CS265910B1 - Retractable shoe rack - Google Patents

Retractable shoe rack Download PDF

Info

Publication number
CS265910B1
CS265910B1 CS868552A CS855286A CS265910B1 CS 265910 B1 CS265910 B1 CS 265910B1 CS 868552 A CS868552 A CS 868552A CS 855286 A CS855286 A CS 855286A CS 265910 B1 CS265910 B1 CS 265910B1
Authority
CS
Czechoslovakia
Prior art keywords
steel
traces
max
diameter
shoe rack
Prior art date
Application number
CS868552A
Other languages
Czech (cs)
Other versions
CS855286A1 (en
Inventor
Frantisek Ing Sykora
Karel Ing Vorel
Original Assignee
Frantisek Ing Sykora
Karel Ing Vorel
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Frantisek Ing Sykora, Karel Ing Vorel filed Critical Frantisek Ing Sykora
Priority to CS868552A priority Critical patent/CS265910B1/en
Publication of CS855286A1 publication Critical patent/CS855286A1/en
Publication of CS265910B1 publication Critical patent/CS265910B1/en

Abstract

Řešení se týká oceli pro svařované konstrukce, zejména tyče do průměru 130 mm i pro užití při teplotách pod 0 °C. Podstata řešeni spočívá v tom, že ocel obsahuje v hmotnostním množství 0,12 až 0,18 % uhlíku, 1,00 až 1,40 % manganu, 0,15 až 0,50 % křemíku, max. 0,025 % fosforu, max. 0,028 % síry, 0,016 až 0,060 % hliníku, 0,010 až 0,050 % titanu, 0,10 až 0,25 % chrómu, stopy až 0,25 % niklu, stopy až 0,28 % mědi.The solution concerns steel for welded structures, in particular bars up to 130 mm in diameter and for use at temperatures below 0 °C. The essence of the solution lies in the fact that the steel contains by weight 0.12 to 0.18% carbon, 1.00 to 1.40% manganese, 0.15 to 0.50% silicon, max. 0.025% phosphorus, max. 0.028% sulfur, 0.016 to 0.060% aluminum, 0.010 to 0.050% titanium, 0.10 to 0.25% chromium, traces of up to 0.25% nickel, traces of up to 0.28% copper.

Description

Vynález se týká oceli pro svařované konstrukce, zejména pro tyčovinu do průměru 130 mm i pro použití při teplotách pod 0 °C.BACKGROUND OF THE INVENTION The present invention relates to steel for welded structures, in particular for bars up to 130 mm in diameter, for use at temperatures below 0 ° C.

V současné době konstrukční oceli pro práci za nízkých teplot nezaručují zvláště při teplotách pod 0 °C vyhovující mechanické vlastnosti, předevěím hodnoty vrubové houževnatosti n svnřitelnont, zejména pro ocelové tyče o průměru nad 100 mm.At present, structural steels for working at low temperatures do not guarantee satisfactory mechanical properties, especially at temperatures below 0 [deg.] C., in particular notch toughness values, especially for steel bars with a diameter above 100 mm.

Uvedené nedostatky těchto ocelí podle vynálezu odstraňuje ocel obsahující 0,12 až 0,18 % uhlíku, 1,00 až 1,40 % manganu, 0,15 až 0,50 % křemíku, max. 0,025 % fosforu, max. 0,028 % síry 0,016 až 0,060 % hliníku, 0,010 až 0,050 % titanu, 0,10 až 0,25 % chrómu, stopy až 0,25 % niklu, stopy až 0,28 % mědi.These drawbacks of these steels according to the invention are overcome by steel containing 0.12 to 0.18% carbon, 1.00 to 1.40% manganese, 0.15 to 0.50% silicon, max. 0.025% phosphorus, max. 0.028% sulfur 0.016 to 0.060% aluminum, 0.010 to 0.050% titanium, 0.10 to 0.25% chromium, traces up to 0.25% nickel, traces up to 0.28% copper.

