CS267322B1 - Glass for glass fibres - Google Patents

Glass for glass fibres Download PDF

Info

Publication number
CS267322B1
CS267322B1 CS879838A CS983887A CS267322B1 CS 267322 B1 CS267322 B1 CS 267322B1 CS 879838 A CS879838 A CS 879838A CS 983887 A CS983887 A CS 983887A CS 267322 B1 CS267322 B1 CS 267322B1
Authority
CS
Czechoslovakia
Prior art keywords
glass
oxide
production
fibres
weight
Prior art date
Application number
CS879838A
Other languages
Czech (cs)
Other versions
CS983887A1 (en
Inventor
Jan Ing Surovec
Mojmir Ing Kriz
Original Assignee
Surovec Jan
Mojmir Ing Kriz
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Surovec Jan, Mojmir Ing Kriz filed Critical Surovec Jan
Priority to CS879838A priority Critical patent/CS267322B1/en
Publication of CS983887A1 publication Critical patent/CS983887A1/en
Publication of CS267322B1 publication Critical patent/CS267322B1/en

Abstract

Podstatou riešenia je sklo pre skleně­ né vlákna, najma na výrobu skleněného vlékne β vysokým indexom lomu, ktoré v hmotnostněj koncentrácii obsahuje 53,00 ež 56,40 « SiO2, 11,40 až 15,50 % AlgO,, 3,70 až 5,80 % BgO-j, 19,60 až 22,20 % CaO, Ι,ΘΟ až 2,20 % MgO, 0,95 až 2,90 % ZnO, aLopy aZ ί,ΟΟ % T1O2 a/alebo VegOj, efcopy ež 1,00 % Na20 e/alebo KgO.The essence of the solution is glass for glass fibers, especially for the production of glass fiber β with a high refractive index, which in mass concentration contains 53.00 to 56.40 « SiO2, 11.40 to 15.50% AlgO,, 3.70 to 5.80% BgO-j, 19.60 to 22.20% CaO, Ι,ΘΟ to 2.20% MgO, 0.95 to 2.90% ZnO, aLopy aZ ί,ΟΟ% T1O2 and/or VegOj, efcopy even 1.00% Na20 e/or KgO.

Description

Vynález sa týká chemického zloženia skla pře skleněné vlákna, najma na výrobu skleněného vlákna s vysokým indexem lomu.The invention relates to the chemical composition of glass for glass fibers, in particular for the production of glass fiber with a high refractive index.

Skleněné vlákna ea v súčasnosti vyrábajú z róznych druhov ekiel, ktorých charakteristické vlastnosti sú dané chemickým zložením skla v súvislosti a účelom ku ktorému sú1 určené. Sú to sklá obsahujúce alkalické oxidy a spravidla neobsahujúce oxid boritý alebo sklá bezalkalické, ktoré obsehujú oxid boritý o různých hmotnostných obsahoch. Zvláštnu skupinu tvořia bezalkalické, bezborité sklá. Najrozšírenejším typom skiel na výrobu skleněných vlákien sú tzv. E - sklá, sú to sklá s vysokým obsahom oxidu hlinitého, oxidu vápenatého a oxidu křemičitého, ktorých fyzikálnochemické vlastnosti sú do určitéj miery modifikované prídavkom oxidu horečnatého a hlavně oxidu boritého.Glass fibers ea currently produced from various species ekiel whose characteristics are determined by the chemical composition of the glass in relation to the purpose and they are designated 1. These are glasses containing alkali oxides and generally not containing boric oxide or non-alkaline glasses which contain boric oxide of different weight contents. A special group consists of alkali-free, boron-free glasses. The most widespread type of glass for the production of glass fibers are the so - called E - glasses, they are glasses with a high content of alumina, calcium oxide and silica, whose physicochemical properties are to some extent modified by the addition of magnesium oxide and especially boron oxide.

Medzi tieto sklá patří aj typ E - skla znány pod obchodnou značkou Euthal. Nevýhodou tohoto druhu skla je poměrně vysoký obsah oxidu boritého. Vysoká cena oxidu boritého nepriaznivo vplýva na ekonomiku výroby. Okrem toho oxid boritý je prchavou zložkou sklářského kmeňa a pri tavení skloviny vplýva na zhoršovanie životného prostredia.These glasses also include the E-type glass known under the Euthal brand. The disadvantage of this type of glass is the relatively high content of boric oxide. The high price of boric oxide adversely affects the economy of production. In addition, boric oxide is a volatile component of the glass stem and affects the environment when the glass melts.

Vyššie uvedenu nevýhodu čiastočne odstraňuje a technický problém rieši chemické zloženie skla pře skleněné vlákna podlá tohoto vynálezu, ktorého podstatou je, že obsahuje v hmotnostnej koncentrácii 53 až 56,4 % oxidu křemičitého, 11,4 až 15,5 % oxidu hlinitého, 3,7 až 5,8 % oxidu boritého, 19,6 až 22,2 % oxidu vápenatého, 1,8 až 2,2 % oxidu horečnatého, 0,95 až 2,9 * oxidu zinočnatého, atopy až 1 % oxidu titaničitého a/alebo oxidu železitého, stopy až 1 % oxidu sodného a/alebo oxidu draselného.The above-mentioned disadvantage is partially eliminated and the technical problem is solved by the chemical composition of glass for glass fibers according to the present invention, the essence of which is that it contains 53 to 56.4% by weight of silica, 11.4 to 15.5% of alumina by weight. 7 to 5.8% boric oxide, 19.6 to 22.2% calcium oxide, 1.8 to 2.2% magnesium oxide, 0.95 to 2.9 * zinc oxide, atopes up to 1% titanium dioxide and / or or iron oxide, traces of up to 1% sodium oxide and / or potassium oxide.

