CS270862B1 - Water-tight diffusion-active substance - Google Patents
Water-tight diffusion-active substance Download PDFInfo
- Publication number
- CS270862B1 CS270862B1 CS876227A CS622787A CS270862B1 CS 270862 B1 CS270862 B1 CS 270862B1 CS 876227 A CS876227 A CS 876227A CS 622787 A CS622787 A CS 622787A CS 270862 B1 CS270862 B1 CS 270862B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- parts
- acrylic acid
- weight
- water
- composition according
- Prior art date
Abstract
Description
(57) Vodotěsná difúzně aktivní hmota je určena pro venkovní i vnitřní povrchové úpravy porézních i hutných podkladů. Je formulována na bázi vodných disperzí syntetických polymerů vinylehlorid-estery kyseliny akrylové o počtu atomů uhlíků C~ až Cg v alkylu radikálu-kyselina akrylová a°na bázi modifikačních přísad sestávajících z dispergátorů pigmentů a plniv, látek usnadňujících zpracování a reologické vlastnosti, z amoniaku, konzervačních prostředků, organických ředidel a látek prodlužujících vysychání, z odpěnovačů a vody. Hmota dále obsahuje mletá minerální plniva, mletý mastek nebo slídu a pigmenty. Tixotropní hmotu lze nanášet natíráním, válečkováním, ponořováním nebo střídáním. Po vyreagování vytváří monoliticky, vodotěsný, neprašný povlak soudržný s podkladem, pružný a houževnatý, s dobrými mechanickými vlastnostmi a s nízkým koeficientem difúze.(57) The waterproof diffusion active material is designed for external and internal surface treatment of porous and dense substrates. It is formulated on the basis of aqueous dispersions of synthetic polymers of vinyl chloride-acrylic acid esters of carbon numbers from C to C8 in alkyl radical-acrylic acid and based on modification additives consisting of dispersants of pigments and fillers, processing aids and rheological properties, of ammonia, preservatives, organic diluents and drying agents, antifoams and water. The composition further comprises ground mineral fillers, ground talc or mica and pigments. The thixotropic composition can be applied by brushing, rolling, dipping or alternating. Once reacted, it forms a monolithic, waterproof, non-dusty coating consistent with the substrate, resilient and tough, with good mechanical properties and low diffusion coefficient.
CS 270 862 B1CS 270 862 B1
Vynález se týká vodotěsné difúzně aktivní hmoty pro tenkovrstvé povrchové úpravy porézních i hutných substrátů formulované na bázi vodných disperzí kopolymeru vinylchloridestery kyseliny akrylové- kyselina akrylová s obsahem karboxylových skupin v polymerním řetězci, minerálních plniv, pigmentů a modifikačních přísad.BACKGROUND OF THE INVENTION The present invention relates to a waterproof diffusion active composition for thin coatings of porous and dense substrates formulated with aqueous dispersions of vinyl chloride-acrylic acid-acrylic acid copolymers containing carboxyl groups in the polymer chain, mineral fillers, pigments and modifiers.
Doposud se pro tenkovrstvé povrchové úpravy používají polymercementové kompozice a hmoty na bázi vodných disperzí syntetických polymerů. Polymercementové hmoty mají vyhovující difúzní charakteristiky, ale nejaou vodotěsné a při zvýšené vlhkosti negativně ovlivňují tepelně izolační vlastnosti podkladů. Mají omezený rozsah barevného ztvárnění a sklon к tvorbě nerovnoměrných odstínů. Tyto nedostatky částečně odstraňují disperzní hmoty, ale mají zase vysoký difúzní odpor, který limituje jejich použití zejména na lehčené podklady. Proto se aplikují převážně na tuhé a hutné podklady nebo se nanášejí ve velmi malých tloušťkách.Until now, polymer-cement compositions and compositions based on aqueous dispersions of synthetic polymers have been used for thin-film coatings. Polymer cement materials have satisfactory diffusion characteristics, but are not waterproof and negatively affect the thermal insulation properties of the substrates at elevated humidity. They have a limited range of color rendering and tend to create uneven shades. These drawbacks partially eliminate the dispersion masses, but have a high diffusion resistance, which limits their use, in particular, to lightweight substrates. Therefore, they are mainly applied to rigid and dense substrates or applied in very small thicknesses.
