvláště vápenného mléka a vypra-covat .způsob jejich výroby a použití. Dále je úkolem vy-nálezu příprava suchých směsí pevných látek, obsahujícíchstabilisacní prostředek, obzvláště směsí na basi vápen-ných produktů, jako je například hydroxid vápenatý. Výše uvedený úkol byl vyřešen zhotovením vodných ·.suspensí organických nebo anorganických, popřípadě mine-rálních, pevných látek, stabilních vůči sedimentaci, kte-ré jako stabilisacní prostředek vůči sedimentaci obsahujívodní sklo. 4. Thus, a great need is to eliminate the aforementioned advantages and find the means by which they would be. the sedimentation of aqueous solids suspensions, and in particular of lime, prevented or substantially suppressed. Accordingly, the present invention solves the task of providing at least sufficient sedimentation of a stable aqueous suspension of solids, in particular lime milk, and a process for their preparation and use. The present invention relates to the preparation of dry solids compositions comprising a stabilizing agent, in particular mixtures based on lime products such as calcium hydroxide, and the above object has been solved by providing aqueous sedimentation-stable organic or inorganic or mineral solids. containing a glass as stabilizer for sedimentation

Podstata předloženého vynálezu spočívá .na úplně pře- .kvapivém zjištění, že sedimentace vodných suspensí orga-nických a anorganických, popřípadě minerálních, pevných .látek a obzvláště vápenné- ho mléka, se může dalekosáhle potlačit již přídavkem ne- - 5 - patrného množství vodního skla, bez toho, že by bylo za- T^olřebí-míchání— nebo-mí-sení— odpov-í-daj-í-cí— stavu--techniky-.The present invention is based on the surprising finding that the sedimentation of aqueous suspensions of organic and inorganic, or mineral, solids and, in particular, lime milk can be largely suppressed by the addition of a noticeable amount of water. glass, without mixing or mixing of the corresponding state of the art.

Když se odhlédne ód takto dosažených úspor přístrojůna míchání nebo míšení pro takovéto suspense pevných lá-tek a od s tím spojených značných úspor energie, oteví-rá předložený vynález rovněž možnost vyrábět takovétosuspense v malých nádobách, konteinerech, sudech a podob-ně a tímto způsobem vyloučit pro malospótřebitele nutnostnepříjemné manipulace s mísícími zařízeními. ·- ;y ... r ·>·' "/t: ·· <·'” .. Náklady spojené s použitím vodního skla jsou vzhle-dem, k nízkým cenám tohoto materiálu velmi nízké.- Kromětoho:jsou druhy vodního skla různých specifikací k dispo-sici ve ..velkých množstvích. ·;·. , λ 'z ' : l-\;/.K tomu je. třeba přičíst, že. na základě, nařízení o .lpi tne/ 'vodě j e přípustný přídavek vodního skla až do kon-centrace. 50 ,mg Si0o/l ;' takže oďpovidajícím způsobem .stábilišováné produkty se mohou použitna základě svého.nepatřného-obsahu’silikátů 'například také -y sektoru potrá- vihářskétechnologie·.··, >·'·- L L:; ? ··.; - \. ·:<Γ·;'·,...·/.·^:Λ'·/; --.v:-/- <...'xv - . ./ιΎί' ;·výhodná-forma provedení .yynáléžú .spočívá, v tom, ze /.částice pevné látky v sušperisích stabilních yůči Sedimen-' tací sestávají z vápenných produktů, jako je vápencová 'moučka, jílových minerálů, bentonitů a/nebo z organic-kých a/nebo anorganických, popřípadě minerálních pig-mentů. ' ' - ’ - ///.1 "Λ . 1 . ' /· , í ‘u ‘ . -', -'·„%·'· 1' . .··, Podle obzvláště výhodné formy provedení vynálezusestávají-uvedené suspense z vápenného, mléka, popřípaděhydroxidu vápenatého, vápenného hydrátu nebo dolomitické-ho vápenného hydrátu. . , . Suspense oddolné vůči sedimentaci podle předloženého•vynálezu obsahují obzvláště výhodně vodní sklo v množst-ví, odpovídajícím přídavku ’ . /a/ 0,5 až Q % hmotnostních a výhodně 1 až 2 / hmot- nostní vodního skla, obsahujícího, 17 · až 20 % hmot-nostních vody, popřípadě - S - /b/ 1 až 19 % hmotnostních a výhodně -2 až 5 % hmotnostních kapalného vodního skla o hustotě 37až 40 0 Bé , vady vztaženo na sušinu suspendované, pevné látky v odpo-vídající suspensi.Disregarding the aforementioned savings of mixing or blending devices for such a solids suspension and the associated considerable energy savings, the present invention also opens up the possibility of producing such a suspension in small containers, containers, barrels and the like and in this manner to avoid the need for unpleasant handling of mixing equipment for small consumers. The costs associated with the use of water glass are very low in relation to the low prices of this material. different specifications available in large quantities. ·; ·., λ 'z': l - / /. addition of water glass until concentration 50 mg SiO / l; so, in an appropriate manner, the softening products can be used on the basis of their non-volatile contents, for example also in the food-processing industry, LL :; : ·; '·, ... · /. · ^: Λ' · /; -. V: - / - <... 'xv -. ./ΙΎί'; in that the solids particles in the stable sedimentation dryers consist of lime products such as limestone flour, clay minerals, bentonites and / or organic and / or inorganic or mineral pigments . '' - '- ///.1 "Λ. 1. '/ ·, Í ‘u‘. - ', -' · '% ·' · 1 '. According to a particularly preferred embodiment of the invention, said suspensions are made of lime, milk, calcium hydroxide, lime hydrate or dolomitic lime hydrate. . ,. The sedimentation suspensions of the present invention contain particularly preferably water glass in an amount corresponding to the addition. % (a) 0.5 to Q% by weight and preferably 1 to 2% by weight of water glass containing 17 to 20% by weight water, optionally S - / b / 1 to 19% by weight and preferably -2 up to 5% by weight of liquid waterglass having a density of 37 to 40%;

