CZ197997A3 - Prostředek k zabránění elektrostatického nabíjení pneumatik - Google Patents

Prostředek k zabránění elektrostatického nabíjení pneumatik

Info

Publication number
CZ197997A3
CZ197997A3 CZ971979A CZ197997A CZ197997A3 CZ 197997 A3 CZ197997 A3 CZ 197997A3 CZ 971979 A CZ971979 A CZ 971979A CZ 197997 A CZ197997 A CZ 197997A CZ 197997 A3 CZ197997 A3 CZ 197997A3
Authority
CZ
Czechia
Prior art keywords
carbon black
particle size
alcohol
conductive
retort
Prior art date
Application number
CZ971979A
Other languages
English (en)
Inventor
Herbert Wagner
Original Assignee
Rhein Chemie Rheinau Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rhein Chemie Rheinau Gmbh filed Critical Rhein Chemie Rheinau Gmbh
Publication of CZ197997A3 publication Critical patent/CZ197997A3/cs

Description

Oblast techniky
Vynález se týká vnějšího separačního prostředku pro pneumatiky.
Dosavadní stav techniky
Pneumatiky, které místo sazí obsahují určitá silikátová plnidla, mají vynikající jízdní vlastnosti a odolnost proti otěru. Takové pneumatiky bez sazí - označované též green tires - máji ale sklon k tomu, aby se elektrostaticky nabíjely, protože jejich elektrický odpor je značně vyšší a tedy jejich elektrická vodivost je značně nižší než u pneumatik se sazemi. Elektrostatické nabíjení pneumatik a - při vysokém odporu - zabránění odvedení elektrických nábojů z vozidla do země může vést ke značným poruchám a ohrožení, když takový elektrický náboj odteče do země vodivým spojením. Takové spojení může vzniknout nastupující nebo vystupující osobou, nebo při vložení tankovací hadice.
Pneumatiky se sazemi mají obecně odpor asi 10^ Ohmů, měřeno od vrcholu pláště k patce. Pro toto měření existuje předběžný předpis, uvedený ve směrnici VDK 110. Podle něj je pneumatika elektrostaticky účinná třídy I, pokud má svodový odpor pod 10Ohmů.
Pneumatiky bez sazí tuto zkoušku nesplňují, jejich elektrický odpor je asi ΙΟ^θ Ohmů. Jak bylo výše vysvětleno, může to vést ke značným potížím. Proto je potřeba nějaké metody ke snížení elektrického odporu.
Při tvarování a vulkanizaci pneumatik se na povrch surových pneumatik nanáší roztok, který po zaschnutí vytváří film, jímž se zabraňuje připečení pneumatiky k vulkanizační formě. Rozlišuje se vnější separační prostředek a vnitřní separační prostředek a to vždy pro vnější a vnitřní stranu pneumatiky. Proto jsou zapotřebí dva separační prostředky, protože vnější a vnitřní strana pneumatiky jsou tvořeny různými materiály, případně mají při vulkanizaci různé požadavky na separační prostředek. Četné vnější separační prostředky jsou vyrobeny na základě organických rozpouštědel. Je však značnou výhodou, použít vnější separační prostředek na basi vody. Takový prostředek je popsán v patentu NSR 43 43 818. Na takový separační prostředek jsou kladeny dosti značné nároky. Musí působit na oddělení od formy, současně ale nesmí ovlivnit spojení různých částí pneumatiky, například kostry a běhounu. Optimální vnější separační prostředek však vedle toho plní ještě další funkce. Odvádí vzduchové bublinky, zachycené mezi formou a povrchem pneumatiky, které by jinak mohly vyvolat nestejnoměrnou vulkanizaci, a zlepšuje tečení ještě nevulkanizovaného kaučuku tak, aby forma byla úplně zaplněna. Konečně separační prostředek pečuje o opticky odpovídající vzhled hotové pneumatiky.
Podstata vynálezu
Předložený vynález vychází z poznatku, že je možné modifikovat vodné vnější separační prostředky tak, aby dodatečně snižovaly elektrický odpor na hodnotu okolo 10^ Ohmů.
Předmětem vynálezu je vodný vnější separační prostředek pro výrobu pneumatik, který obsahuje ether mastného alkoholu a polyglykolu a elektricky vodivé saze. Ether mastného alkoholu a polyglykolu (dále též zkráceně ether} a saze vyvolávají positivní synergický efekt. Ether je výhodně reakční produkt alkylalkoholu se 16 až 18 atomy uhlíku a ethylenglykolu nebo propylenglykolu, kde na jeden mol alkoholu se 16 až 18 atomy uhlíku připadá 5 až 80 molů ethylenglykolu nebo propylenglykolu. U sazí se jedná o vodivé retortové saze s částicemi o středním průměru od 20 do 30 nm. Vnější separační prostředek obsahuje asi 1 až 20 % hmotnostních etheru a 3 až 15 % hmotnostních uvedených sazí. Používá se obecně v takovém množství, že na jedné osobní pneumatice je asi 12 až 30, výhodně 15 až 25 g separační ho prostředku, což odpovídá 0,5 až 5 g etheru a 0,45 až 5 g retortových sazí.
Všechny dosavadní pokusy o zavedení uvedených přísad do směsí na běhouny, aby se dosáhlo požadovaných hodnot vodivostí, nepřinesly úspěch, protože se tím zhoršila kvalita pneumatik.
