CS243920B1 - A method of solidifying liquid radioactive waste - Google Patents

A method of solidifying liquid radioactive waste Download PDF

Info

Publication number
CS243920B1
CS243920B1 CS843198A CS319884A CS243920B1 CS 243920 B1 CS243920 B1 CS 243920B1 CS 843198 A CS843198 A CS 843198A CS 319884 A CS319884 A CS 319884A CS 243920 B1 CS243920 B1 CS 243920B1
Authority
CS
Czechoslovakia
Prior art keywords
radioactive waste
liquid radioactive
parts
ratio
added
Prior art date
Application number
CS843198A
Other languages
Czech (cs)
Slovak (sk)
Other versions
CS319884A1 (en
Inventor
Anton Pekar
Jan Petrovic
Jan Timulak
Original Assignee
Anton Pekar
Jan Petrovic
Jan Timulak
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anton Pekar, Jan Petrovic, Jan Timulak filed Critical Anton Pekar
Priority to CS843198A priority Critical patent/CS243920B1/en
Publication of CS319884A1 publication Critical patent/CS319884A1/en
Publication of CS243920B1 publication Critical patent/CS243920B1/en

Abstract

Vynález sa týká sposobu spevňovania kvapalných rádioaiktívnych odpadov. Podstatou vynálezu je sposob spevňovania kvapalných rádioaktívnych odpadov s obsahom solí kyseliny boritej spočívajúci v miešaní kvapalných rádioaktívnych odpadov s cementom. Kvapalný rádioaktívny odpad sa zmieša so zeolitovým tufom (klinoptilolitový tulit, mordenitový tuf atď.) v pomere 0,75 až 1,5, zneutralizuje sa prebytkom vápna, pričom molárny poměr bóru a vápnika je 1 : 2 až 1 : 3, přidá sa elektrárenský piopolček v pomere 1.5 až 3,0 s jednosložkovým portlandským cementom v pomere 0,75 až 1,5 alebo zmesný portlandský cement v pomere 0,5 až 1,0, v množstve zabezpečujúcom vodný súčinitel v rozmedzí 0,3 až 0,6 a popřípadě sa před dávkováním do obalov přidá aniónaktívna bitúmenová emulzia alebo vodná emulzia. solí mastných kyselin a volných mastných kyselin, nerozpustilých vo vodě, v množstve do 5 % hmot. na suchu zmes. Uvedený postup spevňovania kvapalných rádioaktívnych odpadov je možné využit pri spevňovaní kvapalných rádioaktívnych odpadov s obsahom solí kyseliny boritej z jádrových elektrární s tlakovod/nými reaiktormí.The invention relates to a method of solidifying liquid radioactive waste. The essence of the invention is a method of solidifying liquid radioactive waste containing boric acid salts, consisting in mixing liquid radioactive waste with cement. Liquid radioactive waste is mixed with zeolite tuff (clinoptilolite tulite, mordenite tuff, etc.) in a ratio of 0.75 to 1.5, neutralized with excess lime, with a molar ratio of boron to calcium of 1:2 to 1:3, power plant slag is added in a ratio of 1.5 to 3.0 with single-component Portland cement in a ratio of 0.75 to 1.5 or mixed Portland cement in a ratio of 0.5 to 1.0, in an amount ensuring a water coefficient in the range of 0.3 to 0.6 and, if necessary, an anionic bitumen emulsion or water emulsion is added before dosing into the containers. salts of fatty acids and free fatty acids, insoluble in water, in an amount of up to 5% by weight of the dry mixture. The above-mentioned process for solidifying liquid radioactive waste can be used for solidifying liquid radioactive waste containing boric acid salts from nuclear power plants with pressurized water reactors.

