DD242233A1 - Verfahren zur herstellung von bindemitteln verbesserter lagerstabilitaet - Google Patents
Verfahren zur herstellung von bindemitteln verbesserter lagerstabilitaet Download PDFInfo
- Publication number
- DD242233A1 DD242233A1 DD28251685A DD28251685A DD242233A1 DD 242233 A1 DD242233 A1 DD 242233A1 DD 28251685 A DD28251685 A DD 28251685A DD 28251685 A DD28251685 A DD 28251685A DD 242233 A1 DD242233 A1 DD 242233A1
- Authority
- DD
- German Democratic Republic
- Prior art keywords
- formaldehyde
- condensates
- urea
- hmf
- wood
- Prior art date
Abstract
Die Erfindung betrifft die Herstellung von Harnstoff-Formaldehyd- bzw. Harnstoff-Melamin-Formaldehyd-Kondensation verbesserter Lagerstabilitaet, die fuer die Verleimung von Holz und die Herstellung von Holzwerkstoffen eingesetzt werden. Durch geeignete Zusatzstoffe soll eine wirtschaftliche Verfahrensweise zur Herstellung von Harnstoff-Formaldehyd- und Harnstoff-Melamin-Formaldehyd-Kondensaten verbesserter Stabilitaet bzw. die Wiederherstellung der Verarbeitbarkeit von ueberlagerten Harnstoff-Formaldehyd- bzw. Harnstoff-Melamin-Formaldehyd-Kondensatenentwickelt werden. Nach der erfindungsgemaessen Verfahrensweise koennen Harnstoff-Formaldehyd- bzw. Harnstoff-Melamin-Formaldehyd-Kondensate verbesserter Lagerstabilitaet hergestellt bzw. die Wiederverarbeitbarkeit ueberlagerter Harnstoff-Formaldehyd- bzw. Harnstoff-Melamin-Formaldehyd-Kondensate erreicht werden, indem diesen ein formaldehydarmes Harnstoff-Formal-dehyd-Kondensat zugemischt wird. Durch den Zusatz der formaldehydarmen HF-Kondensate wird auch die Formaldehydabgabe der mit der Mischung hergestellten Holzverleimungen bzw. Holzwerkstoffe verringert.
Description
Die formaldehydarmen HF-Kondensate werden den HF- bzw. HMF-Kondensaten zur Stabilitätserhöhung zugemischt. Die Menge des Zusatzes hängt vom HF-Molverhä!tnis des Bindemittels und vom gewünschten Stabilisierungseffekt ab bzw. bei überlagerten Bindemitteln vom HF-Molverhältnis und dem Grad der Überlagerung. Durch den Zusatz eines abgewandelten Harzes der gleichen Stoffklasse wird überraschend ein Stabilisierungseffekt erzielt. Es werden durch den Zusatz des formaldehydarmen Harnstoff-Formaldehyd-Kondensates sowohl die Bindemittel stabilisiert, daß sie über einen längeren Zeitraum verarbeitbar sind als auch überlagerte Bindemittel wieder zu einen verarbeitbaren Zustand gebracht.
Ausführungsbeispiele
Beispiel 1 (Vergleichsbeispiel)
Aus einem handelsüblichen HF-Bindemittel (HF-Molverhältnis 1:1,35, Viskosität 495mPa.s wird eine Leimflotte hergestellt:
Leim 50 kg
Wasser 12,5 kg
Paraffinemulsion 3 kg
40%ig
15%igeNH4CI-Lösung 2 kg
Die Leimflotte wird in einer Menge von 8% Festharz, bezogen auf absolut trockenes Holz, auf Kiefemschneidspäne (Länge 15 bis 20mm, Breite 3 bis 5mm, Dicke 0,2 bis 0,4mm) aufgebracht, die beleimten Späne werden unter den Bedingungen
Preßtemperatur 160bis165°C
' Preßdruck 1,5 N/mm2
Preßzeit 7 min.
