CS261834B1 - Pre-sensitized negative type offset plate - Google Patents

Pre-sensitized negative type offset plate Download PDF

Info

Publication number
CS261834B1
CS261834B1 CS873099A CS309987A CS261834B1 CS 261834 B1 CS261834 B1 CS 261834B1 CS 873099 A CS873099 A CS 873099A CS 309987 A CS309987 A CS 309987A CS 261834 B1 CS261834 B1 CS 261834B1
Authority
CS
Czechoslovakia
Prior art keywords
weight
light
hydrophilic
sensitive
negative
Prior art date
Application number
CS873099A
Other languages
Czech (cs)
Slovak (sk)
Other versions
CS309987A1 (en
Inventor
Gabriel Ing Csc Cik
Anton Prof Ing Drsc Blazej
Milan Ing Zuffa
Milan Ing Lederleitner
Peter Ing Sterusky
Original Assignee
Cik Gabriel
Anton Prof Ing Drsc Blazej
Zuffa Milan
Lederleitner Milan
Peter Ing Sterusky
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cik Gabriel, Anton Prof Ing Drsc Blazej, Zuffa Milan, Lederleitner Milan, Peter Ing Sterusky filed Critical Cik Gabriel
Priority to CS873099A priority Critical patent/CS261834B1/en
Publication of CS309987A1 publication Critical patent/CS309987A1/en
Publication of CS261834B1 publication Critical patent/CS261834B1/en

Abstract

Riešenie sa týká predscitlivenej ofsetovej tlačovej platné negativného typu, ktorá pozostáva z hliníkovej podložky s mechanicky alebo elektrochemicky zdrsněným povrchom, upraveným anodickou oxidáciou, na ktorej je hydrofilná medzivrstva na báze é- terov celulózy modifikovaných chlórtriazí- novým farbivom, obsahujúcim konjugovaný systém dvojitých vázieb a svetlocitlivú azo- skupinu. Na hydrofilnej medzivrstve je negativné pracujúca svetlocitlivá vrstva zlo- žená z 2,0 až 20,0 % hmot. novolakovej vy- sokomolekulovej živice, 0,5 až 10,0 % hmot. polyvinylacetátu, 0,5 až 10,0 % hmot. 2,6- -bis (4-azidobenzilidén ] -4-metylcykIohe- xanónu, 0,5 až 10,0 % hmot. C-(4-azidofe- nyl)-N-fenylnitrónu a zvyšku do 100% hmot. polárného organického rozpúšťadla. Riešenie je možné využit v polygrafickom priemysle.The present invention relates to a pre-sensitized offset print valid negative type consisting of an aluminum pad with a mechanically or electrochemically roughened surface treated with anodic oxidation having a hydrophilic interlayer based on cellulose modified chlorotriazine dye containing a conjugated double bond and light sensitive system. azo-group. On the hydrophilic interlayer, the negative working light-sensitive layer is composed of 2.0 to 20.0% by weight. of novolak high molecular weight resin, 0.5 to 10.0 wt. % polyvinyl acetate, 0.5 to 10.0 wt. 2,6-bis (4-azidobenzilidene) -4-methylcyclohexanone, 0.5 to 10.0% by weight of C- (4-azidophenyl) -N-phenylnitrone and a residue to 100% by weight of polar organic The solution can be used in the printing industry.

Description

2B1834

Vynález sa týká predscitlivenej ofsetové]tlačove] platné negativného typu, pozostá-vajúcej z hliníkové] podložky, hydrofilnejmedzivrstvy a negativné pracujúcej svetlo-citlive] vrstvy určenej na zhotovovanie of-setových tlačových foriem negativným ko-pírovacím postupom.

Doteraz známe negativné priamotlačiaceofsetové platné zložené z hliníkovej podlož-ky s mechanicky alebo elektrochemickyzdrsněným povrchom upraveným anodickouoxidáciou, na ktorý ]e priamo alebo na ba-riérovej medzivrstve nanesená svetlocitlivávrstva. Ako bariérové medzivrstvy sa použí-vajú rožne nízkomolekulové aromatické sul-folátky, polyfosforečnany alebo hydrofilnépolymery s prídavkom nízkomolekulovýchanorganických látok. Přítomnost nízkomolekulových anorganic-kých látok (hlavně solí fažkýcli kovo v —vápnika, zinku, stroncia, kobaltu, mangá-nu] nesie so sebou nepriaznivé ekologickédopady — znečisťovanie odpadových vod,negativné vplyvy na pracovně prostredie.Ich vylúčenie z celého viackomponentnéhosystému nie je možné, nakoíko po vyvolanítlačových platní dochádza k ich tónovaniuv. tlačí.

