DD240318A3 - METHOD FOR PRODUCING A PHOTO-SENSITIVE MATERIAL - Google Patents
METHOD FOR PRODUCING A PHOTO-SENSITIVE MATERIAL Download PDFInfo
- Publication number
- DD240318A3 DD240318A3 DD14527070A DD14527070A DD240318A3 DD 240318 A3 DD240318 A3 DD 240318A3 DD 14527070 A DD14527070 A DD 14527070A DD 14527070 A DD14527070 A DD 14527070A DD 240318 A3 DD240318 A3 DD 240318A3
- Authority
- DD
- German Democratic Republic
- Prior art keywords
- photosensitive
- suspension
- layer
- image
- producing
- Prior art date
Abstract
Patentanspruch 1: Verfahren zur Herstellung eines fotoempfindlichen Materials durch Aufbringen einer fotoempfindlichen Zinkoxidbindemittelsuspension mit linear kolloidalen Cellulosenitraten auf ein leitfähiges Trägermaterial für die randeffektfreie Bildaufzeichnung elektrostatischer Reproduktionsverfahren, dadurch gekennzeichnet, dass die fotoempfindliche Suspension auf den sich in Schräglage bewegenden Schichtträger aufgebracht und in dieser Lage getrocknet wird. Fig.Claim 1: A process for the preparation of a photosensitive material by applying a photosensitive Zinkoxidbindemittelsuspension with linear colloidal cellulose nitrates on a conductive support material for edge-free imaging of electrostatic reproduction methods, characterized in that the photosensitive suspension is applied to the moving in inclined layer support and dried in this position , FIG.
Description
Hierzu 1 Seite ZeichnungFor this 1 page drawing
Die Erfindung betrifft ein Verfahren zur Herstellung eines fotoempfindlichen Materials durch Aufbringen einerfotoempfindlichen Schicht auf ein leitfähiges Trägermaterial für die randeffektfreie Bildaufzeichnung elektrostatischer Reproduktionsverfahren.The invention relates to a method of producing a photosensitive material by applying a photosensitive layer to a conductive substrate for edge-free image recording of electrostatic reproduction methods.
Nach den bekannten elektrostatischen Bildaufzeichnungsverfahren können Reproduktionen von Bildvorlagen dadurch erzeugt werden, daß fotoempfindliche Materialien durch Aufsprühen von Ladungsträgern elektrisch aufgeladen und anschließend einer der gewünschten Abbildung entsprechenden Belichtung ausgesetzt werden, wobei die Ladungen wegen der durch die Belichtung hervorgerufenen Verringerung des elektrischen Widerstandes des fotoempfindlichen Aufnahmematerials an den belichteten Stellen der Schicht abfließen und an den unbelichteten Stellen verbleiben. Die latente bildmäßige Ladungsverteilung wird durch Aufbringen eines farbigen Pulvers, des Toners, sichtbar. Das auf diese Weise hergestellte elektrostatische Bild wird in üblicher Weise entwickelt und fixiert oder auf ein anderes Aufzeichnungsmaterial übertragen und dort fixiert.According to the known electrostatic image recording methods, reproductions of image forms can be produced by electrically charging photosensitive materials by spraying charge carriers and then exposing them to an exposure corresponding to the desired image, the charges being due to the reduction in electrical resistance of the photosensitive recording material caused by the exposure drain the exposed areas of the layer and remain at the unexposed areas. The latent image-wise charge distribution becomes visible by the application of a colored powder, the toner. The thus prepared electrostatic image is conventionally developed and fixed or transferred to another recording material and fixed there.
Bekanntlich bereitet es besondere Schwierigkeiten, relativ große Bildflächen latenter Ladungsbilder und vor allem ihr Zentrum homogen durch Tonerteilchen einzufärben. Da im Inneren einer relativ großflächigen Bildstelle trotz konstanter Beleuchtungsstärke das elektrische Feld wesentlich schwächer ausfällt als das am Rande, haften aufgebrachte Tonerteilchen vorwiegend in den Randzonen. Dieser Randeffekt tritt bei lichtempfindlichen Schichten mit mikroskopisch homogener Oberfläche sehr stark in Erscheinung, da die elektrische Feldstärke nur an den Grenzen eines entsprechenden Belichtungsgradientenstark genug ist, die Tonerteilchen mit ihrem elektrischen Feld anzuziehen.It is known that it is particularly difficult to color relatively large image areas of latent charge images and above all their center homogeneously by toner particles. Since, in the interior of a relatively large area of the image, despite the constant illuminance, the electric field is much weaker than that at the edge, applied toner particles adhere predominantly to the edge zones. This edge effect is very pronounced in photosensitive layers with a microscopically homogeneous surface, since the electric field strength is strong enough only at the boundaries of a corresponding exposure gradient to attract the toner particles with their electric field.