Pod pojmem vodní .sklo se rozumí ve vodě rozpustnékřemičitany sodné a draselné,, získané z odpovídajících ta-venin, popřípadě jejich vodné roztoky; . označují se rov-něž jako sodné, popřípadě draselné vodní sklo. , Vodní sklajsou na trhu běžné v pevně formě, vě.tšinou jako prášky,jakož i ve formě viskosních vodných roztoků, které se mo-hou dalším přídavkem vody dále ředit. Tyto na trhu běž-ené typy kapalného vodního, skla obsahují typicky asi ^17 '.až '20 % hmotnostních vody. ' '· Λ/'..—·Λ Vápenné mléko podle vynálezu'má výhodně obsah hydro- ;ν.·; xidu vápenatého / Ca/0H/o / v oblasti .'.35' ,až '45 % ’>. hmotnostních á Výhodně "'.38 až A.40 % hmotnostních, vzta- -7’" ženo "na celkovou" hmotnost .vápenného mléka bez přídavku. :./- '.· ·.< •vodního skla. v S- .i ; Směsi pevných látek podle předloženého vynálezu nabasi organických-nebo anorganických,-popřípadě minerál- -nich částic pevných látek, obzvláště z hydroxidu vápéna-·tého, popřípadě vápenného hydrátu nebo dolomitického vá-penného hydrátu, jsou vyznačené tím, že obsahují pevnévodní sklo, výhodně vodní sklo s obsahem vody asi 17 až20 % hmotnostních, v množství 0,5 až 8 % hmotnostnícha výhodně 1 až 2 % hmotnostní, vždy vztaženo na'sušinučástic pevné látky bez přísad. ,As used herein, the term "water" refers to the water-soluble sodium and potassium silicates obtained from the corresponding therapeutics or their aqueous solutions; . they are also referred to as sodium or potassium water glass. Waterglasses are commercially available in solid form, mostly as powders, as well as in the form of viscous aqueous solutions, which can be further diluted with additional water. Typically, these types of liquid water glass typically contain from about 17% to about 20% water by weight. The lime milk according to the invention preferably has a hydrocarbon content; calcium oxide / Ca / 0H / o / in the region. '', 35 ', to '45%'>. % and preferably 40 to 40% by weight, relative to the total weight of the non-added milk. : ./ water glass. in S- .i; The solids mixtures according to the invention comprise organic or inorganic, optionally mineral solid particles, in particular calcium hydroxide or hydrated lime or dolomitic calcium hydrate, characterized in that they contain solid glass, preferably water glass having a water content of about 17 to 20% by weight, in an amount of 0.5 to 8% by weight and preferably 1 to 2% by weight, in each case based on the solid particles without additives. ,

Pro zvláštní účely použití mohou- suspense podle před-loženého vynálezu obsahovat také další přísady, jako jenapříklad pálený jíl, aktivní uhlí, bentonity á podobně.,například bentonity s nepatrným podílem mohtmorillonitu. V souvislosti se stabilisací sedimentace u suspensi Γ přídavkem vodního skla bylo v rámci předloženého vynále-zu dále zjištěno, že tixotropní bentonity /jako je na- - 7 - η i. , 1. ... . fJA' příklad Bentone LT firmy Kronos Titan/, jakož i ooly-akryláty /jako je například .Rohagit SL 140 firmy RíJhm--Chemie/ při dávkovaném množství 1 až 4 % hmotnostní,vztaženo na hotovou suspensi, například asi 40% vápennémléko, mohou potlačovat sedimentaci suspensi.For particular applications, the suspensions of the present invention may also contain other additives, such as, for example, burnt clay, activated carbon, bentonites and the like, for example bentonites with a low proportion of mohmorillonite. In connection with the stabilization of the sedimentation of the slurry by the addition of water glass, it has further been found in the present invention that the thixotropic bentonites (such as the skla-η i., ...). fJA ' an example of Bentone LT from Kronos Titan (as well as polyacrylates) such as, for example, Rohagit SL 140 from Rihm-Chemie at a feed rate of 1 to 4% by weight based on the finished slurry, e.g. to suppress sedimentation of the suspension.