Uvedené nedostatky odstraňuje vodotěsná difúzně aktivní hmota pro povrchové úpravy obsahující 15,0 až 30,0 dílů minerálních plniv o zrnitosti do 0,5 mm, 2,0 až 10,0 dílů mastku a/nebo slídy, Ю,0 až 25,0 dílů pigmentů, 10,0 až 20,0 dílů vody, 0,2 až 1,0 dílů konzervačních prostředků, případně 0,1 až 0,5 dílů odpěňovačů, vše v hmotových dílech, Jejíž podstata spočívá v tom, že obsahuje v hmotových dílech 15,0 až 50,0 dílů vodné disperze vinylehlorid-estery kyseliny akrylové o počtu atomů uhlíků C^ až Cg v alkylovém radikálu-kyselina akrylová o sušině 40 až 60 % hmot, a o obsahu vinylchloridu 12 až 45 % hmot, a kyseliny akrylové 1,0 až 5,0 % hmot., vztaženo na sušinu polymeru. Dále z 2,5 až 11,0 dílů modifikačních přísad sestávajících z 0,1 až 0,5 dílů dispergátorů pigmentů a plniv, 0,5 až 3,0 dílů solí alkalických kovů kyseliny polyfosforečné o sušině 10 až 30 % hmot., 0,1 až 0,5 dílů koncentrované čpavkové vody, 0,5 až 1,5 dílů tixotropní přísady, 0,5 až 2,0 dílů organických ředidel o teplotě varu nad 120 °C, 0,5 až 2,0 dílů látek prodlužujících vysychání a to jednotlivě nebo ve vzájemné kombinaci.The above-mentioned drawbacks are eliminated by a waterproof diffusion active compound for surface treatment comprising 15.0 to 30.0 parts of mineral fillers with a grain size of up to 0.5 mm, 2.0 to 10.0 parts of talc and / or mica, Ю, 0 to 25.0 parts of pigments, 10.0 to 20.0 parts of water, 0.2 to 1.0 parts of preservatives, or 0.1 to 0.5 parts of antifoams, all in the mass parts, which consists in 15.0 to 50.0 parts by weight of an aqueous dispersion of vinyl chloride-acrylic acid esters having a carbon number of C 4 to C 8 in the alkyl radical-acrylic acid having a dry matter content of 40 to 60% by weight, and a vinyl chloride content of 12 to 45% by weight, and acrylic acid 1.0 to 5.0% by weight, based on the dry weight of the polymer. Further, from 2.5 to 11.0 parts of modifying additives consisting of 0.1 to 0.5 parts of pigment and filler dispersants, 0.5 to 3.0 parts of alkali metal salts of polyphosphoric acid having a dry weight of 10 to 30% by weight. , 1 to 0.5 parts of concentrated ammonia water, 0.5 to 1.5 parts of thixotropic additive, 0.5 to 2.0 parts of organic solvents boiling above 120 ° C, 0.5 to 2.0 parts of extender drying out individually or in combination.
Estery kyseliny akrylové Jsou etyl-, butyl-, nebo 2-etylhexylakrylát.Acrylic acid esters are ethyl, butyl, or 2-ethylhexyl acrylate.
Dispergátory pigmentů a plniv jsou etoxilované vyšší mastné aminy, kvartérní soli etoxilovaných mastných alkoholů o počtu uhlíků C12 až C^ a/nebó alkyl ary 1 sulf on any.The pigment and filler dispersants are ethoxylated higher fatty amines, quaternary salts of ethoxylated fatty alcohols having a carbon number of C 12 to C 14 and / or alkyl aryl sulfonates.
Tixotropní přísady jsou amonné soli hydroxyalkylamoniové estery vodných disperzí karboxylovaných syntetických polymerů a/nebo polyvinylalkohol.Thixotropic additives are ammonium salts of hydroxyalkylammonium esters of aqueous dispersions of carboxylated synthetic polymers and / or polyvinyl alcohol.
Organická ředidla a látky prodlužující dobu zasychání a tuhnutí jsou ze skupiny látek butylglykol, butyldiglykol, butylglykolacetát, butyldiglykolacetát, těžké benziny, benziny s obsahem aromatických sloučenin, metanol, metylbenzylalkohol, dipenten, dekalin, propylenglykol, hexylenglykol a to jednotlivě nebo ve vzájemné kombinaci.Organic diluents and drying and setting time extenders are selected from the group consisting of butyl glycol, butyldiglycol, butylglycol acetate, butyldiglycol acetate, naphtha, aromatic compounds, methanol, methylbenzyl alcohol, dipentene, decalin, propylene glycol, hexylene glycol individually or in combination.