zu den Spanplatten von 20 mm Dicke verarbeitet, die die folgenden nach bekannten Methoden bestimmten Eigenschaften haben:
Dichte kg/m3 610
Biegefestigkeit N/mm2 26,2
Querzugsfestigkeit N/mm2 0,54
Formaldehydabgabe % 0,035
Einem handelsüblichen HF-Bindemittel (H F-M ο !verhältnis 1:1,35) wird a Is Zusatz ei η HF-Kondensat mit einem H F-MoI verhältnis von 1:0,3 (Feststoffgehalt 60%), welches aus Harnstoff, Formaldehyd, einem HF-Kondensat mit einem HF-Molverhältnis 1:1,35 und Wasser durch 60minütiges Rühren bei 900C und einem pH-Wert von 9 hergestellt wurde, zugemischt und gemäß Beispiel 1 verarbeitet bzw. die Lagerstabilitäten der Leime verfolgt. Die Mischungsverhältnisse und die Ergebnisse enthält Tabelle 1.
Ein handelsüblicher HF-Leim (HF-Molverhältnis 1:1,2) wird mit einem HF-Kondensat gemäß Beispiel 2 (Feststoffgehalt 63%) gemischt und gemäß Beispiel 1 verarbeitet bzw. die Lagerstabilitäten der Leime verfolgt. Die Mischungsverhältnisse und die Ergebnisse enthält Tabelle 2.
Einem handelsüblichen überlagerten HF-Leim (HF-Molverhältnis 1:1,35) wird als Zusatz ein HF-Kondensat gemäß Beispiel 2 mit einem HF-Molverhältnis 1:0,5 und einem Feststoffgehalt von 60% zugesetzt und gemäß Beispiel 1 verarbeitet bzw. die Lagerstabilität der Leime verfolgt. Die Mischungsverhältnisse und die Ergebnisse enthält Tabelle 3.
Ein HMF-Leim mit einem Meiamingehalt von 20% und einem auf Harnstoff und Formaldehyd umgerechneten Molverhältnis von 1:1,55 wird mit einem HF-Kondensat gemäß Beispiel 2 (HF-Molverhältnis 1:0,3, Feststoffgehalt 60%) gemischt und gemäß Beispiel 1 (12% Festharz pro absolut trockenes Holz) verarbeitet bzw. die Lagerstabilität der Leime verfolgt. Die Mischungsverhältnisse und die Ergebnisse enthält Tabelle 4.
| Massenverhältnis | Viskosität | Querzugfestig | Viskosität nach | Formaldehydabgabe |
| Feststoff (Leim): | keit | 4Mon.20°C | Perforator-Methode) | |
| Feststoff (Zusatz) | mPa-s | N/mm2 | mPa · s | % |
| 1:0,00 | 495 | 1710 | ||
| 0,95:0,05 | 350 | 1520 | ||
| 0,91:0,09 | 268 | 585 | ||
| 0,86:0,14 | 184 | 304 | ||
| Fortsetzung Tabelle 1 | ||||
| Spann plattenwerte | ||||
| Dichte Biegefestigkeit | ||||
| kg/m3 N/mm2 | ||||
610 26,2 0,51 . 0,035
605 25,8 0,52 0,029
| Dichte | Biegefestigkeit | Biegefestigkeit | Biegefestigkeit | Viskosität | Querzugfestig | • · | Formaldehydabgabe | Formaldehydab | Formaldehydabgabe |
| keit | (Perforator-Methode) | gabe (Perforator- | (Perforator-Methode) | ||||||
| kg/m3 | N/mm2 | N/mm2 | mPa -s | N/mm2 | % | Methode) | % | ||
| 600 | 25,4 | N/mm2 | 25,3 | 422 | 0,51 | 0,022 | % | 0,017 | |
| 610 | 25,3 | 25,3 | 24,7 | 330 | 0,50 | 0,016 | 0,016 | 0,014 | |
| Tabelle 2 | 24,5 | 24,6 | 210 | 0,012 | 0,011 | ||||
| Massenverhältnis | 24,1 | Viskosität nach | 0,009 | ||||||
| Feststoff(Leim): | Massenverhältnis | 3Mon.20°C | |||||||