Ve mnoha případech tedy může být vhodné přidávat ksuspensím pevných látek, stabilním vůči sedimentaci, po-případě ke směsím pevných látek, obsahujícím vodní sklo,tixotropní.bentonity a/nebo polyakryláty, přičemž potomje většinou zapotřebí menší přidávané množství vodníhoskla než v případě, kdy se tyto přísady nepoužijí. Tixo-tropní bentonity a/nebo polyakryláty se- výhodně použí-vají v množství 1 až 15 % hmotnostních} vztaženo na -hmotnost, pevné, látky suspense bez přísady. - · Předmětem předloženého vynálezu je dále způsob výro-··._· .by suspensi oddolných vůči sedimentaci, jehož podstata..., spočívá v tom, že se . -1'·:přimísí pevné vodní sklo nebo .voditý. roztok vodního.' h/v skla do již dříve připravené suspense, organických he- , . ... <’!.·< bo anorganických, popřípadě minerálních částic pevné " ' ; 'látky, ·'.·.'·. ·. '’- . nebo se ·.'·.'* T&! - přimísí pevné vodní sklo nebo vodný roztok vodníhoskla do napájecí vody pro přípravu suspense, načežse do ní přimísí částice pevné látky, - nebo se /0/ přimísí do suchého prášku, částic pevné látky, urče-ného pro suspendování, pevné vodní sklo, načež se ta-to směs suspenduje vé vodě. Výroba vápenného mléka, stabilního vůči sedimentaci,může podle vynálezu rovněž'různými způsoby probíhat tak, Í I . ' že se ' /A/ přimísí pevné vodní sklo nebo vodný roztok vodníhoskla do již předem připraveného vápenného mléka,nebo se - a - /3/ přimísí pevné vodní sklo nebo vodný roztok vodníhoskla do napájecí vody pro přípravu vápenného mléka'a potom se přimísí hašené vápno, nebo se /0/ smísí suché hašené vápno, popřípadě' dolomitové váp-no, s pevným vodním sklem a tato směs se suspenduje ve vodě,nebo se /1)/ přimísí pevné vodní sklo nebo vodný roztok vodníhoskla do napájecí vody pro hašení páleného vápna/CaO/ , popřípadě dolomitového vápna a vápno se tou-to vodou vyhasí, nebo se ' . / ' /E/. smísí pevné vodní sklo s páleným vápnem '/CaO/ , po-,' ~ případě dolomitovým vápnem, a toto vápno še vyhaší , vodou na požadovanou suspensi. i. ' " Množství použitých látek se při tom nastaví tak, abyse dosáhla požadovaná konečná koncentrace.vodního skla, popřípadě hydroxidu vápenatého. Pro. odborníky je samo-zřejmé, že při hašení páleného vápna se vzhledem k' silné-mu vyvíjení tepla při tomto procesu /1156 kJ/kg ČaO/pást přidávané hasící vody odpaří, a proto je při technic-ké výrobě hydroxidu vápenatého třeba použít odpovídající-ho přebytku vody.Thus, in many cases, it may be desirable to add solids, stable to sedimentation, to mixtures of solids containing water glass, thixotropic bentonites and / or polyacrylates, whereby a smaller amount of waterglass added is usually required than when they do not use these additives. Thixotropic bentonites and / or polyacrylates are preferably used in an amount of 1 to 15% by weight, based on the weight of the solid, suspension-free substance. It is a further object of the present invention to provide a sedimentation-resistant suspension, the essence of which is to be. -1 '·: mix solid water glass or water. aqueous solution. h / v glass to previously prepared suspensions, organic heels. Inorganic and / or mineral particles are solid or admixed. solid waterglass or aqueous waterglass solution to feed water to prepare the slurry, admixing solid particles therein, or admixing it to dry powder, solids particles to be suspended, solid waterglass, According to the invention, the production of lime milk, which is stable to sedimentation, can also be carried out in various ways by admixing solid water glass or an aqueous solution of waterglass to the previously prepared lime milk. or - to mix solid water glass or an aqueous solution of waterglass into the lime milk feed water, and then slaked lime is admixed or dry slaked lime or dolomite lime is mixed with a solid vodním sk The mixture is suspended in water, or solid water glass or admixture of waterglass is admixed to feed water to quench burnt lime (CaO) or dolomite lime, and lime is quenched with water. / '/ E /. the solid water glass is mixed with quicklime (CaO), if desired with dolomite lime, and the lime is leached with water to the desired suspension. In this context, the amount of substances used is adjusted to achieve the desired final concentration of water or calcium hydroxide. the process / 1156 kJ / kg CO 2 / paste of the extinguishing water added evaporates, and therefore a corresponding excess of water is required in the calcium hydroxide production process.

Pracovní postupy B a D jsou z praktického hledis-ka obzvláště výhodné, nebot se vodní sklo v napájecí vodě,která se používá pro rozmíchání hydroxidu vápenatéhopo-případě k vynášení oxidu vápenatého, obzvláště lehce arychle rozpouští. Při pracovním postupu -C vzniká nejprve směs suchépevné látky, například suchého vyhaseného vápna’s pevnýmvodním sklem, což je stejně, jako suspense stabilní vůčisedimentaci vhodný obchodní produkt. Toto je rovněž za-,hrnuto do předmětu vynálezu. Takovéto směsi je třebapouze suspendovat v odpovídajícím množství vody, aby sezískala susoense, stabilní vůči sedimentaci, například -0)- asi 40% vápenné mléko. Pří nižších koncentracích vápen*·ného mléka se použijí vyšší podíly vodního 3kla. Vápenné mléko oddolné vůči sedimentaci podle předlo-ženého vynálezu se dá využít prakticky ve-všech oblastechWorking procedures B and D are particularly advantageous in practice, since the water glass in the feed water, which is used to mix the calcium hydroxide or the calcium oxide, is particularly easy to dissolve. In the -C process, a dry substance mixture, for example, dry extinction lime, is first formed by a solid waterglass, which is, as well as a suspension stable, suitable commercial product. This is also within the scope of the invention. Such mixtures may need to be suspended in an appropriate amount of water in order to obtain a susoense, stable to sedimentation, for example -0) - about 40% lime milk. At lower concentrations of lime, higher proportions of water are used. The sedimentation-resistant lime milk of the present invention can be used practically in all areas

I použití, p ve kterých se používá dosavadní,vůči sedimen-taci nestabilní, vápenné_mléko, obzvláště jako hnojivonebo pojivo pro nátěrové pigmenty, pro kypová barviva,pro zpracování odpadních voď, obzvláště pro oddělovánísíranů, například podle SP č. 25Q 626 , pro zpracovánípitné vody, při čištění spalin ze spalování fosilních pa-liv, jakož i pro výrobu malty.Even uses in which the prior art, unstable, lime milk, particularly as a fertilizer or binder for coating pigments, for vat dyes, for wastewater treatment, especially for the separation of sulphates, for example according to SP No. 25Q 626, for the treatment of potable water , for the cleaning of flue gases from the combustion of fossil fuels as well as for the production of mortar.