Bylo zjištěno, že film z takové disperze má vysokou vodotěsnost a nízký součinitel difúze. Je odolný vůči alkalické hydrolýze, odolává atmosférickým vlivům a má zvýšenou požární odolnost. Disperzní nízkomolekulární a nízkoviskózní pojivo se dále upravuje mletými minerálními plnivy, pigmenty a modifikačními přísadami na hmotu pro povrchové úpravy s vysokou funkční vodotěsností a s nízkým součinitelem difúze. Optimální plniva se skládají z kombinace mikronizováných, případně povrchově upravených vápenců a nebo křemenných písků o zrnitosti menší než 0,5 mm, v kombinaci s mastkem a nebo se slídou. Modifikační přísady ve vhodné kombinaci umožňují určit výsledné vlastnosti hmoty podle požadavků a předpokládané expozice·It has been found that the film of such a dispersion has a high water-tightness and a low diffusion coefficient. It is resistant to alkaline hydrolysis, resistant to atmospheric influences and has increased fire resistance. The dispersion low-molecular and low-viscosity binder is further treated with ground mineral fillers, pigments and modifying additives to the surface treatment material with high functional waterproofness and low diffusion coefficient. Optimal fillers consist of a combination of micronized or surface-treated limestones and / or quartz sands with a grain size of less than 0.5 mm, in combination with talc or mica. Modifying additives in a suitable combination allow to determine the resulting properties of the mass according to the requirements and the expected exposure ·
Dispergátory na bázi etoxilovaných mastných aminů nebo alkylarylsulfonanů výrazně zlepšují stejnoměrné rozptýlení pigmentů a plniv, soli kyseliny polyfosforečné zlepšují zpracovatelnost směsi, konzervační prostředky eliminují mikrobiologické vlivy, tixotropní přísady upravují reologické vlastnosti hmoty při nanášení a zabraňují stékání a sedimentaci. Volí se ze skupiny polyakrylanů, polyvinylalkoholu, amonných solí karboxylovaných vodných disperzí syntetických polymerů a nebo aminovaných nebo alkanolamoniových esterů karboxylovaných vodných disperzí polymerů.Organická ředidla v malém množství zlepšují fllmotvornou teplotu disperzního pojivá, zvyšují odolnost vůči mrazu a zlepšují rozetíratelnost.Dispersing agents based on ethoxylated fatty amines or alkylarylsulfonates significantly improve uniform dispersion of pigments and fillers, polyphosphoric acid salts improve the processability of the mixture, preservatives eliminate microbiological effects, thixotropic additives modify the rheological properties of the material during application and prevent runoff and sedimentation. It is selected from the group of polyacrylanes, polyvinyl alcohol, ammonium salts of carboxylated aqueous dispersions of synthetic polymers, or amine or alkanolammonium esters of carboxylated aqueous dispersions of polymers. Organic solvents in small amounts improve the film-forming temperature of the dispersion binder, increase frost resistance and improve spreadability.
CS 270 862 BisCS 270 862 Bis
Při tendenci к pěnění se ke hmotě přidávají odpěňovače, zejména při provádění nástřiku.In the foaming tendency, antifoams are added to the composition, especially when spraying.
Jednotlivé přísady se mohou použít samostatně nebo ve vzájemné kombinaci.The individual additives may be used alone or in combination.
Vodotěsná difúzně aktivní hmota podle vynálezu má vysokou stabilitu při *klování a při zpracování, odolává v kapalném stavu nízkým teplotám a dlouhodobě nemění svoje vlastnosti. Nanáěí se na podklady natíráním, stříkáním, válečkováním nebo ponořováním. Vytváří v krátké době film s vysokou mechanickou odolností proti poškození, otěru a obrusu za sucha i za mokra. Vyreagovaná vrstva hmoty Je vodotěsná, půdorysná a vytváří účinnou ochranu podkladům při dobré estetické úrovni. Hmotu podle vynálezu lze použít pro všechny druhy podkladů pro interiéry i pro ejeteriéry.The waterproof diffusion active composition according to the invention has high stability during pecking and processing, resists low temperatures in the liquid state and does not change its properties in the long term. It is applied to substrates by painting, spraying, rolling or dipping. Creates a film with high mechanical resistance to damage, abrasion and abrasion in dry and wet conditions in a short time. Reacted material layer It is waterproof, ground plan and creates effective protection of substrates at a good aesthetic level. The composition according to the invention can be used for all kinds of substrates for interiors and ejeterriers.