Aus diesem Grunde erfahren die Umrisse der auf belichteten Flächen verschiedener Beleuchtungsstärke eine wesentlich dichtere Färbung als das Innere dieser Flächen.For this reason, the outlines of illuminated areas of different illuminance are much denser in color than the interior of these areas.
Es sind bereits verschiedene Verfahren bekannt, den störenden Randeffekt bei diesen Reproduktionsverfahren zu beseitigen.Various methods are already known to eliminate the disturbing edge effect in these reproduction methods.
Es ist beispielsweise bekannt, während des Belichtungsvorganges zwischen Original und fotoempfindlicher Schicht des Aufnahmematerials ein optisches Raster einzufügen, um ein rasterförmiges Bild, d. h. ein in viele kleine Flächen aufgeteiltes Bild, zu erhalten.For example, it is known to insert an optical raster between the original and the photosensitive layer of the recording material during the exposure process to form a raster-shaped image, i. H. to get a split into many small areas image.
Weiterhin ist bekannt, den Randeffekt dadurch zu unterdrücken, daß eine fotoempfindliche Schicht verwendet wird, die neben Fotoleitern fotochemisch inerte, organische oder anorganische Stoffe enthält, die in der Form eines unregelmäßigen Rasters in der Schicht selbst verteilt sind und auch den Zweck verfolgen, die relativ großen Bildflächen in mehrere kleine aufzuspalten.Furthermore, it is known to suppress the edge effect by using a photosensitive layer which photochemically inert next photoconductors, organic or inorganic substances which are distributed in the form of an irregular grid in the layer itself and also pursue the purpose of relative split large image areas into several small ones.
In einem anderen bekannten Verfahren bedient man sich mehrerer mit Vorspannung betriebener Magnetbürsten während des Entwicklungsvorganges.In another known method, one uses a plurality of bias magnetic brush during the development process.
Die meist angewandte Methode, die Erscheinungen des Randeffektes zu mildern, ist die zusätzliche Anordnung einer Entwicklungselektrode in geringer Entfernung von der Oberfläche des fotoempfindlichen Materials, um nicht nur große Feldstärken in den Randzonen der einzelnen Bildflächen zu erzeugen, sondern auch im Zentrum großflächiger Bildstellen homogene Felder entstehen zu lassen, die eine gleichmäßige Tönung gleich hell belichteter Flächen ermöglichen.The most commonly used method of mitigating the phenomena of edge effect is the additional placement of a development electrode a short distance from the surface of the photosensitive material, not only to produce large field strengths in the peripheral areas of the individual image areas, but also homogeneous fields in the center of large area image areas to give rise to a uniform tint equal brightly illuminated surfaces.
Außerdem ist bekannt, daß makromolekulare Stoffe mit Korngrößen zwischen 1 und 5μ.Γη, die in fotoempfindlichen Polymeren dispergiert sind, die Entstehung des Randeffektes teilweise verhindern. Solche makromolekularen Stoffe sind beispielsweise Cellulose, Stärke, Gelatine, Polyäthylen, Tonerde.In addition, it is known that macromolecular substances with particle sizes between 1 and 5μ.Γη, which are dispersed in photosensitive polymers, partially prevent the formation of the edge effect. Such macromolecular substances are, for example, cellulose, starch, gelatin, polyethylene, alumina.