Dva typické, na trhu běžné druhy natronového vodního. skla 7/Portil? K ;":a; Portil^.A firmy Henkel KG, Dťlssel-Two typical, common types of soda water. glass 7 / Portil? K; "; a; Portil.

l'dorf, SRK/ ' mají následující chemické složení. : . ‘ 1 '4- * **·*·*,1 ' 'A ' '·.' '· '‘V"’,*’*' ' /''7/ · ΐ’Λ’ ,o : ‘· - - y ' . * . ., , _ *ν Portil N Portil A 'U · ·.?; -?·’ ’·'ίΛ '.’ί'.ν?'.1· '>· 1 . SiO2 /%' hmo tno stni/ ;7 - ca. 63' ‘ .7.,1-- '· . 17 .· · *1.1' H ca. 54 7 i lůr •'.•X’.···* •,·’/' ’Ί?* J'τ .' '>*-.i4*’Λν* ti?4'-*·b; .·. ν' _ ‘4'-. / ,/ Hjš l iíágó /% hmotnostní/ ll-v:ca,íl9 liliilil ,·1. V '1.1 lcal'27 ll i 7 ’ 1 * M , Λ · »'* |l ý,' ' \ — J híííO /% hmotnostní/ '->'1 ’ ,7':· '.....<; · · ' "ca.. 18 ·' 7 Vli ca. 19 i 'hmotnostní poměr ' '·. 1' ' ’ '· : · 11 -7, . 7. · '' · • .. .. SiO2 i/ Na20 , 3,3 - 3,4 . . 2,0 -2,1 Γ 1 . " · \ ‘ •molovy poměr * * - .7- ‘ ·. SiO : Ka20 3,4 - 3,5 2,1 - 2,2 ' · ί ' Ha trhu.běžné draselné vodní sklo /PortilR : my Henkel KG,-Dttsseldorf, SRIí/ má dále následující che-mické složení ' ' -l'dorf, SRK / 'have the following chemical composition. :. '1' 4- * ** · * · *, 1 '' A '' ·. ' '·' 'V' ', *' * '' / '' 7 / · ΐ'Λ ', o:' · - - y '. *..,, _ * Ν Portil N Portil A' U · ·. ;? O. O O O O O O O O O O O O O O O O O O O O O O O O O O O O O O O O '17. · · * 1.1' H ca. 54 7 i lur • '. • X'. ··· * •, · '/' 'Ί? * J'τ.' '> * -. i4 *' Λν * ti? 4 '- * · b;. ·. ν' _ '4'-. /, / Hjš l iíágó /% weight / ll-in: ca, íl9 liliilil, · 1. V '1.1 lcal'27 ll i 7' 1 * M, Λ · »'* | l ý,' '- J híííO /% weight /' -> '1', 7 ': ·' ... .. <; · · '"ca .. 18 ·' 7 Vli ca. 19 i 'mass ratio' '. 1 '' '':: 11 -7,. SiO 2 i / Na 2 O, 3.3-3.4. . 2.0 -2.1 Γ 1. "• molar ratio * * - .7-" · SiO: Ka20 3,4 - 3,5 2,1 - 2,2 '· ß' Ha market. Common potassium water glass / PortilR: my Henkel KG , -Dttsseldorf, SRIi / has the following chemical composition '' -

SiO^ /% hmotnostní/ ca. 56SiO 2 / wt% / ca. 56

KgO /% hmotnostní/ . ca. 28 - - 'HgO /% hmotnostní/ ' ca. 17 7 ? . hmotnostní poměrKgO /% w / w. ca. 28 - "HgO /% w / w" ca. 17 7? . weight ratio

SiO2 : K20 ' ca. 2,0 molovy poměrSiO2 : K20 ca· 3 , 1 10 - Výše uvedené tržní produkty vodního skla jsou' pevné ,hydratované produkty, které jsou rozemleté na prášek.SiO2: K20 'ca. 2.0 molar ratio SiO2: K20 ca · 3, 10 10 The above water glass market products are solid, hydrated products that are ground to a powder.

Ha trhu běžné standardní natronová vodní skla /ka-palná/ /firma Van Saerle a Co.', Chemische .Fabrik, Gerns-heim/Rhein, SRH/ mají například následující hodnoty :For example, conventional standard soda water glasses (Van Saerle and Co., Chemische Fabrik, Gernheim / Rhein, SRH) have the following values:

Stuoňovitost 29 - 30.. 37 - -40 40 .-.42/°BŽ/ 48 - 50 58 - 60 . hustota 1,25-1,27 1,34-1 ,381,38-1, 411,49-1,531,67-1,71 /g/ml/ HagÓ . ./% hmot- nostní/ 5,6 8,2 , . 9,7 Ί 12,4 18,0 . 'SiO2 . 7 21,9 27,3 _ 30,0 32,4 ''· '' 37,0 //· /#.hmotnostní/ H20.. 72,5 64,5 . 60,9 .55,2 . 45,0 7% hmotnostní/ ·'.//·_ .- 7 ; 7-'h. 'u t- ' 7 ·· X *' · , * -hmot .- poměr - '/7/ ' -Si02 :.Ha20 3,9... ' 3,3 / 3,25 ; /2,6 . - 2,05 , ' - ' ' ' · .·( molovy poměr · 1 - · -.1 -> ' · ’SiO2 Ha20 4,0 .3,41 . 3,35 •2,68 2,1. / viskosita.. > - /cP/ - 70-150 200-500 1000-1700 >50000 kapal-skla 'sedobrýms vyšší V rámci předloženého vynálezu- se při použitíných druhů vodního skla především používají vodnístupňovitostí 37 až 40 °Bé . Mohou se vsak súspěchem použít také typy kapalného, vodního skla nebo nižší stupňovitostí, popřípadě koncentrací, přičemžpřidávaná množství vodního skla sé odpovídajícím způsobem přepočítají. 11Stuoňovitost 29 - 30 .. 37 - -40 40 .-. 42 / ° BŽ / 48 - 50 58 - 60. density 1.25-1.27 1.34-1, 381.38-1, 411.49-1.531.67-1.71 / g / ml / Hago. ./% weight / 5.6 8.2,. 9.7 Ί 12.4 18.0. SiO2. 7 21.9 27.3 _ 30.0 32.4 '' · '' 37.0 // // // weight / H2O .. 72.5 64.5. 60.9 .55.2. 45.0 7% w / w; 7-'h. the weight ratio of [lambda] - [lambda] -SiO2: [lambda] 20 = 3.9 ... 3.3 / 3.25; / 2.6. - 2,05, '-' '' · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · · mol. viscosity ..> - / cP / - 70-150 200-500 1000-1700> 50000 liquid-glass' sedobrmies higher In the context of the present invention, water grades of 37 to 40 ° B are mainly used in the types of waterglass used. also use types of liquid, waterglass or lower grades or concentrations, whereby the added amounts of waterglass are recalculated accordingly.

