CS253084B1

CS253084B1 - Polyethylene sackcloth

Info

Publication number: CS253084B1
Application number: CS851862A
Authority: CS
Inventors: Jiri Budin; Jaroslav Kubicek; Dalibor Vacek
Original assignee: Jiri Budin; Jaroslav Kubicek; Dalibor Vacek
Priority date: 1985-03-18
Filing date: 1985-03-18
Publication date: 1987-10-15
Also published as: CS186285A1

Abstract

Řešení se týká profilové žíně z polyetylénu, která sestává z polyetylénu o hustotě nižší než 925 kg.m-3 a indexu toku taveniny v rozmezí 0,6 až 3,0 g/10 minut, přičemž příčný průřez žíně tvoří symetrický kříž s nezaoblenýmí rameny na sebe kolmými, u kterého podíl průměru kružnice profilu opsané a průměru kružnice do profilu vepsané se pohybuje v rozmezí od 2 do 5 a podíl délky ramene profilu k jeho šířce se pohybuje v rozmezí od 2 do 6. Žíně je určena k výrobě rotačních kartáčů pro umývárny automobilů.The solution relates to a profiled polyethylene wire mesh, which consists of polyethylene with a density lower than 925 kg.m-3 and a melt flow index in the range of 0.6 to 3.0 g/10 minutes, with the cross-section of the wire mesh forming a symmetrical cross with non-rounded arms perpendicular to each other, in which the ratio of the diameter of the circle circumscribed by the profile to the diameter of the circle inscribed in the profile ranges from 2 to 5 and the ratio of the length of the arm of the profile to its width ranges from 2 to 6. The wire mesh is intended for the production of rotary brushes for car washes.

Description

253084 2253084 2

Vynález se týká profilové polyetylénové žíně vhodné zejména pro rotační kartáče, u kterése řeší její struktura a příčný průřez.BACKGROUND OF THE INVENTION 1. Field of the Invention The invention relates to a profiled polyethylene horsehair suitable in particular for rotary brushes, in which its structure and cross-section are solved.

Rotační kartáče, které patří mezi významné výrobky kartáčnického průmyslu nachází stáleširší uplatnění v moderních automatických linkách pro čištění a mytí v nejrůznějších oblastechprůmyslu, zemědělství a dopravy. Příkladem mohou být mycí linky pro automobily, stavebnístroje a železniční vagóny. Pro bezporuchový chod a vysokou účinnost mycího zařízení má roz-hodující význam i kvalita žfňové části rotujícího kartáče, která zprostředkuje vlastní mytíčištěného prostředku.Rotary brushes, which are among the most important products of the brush industry, find a wider application in modern automatic cleaning and washing lines in a wide range of industries, agriculture and transport. Examples include carwashes for cars, construction machines and railway wagons. For the trouble-free operation and high efficiency of the washing device, the quality of the rotating brush's refractory part is also of decisive importance, which mediates the cleaning agent itself.

Pro rotační kartáče se zpočátku používaly přírodní žíně. Ze syntetických materiálů tobyl především polyamid 6. S rozvojem výroby nových polymerů našly v tomto odvětví uplatněnízejména polyolefiny jako je polypropylen a polyetylén.For brushes, natural horsehair was initially used. Above all, polyamide 6 from synthetic materials tobyl. In particular, polyolefins such as polypropylene and polyethylene have been found in the industry to develop new polymers.