Description

Autor vynálezu PEKAR ANTON ing., TRNAVA; PETROVIC JAN ing. CSC., BRATISLAVA; TIMULÁK JÁN ing., PIEŠŤANY (54) Sposob spevňovania kvapalných rádioaktívnych odpadovAuthor of the invention PEKAR ANTON ing., TRNAVA; PETROVIC JAN ing. CSC., BRATISLAVA; TIMULÁK JÁN ing., PIEŠŤANY (54) Method of solidification of liquid radioactive waste

Vynález sa týká sposobu spevňovania kvapalných rádioaiktívnych odpadov. Podstatou vynálezu je sposob spevňovania kvapalných rádioaktívnych odpadov s obsahom solí kyseliny boritej spočívajúci v miešaní kvapalných rádioaktívnych odpadov s cementom. Kvapalný rádioaktívny odpad sa zmieša so zeolitovým tufom (klinoptilolitový tulit, mordenitový tuf atď.) v pomere 0,75 až 1,5, zneutralizuje sa prebytkom vápna, pričom molárny poměr bóru a vápnika je 1 : 2 až 1 : 3, přidá sa elektrárenský piopolček v pomere 1.5 až 3,0 s jednosložkovým portlandským cementom v pomere 0,75 až 1,5 alebo zmesný portlandský cement v pomere 0,5 až 1,0, v množstve zabezpečujúcom vodný súčinitel v rozmedzí 0,3 až 0,6 a popřípadě sa před dávkováním do obalov přidá aniónaktívna bitúmenová emulzia alebo vodná emulzia. solí mastných kyselin a volných mastných kyselin, nerozpustilých vo vodě, v množstve do 5 % hmot. na suchu zmes. Uvedený postup spevňovania kvapalných rádioaktívnych odpadov je možné využit pri spevňovaní kvapalných rádioaktívnych odpadov s obsahom solí kyseliny boritej z jádrových elektrární s tlakovod/nými reaiktormí.The invention relates to a method for solidifying liquid radioactive waste. SUMMARY OF THE INVENTION The present invention provides a method of solidifying liquid radioactive waste containing boric acid salts by mixing liquid radioactive waste with cement. The liquid radioactive waste is mixed with a zeolite tuff (clinoptilolite tulite, mordenite tuff, etc.) in a ratio of 0.75 to 1.5, neutralized with an excess of lime, with a boron to calcium molar ratio of 1: 2 to 1: 3, adding a power plant. 1.5 to 3.0 piopol with a one-component Portland cement at a ratio of 0.75 to 1.5 or a mixed Portland cement at a ratio of 0.5 to 1.0, in an amount providing a water ratio of 0.3 to 0.6, and optionally, an anionic bitumen emulsion or an aqueous emulsion is added to the containers prior to dosing. % salts of fatty acids and free fatty acids, insoluble in water, in an amount of up to 5 wt. dry mix. The process of solidification of liquid radioactive waste can be used for solidification of liquid radioactive waste containing boric acid salts from nuclear power plants with pressurized / reactive reactors.

Vynález sa týká spůsobu spevňovania kvapalnýcli rádioaktívnych odpadov použitým cementu.The present invention relates to a method of solidifying liquid radioactive waste using cement.

Dosial' známe sposoby spevňovania kvapalných rádioaktívnych odpadov· s obsahom kyseliny boritej a jej solí sa usikutoeňujú aj za použitia různých druhov maltovin — portlandský cement, hlinitanový cement, sadr,a, Soirellová maltovina. Pre zlepšenie vlastností zatvrdnutého cementového· kameňa sa používajú, v nieiktorých prípadoch, zimesné cementy na. báze vysokopecnej trosky alebo· prírodných a umělých pucolánov.Hitherto known methods of solidification of liquid radioactive wastes containing boric acid and its salts are also made using different types of mortars - Portland cement, aluminous cement, gypsum, and Soirell mortar. To improve the properties of the hardened cementitious stone, in some cases, intermediate cements are used. blast furnace slag bases or natural and artificial pozzolans.

Pre zlepšenie sorpčných vlastností cementov používajú sa rožne íly a ílové minerály, ako· sorbenty. Je známe použitie kaolínu, bentonitu, vermikulitu, attapulgitu a pod.To improve the sorption properties of cements, various clays and clay minerals are used as sorbents. It is known to use kaolin, bentonite, vermiculite, attapulgite and the like.

Nevýhodou týchto je v nedostupnosti nlektorých mlnerálov u nás a v nestabilitě niektorých v zatvrdnutom cementovom kameni.The disadvantage of these is in the unavailability of some millers in our country and in the instability of some in hardened cement stone.