Vnější separační prostředek má výhodně následující složení:
Podíly v % hmotnostních
3-20 amorfní práškový křemičitý gel s 3-70 % krystalické vody, výhodně se 65 %, střední velikost částic 15 až 30 gm, výhodně 20 gm
0,2-0,5 pyrogenní kyselina křemičitá, střední velikost
částic 8-20 nm, výhodně 12 nm
1-20 retortové saze (prášek, vodivé), střední velikost částic 20-30 nm (může být nahrazeno disperzí sazí);
nebo
4-70 disperze retortových sazí (vodivých) 25 % retortových sazí, střední velikost částic 20-30 nm 6 % neiontového smáčedla 69 % vody
0,3-15 (počítáno jako SiOg) křemičitý sol 15-20 % hmotnostních Si02 o povrchu 50-500 m2/g, výhodně 200 m2/g, průměr částic 6-40 nm
0-8 25 % disperze polyethylenu (jako pojivo)
1-20 etheru mastného alkoholu a polyglykolu, výhodně alkoholu s 16-18 atomy uhlíku + 5 mol EO/mol až alkoholu s 16 až 18 atomy uhlíku + 80 mol EO/mol (neionogenní tensid pro vytvoření vodivosti a jako dispergační prostředek a pojivo)
0,2-10 ligninsulfonát vápenatý (smáčedlo, dispergační prostředek a poj ivo)
0,1-3 sodná sůl methyltauridu mastné kyseliny (smáčedlo, dispergační prostředek a pojivo)
0-5 odpěňovadlo
0,01-0,05 biocid
30-80 voda.
Zvláště výhodný produkt pro povrstvení surových pneumatik má následuj ící složení :
Podíly % hmotnostní (obecně) (speciálně)
Plnidla
3-20
8,75 amorfní práškový křemičitý gel s asi 65 % krystalické vody, střední velikost částic 20 gm (Daraclar 920)
0-2
0,5 pyrogenní kyselina křemičitá, střední velikost částic 12 nm (Aerosil 200)
1-20
4,5* retortové saze (vodivé) (Prlntex 3 nebo Printex V) nebo
4-70
19* 25% disperze retorotových sazí (vodivých) (Derussol AN 1/25 L)
0,3-15 (počítáno jako SÍO2) křemičitý sol 15-20 hmotnostních SiO2 o povrchu 50-500 m /g, 9 o výhodně 200 m /g, střední průměr částic
6-40 nm
0-8 4 25% disperze polyethylenu (Permaid DI)
Antistatium a dispergační činidlo
1-20 7,25* ether mastného alkoholu s polyglykolem (alkohol s 16 až 18 atomy uhlíku + 6 mol EO/Mol) (Rhenosin RC 100)
Smáčecí a dispergační prostředek
0,2-10 2 ligninsulfonát vápenatý
0,1-3 1,5 sodná sůl methyltauridu mastné kyseliny
Odpěňovadlo
0,5 0,15 triisobutylfosfát (Etingal A)
Biocid
0,01-0,05 0,02 1,2-benzisothiazolin-3-on (Proxel GXL)
Voda
30-80 53,83 voda
Elektrostatická účinnost spočívá v podstatě na etherech mastného alkoholu s glykolem a na vodivých retortových
Ί sazích, které spolu vytvářejí positivní synergický efekt.
Příklady provedení vynálezu
Příklad 1
Složení separačního prostředku
Hmotnostní díly
62,03 voda
0,10 Kelzan D
0,70 sodná sůl methyltauridu mastné kyseliny
2,00
8,75
0,50
7,00
4,00
7,25
7,50
0,2
0,15 (Hostapon CT-pasta) ligninsulfonát vápenatý amorfní prášek křemičitého gelu % krystalické vody, střední velikost částic 20 pm (Daraclar 920) pyrogenní kyselina křemičitá, o průměrné velikosti částic 12 pm (Aerosil 200) retorotové saze (Printex L) % disperze polyethylenu (Permaid DI) ether mastného alkoholu a polyglykolu (alkohol* s 16 až 18 atomy uhlíku/6 mol-ethylenglykolu/mol) (Rhenosin RC 100) křemičitý sol 30 % hmotnostních, SiC>2
200 m^/g, velikost částic 7-15 nm (Levasil 200 A 10)
1,2-benzisothiazolin-3-on (Proxel GXL) triisobutylfosfát (Etingal A)
Výroba
Předloží se voda a pak se přidávají jedna po druhé účinné součásti ve výše uvedeném pořadí a vždy se 10-15 minut míchá. Pak se získaná suspenze prolije sítem o velikosti ok 200 μπι. Pak je přímo stříkatelná.
Použití
Při výrobním pokusu bylo asi 50.000 pneumatik pro osobní auta, jejichž běhouny byly vyrobeny se silikátovými plnidly, obvyklým způsobem před vulkanizací nastříkáno tímto přípravkem, při čemž se na pneumatiku použilo 29 g roztoku, což odpovídá asi 6-7 g pevných látek. Všechny pneumatiky měly elektrický odpor v oblasti 10^ Ohmů.
Příklad 2
Stříkací roztok pro povrchové ošetření vytlačovaných běhounů
Podíly % hmotnostní
1-15 retortové saze (práškové, vodivé), střední velikost částic 20-30 nm nebo
4-50 disperze retortových sazí (vodivých), 25 % sazí, % neionogenního smáčedla, 69 % vody
1-5 etheru mastného alkoholu a polyglykolu, výhodně alkohol s 16-18 atomy C + 6 mol EO/mol až alkohol s 16-18 atomy C + 80 mol EO/mol křemičitý sol, 15-50 % hmotnostních Si02
0,5-15
0,01-0,2
0,01-0,1
50-80 (počítáno jako S1O2), specifický povrch
50-500 m^/g, střední velikost částic 40 nm, výhodně 7-15 nm. Křemičitý sol je pojivo odolné vůči chladicí vodě.
polysacharid, zahušťovadio biocid voda
Stříkacím roztokem se povlékaji místo surových pneumatik extrudované běhouny, které byly vyrobeny se silikátovými plnidly. S nimi vyrobené pneumatiky měly elektrický odpor v oblasti okolo 10^ Ohmů.

