CS263579B1 - Self-hardening silicate suspension - Google Patents
Self-hardening silicate suspension Download PDFInfo
- Publication number
- CS263579B1 CS263579B1 CS878113A CS811387A CS263579B1 CS 263579 B1 CS263579 B1 CS 263579B1 CS 878113 A CS878113 A CS 878113A CS 811387 A CS811387 A CS 811387A CS 263579 B1 CS263579 B1 CS 263579B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- suspension
- silicate
- cement
- hardening
- water
- Prior art date
Abstract
Samotvrdnúca silikátová suspenzia na báze silikátových úletov, cementu a vody sa používá v stavebníctve pri špeciálnom zakladení stavieb. Stabilitu a čerpatetnosť suspenzie zabezpečuje přítomnost silikátových úletov. Róznou volbou váhových pomerov silikátových úletov, cementu a vody je možné regulovat v širokom rozsahu Teologické parametre suspenzie a pevnosti vytvrdnutej suspenzie. Samotuhnúca suspenzia zložená zo silikátových úletov, cementu a vody po vytvrdnutí těsní a spevňuje nesúdržné zeminy a horniny, vytvára tesniace podzemně steny a v spojitosti s ocelovou výstužou vytvára konstrukčně podzemně steny.Self-hardening silicate suspension based on silicate flakes, cement and water is used in construction for special foundations of buildings. The stability and pumpability of the suspension is ensured by the presence of silicate flakes. By choosing different weight ratios of silicate flakes, cement and water, it is possible to regulate the theological parameters of the suspension and the strength of the hardened suspension in a wide range. After hardening, the self-hardening suspension composed of silicate flakes, cement and water seals and strengthens non-cohesive soils and rocks, creates sealing underground walls and, in conjunction with steel reinforcement, creates structural underground walls.
Description
(54) Samotvrdnúca silikátová suspenzia(54) Self-hardening silicate suspension
22
Samotvrdnúca silikátová suspenzia na báze silikátových úletov, cementu a vody sa používá v stavebníctve pri špeciálnom zakladení stavieb. Stabilitu a čerpatetnosť suspenzie zabezpečuje přítomnost silikátových úletov. Róznou volbou váhových pomerov silikátových úletov, cementu a vody je možné regulovat v širokom rozsahu Teologické parametre suspenzie a pevnosti vytvrdnutej suspenzie. Samotuhnúca suspenzia zložená zo silikátových úletov, cementu a vody po vytvrdnutí těsní a spevňuje nesúdržné zeminy a horniny, vytvára tesniace podzemně steny a v spojitosti s ocelovou výstužou vytvára konstrukčně podzemně steny.Self-hardening silicate suspension based on silicate flakes, cement and water is used in construction for special foundations of buildings. The stability and pumpability of the suspension is ensured by the presence of silicate flakes. By choosing different weight ratios of silicate flakes, cement and water, it is possible to regulate the theological parameters of the suspension and the strength of the hardened suspension in a wide range. After hardening, the self-hardening suspension composed of silicate flakes, cement and water seals and strengthens non-cohesive soils and rocks, creates sealing underground walls and, in conjunction with steel reinforcement, creates structural underground walls.
Vynález sa týká samotvrdnúcej silikátové] suspenzie na báze silikátových úletov a cementu pre podzemně steny a injektáž. Suspenzia je použitelná pre injektáž tesniacu a spevňovaciu a pri podzemných stěnách ako samotvrdnúca alebo konštrukčné. Uvedené technológie ,sa používajú v stavebníctve pri špeciálnom zakladení stavieb.The invention relates to a self-hardening silicate suspension based on silicate flakes and cement for underground walls and injection. The suspension is applicable for sealing and reinforcing injection and for underground walls as self-hardening or structural. The mentioned technologies are used in construction for special foundations of buildings.