Weiterhin ist bekannt, durch Aufrauhen sowohl der fotoempfindlichen Oberfläche als auch des leitenden Schichtträgers denFurther, by roughening both the photosensitive surface and the conductive substrate, it is known
störenden Randeffekt zu beseitigen. .eliminate disturbing edge effect. ,
Allen vorgenannten bekannten Verfahren, den störenden Randeffekt zu unterdrücken, haften bedeutende Nachteile an. Das-Einschalten von Rastern im Belichtungsprozeß oder eine Rasterstruktur erzeugende Stoffbeimengung oder das Aufrauhen sowohl der'Oberfläche als auch des Schichtträgers des fotoempfindlichen Materialssind zeitraubend, umständlich und mitunter sehr kostspielig. Ebenso wirkt sich das Dispergieren von fotochemisch inerten, organischen oder anorganischen Stoffen in die fotoempfindliche Schicht nachteilig auf einen zeitsparenden, unkomplizierten Produktionsfluß der Schichtherstellung aus undAll the aforementioned known methods to suppress the disturbing edge effect adhere to significant disadvantages. Turning on grids in the exposure process, or patterning fabric addition or roughening of both the surface and the support of the photosensitive material is time consuming, cumbersome, and sometimes very costly. Likewise, the dispersing of photochemically inert, organic or inorganic substances into the photosensitive layer has a disadvantageous effect on a time-saving, uncomplicated production flow of the layer preparation and
steigert die Kosten. -increases the costs. -
Der Zweck der Erfindung besteht darin, den bisher nur mit einem relativ hohen Aufwand an zusätzlichem Material und speziellen Geräten vermeidbaren Randeffekt, der bei elektrostatischer Reproduktion von Bildvorlagen auftritt, mit einfachen Mitteln sicherThe purpose of the invention is the previously avoided only with a relatively high cost of additional material and special equipment edge effect that occurs in electrostatic reproduction of image templates, with simple means safe
zu beseitigen. "to eliminate. "
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren anzugeben, das die Herstellung eines elektrostatischen Aufzeichnungsmateriais mit einwandfreier Wiedergabe geschlossener Flächen ohne Randeffekt bei gleichzeitig guter Wiedergabe von Strichvorlagen im Reproduktionsprozeß ermöglicht.The invention has for its object to provide a method which allows the production of an electrostatic recording Materiais with perfect reproduction of closed areas without edge effect with good playback of line art in the reproduction process.
Erfindungsgemäß wird die Aufgabe dadurch gelöst, daß eine fotoempfindliche Zinkoxidbindemittelsuspension mit linearkolloidalen Cellulosenitraten als aktives Bindemittel auf den sich in Schräglage bewegenden Schichtträger aufgebracht wird und daß der beschichtete Schichtträger so lange in Schräglage verbleibt, bis durch Trocknung innerhalb der Schicht keine gegenseitigen Molekularbewegungen der Schichtkomponenten mehr stattfinden.According to the invention the object is achieved in that a photosensitive zinc oxide binder suspension with linear colloidal cellulose nitrate is applied as an active binder on the moving in oblique layer carrier and that the coated substrate remains in an inclined position until no mutual molecular movements of the layer components take place by drying within the layer ,
In vorteilhafter Ausgestaltung der erfindungsgemäßen Lösung wird die fotoempfindliche Zinkoxidbindemittelsuspension im tiefsten Punkt der sich bewegenden, gegebenenfalls in Länge und eingeschlossenem Winkel veränderbare Schichtträgermaterialbahn aufgebracht.In an advantageous embodiment of the solution according to the invention, the photosensitive zinc oxide binder suspension is applied at the lowest point of the moving, optionally in length and trapped angle changeable Schichtträgermaterialbahn.
Der Vorteil der Erfindung liegt in der besonders großen Wirtschaftlichkeit, mit der das erfindungsgemäße Verfahren gegenüber bisher bekannten Methoden der Randeffektunterdrückung anzuwenden ist, da keine zusätzlichen Instrumente, Gerätschaften oder Vorrichtungen außer den für den herkömmlichen Beschichtungsprozeß benötigten erforderlich werden. Außerdem wirkt sich das erfindungsgemäße Verfahren nicht nachteilig auf die Produktionskosten aus, da keine zusätzlichen Substanzen der fotoempfindlichen Schicht zugesetzt werden müssen.The advantage of the invention lies in the particularly high efficiency with which the method according to the invention is to be used in comparison to hitherto known methods of edge effect suppression, since no additional instruments, equipment or devices are required other than those required for the conventional coating process. In addition, the inventive method does not adversely affect the production costs, since no additional substances of the photosensitive layer must be added.