Pomocí předloženého vynálezu se dosahuje značné vý-hody, obzvláště při průmyslové výrobě a skladování sus- pensí, zvláště vápenného mléka ve velkých nádržích, totižže odpadají míchací zařízení. Tím je způsobena podstat-ná úspora na míchacích zařízeních, totiž na investičníchnákladech a nákladech na energii.The present invention achieves a considerable advantage, in particular in the industrial production and storage of suspensions, in particular lime milk in large tanks, since mixing devices are not required. This results in substantial savings on the mixers, namely the investment costs and energy costs.

Hlavní výhodu je však třeba spatřovat v tom, že sus-pense pevných látek, stabilisované podle předloženého vy-nálezu, vykazují dlouhou dobu skladovatelnosti bez mecha-nického míchání, přičemž v mnoha případech již míchadlovůbec není zapotřebí. Tak je například vápenné mléko,stabilní vůči sedimentaci, podle vynálezu, skladovatelnébez mechanického míchání po.dobu minimálně 5 týdnů. Re-suápendování sedimentu, vytvořeného eventuelně při ještě .'delší době skladování, se může například provést takérozvířením‘pomocí zavádění tlakového vzduchu. Tím umož-However, a major advantage is that the solids stabilized according to the present invention exhibit a long shelf life without mechanical agitation, and in many cases no need for agitation. Thus, for example, sedimentation-stable lime milk according to the invention can be stored without mechanical agitation for at least 5 weeks. The re-deposition of the sediment, eventually with a longer storage time, can also be effected, for example, by swirling it through the introduction of pressurized air. This allows

•b V1 ” * t Z .nuje.koncepce podle vynálezu značně vysoké úspory energie,nebol náklady na míšení, popřípadě míchání v.případě ρο- ζ “dle. vynálezu jsou zanedbatelné proti nákladům podle.sta-,p.yu_; techniky. ' ;Další výhodu je třeba vidět v tom, že vápenné-mléko; podle vynálezu je možno použít také při přípravě a zpra-' cování pitné vody, nebot nepatrná množství přidávaného vodního skla jsou například daleko pod. přípustnými hodno-tami, německých nařízení o pitné vodě. Příklady provedení vynálezu Předložený vynález je v následujícím blíže objasněnpomocí příkladů provedení, které, se týkají výroby stabi-lisóvaného vápenného mléka. zIn accordance with the invention, the energy savings are considerably high, the cost of mixing and / or mixing in the case of ρο-ζ according to the invention. the invention is negligible against the costs of the present invention; techniques. Another advantage to be seen is that lime-milk; According to the invention, it is also possible to use it in the preparation and treatment of drinking water, since, for example, small amounts of water glass added are far below. admissible values, the German Drinking Water Regulations. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be explained in more detail below with reference to embodiments which relate to the production of stabilized lime milk. from

Procentické údaje se týkají hmotnostních procent,pokud není uvedeno jinak. Přikladl Výroba 40% vápenného mléka, oddolného vůči sedimentaciPercentages refer to weight percent unless otherwise indicated. Example 1 Production of 40% lime milk, sedimentation resistant

Pro pokusy se vždy vyrábí 40% vápenné mlsko v ná-sadním množství 5 kg * Pracuje se při teplotě místnosti.Postup A /podle patentového nároku 9, popřípadě >12/ V 5 kg 40% vápenného mléka, které bylo předloženodo nádrže opatřené míchadlem, se rozmíchá 100 g kapal- . ného běžného vodního skla /37 až 40 °Bé/ .For experiments, 40% lime milk is always produced in an amount of 5 kg. * Work at room temperature. Process A / according to claim 9 or > 12/5 kg of 40% lime milk which has been introduced into a tank equipped with a stirrer. 100 g of liquid are stirred. common water glass (37 to 40 ° Bé).

Postup 3 /podle patentového nároku 9 , popřípadě 12/Method 3 / according to claim 9 or 12 /