Příklad 1Example 1
Dokonale ae zhomogenizuje v hmotových dílech 14,6 dílů vody, 0,1 dílu dinaftylmetan’ dieulfonanu sodného, 1,0 díl trimetafosfořečnanu sodného o sušině 30 % hmot., 0,5 dílů čpavkové vody, 0,8 dílů amonné soli kyseliny polyakrylové o sušině 20 % hmot., 0,6 dílů těžkého benzinu o teplotě varu 160 °C, 1,5 dílů butylglykolu, 0,5 dílů konzervačního prostředku, 17,0 dílů křemenného písku o změní do 0,2 mm, 8,0 dílů mletého mastku, 8,0 dílů titanové běloby a 5,0 dílů pigmentu. Po promíchání se к pastovité hmotě přidá 41,0 dílů vodné disperze vinylchlorid-etylakrylát-kyselina akrylová o sušině 45 % hmot.It perfectly homogenizes in parts by weight 14.6 parts of water, 0.1 part of sodium dinaphthylmethane disulphonate, 1.0 part of sodium trimetaphosphate with dry matter 30% by weight, 0.5 parts of ammonia water, 0.8 parts of polyacrylic acid ammonium salt o 20 parts by weight, 0.6 parts of naphtha 160 ° C, 1.5 parts of butyl glycol, 0.5 parts of preservative, 17.0 parts of quartz sand to 0.2 mm, 8.0 parts ground talc, 8.0 parts titanium dioxide and 5.0 parts pigment. After mixing, 41.0 parts of an aqueous vinyl chloride-ethyl acrylate-acrylic acid dispersion having a dry weight of 45% by weight are added to the pasty mass.
a o obsahu 25 % vinylchloridu a 1,5 % kyseliny akrylové vztaženo na sušinu kopolymeru a 0,4 díly odpěňovače. Po dokonalé homogenizaci vznikne tixotropní stabilní hmota, vhodná pro nanášení natíráním, válečkováním a po zředění 5 % hmot, vody i stříkáním a ponořováním. Hmota má velmi dobrou krycí schopnost, nesedimentuje, filmotvomá teplota je při *4 °C, má dobré tixotropní vlastnosti a Je dlouhodobě beze změn skladovatelná. Po nanesení na podklady vytváří během 30 min povrchovou úpravu, která při tloušťce 1 mm má přídržnost к podkladům nad 1,0 MPa, difúzi 0,3 m, vodotěsnost 0,1 m“2, otěr za mokra 60 min a protažení 400 %.and having a content of 25% vinyl chloride and 1.5% acrylic acid based on the dry weight of the copolymer and 0.4 parts of an antifoam. After perfect homogenization, a thixotropic stable mass is obtained, suitable for application by brushing, roller coating and after dilution with 5% by weight, water, spraying and dipping. The material has a very good hiding power, does not sediment, the film-forming temperature is at * 4 ° C, it has good thixotropic properties and is shelf-stable for a long time. After application to the substrates, it forms within 30 minutes a surface treatment which, at a thickness of 1 mm, has adhesion to substrates above 1.0 MPa, diffusion of 0.3 m, water resistance of 0.1 m 2 , wet abrasion of 60 min and elongation of 400%.
Příklad 2 .Example 2.