Die Erfindung wird nachstehend an einem Ausführungsbeispiel näher erläutert.The invention will be explained in more detail using an exemplary embodiment.
Die zugehörige Zeichnung zeigt ein Schema der Auftragvorrichtung.The accompanying drawing shows a schematic of the applicator.
Es wird zunächst eine Suspension aus folgenden Komponenten zusammengestellt:A suspension of the following components is first compiled:
20g Zinkoxid . .20g zinc oxide. ,
10ml einer Lösung, in der auf 100g Lösung folgende Komponenten entfallen:10ml of a solution in which the following components are dispensed on 100g solution:
16g Collodiumwolle16g collodion wool
10g Cyclohaxanon-Formaldehyd^Harz 10 g of cyclohaxanone-formaldehyde ^ resin
. 4g Dibutylphthalat, 4 g of dibutyl phthalate
6g Meladurol6g Meladurol
35 g Isoamylacetat35 g of isoamyl acetate
3,5g Leunasolvan ' " ' ·,3,5g Leunasolvan '"' ·,
1OgToIuOl1OgToIuOl
4g Butanol ·4g butanol ·
2,3g Butylacetat2.3 g of butyl acetate
0,4g Methylcyclohexanon0.4 g of methylcyclohexanone
3gÄthylglykol ' .3g ethylglycol '.
5,8g Spezialbenzin 5.8g special gasoline
20 bis 50ml Methanol (Streckmittel)20 to 50ml methanol (diluent)
0,002g Rose bengale0.002g Rose bengal
0,004g Methylengrün0.004g methylene green
0,002g Orthosensibilisator Sto 575 (Filmfabrik VEB ORWO Wolfen)0,002g Orthosensitizer Sto 575 (Filmfabrik VEB ORWO Wolfen)
Nach entsprechend langer Dispersion aller Komponenten in einer Kugelmühle, die je nach physikalischer Beschaffenheit der Komponenten eine bis zwei Stunden beträgt, steht die Suspension zur Weiterverarbeitung zur Verfugung. Als Material für den Schichtträger der fotoempfindlichen Schicht werden Folien oder Platten aus Metallen, wie Aluminium oder Kupfer und mit Metallfolien beklebte oder mit Metallen bedampfte Papiere oder Kunststoffolien verwendet Das Begießen des Schichtträgers erfolgt zweckmäßig so, daß der zwischen zwei gleichförmig angetriebenen Transportwalzenpaaren hängende einein einem Materialleitwerk geführte Schlaufe bildende Schichtträger im tiefsten Punkt mit der Zinkoxidbindemittelsuspension beschichtet wird. Der beschichtete Träger wird so lange in der Schräglage gehalten, bis . keine nennenswerte Verschiebung der Zinkoxidbindemittelsuspensionskomponenten auf dem Trägermaterial erfolgt. Um den Begießvorgang in der beschriebenen Weise zu ermöglichen, findet die erfindungsgemäße Vorrichtung Anwendung. Der in Rollen konfektionierte Schichtträger gelangt von der Abrollstation 1 über ein Transportwalzenpaar 2 zum Begießapparat, derausdemZinkoxidbindemittelsuspensionsbehälter4, derReguJiereinrichtung 5 und einem Materialleitwerk7 besteht und der über dem tiefsten Punkt einer von der Schichtträgermaterialbahn 3 gebildeten Schlaufe angebracht ist. Das fotoempfindliche Material wird nach der Beschichtung im Punkt 6 im aufsteigenden Teil der Schlaufe unter einem Trocknungsbeschleuniger 8 hindurchgeleitet, danach vom Transportwalzenpaar 9 erfaßt und der Aufrollstation 10 zugeführt.After a correspondingly long dispersion of all components in a ball mill, which is one to two hours depending on the physical nature of the components, the suspension is available for further processing. As a material for the support of the photosensitive layer foils or plates of metals such as aluminum or copper and coated with metal foils or metal-coated papers or plastic films are used. The casting of the support is advantageously carried out so that the hanging between two uniformly driven transport roller pairs one in a Materialleitwerk guided loop-forming substrate is coated at the lowest point with the Zinkoxidbindemittelsuspension. The coated carrier is held in the inclined position until. There is no significant shift of the zinc oxide binder suspension components on the support material. In order to enable the Begießvorgang in the manner described, the device according to the invention is applied. The roll-formed substrate passes from the unwinding station 1 via a pair of transport rollers 2 to the embosser, which consists of the zinc oxide binder suspension container 4, the control device 5 and a material guide 7 and which is mounted above the lowest point of a loop formed by the substrate web 3. The photosensitive material is passed after the coating at point 6 in the ascending part of the loop under a drying accelerator 8, then detected by the transport roller pair 9 and fed to the reeling station 10.