Doteraz známe suspenzie pre uvedené účely sú na báze cementovej, ílo-cememtovej, resp. bentonito-cementovej. Stabilita injekčných suspenzií a ich čerpatelnosť je zabezpečovaná přísadou ílu, resp. bentonitu, ktorý vytvára vnútorné štruktúrne vazby tak, že cementové zrná vzdorujú účinkom gravitácie. Přísada ílov, resp. bentonitu má rozhodujúci vplyv na vytvorenie stabilnej suspenzie, ale na druhej straně negativné ovplyvňuje výslednú pevnosť vytvrdnutej suspenzie. Výsledná pevnosť vytvrdnutej suspenzie je závislá na množstve cementu, ílu, resp. bentonitu a vody. Nevýhodou takto pripravenej suspenzie je skutočnosť, že stabilita je závislá na kvalitě použitého ílu, resp. bentonitu a na čase dozrievania bentoinitovej, resp. ílovej suspenzie. Ďalšou nevýhodou je nutnost dvojfázovej technológie výroby. Bez přísady plastifikátorov nevykazuje retardačně vlastnosti.The suspensions known so far for the above purposes are based on cement, clay-cement or bentonite-cement. The stability of injection suspensions and their pumpability is ensured by the addition of clay or bentonite, which creates internal structural bonds so that the cement grains resist the effects of gravity. The addition of clay or bentonite has a decisive influence on the creation of a stable suspension, but on the other hand negatively affects the resulting strength of the hardened suspension. The resulting strength of the hardened suspension depends on the amount of cement, clay or bentonite and water. The disadvantage of the suspension prepared in this way is the fact that the stability depends on the quality of the clay or bentonite used and on the maturation time of the bentonite or clay suspension. Another disadvantage is the necessity of a two-phase production technology. Without the addition of plasticizers, it does not exhibit retarding properties.
Uvedené nedostatky rieši samotvrdnúca silikátová suspenzia na báze cementu, silikátových úletov a vody podlá vynálezu, ktorá obsahuje 5 až 25 hmotnostných % silikátových úletov s obsahom najmenej 80 °/o oxidu křemičitého, 5 až 55 hmotnostných % portlandského alebo struskoportlandského cementu a 20 ažž 90 hmotnostných % vody.The above-mentioned shortcomings are solved by a self-hardening silicate suspension based on cement, silicate fly ash and water according to the invention, which contains 5 to 25% by weight of silicate fly ash with a content of at least 80% silicon dioxide, 5 to 55% by weight of Portland or slag Portland cement and 20 to 90% by weight of water.
V samotvrdnúcej silikátovej suspenzii podlá vynálezu je stabilita a čerpatelnosť zabezpečovaná prítomnosťou silikátového úletu, ktorý obsahuje viac ako 80 % amorfného oxidu křemičitého. Silikátový úlet vzniká ako odpad so zrnitostnou štruktúrou s absolútnou převahou zrn pod 0,063 mm. Tieto uzavreté porézně částice o vysokom špecifickom povrchu viažu na celý svoj povrch vodu a po premiešaní vytvárajú stabilnú suspenziu. Vzhíadom k svojmu guíkovitému tvaru majú optimálně trenie, čo priaznivo ovplyvňuje čerpatelnosť vzniknutej suspenzie. Vzhíadom k vysokému obsahu amorfného oxidu křemičitého v silikátovom úlete vykazuje suspenzia na báze cementu a silikátového úletu podstatné váčšie pevnostně parametre ako doteraz používané adekvátně ílocementové, resp. bentonitocementové suspenzie. Uvedená skutočnosť je spůsobená mikroskopickými křemičitými časticami, ktoré pri hydratácii cementu menia velkú časť 1'ahko rozpustného hydroxidu vápenatého na trvalú gelovitú kremičitú hmotu. Volhou váhových pomerov silikátového úletu, cementu a vody je možné regulovat v širokom rozsahu rozhodujúce reologické parametre suspenzie a pevnosti vytvrdnutej suspenzie. Reologické parametre silikátovej suspenzie na báze cementu a silikátového úletu móžu byť podía potřeby regulované aj s použitím plastifikátorov. Samotvrdnúcu silikátová suspenziu pozostávajúcu z cementu, silikátového úletu a vody na rozriel od doteraz používaných suspenzií je možné miešať priamo. Nie je potřebné najskór namiešat ílovú suspenziu, resp. bentonitovú suspenziu, túto nechať dozrievať a až potom přidávat cement.In the self-hardening silicate suspension according to the invention, stability and pumpability are ensured by the presence of silicate fly ash, which contains more than 80% amorphous silicon dioxide. Silicate fly ash is produced as waste with a grain structure with an absolute predominance of grains below 0.063 mm. These closed porous particles with a high specific surface bind water on their entire surface and, after mixing, form a stable suspension. Due to their spherical shape, they have optimal friction, which favorably affects the pumpability of the resulting suspension. Due to the high content of amorphous silicon dioxide in silicate fly ash, the suspension based on cement and silicate fly ash exhibits significantly greater strength parameters than the clay-cement or bentonite-cement suspensions used to date. This is due to microscopic silica particles, which, when the cement is hydrated, convert a large part of the readily soluble calcium hydroxide into a permanent gel-like silica mass. By choosing the weight ratios of silicate fly ash, cement and water, it is possible to control the decisive rheological parameters of the suspension and the strength of the hardened suspension within a wide range. The rheological parameters of the silicate suspension based on cement and silicate fly ash can also be controlled, if necessary, by using plasticizers. The self-hardening silicate suspension consisting of cement, silicate fly ash and water, in contrast to the suspensions used so far, can be mixed directly. It is not necessary to mix the clay suspension or bentonite suspension first, let it mature and only then add the cement.