Dokonale se zhomogenizuje 15,0 dílů vody, 1,8 dílů hexametafosforečnanu sodného o sušině 15 % hmot., 0,3 díly čpavkové vody, 0,3 díly konzervačního prostředku, 1,0 díl polyakrylanu amonného a/nebo polyvinylalkoholu o sušině 16 % hmot., 1,0 díl směsi benzinu a metanolu (1 í 1), 1,0 díl butyldiglykolu, 0,2 dílů odpěňovače, 0,2 díly etoxilovaného mastného aminu, 25,0 dílů mletého vápence o zrnitosti do 0,5 mm, 6,0 dílů mleté slídy, 20,0 dílů směsi práškových pigmentů a 28,0 dílů vodné disperze vinylchlorid-butylakrylátkyselina akrylová o sušině 50 % hmot, obsahu 43 % hmot, vinylchloridu a 4,0 % hmot, kyseliny akrylové vztaženo na sušinu polymeru, vše v hmotových dílech. Po dokonalé homogenizaci vznikne tixotropní hmota, která má po vyreagování přídržnost к podkladům 0,9 MPa, difúzi 0,2 m, vodotěsnost 0,1 m“2. Otěr za mokra 60 min, objemovou stálost a vynikající odolnost vůči povětrnostním vlivům.15.0 parts of water, 1.8 parts of sodium hexametaphosphate 15% by weight, 0.3 parts of ammonia water, 0.3 parts of preservative, 1.0 part of ammonium polyacrylate and / or 16% polyvinyl alcohol are perfectly homogenized by weight, 1.0 part of a mixture of petrol and methanol (1 l), 1.0 part of butyldiglycol, 0.2 parts of antifoam, 0.2 parts of ethoxylated fatty amine, 25.0 parts of ground limestone with a grain size of up to 0.5 mm , 6.0 parts of ground mica, 20.0 parts of a mixture of powder pigments and 28.0 parts of an aqueous dispersion of vinyl chloride-butyl acrylate acrylic acid with a dry weight of 50% by weight, a content of 43% by weight, vinyl chloride and 4.0% by weight, acrylic acid polymer, all in mass parts. After perfect homogenization, a thixotropic mass is obtained which, after reacting, has a adhesion to the substrates of 0.9 MPa, a diffusion of 0.2 m, a water-tightness of 0.1 m 2 . Wet abrasion 60 min, volume stability and excellent weathering resistance.
Příklad 3Example 3
Dokonale se zhomogenizuje v hmotových dílech 13,0 dílů vody, 2,5 dílů hexametafosforečnanu sodného o sušině 10 % hmot., 0,4 díly kvartérní soli etoxilovaného aminu mastných alkoholů a obsahu uhlíků C12 až C15, 0,2 díly čpavkové vody, 0,2 díly fungicidu, 1,3 díly amonné soli kyseliny poakrylátmětakrylové o sušině 20 % hmot., 1,4 díly metylbenzylalkoholu, 0,7 dílů butylglykolacetátu, 0,3 díly odpěňovače, 20,0 dílů mletého povrchově upraveného vápence, 5,0 dílů mletého mastku, 20,0 dílů titanové běloby a 35,0 dílů vodní disperze vinylchlorid-2-etylhexalakrylát-kyselina akrylová o sušině 47 % hmot, a o obsahu vinylchloridu 15 % hmot, a kyseliny akrylové 1,0 % hmot, vztaženo na sušinu polymeru.It is perfectly homogenized in parts by weight of 13.0 parts of water, 2.5 parts of sodium hexametaphosphate with a dry weight of 10% by weight, 0.4 parts of a quaternary salt of ethoxylated amine of fatty alcohols and C 12 to C 15 carbons, 0.2 parts of ammonia water , 0.2 parts of fungicide, 1.3 parts of ammonium salt of acrylic acid acrylic acid with a dry weight of 20% by weight, 1.4 parts of methylbenzyl alcohol, 0.7 parts of butyl glycol acetate, 0.3 parts of antifoam, 20.0 parts of ground limestone ground, 5 0 parts of ground talc, 20.0 parts of titanium dioxide and 35.0 parts of a water dispersion of vinyl chloride-2-ethylhexalacrylate-acrylic acid with a dry matter content of 47% by weight, and a vinyl chloride content of 15% by weight, and acrylic acid of 1.0% by weight to the dry matter of the polymer.
* Vzniklá tixotropní hmota má po nanesení na podklady vodotěsnost 0,1 m2, difúzi 0,35 m>* The resulting thixotropic material has a waterproofness of 0,1 m 2 , diffusion 0,35 m>
otěr za mokra 60 min, přídržnost к podkladům 1 ,2 MPa, tažnost 960 % a odolává účinkům vyšších teplot, je samozhášivá a při expozici přímému ohni neovlivňuje šíření ohně a ani tento nepodporuje.wet abrasion 60 min, adhesion to substrates 1, 2 MPa, elongation 960% and withstands the effects of higher temperatures, it is self-extinguishing and does not affect the propagation of fire or support it when exposed to direct fire.
CS 270 862 B1CS 270 862 B1
PŘEDMĚT VYNÁLEZUSUBJECT OF THE INVENTION
Claims (5)