Složení oceli podle vynálezu zaručuje dobrou svařitelnost tyčí dó průměru 130 mm pro užití při teplotách pod 0 °C, při docílení vysoké vrubové houževnatosti oceli. Po vyválcování tyči za tepla a po normalizačním žíhání nebo normalizačním žíháním a popouštěním bylo dosaženo meze pevnosti 640 až 630 MPa, meze kluzu min. 290 MPa, při +20 °c vrubové houževnatosti 80 J.cm při -20 °C vrubové houževnatosti 60 J.cm 2 a při -60 °C vrubové houževnatosti 40 J.cm 2.The composition of the steel according to the invention guarantees good weldability of bars up to 130 mm in diameter for use at temperatures below 0 ° C, while achieving high notch toughness of the steel. After hot-rolling and after normalization or normalization and tempering, a breaking strength of 640 to 630 MPa, a yield strength of min. 290 MPa, at + 20 ° C notched toughness 80 J.cm at -20 ° C notched toughness 60 J.cm 2 and at -60 ° C notched toughness 40 J.cm 2 .

Příkladně byla vyrobena ocel obsahující v hmotnostním množství 0,17 % uhlíku, 1,27 % manganu, 0,40 % křemíku, 0,019 8 fosforu, 0,014 8 síry, 0,040 8 hliníku, 0,026 % titanu,For example, steel containing 0.17% carbon, 1.27% manganese, 0.40% silicon, 0.019% phosphorus, 0.014% sulfur, 0.040% aluminum, 0.026% titanium,

0,15 % ohromu, 0,14 8 niklu, 0,15 % mědi a byla použita na svařovanou jeřábovou konstrukci. Ocel má proti známým ocelím nižší obsah fosforu a síry, stanovený min. obsah hliníku, stanovený rozsah titanu a ohromu. Mechanické vlastnosti oceli byly velmi dobré, ocel vykazovala např. mez pevnosti 525 MPa, mez kluzu 343 MPa, tažnost 33,2 8, zúžení 67,2 8, při -20 °C podélnou vrubovou houževnatost 163 J.cm-2, při -60 °C podélnou vrubovou houževnatost 115 J.cm měřena na tyči o průměru 125 mm.0.15% overwhelming, 0.14% nickel, 0.15% copper and was used on the welded crane structure. The steel has a lower phosphorus and sulfur content than the known steels, determined by min. aluminum content, specified titanium range and astonishment. The mechanical properties of the steel were very good, for example, the steel showed a yield strength of 525 MPa, a yield strength of 343 MPa, an elongation of 33.2 8, a taper of 67.2 8, at -20 ° C a longitudinal notch toughness of 163 J.cm -2 ; 60 ° C longitudinal notch toughness 115 J.cm measured on a 125 mm diameter rod.

Ocel dle vynálezu lze využít na svařované konstrukce a strojní součásti pro práci ve ztížených klimatických podmínkách, zejména do průměru nebo tlouštky do 130 mm.The steel according to the invention can be used for welded structures and machine parts for working in difficult climatic conditions, especially up to a diameter or thickness up to 130 mm.

Claims (1)

Ocel pro svařované konstrukce, zejména tyče do průměru 130 mm i pro užití při teplotách pod 0 °C, vyznačující se tlm, že obsahuje v hmotnostním množství 0,12 až 0,18 % uhlíku,Steel for welded structures, in particular bars up to 130 mm in diameter and also for use at temperatures below 0 ° C, characterized in that it contains 0.12 to 0.18% by weight of carbon, 1,00 až 1,40 % manganu, 0,15 až 0,50 % křemíku, max. 0,025 % fosforu, max. 0,028 % síry, 0,016 až 0,060 8 hliníku, 0,010 až 0,050 % titanu, 0,10 až 0,25 % chrómu, stopy až 0,25 8 niklu, stopy až 0,28 % mědi.1.00 to 1.40% manganese, 0.15 to 0.50% silicon, max. 0.025% phosphorus, max. 0.028% sulfur, 0.016 to 0.060% aluminum, 0.010 to 0.050% titanium, 0.10 to 0, 25% chromium, traces up to 0.25 8 nickel, traces up to 0.28% copper.
CS868552A 1986-11-24 1986-11-24 Retractable shoe rack CS265910B1 (en)