Silikátová suspenzia, ktorá je predmetom vynálezu aj po súčasnom nadávkovaní cementu a silikátového úletu ’do vody a po krátkom premiešaní vykazuje vysokú objemová stálost a prakticky sa nemenia jej reologické parametre. Silikátová suspenzia na báze silikátového úletu, cementu a vody má retardačně vlastnosti, ktoré umožňujú jej transport v dlhších časových úsekoch. Po vytvrdnutí vykazuje váčšie pevnostně parametre ako adekvátna ílocementová alebo bentonitocementová suspenzia. Silikátová suspenzia na báze silikátových úletov, cementu a vody umožňuje úsporu cementu pri dodržaní výsledných Teologických parametrov. Silikátová suspenzia má zvýšenú odolnost voči agresivitě vód.The silicate suspension, which is the subject of the invention, even after simultaneous dosing of cement and silicate fly ash into water and after short mixing, exhibits high volumetric stability and its rheological parameters practically do not change. The silicate suspension based on silicate fly ash, cement and water has retarding properties that enable its transport over longer periods of time. After hardening, it exhibits greater strength parameters than an adequate clay-cement or bentonite-cement suspension. The silicate suspension based on silicate fly ash, cement and water allows for saving cement while maintaining the resulting rheological parameters. The silicate suspension has increased resistance to the aggressiveness of water.
Příklady samotvrdnúcej silikátovej sus-Examples of self-hardening silicate sus-
Namerané parametre: viskozita Marsch (s): 32 až 34 odstoj 2 hod. (%): 0,25 až 0,50 pevnost v tlaku (MPa) dní: 0,144 14 dní: 1,16 28 dní: 1,363 90 dní: 1,710 priepustnosť (m. s-1) dní: 3,2.10-8 Measured parameters: Marsch viscosity (s): 32 to 34 2-hour settling time (%): 0.25 to 0.50 compressive strength (MPa) days: 0.144 14 days: 1.16 28 days: 1.363 90 days: 1.710 permeability (m. s- 1 ) days: 3.2.10- 8
2.2.
160 kg silikátový úlet 13,18 %160 kg silicate drift 13.18%
160 kg cement SPC-325 13,18 %160 kg cement SPC-325 13.18%
894 1 voda 73,64 %894 1 water 73.64%
Namerané parametre: viskozita Marsch (s): 37 až 39 odstoj 2 hod. (%): 0,0 pevnosť v tlaku (MPa) dní: 0,057 14 dní: 0,726 28 dní: 0,840 90 dní: 1,283 priepustnosť (m.s-1) dní: 2,9.10-8 Measured parameters: Marsch viscosity (s): 37 to 39 2-hour settling time (%): 0.0 Compressive strength (MPa) days: 0.057 14 days: 0.726 28 days: 0.840 90 days: 1.283 Permeability (ms -1 ) days: 2.9.10- 8
283579283579
3.3.
kg silikátový úlet 5,88 %kg silicate drift 5.88%
500 kg cemejit PC-400 39,21 %500 kg cement PC-400 39.21%
700 1 voda 54,90 %700 1 water 54.90%
Namerané parametre:Measured parameters:
viskozita Marsch (s): 35,2 až 36,8 odstoj 2 hod. (%): 1,0 pevnost v tlaku (MPa) dní: 2,343 14 dní: 3,260 βMarsch viscosity (s): 35.2 to 36.8 standoff 2 hrs. (%): 1.0 compressive strength (MPa) days: 2.343 14 days: 3.260 β
Samotvrdnúca silikátová suspenzia zložená zo' silikátových úletov, cementu a vody volbou poměru základných hmot po vytvrdnutí těsní a spevňuje nesúdržné zeminy a horniny. Samotvrdnúca silikátová suspenzia voíbou poměru základných hmot po vytvrdnutí vytvára tesniaca podzemně steny a v spojitosti s ocelovou výstužou vytvára konstrukčně podzemně steny.Self-hardening silicate suspension composed of silicate flakes, cement and water, by selecting the ratio of basic materials, after hardening seals and strengthens non-cohesive soils and rocks. Self-hardening silicate suspension by selecting the ratio of basic materials after hardening creates sealing underground walls and in conjunction with steel reinforcement creates structural underground walls.
Claims (1)