Napájecí voda se předloží v potřebném množství donádrže opatřené míchadlem a za míchání se smísí se 100 gkapalného, na trhu běžného sodného vodního skla /37 až40 °Bé/. ;/ ··</λ V.obo'u případech se předložila, odpovídající končen-,trace vodního skla . 20 g/kg vápenného mléka, popřípadě .. koncentrace vodního skla . 2 % , vztaženo na 40% 3usypensi vápenného mléka, což odpovídá koncentraci vodního 1 '· Λ,.·.'.‘.skla5 % t vztaženo na sušinu vápenného mléka, počítáno' ‘"z’ 1 ' /jako 'vodní sklo ovsahující vodu.1 . / ·. '.·.·;· ·. · · i?;λ'·;···'. ' „ ··- ' ' .·''' · . \ fí;'??ři "nbou řadách pokusů se zjišťuje a vyhodnocuje pó ' stání bez míchání po dobu 2 , 3 » 5 » 20 , popřípadě . 3θ ’ .. dnůsh rozplavovatelnošt, jakož i tvorba sera. ‘ ' V/·’·'"' . .Mez.ioběma použitými pracovními postupy není žádnýzjistitelný rozdíl ve výsledcích ; \ Tvoří še podíl sera /čirý zbytek na. stabilisované- suspensi/ maximálně 2 až 5 % » který po 2 až 3 dnech- zůstává konstantní. , -Vápenné mléko je během klidové fáze poněkud kompakt-. vnější, nevykazuje však žádnou sedimentaci. . . Aby se chování při sedimentaci mohlo lépe pozorovat,přidá se do vápenného mléka práškovéuhlí se střední ve-likostí zrn 1 mm . Samotné největší částice nemají.žád-nou tendenci k usazování.The feed water is placed in the required amount with a stirrer and mixed with 100 g of liquid, commercially available sodium waterglass (37 to 40 ° B) under agitation. In the case of the cases, a corresponding water glass trace was submitted. 20 g / kg of lime milk, or water glass concentration. 2%, based on 40% of lime milk, which corresponds to a water concentration of 5% t based on lime milk content, calculated as 1 / as water glass containing water, water, water, water, water, water, water, water, water, water; By means of a series of experiments, the standing position without agitation is determined and evaluated for 2, 3, 5, 20, respectively. 3θ '.. dayssh floatable as well as sera formation. There is no detectable difference in the results between the working procedures used and the proportion of sera / clear residue on the stabilized suspension (maximum 2 to 5%) which after 2-3 days - remains constant., -The calcareous milk is somewhat compact outside during the resting phase, but does not show any sedimentation .. In order to better observe the sedimentation behavior, powdered lime milk with a mean grain size of 1 mm is added to the lime milk. the largest particles have no tendency to settle.

Také po , 30 dnech klidové fáze je moisno vápenné mle- l ko bez velkých energetických nároků rozmíchat. - 13 -Also, after 30 days of rest, lime-free milk can be mixed without major energy demands. - 13 -

Když se nechá tato směs při teplotě místnosti vysu-Šit, tak zůstává původní forma nasazené suspense. Roz- i· 5 ’Ž 7 ·Η •a <1^ \«u * drobená tělíska mají při visuelním pozorování homogennírozdělení vápenného hydrátu, aktivního uhlí a prostorůvzduchových pórů. Vápenné mléko podle vynálezu je možno bez mícháníje možno dlouhodobě skladovat bez tvorby sedimentu. Předodběrem vápenného mléka z nádrže je třeba pouze krátcepromíchat, aby se rozmíchaly nepatrné sedimenty.When this mixture is allowed to dry at room temperature, the suspension remains in its original form. In the visual observation, the tiny particles have a homogeneous distribution of lime hydrate, activated carbon and air pore space. The lime milk of the present invention can be stored without mixing for long periods without sediment formation. Pre-harvesting of lime milk from the tank should only be mixed briefly in order to stir up slight sediments.

Stejným způsobem provedené pokusy s dávkovaným množ-stvím vodního skla menším než 1,5 % vedou k menší, po-případě -pouze ke krátkodobé stabilisaci. Pokusy s přídav- . kem vodního skla větším.než ’3 % . vedou .ke kompaktní hmo-Itě, 'která již nějdě?čerpat. .. .v < ; v.:· t P ř.í k 1 a<d rpo -raultiliftpvého kontejneru o obsahu -5,55 ni se -r·* i-*. naplní £3,7 t’^340%’;3vápenného -mlékaz^Koňt einěř'.'je. opatřenponorným. "Čerpadlem s" oběhovým., výkonem;;’SO.m^/h ΐ sJSte. po-á.cátku ‘řecirkuiáce. se ,do vápenného mléka''přidá <74 'kg ka-..-.palného, na trhu běžného sodného vodního skla. /37 .až‘40 Bé/ ., načež .se suspense recirkuluje "po dobu.' 24 hodin.In the same way, experiments with water glass dosages of less than 1.5% result in less, if only, short-term stabilization. Addition experiments. more than 3%. they lead a compact hmo-ita that has already been drawn. .. .v <; v.:· t to 1 and <d rpo -raultilift the first container of -5.55 ni with -r · * i- *. fills £ 3.7 t '^ 340%'; nursing. "Pump with" Circulation, Power ;; "SO.m ^ / h ΐ sJSte. post-turn. In the lime milk, < 74 < RTI ID = 0.0 > kg < / RTI > After which the suspension is recirculated for a period of time. 24 hours.

Koncentrace vodního skla činí 2 %' , vztaženo nahmotnost 40% suspense, popřípadě 5 % , vztaženo na po- .díl sušiny suspense. „ ‘ -Vápenné mléko se potom..nechá stát bez míchání po do-bu- 6 týdnů. Tvorba séra činí maximálně 2. až 5 %-U použité nádrže je .výška čiré kapaliny asi 3 cm přivýšce' plnění 1 metr. Vápenné, mléko lze potom pomocí re-cirkulačního zařízení bez problémů.a rychle rozmíchat. , . Pokusy se prováděly při vnějších teplotách v rozme-zí 10 až asi 22 °C . ' Zvýšení teploty na asi ·40. °C/během řecirkuiáce nemělo, stejně jako lehké působenímrazu ./-3°C/ , žádný negativní vliv na stabilitu sus-pense.The water glass concentration is 2% by weight of the suspension 40%, or 5% by weight of the slurry solids. The lime milk is then left to stand without stirring for up to 6 weeks. Serum formation is a maximum of 2 to 5% -U used in the tank is a clear liquid height of about 3 cm filling 1 meter. Lime, milk can then be re-circulated without problems and quickly mixed. ,. The experiments were carried out at ambient temperatures of 10 to about 22 ° C. 'Increase temperature to about 40. ° C / no negative effect on sus-pense stability, as well as light effect.