Uvedené nevýhody odstraňuje predscitli-vená ofsetová tlačová platňa negativnéhotypu pódia vynálezu, pozostávajúca z hliní-kové] podložky s mechanicky alebo elektro-chemicky zdrsněným povrchom upravenýmanodickou oxidáciou, hydrofilnej medzivrst-vy a negativné pracujúcej svetlocitlivej vrst-vy. Podstata vynálezu spočívá v tom, že nahliníkovej podložke s mechanicky alebo e-lektrochemicky zdrsněným povrchom, upra-veným anodickou oxidáciou je nanesenáhydrofilná medzivrstva na báze éterov ce-lulózy modifikovaných chlórtriazínovýmfarbivom obsahujúcim konjugovaný systémdvojitých vazieb a svetlocitlivú azoskupinuv množstve 0,1 až 1,0 g . m-2 sušiny. Na tej-to hydrofilnej medzivrstvo je nános negativ-né pracujúcej svetlocitlivej vrstvy, zlože-nej z 2,0 až 20,0 % hmotnostných novolakovejvysokomolek úlove j živice, 0,5 až 10,0 % hmotnostných polyviuylacctá-tu, 0,5 až 10,0% hmotnostných 2,6-bis(4-azido-benzilidén j -4-metylcyklohexanónu, 0,5 až 10,0% hmotnostných C-(4-azidofe-nyl j-N-fenylnitrónu a zvyšku do 100 %hmot. polárného organického rozpúšťad-la. Nános negativné pracujúcej svetlo-citlivej vrstvy je 1,0 až 3,0 g . m~2 suši-ny.

Predscitlivená ofsetová tlačová platňa po-dlá vynálezu sa připraví tak, že na hliní-kovú podložku sa nanesie bariérová medzi-vrstva vodného roztoku na báze modifiko-vaného éteru celulózy a po jej vysušeni sana povrch nanesie negativny svetlocitlivýroztok. Tento sa na povrch platné může na-nášať odstředivými ovrstvovacími zariade-niami, sústavou valcov,, štrbinovým polieva-ním alebo iným spasobom. Do svetlocitlivejvrstvy je možné pridať — na lepšiu vizuali-záciu — farbivo. Výhodou predscitlivenej ofsetovej tlačo-vej platné pódia vynálezu je skutočnosť, žehydrofilnou medzivrstvou na báze éterovcelulózy modifikovaných chlórtriazínovýmfarbivom obsahujúcim konjugovaný systémdvojitých vazieb a svetlocitlivú azoskupinusa vylúči nevyhnutnosť použitia viackom-ponentných systémov obsahujúcich soli ťaž-kých kovov, čo má priaznivý dopad na eko-lógiu. Okrem toho sa odstraňuje potřeba ú-pravy fyzikálno-chemických vlastností po-vrchu hliníkovej platné naplňováním pórovoxidové] vrstvy v různých naplňovacíchroztokoch za zvýšenej teploty, čím sa znížienergetická náročnost výroby. Predscitlive-ná ofsetová tlačová platňa s hydrofilnoumedzivrstvou na báze modifikovaného éte-ru celulózy sa dá dokonale vyvolat' a od-straňují! sa problémy s tónováním netlačia-cich miest v tlačovom stroji.

Platňa osvitnutá cez negativnu montáž savyvolá vodnoalkalickým roztokom s prídav-kom alkoholov. Po vyvolaní je tlačová for-ma připravená pre tlač.

Uvedené příklady ilustrujú, ale neobme-dzujú predmet vynálezu. Příklad 1

Na hlitňkovú platňu s elektrochemickyzdrsněným povrchom a oxidovou vrstvou sananesie vodný roztok hydrofilnej vrstvy na-sledujúceho zloženia: 0,5 % hmot. hydroxyetylcelulózy modifiko-vanej chlórtriazínovým farbivom vzorca

ch*I 3N X. ct

SOjNA ct

2B1834

BACKGROUND OF THE INVENTION The present invention relates to a pre-sensitized offset print of a valid negative type consisting of an aluminum substrate, a hydrophilic layer, and a negative light-sensitive layer designed to produce an off-set printing form by a negative co-process.