Výhoda skla pre skleněné vlákna podlá vynálezu spočívá najma ▼ znížení obsahu oxidu boritého pri zachovaní, príp. zlepšení fyzikálno-chemických vlastností predpísaných normou pre tento druh skla.The advantage of glass for glass fibers according to the invention lies in particular in the reduction of the boric oxide content while maintaining or improving the physico-chemical properties prescribed by the standard for this type of glass.

Podstata vynálezu je objasněná tabulkovou formou príkladmi zloženia skla pre skleněné vlákna v hmotnostněj koncentrácii s příslušnými fyzikálno-chemickými parametrami.The essence of the invention is illustrated in tabular form by examples of glass compositions for glass fibers in mass concentration with corresponding physicochemical parameters.

Zloženie Composition 1 1 2 2 3 3 4 4 SiO2 SiO 2 56,00 56.00 56,40 56.40 53,50 53.50 55,40 55.40 ai2°3 to 2 ° 3 12,70 12.70 11,60 11.60 15,40 15.40 14,90 14.90 B2°3B 2 ° 3 3,90 3.90 3,70 3.70 5,80 5.80 4,90 4.90 CaO CaO 21,30 21.30 22,20 22.20 20,60 20.60 20,00 ’ 20.00 ’ MgO MgO 1,90 1.90 2,10 2.10 2,10 2.10 2,00 2.00 ZnO ZnO 2,70 2.70 2;4O 2; 4O 1,20 1.20 1,10 « 1.10 « TiO2 TiO 2 0,42 0.42 0,46 0.46 0,36 0.36 0,28 0.28 Pe2°3 .At 2 ° 3 . 0,27 0.27 0,13 0.13 0,22 0.22 0,46 0.46 Na20At 2 0 0,10 0.10 0,20 0.20 0,20 0.20 0,26 0.26 k2ok 2 o 0,70 0.70 0,70 0.70 0,60 0.60 0,64 0.64

CS 267322 BlCS 267322 Bl

Zloženie Composition 1 1 2 2 3 3 4 4 teplota liquidus (°C) liquidus temperature (° C) 1123 1123 1109 1109 1125 1125 1095 1095 teplota v (°C) pri log^ = 2,00 temperature in (° C) at log ^ = 2.00 1380 1380 1380 1380 1374 1374 1425 1425 log# 3 2,5log # 3 2.5 1271 1271 1268 1268 1274 1274 1310 1310 log^ 3 2,75log ^ 3 2.75 1230 1230 1230 1230 1233 1233 1263 1263 • log? = 3,0 • log? = 3.0 1190 1190 1190 1190 1192 1192 1216 1216 ' chemická odolností voči vodě Cml 0,1 N H2SO4)'chemical resistance to water Cml 0,1 NH 2 SO 4 ) 0,125 0.125 0,200 0.200 0,075 0.075 0,17 0.17 2 kyselině (mg/100 cm ) 2 acid (mg / 100 cm) 314 314 170 170 1080 1080 290 290 zásadě (mg/100 cm^) base (mg / 100 cm ^) 263 263 300 300 151 151 244 244 index lomu n$ refractive index n $ 1,563 1,563 th most common 1,569 1,569 th most common 1,566 1,566 th most common 1,561 1,561 th most common

Ostatně fyzikálno-chemické parametre sú zrovnatelné s doteraz používaným E - sklom.After all, the physico-chemical parameters are comparable to the E-glass used so far.

Claims (1)

Sklo pre skleněné vlákna, najma na výrobu skleněného vlákna s vysokým indexom lomu, vyznačujúce sa tým, že obsahuje v hmotnostnej koneentrácii 53,00 až 56,40 % oxidu křemičitého, 11,40 až 15,50 % oxidu hlinitého, 3,70 až 5,80 % oxidu boritého, 19,60 až 22,20 % oxidu vápenatého, 1,80 až 2,20 % oxidu horečnatého, 0,95 až 2,90 % oxidu zinočnatého, stopy až 1,00 % oxidu titaničitého a/alebo oxidu železitého, stopy až 1,00 % oxidu sodného a/alebo draselného. ·Glass fiber glass, in particular for the production of glass fiber with a high refractive index, characterized in that it contains 53.00 to 56.40% by weight of silica, 11.40 to 15.50% of alumina, 3.70 to 3.40% by weight. 5.80% boric oxide, 19.60 to 22.20% calcium oxide, 1.80 to 2.20% magnesium oxide, 0.95 to 2.90% zinc oxide, traces up to 1.00% titanium dioxide and / or iron oxide, traces of up to 1.00% sodium and / or potassium oxide. ·
CS879838A 1987-12-27 1987-12-27 Glass for glass fibres CS267322B1 (en)