| Feststoff (Zusatz) | Massenverhältnis | Feststoff (Leim): | mPa'S | Viskosität nach | |||||
| 1:0,00 | Feststoff (Leim): | Feststoff (Zusatz) | 900 | 2Mon.20°C | |||||
| 0,94:0,06 | Feststoff (Zusatz | 1:0,00 | 510 | mPa -s | |||||
| 0,90:0,10 | 1:0,00 | 0,90:0,10 | 390 | — | |||||
| Fortsetzung Tabelle 2 | 0,86:0,14 | 0,87:0,13 | 3100 | ||||||
| Spannplattenwerte | 0,81:0,19 | 0,83:0,17 | 1700 | ||||||
| Dichte | 0,77:0,23 | Querzugfestigkeit | 730 | ||||||
| Fortsetzung Tabelle 3 | |||||||||
| Spannplattenwerte | Viskosität | ||||||||
| kg/m3 | Dichte | N/mm2 | |||||||
| 610 | mPa-s | 0,50 | |||||||
| 600 | kg/m3 | 8400 | 0,50 | ||||||
| 610 | 600 | 1040 | 0,49 | ||||||
| Tabelle 3 | 590 | 610 | |||||||
| 600 | 420 | ||||||||
| Tabelle 4 | |||||||||
| 3Mon.20°C | |||||||||
| mPa-s | |||||||||
| 1 500 | |||||||||
| 900 | |||||||||
| 750 | |||||||||
| 370 | |||||||||
| Querzugfestigkeit | |||||||||
| keit | |||||||||
| N/mm2 | |||||||||
| 0,45 | |||||||||
| 0,43 | |||||||||
| 0,42 | |||||||||
| Viskosität nach | |||||||||
| mPa-s | |||||||||
| 500 | |||||||||
| 210 | |||||||||
| 240 | |||||||||
| 200 | |||||||||
Fortsetzung Tabelle
Spanplattenwerte Dichte
kg/m3
Biegefestigkeit N/mm2
Querzugfestigkeit N/mm2
Formaldehydabgabe (Perforator-Methode)
26,0 25,3 27,0 26,7
0,78 0,78 0,77 0,77
0,060 0,035 0,025 0,020
Claims (1)
- Erfindungsanspruch:Verfahren zur Herstellung von Bindemitteln verbesserter Lagerstabilität auf Basis von Harnstoff-Formal-dehyd- bzw. Harnstoff-Melamin-Formaldehyd-Kondensaten durch aminogruppenhaltige aliphatische Verbindungen, für die Verleimung von Holz und die Herstellung von Holzwerkstoffen, dadurch gekennzeichnet, daß Harnstoff-Formaldehyd- bzw. Hamstoff-Melamin-Formaldehyd-Kondensate,auch solche in überlagerter Form, mit einer lag erstabilen wäßrigen Lösung eines forma Id ehydar-m en Harnstoff-Formaldehyd-Kondensates mit einem Harnstoff-Formaldehyd-Molverhältnis von 1:0,20 bis 1:0,70, in einem auf die Feststoffmengen bezogenen Massenverhältnis von 0,99:0,01 bis 0,50:0,50, vorzugsweise von 0,97:0,03 bis 0,70:0,30, gemischt werden.Anwendungsgebiet der ErfindungDie Erfindung betrifft die Herstellung von Harnstoff-Formaldehyd (HF)- bzw. Hamstoff-Melamin-Formaldehyd(HMF)-Kondensaten verbesserter Lagerstabilität bzw. die Wiederherstellung der Verarbeitbarkeit überlagerter HF-bzw. HMF-Kondensate. Die stabilisierten HF- bzw. HMF-Kondensate können zur Verleimung von Holz und für die Herstellung von Holzwerkstoffen eingesetzt werden.Charakteristik der bekannten technischen LösungenDie Lagerstabilität von HF- bzw. HMF-Kondensaten, die für die Verleimung von Holz und die Herstellung von Holzwerkstoffen eingesetzt werden, ist für die Verarbeitung dieser Kondensate von großer Bedeutung. Die Lagerstabilität beträgt je nach Art der Kondensate 1 bis 3 Monate bei einer Lagertemperatur