Until now, the negative direct printing set is comprised of an aluminum backing with a mechanically or electrochemically abraded surface treated with anodic oxidation, on which a light sensitive coating is applied directly or on the intermediate layer. Low-molecular aromatic sulphonates, polyphosphates or hydrophilic polymers with the addition of low molecular weight inorganic substances are used as barrier intermediate layers. The presence of low molecular weight inorganic substances (mainly salts of brassic acid in zinc, zinc, strontium, cobalt, manganese) carries unfavorable environmental impacts - wastewater pollution, negative impacts on the working environment. Their exclusion from the whole multi-component system is not possible, as the printing plates are tinted after printing.

These disadvantages are eliminated by the pre-impression offset printing plate of the negative type of the invention, consisting of an aluminum substrate with a mechanically or electro-chemically roughened surface treated with anodic oxidation, a hydrophilic interlayer and a negative working light sensitive layer. SUMMARY OF THE INVENTION The present invention is based on the fact that an aluminum anodic oxidized or electrodeposited surface is coated with a hydrophilic intermediate layer based on cellulose ethers modified with a chlorotriazine dye containing a conjugated double bond system and a light sensitive azo group in an amount of 0.1 to 1.0 g. . m-2 dry matter. For this hydrophilic interlayer, the deposition of the negative working light-sensitive layer, comprised of 2.0 to 20.0% by weight of the novolak superfine of the resin, is 0.5 to 10.0% by weight of polyvinyl acetate, 0.5 to 10% by weight. 10.0% by weight of 2,6-bis (4-azido-benzilidene-4-methylcyclohexanone, 0.5 to 10.0% by weight of C- (4-azidophenyl) N-phenylnitrone and a residue of up to 100% by weight of polar The deposition of the negative working light-sensitive layer is 1.0 to 3.0 gm-2 of dry matter.

The pre-sensitized offset printing plate of the present invention is prepared by applying a barrier intermediate layer of a modified cellulose ether-based aqueous solution to the aluminum substrate and applying a light sensitive solution after drying. This can be applied to the surface by means of centrifugal coating devices, a roll assembly, a slot coating or other spasob. A dye may be added to the light-sensitive layer for better visualization. An advantage of the pre-sensitized offset printing valid invention is that the hydrophilic ether-cellulose-based intermediate layer modified with chlorotriazine dye containing the conjugated double bond system and the light-sensitive azo group eliminates the need for multi-component heavy metal salt containing systems, which has a beneficial effect on ecology. In addition, the need to modify the physicochemical properties of the aluminum surface by filling the porous oxide layer in different elevated temperature fill solutions is eliminated, thereby reducing the manufacturing cost. A pre-hypersensitive offset printing plate with a hydrophilic modified layer of modified cellulose ether can be perfectly induced and removed! there is a problem with tinting of non-printing spots in the printing machine.

The plate is exposed to a negative assembly with a water-alkaline solution with the addition of alcohols. After invocation, the print form is ready for printing.

These examples illustrate, but do not limit the invention. Example 1

For an electrochemically abrasive surface with an electrochemical surface and a sananesium oxide layer, an aqueous solution of the hydrophilic layer of the following composition: 0.5 wt. hydroxyethylcellulose modified with a chlorotriazine dye of formula

ch * I 3N X. ct

SOjNA ct

Claims (3)