Podobnou problematikou spevňoivania rádioaktívnych odpadov sa zaoherá patent NSR 26 03116.A similar issue of solidification of radioactive waste is covered by the German patent 26 03116.

Podstatou vynálezu je spósob spevňovania kvapalných rádioaktívnych odpadov s obsahem soli kyseliny boritej, spočívajúci v miešanJ kvapalných rádioaktívných odpadov s cementem, vyznačujúci sa tým, že kvapalný rádioaiktívny odpad sa zmieša so· zeolitovým tufom v· pomere odpad/tuf 0,75 až 1,5, zneutralizuje sa prebytkom vápna, pričom molárny poměr bóru a vápnika je 1 : 2 až 1 : 3, přidá sa elektrárenský popolček v pomere odpad/popolčék 1,5 až 3,0 s jednozložkovým portlandským ceimentom v pomere odpad/cement 0,75 až 1,5 alebo· zmesný portlandský cement v pomere odpad/zmesný cement 0,5 až 1,0, v množstve zatoezpečujúcom vodný súčiniteí' v rozmedzí 0,3 až 0,6 a popřípadě sa před dávkováním do obalov přidá aniónaktívna bitúmenová emulzaia alebo vodná emulzia solí mastných kyselin a volných mastných kyselin nerozpustných vo vodě v množstve 5 % hmot. na suchu zmes.SUMMARY OF THE INVENTION The present invention provides a method for solidifying liquid radioactive wastes containing boric acid salt by mixing liquid radioactive wastes with cement, wherein the liquid radioactive waste is mixed with a zeolite tuff in a waste / tuff ratio of 0.75 to 1.5 , neutralized with an excess of lime, with a boron to calcium molar ratio of 1: 2 to 1: 3, a power / ash fly ash / fly ash ratio of 1.5 to 3.0 with a one-component Portland ceiment in a waste / cement ratio of 0.75 to 1.5 or a mixed Portland cement in a waste / mixed cement ratio of 0.5 to 1.0, in an amount to provide an aqueous ratio of from 0.3 to 0.6, and optionally an anionic bitumen emulsion or an aqueous emulsion is added to the containers before dosing. % emulsion of salts of fatty acids and free water-insoluble fatty acids in an amount of 5 wt. dry mix.

Výhodou postppu je využitelnost 1'ahkodostupných surovin a výsledný produkt spevňovania má v perovnaní s uvedenými patentaimi lepšiu hodnotu vychovatelnosti rádionuklidov. Zeolitové tufy obsahujú cca 40 % volného S1O2 a cca 50 % zeolitu (klinoptilolit, mordenit). Přednostou použitia zeoilitových tufov tohoto typu je, že v zmesi s cementom pri tuhnutí a tvrdnutí dochádza k reakcii medzi Ca(OH]2, ktorý sa uvolňuje v. priebehu hydratačného procesu z alitu a belitu — hlavných mineralogických zložiek sliriku portlandského cementu, a volného SiO3 z tufu za tvorby tobermoritu alebo jeho· fáz, ktoré vylepšujú vlastnosti výsledného· produktu. Druhá zložka tufu — zeolit — je za přítomnosti Ca.(0H)2 v tvrdnúcom. a zatvrnutom cemente stála a nepodlieha žiadnyím změnám — sorpč.né vlastnosti zostávajú Zachovalé.The advantage of postppu is the usability of 1 'readily available raw materials and the resulting consolidation product has a better value of radionuclide educability when compared to said patents. Zeolite tuffs contain about 40% free S1O2 and about 50% zeolite (clinoptilolite, mordenite). The advantage of using zeoilite tuffs of this type is that in the mixture with cement during setting and hardening there is a reaction between Ca (OH) 2 , which is released during the hydration process from alite and belite - the main mineralogical constituents of Portland cement sliric and free SiO 3, tuff to form the tobermorite phase · or to improve properties of the final product ·. the other component of tuff - zeolite - the presence of Ca (0H) 2 in the hardened. zatvrnutom a cement stable and not subject to change žiadnyím - sorpč.né characteristics remain preserved.