von 20°C. Während der Lagerung steigt die Viskosität der Kondensate kontinuierlich durch langsam ablaufende Kondensationsreaktionen an. Eine Verlängerung dieser relativ kurzen Lagerzeiten ist erstrebenswert, da überlagerte Leime wegen der hohen Viskositäten nicht mehr oder nur mit großen Schwierigkeiten verarbeitbar sind. DerGrenzwert der Verarbeitbarkeit liegt z. B. bei der Spanplattenherstellung bei einer Viskosität von etwa 2000 mPa.s. Die Wiederherstellung der Verarbeitbarkeit überlagerter Leime ist aus den gleichen Gründen von Interesse. Es ist bekannt, die Lagerstabilität durch den Zusatz stabilitätsfördernder Produkte, wie Aminoalkohole (DE-OS 2163061), Urethane (DE-AS 833855), Polymethylentetramine (DE-PS 965766), zu verbessern. Nachteilig an dieser Verfahrensweise ist, daß verfahrensfremde und im Preis ungünstige Zusatzstoffe eingesetzt werden.Ziel der ErfindungT .Das Ziel der Erfindung besteht darin, die Lagerstabilität von HF- bzw. HMF-Kondensaten zu verbessern bzw. überlagerte HF- bzw. HMF-Kondensate wieder verarbeitbar zu machen.Darlegung des Wesens der ErfindungEs bestand die Aufgabe, durch geeignete Zusatzstoffe eine wirtschaftlich günstige Verfahrensweise zu entwickeln, um HF- bzw. HMF-Kondensate verbesserter Lagerstabilität herzustellen bzw. die Wiederverarbeitung überlagerter HF- bzw. HMF-Kondensate zu ermöglichen. Diese Aufgabe wird durch ein Verfahren zur Herstellung von Bindemitteln verbesserter Lagerstabilität auf Basis von Harnstoff-Formaldehyd- bzw. Harnstoff-Melamin-Formaldehyd-Kondensaten durch aminogruppenhaltige aliphatische Verbindungen, für die Verleimung von Holz und die Herstellung von Holzwerkstoffen erfindungsgemäß dadurch gelöst, daß HF- bzw. HMF-Kondensate, auch solche in überlagerter Form, mit einer lagerstabilen wäßrigen Lösung eines formaldehydarmen HF-Kondensates mit einem HF-Molverhältnis von 1:0,20 bis 1:0,70, in einem auf die Feststoffmengen bezogenen Massenverhältnis von 0,99:0,01 bis 0,50:0,50, vorzugsweise von 0,97:0,03 bis 0,70:0,30, gemischt werden. Die zur Verleimung von Holz und Holzwerkstoffen einsetzbaren HF-bzw. HMF-Kondensate sind handelsübliche Bindemittel, die als wäßrige Lösungen oder Pulver erhältlich sind. Die Bindemittel aus Harnstoff und Formaldehyd haben ein Harnstoff-Formaldehyd-MV von 1:1,7 bis 1:1,2. Wenn Melamin enthalten ist, bleibt das Verhältnis zwischen der Carbonylgruppe des Formaldehydsund der mit dieserzur Reaktion befähigten Gruppierung meistens in dem Bereich wie in den Kondensaten, die nur Harnstoff und Formaldehyd enthalten.Die erfindungsgemäße zur Verbesserung der Lagerstabilität von HF- bzw. HMF-Kondensaten bzw. zur Wiederherstellung der Verarbeitbarkeit von überlagerten HF-bzw. HMF-Kondensaten eingesetzten formaldehydarmen HF-Kondensate haben ein Harnstoff-Formaldehyd-Molverhältnis von 1:0,7 bis 1:0,2.