Další důležitou vlastností žíně, která rozhoduje o jejím úspěšném použití v rotačníchkartáčích je její příčný profil, žíně kruhového nebo oválného průřezu nejsou pro tuto apli-kaci příliš vhodné. Zině v rotačním kartáči při mycím procesu nejen mechanicky stírá nečisto-ty z čištěného předmětu, ale také zajišťuje plynulý transport vody ze středu kartáče k čiště-nému povrchu. Proto se v tomto případě uplatňují lépe profilové žíně s příčným průřezem vetvaru tří až šesticípé hvězdy se zaoblenými konci ramen a s výrazným přechodovým obloukemz jednoho cípu profilu na druhý. Tento tvar profilu u stávajících žíní pro rotační kartáčenezajištuje plně hladký transport vody k čištěnému místu, čímž se snižuje mycí efekt rotačníhokartáče a prodlužuje se doba, potřebná k mytí. Konce žíní v rotačních kartáčích jsou rozště-pené a toto rozštěpení se musí samovolně postupně obnovovat podle toho, jak se žíně v důsled-ku oděru postupně zkracuje, štěpením žíně se zamezuje poškozování laku umývaných vozidel. U stávajících žíní tento proces probíhá ne vždy uspokojivě. Zině se bud nerozštěpí, nebo na-opak se štěpí po celé její délce, štěpení žíně po celé její délce snižuje účinnost mycíhokartáče, zejména při větším nebo starším znečištění. Dále způsobuje zcuchánl kartáče, tvorbusmyček a uzlíků, které se pak zachytávají o výstupky umývaných předmětů. Žíňová část kartáčemusí volně splývat a při myti přesně kopírovat tvary čištěného předmětu. Toho není u stávají-cích typů žíní v plné míře dosaženo. U stávajících žíní se vyskytuje i lámání. Výše uvedené nedostatky stávajících profilových žíní z polyetylénu pro rotační kartáčeo délkové hmotnosti 0,1 až 1,0 g.m 1 jsou odstraněny žíní podle vynálezu, jejíž podstatou _3 je, že sestává z polyetylénu o hustotě nižší než 925 kg.m a indexu toku taveniny v rozmezí0,6 až 3 g/10 minut přičemž příčný průřez žíně tvoří symetrický kříž s nezaoblenými ramenyna sebe kolmými, u kterého podíl průměru d·^ kružnice profilu opsané a průměru dj kružnice doprofilu vepsané se pohybuje v rozmezí od 2 do 5 a podíl délky a ramene profilu k jeho šířces se pohybuje v rozmezí od 2 do 6.Another important characteristic of horsehair, which determines its successful use in rotary brushes, is its transverse profile, horsehair circular or oval cross section is not very suitable for this application. The zinc in the rotary brush does not only mechanically wipe off the dirt from the cleaned article during the washing process, but also ensures a smooth transfer of water from the center of the brush to the cleaned surface. That is why, in this case, the horsehair with a cross-sectional branch of a three to six-pointed star with rounded ends of the shoulder and a pronounced transition arc from one corner of the profile to the other apply better. This profile shape of the existing rotary brush horsehair ensures a fully smooth water transport to the cleaning site, thereby reducing the rotating brush washing effect and extending the washing time. The horsehair ends of the rotary brushes are split and this splitting must spontaneously be renewed as the horsehair gradually becomes shorter as a result of the abrasion, and the damage to the lacquer of the washed vehicles is prevented by splitting the horsehair. For existing horsehair, this process is not always satisfactory. The zinc is either not split or, in contrast, cleaved along its entire length, the cleavage of the horsehair over its entire length decreases the effectiveness of the washing brush, especially at higher or older contamination. In addition, it causes the worms of brushes, sponge-forming knots and knots, which are then trapped on the projections of washed items. The hair part of the brush must loosely coincide with the cleaning of the object to be cleaned. This is not fully achieved with existing horsehair types. Breaking is also present in existing horsehair. The aforementioned drawbacks of the existing polyethylene profiled horsehair brushes of 0.1 to 1.0 gm 1 are eliminated by horsehair according to the invention, the essence of which is that it consists of polyethylene having a density of less than 925 kg and a melt index of 0 6 to 3 g / 10 min, the transverse cross-section of the horsehair forming a symmetrical cross with non-curved shoulders perpendicular to each other, in which the diameter of the circle of the circumscribed circle and the diameter dj of the circle of the profiled circle is in the range of 2 to 5 and the proportion of length and shoulder The profile to its width varies from 2 to 6.