Pepatrné zředění deštovou vodou. /přídavek 150 , as - 14 - 200 litrů, což odpovídá zředění asi o %/ rovněž neovli-;nu je stabilitu suspen3e. - 'Careful dilution with rain water. (addition 150, - 14 - 200 liters, which corresponds to a dilution of about%) and also does not affect the stability of the slurry. - '

Ve výše uvedených příkladech.získané suspense vápen-ného mléka nevykazují v žádném, případě ovlivnění, chemic-ké reaktivity, například při zpracování odpadní vody.'Sedimentační vlastnosti získaných vysrážených kalů bylylepší, než při použití normálního vápenného mléka. PřikladlIn the above examples, the obtained lime milk slurries do not exhibit any chemical reactivity in any case, for example in the treatment of waste water. The sedimentation properties of the precipitated sludge obtained are better than those of normal lime milk. Přikladl

Do pětilitrove nádoby se předloží voda, do které by-• la přimíchána '2 % kapalného vodního skla /37 až 40°3é/ .. Potom se zamíchá potřebné, množství jemného váp-.na /CáO/ .tak,. aby vzniklo. 40%' vápenné mléko.· Stratyvody odpařením se doplní.;.. ·'/ ··. - Výsledky odpovídají výsledkům uvedeným.v příkladě 1 .... .'? ř í k 1 á Γ ..'4 .. " .Water is introduced into a 5 liter vessel to which 2% of the liquid waterglass (37-40 ° C) is admixed. The necessary amount of fine calcium is then stirred in. to be created. 40% lime milk · Evaporation stratification is completed.; .. · '/ ··. - The results correspond to the results given in Example 1 ..... to 1 Γ .. '4 ..'.

Vyrobí· se homogenní 'směs vápenného “hydrátu :7977- g ’‘.hydroxidu vápenatého/ a. pevného-vodního.’skla /Portil :ϊΓ//23 g/ iý:zpcrvědra se předloží potřebné množství vody, iaby sé získalo /‘40% /vápenné mléko, načeš se di ní uvede-<há homogenní směs pomalu přidává.· Mícháním je možno vy-'robit stabilizovanou suspensi. ’ - Výsledky odpovídají výsledkům uvedeným v příkladě 1 a 3 40% vápenné mlsko, použité nebo vyrobené v. příkla-dech '1 a 2 , má následující chemické složení : voda ' 60 % . ' hydroxid vápenatý . : 38 % '·. hydroxid horečnatý '0,4 % oxid křemičitý , 0,4 % oxid železiťý 0,1 % . oxid hlinitý - 0,1 % . Vápenné mléko má dále následující-fyzikální vlast-nosti : 15 -A homogeneous mixture of lime "hydrate: 7977 g" of calcium hydroxide and a solid water glass is produced and the required amount of water is added, and it is obtained. 40% / lime milk, and then the homogeneous mixture is slowly added thereto. The results correspond to those shown in Examples 1 and 3 of 40% lime milk used or produced in Examples 1 and 2, having the following chemical composition: water 60%. ' calcium hydroxide . : 38% '. magnesium hydroxide 0.4% silica, 0.4% iron oxide 0.1%. alumina - 0.1%. Furthermore, lime milk has the following physical properties: 15 -

Neutralisační ekvivalenthustota 10 mol/kg.1,24 kg/1 hodnota pH 12,5 viskosita /Brookfieldův viskosimetr LVT, 25 °C/ ' 2000 mPa.s . Vápenné mléko má následující rozdělení zrnitosti i < 32 ?um <16 / /' /um < < 4 /umZ 2 /Uin 3 /um ca. .97 tr ca. 39 rrt Jo ca. 67 ca. 41 % ca. 20 %Neutralization equivalent density 10 mol / kg 1.24 kg / l pH 12.5 viscosity / Brookfield viscometer LVT, 25 ° C / 2000 mPa.s The lime milk has the following particle size distribution i <32 µm <16 µm / µm <4 / µm 2 / U 3 / µm ca. .97 tr ca. 39 rrt Jo ca. 67 ca. 41% ca. 20%

♦ ·- · A - Koncepce podle předloženého vynálezu vede, jak os- .tatně vyplývá rovněž z· výše uvedených, příkladů, k pod-’ . ; /statným, provozně . technickým a hospodářským výhodám ve//•srovnání s dosavadním stavem technologií. , .Vápenné mléko podle vynálezu je při"běžných teplo-tách skladování -stabilní vůči sedimentaci mez meóhanic- . kého promíchávání.po dobu nejméně 5 týdnů a může'být ta- j kepo delší době skladování- lehce a úplně rozmícháno. Ú malých nádob až asi 1 t je proto prakticky postrada-telné mechanické míchací zařízení. . Vedle provo.zne technických výhod vede vynález koneč-ně k podstatným úsporám energie a tím nákladů, především - ' na základě uspořené -energie na míchání. K tomu se připo-; -juje skutečnost, že vodní sklo je netoxický produkt, do- konce vhodný pro úpravu.pitné vody, který je k.disposicive velikých množstvích za přijatelnou cenu.The concept of the present invention leads, as is also apparent from the above examples, to the sub-section. ; / hefty, operational. technical and economic advantages compared to the prior art. The soaking milk according to the invention is at a "normal storage temperature -stable to sedimentation limit of methanolic agitation. For at least 5 weeks and can be easily and completely stirred for a longer period of storage. Therefore, a mechanical agitator is practically substitutable for up to about 1 tonne.In addition to other technical advantages, the invention ultimately leads to substantial energy savings and hence cost, in particular, based on saved energy for agitation. the fact that water glass is a non-toxic product, still suitable for the treatment of drinking water, which is capable of delivering large quantities at an affordable price.

Claims

A solid suspension that is resistant to sedimentation, from organic or inorganic or mineral particles, characterized in that water stabilizer is included as a stabilizing agent for sedimentation. ''

A suspension according to claim 1, characterized in that the solid mineral particles consist of volatile products, clay minerals, bentonites and / or. activated carbon.