Claims (5)

  1. náToky
    1. Vodný vnější separační prostředek pro pneumatiky, vyznačující se tím, že obsahuje ether mastného alkoholu a polyglykolu a vodivé saze.
  2. 2. Vodný vnější separační prostředek podle nároku 1, vyznačující se tím, že má složení v % hmotnostních :
  3. 3- 20 amorfní práškový křemičitý gel s 3-70 % krystalové vody, střední velikost částic 15 až 30 pm,
    0,2-0,5 pyrogenní kyselina křemičitá, střední velikost částic 8-20 nm.
    1-20 retortové saze (prášek, vodivé), střední velikost částic 20-30 nm (může být nahrazeno disperzí sazí);
    nebo
  4. 4- 70 disperze retortových sazí (vodivých)
    25 % retortových sazí, střední velikost částic 20-30 nm
  5. 6 % neionogenního smáčedla 69 % vody
    0,3-15 (počítáno jako S1O2) křemičitý sol 15-20 % hmotnostních SiO2 o povrchu
    50-500 m^/g, výhodně 200 m^/g průměr částic 6-40 nm, výhodně 7-15 nm
    0-8 25% disperze polyethylenu
    1-20 ether mastného alkoholu a polyglykolu, výhodně alkoholu s 16-18 atomy uhlíku + 5 mol EO/mol až alkoholu s 16 až 18 atomy uhlíku + 80 mol EO/mol
    0,2-10 ligninsulfonát vápenatý (dispergační prostředek)
    0,1-3 sodná sůl methyltauridu mastné kyseliny (dispergační prostředek)
    0-5 odpěňovadlo
    0,01-0,05 biocid
    30-80 voda
    3. Vodný vnější separační prostředek podle nároku 1, vyznačující se tím, že má složení v % hmotnostních :
    1-15 retortové saze (prášek, vodivé), střední velikost částic 20-30 nm nebo
    4-50 disperze retortových sazi (vodivých) 25 % retortových sazí,
    6 % neionogenního smáčedla 69 % vody
    1-6 ether mastného alkoholu a polyglykolu, výhodně alkoholu s 16-18 atomy uhlíku + 6 mol EO/mol až alkoholu s 16 až 18 atomy uhlíku + 80 mol EO/mol
    0,5-15 křemičitý sol, 15-50 % hmotnostních SiO2 (počítáno jako S1O2), specifický povrch 50-500 m^/g, střední velikost částic 40 nm, výhodně 7-15 nm. Křemičitý sol je pojivo odolné vůči chladicí vodě.
    polysacharid, zahušťovadlo
CZ971979A 1996-06-24 1997-06-23 Prostředek k zabránění elektrostatického nabíjení pneumatik CZ197997A3 (cs)