Zině podle vynálezu se vyznačuje vzhledem ke známým typům při aplikaci do rotačních kar-táčů vyšší životností o jednu polovinu a vyšším čisticím efektem. Zině je vysoce splývavá adokonale kopíruje tvar umývaného předmětu, přičemž současně zajišťuje dokonalý transport vodyrespektive umývaciho roztoku k umývanému místu. To se projevuje zkrácením doby potřebné k mytío 20 %. Při mytí nedochází k odtrhávání a odlamování jednotlivých žíní z rotačního kartáčejako je tomu často u známých typů žíní pro rotační kartáče.The zine according to the invention is characterized by a higher lifetime of one half and a higher cleaning effect due to the known types when applied to rotary brushes. Zine is highly flowing and perfectly replicates the shape of the washed item while at the same time ensuring perfect transport of the water of the wash solution to the wash area. This results in a 20% reduction in washing time. Washing does not tear off and breaks off individual rotary brushes as is often the case with known types of horsehair for rotary brushes.

Dosažení vhodných fyzikálně mechanických vlastností žíně podle vynálezu je zajištěnovhodnou strukturou a složením materiálu, ze kterého je žíně vyrobena a geometrickým tvaremjejího příčného průřezu. Molekulová hmotnost polyetylénu je charakterizována hodnotou indexutoku taveniny.Achieving suitable physico-mechanical properties of the horsehair according to the invention is a reliable structure and composition of the material from which the horsehair is made and the geometric shape of the cross-section. The molecular weight of the polyethylene is characterized by a melt index value.

Profilovou polyetylénovou žíni podle vynálezu lze připravit extruzí taveniny vysokotla-kého nízkohustotního polyetylénu zvlákňovací tryskou, jejíž otvory jsou ve tvaru symetrickéhokříže, sestávajícího ze dvou navzájem kolmých a protínajících se štěrbin, přičemž poměr délkyštěrbiny k její šířce se pohybuje v rozmezí 9 až 13. Mezi jednotlivými rameny profilovéhoThe profiled polyethylene horsehair according to the invention can be prepared by extrusion of a melt of a high pressure low density polyethylene with a spinneret whose apertures are in the form of a symmetrical cross consisting of two mutually perpendicular and intersecting slots, the ratio of the slit length to the width being between 9 and 13. profile arms

Claims

3 253084 nozzle opening is not a transition arc. After passing through the melt through the nozzle, the monofilaments formed are cooled in water at a temperature of 10 to 40 ° C and monosonically drawn in water at a temperature of 40 to 80 ° C and a ratio of 3.0 to 4.3. The elongated monofilaments are then fixed in water at 80 to 95 ° C with a shrinkage of 7 to 12 ° C. An exemplary horsehair according to the invention is shown in cross-section. The horsehair is a monofilament of 0.5 g.m 3 in high pressure polyethylene having a density of 922 kg.m 3 and a melt index of 2 g / 10 minutes. The diameter diameter d 2 of the circle of the circumscribed and the diameter d 2 of the circle to the inscribed profile is 2.7. The length-to-arm ratio of the profile to its width is 3.1. The horsehair of the invention can be wound on spools or skeins in bundles of 50 to 1500 mm in length or in infinite form. Horsehair may be colored, may contain weathering agents. Preferably, horsehair is used at the end of the cleaved. OBJECT OF THE INVENTION Polyethylene profiled horsehair, measuring from 0.1 to 1.0 gm 3, is particularly suitable for spinning brushes characterized in that the polyethylene has a density of less than 925 kg.m 3 and a melt index of 0.6 to 3.0 g / 10 minutes, where the cross-section of the horsehair forms a symmetrical cross with non-curved arms perpendicular to each other, in which the diameter ratio (D f) of the circle of the circle diameter (d 2) to the inscribed profile is in the range of 2 to 5 and the proportion of length (a) of the rameneprofil to its width (s) ranges from 2 to 6. 1 drawing