3. A suspension according to claim 1 or claim 2, characterized in that it is a suspension. In addition, they comprise aqueous suspension calcium calcium hydroxide (Ca / OH) or dolomite lime hydrate or lime milk suspension according to the claims. 1 to * 3 / u - ·. "·,. It is said that as a stabilizing agent. , .containing vodní sodium water glass and / or potassium water glass. 5. A suspension according to any one of claims 1 to 4, characterized in that it contains water glass in a quantity of 5% by weight. %, which - corresponds to an addition of 0.5% to 8% by weight of solid waterglass, comprising 17 to 20% by weight of water, or b / 1 to 19% by weight of liquid waterglass to a density in the range of. up to 40 ° B ', based on the weight of the suspended solid.

6. A suspension according to any one of claims 1 to 5, characterized in that it contains water glass corresponding to the addition of a / 1 to 2% by weight of solid water glass containing 17% by weight of water. with 20% by weight of water, or b / 2- to 5% by weight of liquid waterglass having a density in the range of 37 to 40 ° C, in each case based on the weight of the suspended solid. 7. Lime milk suspension, sediment-resistant. whose,. according to claims 2 to 6,. characterized in that the content of calcium hydroxide or dolomite lime hydrate is up to 10%. 45% by weight, preferably. 33 to 40% by weight based on the total weight of the lime milk without the addition of water glass. '· .......' · ',' ‘- '8 ·. . ' Suspension according to the claims. > 1. aíL · 7:. ·, ·. wherein the composition contains thixotrophic benzenes and / or polyacrylates, suspensions according to the invention. claim .., .. 8y. In the present invention there is provided a polyvinyl phosphonate and / or polyacrylate salt containing polyvinylphosphonate. to -... '15% ... by weight? - "female" to the weight of the solid.

A method for producing sediment-resistant suspensions according to claims 1 to 5, characterized by: it can. solid water glass or aqueous water glass solution is admixed to the previously prepared suspension. organic or inorganic or mineral particulate matter, ‘or se - (3). admix the solid water glass or aqueous water glass solution to the feed water to prepare the suspension; . then the solid particles are admixed, or the dry xHspssdExa solids particles to be suspended by the solid aqueous glass are mixed, and the mixture is suspended in water. with the use of solid product particles of clay products, clay minerals, bentonites, pigments and / or activated carbon.

12. A process according to claim 10 or 11, characterized in that solid water glazing or water is added to produce sedimentation-resistant lime ash. water glass solution to pre-made lime milk, or (3) solid water glass or aqueous water glass solution is mixed into the feed water for lime milk and then slaked lime is admixed or 1 7c / / D / 7e / the dry lime, or dolomitic lime, is mixed with the solid water glass, and the mixture is suspended in water as the solid water glass is admixed. or an aqueous solution of water. The lime is extinguished or quenched with the water to be quenched or quenched. The solid water glass is mixed with burnt lime, or dolomitic lime, and the lime is quenched with water. The method according to claims 10 to 13, characterized in that the water glass is used. adding 'amounts corresponding to the addition of 0.5 to 8% by weight of solid water glass containing 17 to 20% by weight of water; ........ / B / 1 .... to ... .... 19 ...,% by weight of liquid water glass, having a density ranging from 37 to 40 ° C. in each case based on the weight of the suspended solid 1S-15-t wherein the amount of glass added is from 1 to 2% by weight of solid water glass containing from 17 to 20% by weight. water, after / b / 2 to. 5% by weight of a liquid aqueous glass having a density in the range of from 37 to 40 ° C, in each case based on the suspended solid.

16. ZpŮ3ob! 10. A composition according to claim 10, wherein the calcium hydroxide is optionally used, optionally containing calcium hydroxide. lime hydrate or dolomitic lime hydrate .. κ '· Λ; ΊΓ 1 -. 45% by weight, preferably in the range of 33 to 40% by weight, based on the dry weight of the lime-free milk. A method according to claims 10-16. The process according to claim 4, wherein the 4- (4-xotropic) bentonites and / or polyacrylates are added to the suspension. Claim 17, characterized in that the thixotropic bentonites and / or polyacrylates are used in an amount of 1 to 15% by weight, based on the weight of the solid suspension, without the additive. · 7 ·.;: -R '. ., 19. Strong substances mixtures for the manufacture of aqueous suspensions which are resistant to sedimentation, based on organic or inorganic or mineral particles, characterized in that they contain solid water glass. . t 1 ·. 't x ·. . · ''. <-. 20 ... -. Solids mixtures according to claim 19, in particular calcium hydroxide or lime hydrate or dolomitic lime hydrate, characterized in that they contain 0.5 to 0.5% by weight of 20% solid waterglass with water content 17 to. 20% by weight, based on the weight of the solid particles, without the additive

Solids mixtures according to claim 19 or 20, characterized in that they contain 1-2% by weight of water-containing glass. 17 to 20% by weight of water, based on the weight of the solid.

Solid compositions according to Claims 19 to 21 they contain thixotropic bentonites and / or polyacrylates. ·. '.

23 ·. Compositions of solids according to claim 1, comprising: and / or. polyacrylates in an amount of about 22% to about 15% by weight based on the weight of the solid suspension without additive. .24 · Use of solid mixtures based on calcium hydroxide or lime hydrate or hydrate-lime hydrate according to the claims. 20 to P23 for lime milk production. ': *' "· · '' - · '

25. Use of waterglass as well as thixotropic bentonites and / or polyacrylates, for aqueous suspensions of organic or inorganic or mineral particles of solids, as stabilizers for sedimentation, in particular for lime milk.

26. Water glass for use as a stabilizer for organic and inorganic or mineral solids in aqueous suspension, sedimentation, in particular for suppressing lime milk sedimentation,

Use of the lime milk stabilized against sedimentation according to claims 9 to 9 as fertilizers, as a binder-coating pigments. vat dyes, for wastewater treatment, for potable water treatment, as acid-binding agent for flue gas cleaning as well as for mortar production.