261834 0,05 % hmotnostných 1 %-ného roztoku Slo-vasolu 0 a 99,45 % hmotnostného voda. Vý-sledný nános hydrofilného polyméru po vy-sušení je 0,25 g . m-2. Na vysušenú hydro-íilnú medzivrstvu sa nanesie svetlocitlivýroztok zloženia: 3.5 % hmotnostného krezolformaldehydo- vá živica, 0,5 % hmotnostného 2,6-bis(4-azidobenzi-lidén]-4-metylcyklohexanón, 2,0% hmotnostně C-(4-azidofenyl)-N-fe- nylnitrón, 1.5 % hmotnostného polyvinylacetát, 0,1 % hmotnostného kryštálová violeť, 46,2 % hmotnostného etylénglykolmonoety-léter, 46,2 % hmotnostného cyklohexanón. Svotlocitlivá vrstva sa vysuší pri teplote40 až 50 °C a 15 min. sa tepelne upravuje pri 80 °C. Nános svetlocitlivej vrstvy po vy-sušení je 1,5 g . m~2. P. Příklad261834 0.05% by weight of a 1% solution of Slo-vasol 0 and 99.45% by weight water. The resulting hydrophilic polymer deposit after drying is 0.25 g. m-2. A light-sensitive composition of the composition was applied to the dried hydrophilic intermediate layer: 3.5% by weight of cresolformaldehyde resin, 0.5% by weight of 2,6-bis (4-azidobenzidene) -4-methylcyclohexanone, 2.0% by weight of C- (4% by weight). -azidophenyl) -N-phenylnitrone, 1.5% by weight of polyvinyl acetate, 0.1% by weight of crystal violet, 46.2% by weight of ethylene glycol monoethyl ether, 46.2% by weight of cyclohexanone. For 15 min, heat treatment at 80 DEG C. The coating of the light-sensitive layer after drying is 1.5 g. 2 Predscitlivená ofsetová platňa sa připra-ví ako v příklade 1, s nánosom medzivrstvypo vysušení 0,3 g . m~2 a nánosom svetlo-citlivej vrstvy 2,5 g . m~2. Po osvitnutí plat-né, vyvolaní a opláchnutí vodou sa na po-vrch platné nanesie prípravok podfa CS AOč. 244 575 a tlačová forma sa pri 220 °C po-čas 5 min. tepelne upravuje, čím sa zvýši tla-čová výdržnosť hotovej tlačovej formy nadvoj- až trojnásobok. Příklad2 The pre-sensitized offset plate is prepared as in Example 1, with an interlayer coating of 0.3 g. m ~ 2 and a light-sensitive layer of 2.5 g. m ~ 2. After exposure to a valid, inducing, and rinsing water, the composition of CS A is applied to the top. 244,575 and printing form at 220 ° C for 5 min. heat treatment, thereby increasing the pressure resistance of the finished printing form to over three to three times. Example 3 Postup ako v příklade 1 len s tým rozdie-lom, že sa použije hliníková platňa mecha-nicky zdrsněná s oxidovou vrstvou. PREDMET Predscitlivená ofsetová tlačová platila ne-gativného typu, pozostávajúca z hliníkovejpodložky s mechanicky alebo elektroche-micky zdrsněným povrchom upraveným a-nodickou oxidáciou, hydrofilnej medzivrstvya negativné pracujúcej svetlocitlivej vrst-vy vyznačujúca sa tým, že na hliníkovejpodložke s mechanicky alebo elektroche-micky zdrsněným povrchom upraveným a-nodickou oxidáciou je hydrofilná medzivrst-va na báze éterov celulózy modifikovanýchchlórtriazínovým farbivom obsahujúcimkonjugovaný systém dvojitých vazieb a svetlocitlivú azo-skupinu v množstve 0,1 až1,0 g . m~2 sušiny a na hydrofilnej medzi-vrstve je negativné pracujúca svetlocitlivávrstva v množstve 1,0 až 3,0 g . m-2 sušiny,obsahujúca 2,0 až 20,0 % hmotnostných no-volakovej vysokomolekulovej živice, 0,5 až10,0 % hmotnostných polyvinylacetátu, 0,5až 10,0% hmotnostných 2,6-bis(4-azidoben-zilidén)-4-metylcyklohexanónu, 0,5 až 10,0pere. hmotnostných C-(4-azidofenyl)-N-fe-nylnitrónu a zvyšok do 100 % hmotnostnýchpolárné organické rozpúšťadlo.3 Procedure as in Example 1, except that an aluminum plate is mechanically roughened with an oxide layer. SUBJECT Pre-sensitized offset printing of a non-negative type, consisting of an aluminum substrate with a mechanically or electrochemically roughened surface treated with anodic oxidation, a hydrophilic interlayer and a negative-working light-sensitive layer characterized in that the surface is mechanically or electrochemically abraded on an aluminum substrate by modified anodic oxidation, the hydrophilic cellulose ether-based intermediate layer is a modified chlorotriazine dye containing a conjugated double bond system and a light sensitive azo group in an amount of 0.1-1.0 g. m ~ 2 dry matter, and the hydrophilic interlayer is a negative light sensitive film in an amount of 1.0 to 3.0 g. m-2 of dry matter, containing 2.0 to 20.0% by weight of non-coding high molecular weight resin, 0.5 to 10.0% by weight of polyvinyl acetate, 0.5 to 10.0% by weight of 2,6-bis (4-azidoben-zilidene) ) -4-methylcyclohexanone, 0.5-10.0. % C- (4-azidophenyl) -N-phenylnitrone and the remainder to 100% by weight polar organic solvent.
CS873099A 1987-04-30 1987-04-30 Pre-sensitized negative type offset plate CS261834B1 (en)