Die Zinkoxidbindemittelsuspension wird dem Begießapparat über eine Leitung 11 und eine Pumpe 12 aus dem großvolumigen Vorratsbehälter 13 zugeführt. Die aus dem Begießapparat austretende Zinkoxidbindemittelsuspensionsmenge wird entsprechend der gewünschten Schichtdicke im Zusammenwirken mit der Viskosität der Suspension, der geforderten Trocknungsdauer und der eingestellten Materiaivorschubgeschwindigkeit mittels der Reguliereinrichtung 5 eingestellt. DasTransportwalzenpaar9 ist verstellbarangeordnet, um den Schichtbildungs- und Trocknungsprozeß durch Veränderung der Strecke s und der Schlaufenhöhe h optimal durchzuführen. Im tiefsten Punkt der Schlaufe der Schichtträgermaterialbahn 3 erfolgt eine Zinkoxidbindemittelsuspensionsanhäufung 6, die sich über die gesamte Breite des Schichtträgers verteilt. Infolge der Schräglage des bewegten Aufzeichnungsträgers fließt von der Oberfläche ein Teil der Suspension zurück in die Mulde der Schlaufe, während die unmittelbar an dem Schichtträger anhaftenden Teile entgegen der Schwerkraft transportiert werden. Durch diesen Vorgang kommt eine Wechselwirkung zwischen allen Komponenten der Suspension zustande, die die gewünschten Inhomogenitäten an der Oberfläche des fotoempfindlichen Materials entstehen läßt. Sind Lösungs-und Verschnittmittel soweit verdunstet, daß keine molekularen Bewegungen mehr in der Zinkoxidbindemittelschicht auftreten, so wird derTrocknungsvorgang durch Trocknungsbeschleuniger 8 aktiviert. Die Transportwalzen besitzen eine Gummioberfläche mittlerer Härte und ermöglichen guten Transport durch die Beschickungseinrichtung. Nach dem Trocknungsvorgang entsteht ein fotoempfindliches Material mit makroskopisch glatter weißer bis leicht getönter Oberfläche.The Zinkoxidbindemittelsuspension is supplied to the casting machine via a line 11 and a pump 12 from the large-volume reservoir 13. The zinc oxide binder suspension quantity leaving the casting apparatus is set in accordance with the desired layer thickness in cooperation with the viscosity of the suspension, the required drying time and the set material feed rate by means of the regulating device 5. The transport roller pair 9 is adjustably arranged to optimally perform the lamination and drying process by changing the distance s and the loop height h. At the lowest point of the loop of the layer substrate material web 3 is a zinc oxide binder suspension accumulation 6, which is distributed over the entire width of the substrate. Due to the inclined position of the moving recording medium, a part of the suspension flows from the surface back into the trough of the loop, while the parts adhering directly to the substrate are transported against the force of gravity. By this process, an interaction between all components of the suspension is achieved, which gives rise to the desired inhomogeneities on the surface of the photosensitive material. If solvents and diluents have evaporated to such an extent that molecular movements no longer occur in the zinc oxide binder layer, the drying process is activated by drying accelerator 8. The transport rollers have a rubber surface of medium hardness and allow good transport through the feeder. After the drying process, a photosensitive material with a macroscopically smooth white to slightly tinted surface is formed.
Weichmacher und gelatinierende Zusätze verleihen dem fotoempfindlichen Material mechanisch stabile und elastische Eigenschaften.Plasticizers and gelatinizing additives impart mechanically stable and elastic properties to the photosensitive material.
Bei der Erprobung des Materials wurden sowohl beliebig große gleichmäßig hell belichtete Bildflächen völlig homogen und deckend gefärbt als auch dünne Linien exakt wiedergegeben.During the testing of the material, arbitrarily large uniformly brightly illuminated image areas were completely homogeneously and opaquely colored, and thin lines were reproduced exactly.
Claims (2)