V ďalšom je predmet vynálezu popísanýThe invention is described below

Claims (1)

ohmedzoval.ohmedzoval. Příklad 1Example 1 Do 23,0 dielov kvapalného rádioaktív,něho odpadu s obsahom soli kyseliny boritej sa přidá 30,8 dielov zeolitového tufu (klinoptilolitoivý, mordenitový atď.) a po premiešaní sa zmes zneutralizuje prebytkom vápna, pričom molárny poměr béru a vápnika má byť 1 : 2 až 1 : 3. K takto prlpravenej zmesi sa za stálého· miešania postupné přidá 15,4 dielov elektrárenského popolčeka a 30,8 dielov jednozložkového· portlandského cementu. Takto· připravená kaša sa dávkuje do vhodných obalov k zatvrdnutiu.To 23.0 parts of liquid radioactive waste containing boric acid salt is added 30.8 parts of zeolite tuff (clinoptilitic, mordenite, etc.) and after mixing the mixture is neutralized with excess lime, the molar ratio of boron to calcium being 1: 2. 15.4 parts of a power plant fly ash and 30.8 parts of a single-component Portland cement are added successively while stirring. The slurry thus prepared is dispensed into suitable containers to harden. Příklad 2Example 2 Do 37,5 dielov kvapalného rádioaktívneho odpadu s obsahom solí kyseliny boritej sa přidá 25,0 dielov zeolitového tufu a po premiešaní sa zmes zneutralizuje prebytkom vápna. K takto pripravenej zmesi sa za stálého miešania přidá 37,5 dielov· zmesného portlandského cementu. Takto· připravená kaša sa dávkuje do vhodných obalov k zatvrdnutímTo 37.5 parts of liquid radioactive waste containing boric acid salts was added 25.0 parts of zeolite tuff and after mixing the mixture was neutralized with excess lime. To this mixture was added 37.5 parts of mixed Portland cement with stirring. The slurry thus prepared is dispensed into suitable containers for hardening Příklad 3Example 3 Do· 37,0 dielov kvapalného rádioaktívneho odpadu s obsahom solí kyseliny boritej sa přidá 25,0 dielov zeolitového tufu a po premiešaní zneutralizuje prebytkom vápna. K takto pripravenej zmesi sa za stálého miešania postupné přidá 12,0 dielov elektrárenského· popoilčeka, 25,0 dielov portlandského cementu jednozložkového a 1,0 diel aniónaktívnej bitúmenovej emulzie. Takto připravená kaša sa dávkuje do vhodných obalov k zatvrdnutím25.0 parts of zeolite tuff are added to 37.0 parts of liquid radioactive waste containing boric acid salts and neutralized with excess lime after mixing. 12.0 parts of a power plant ash, 25.0 parts of Portland one-component cement and 1.0 parts of an anionic bitumen emulsion are successively added to the thus prepared mixture while stirring. The slurry thus prepared is dispensed into suitable containers for hardening P R E D Μ E ΤP R E D Μ E Τ Sposob spevňovania kvapalných rádioaktívnych odpadov s obsahom solí kyseliny boritej spočívajúci v miešaní kvapalných rádioaktívnych odpadov s cementom, vyznačujúci sa tým, že kvapalný rádioaktívny odpad sa zmieša so zeolitovým tufom v poměre 0,75 až 1,5, zneutralizuje sa prebytkom vápna, pričom molárny poměr bóru a vápnika je 1 : 2 až 1 : 3, přidá sa elektrárenský popolček v pomere 1,5 až 3,0 s jedno-zložkovynAlezu vým portlandským cemenitom v poimere 0,75A method of solidifying liquid radioactive waste containing boric acid salts by mixing liquid radioactive waste with cement, characterized in that the liquid radioactive waste is mixed with zeolite tuff in a ratio of 0.75 to 1.5, neutralized by an excess of lime, the molar ratio of boron and calcium is 1: 2 to 1: 3, a power fly ash is added in a ratio of 1.5 to 3.0 with one component of Allen
CS843198A 1984-04-28 1984-04-28 A method of solidifying liquid radioactive waste CS243920B1 (en)