ECSP972073A - HYDRAULIC CEMENT WITH HIGH STRENGTH ACCELERATED DEVELOPMENT - Google Patents
HYDRAULIC CEMENT WITH HIGH STRENGTH ACCELERATED DEVELOPMENTInfo
- Publication number
- ECSP972073A ECSP972073A ECSP972073A ECSP972073A EC SP972073 A ECSP972073 A EC SP972073A EC SP972073 A ECSP972073 A EC SP972073A EC SP972073 A ECSP972073 A EC SP972073A
- Authority
- EC
- Ecuador
- Prior art keywords
- clinker
- calcium
- grinding
- formation
- cement
- Prior art date
Abstract
La invención consiste en un método para la fabricación de cementos a base de sulfoaluminato de calcio, el cual consiste en la formación de un clinker mediante la calcinación de las materias primas a temperaturas superiores a 1200oC de tal manera que el clinker producido tengs un slto contenido de sulfoaluminato de calcio, silicato tricálcico y silicato dicálcico y, durante o previa a la etapa de molienda, adicionar al clinker así producido y con los componentes básicos antes mencionados cantidades optimas de oxido o hidróxido de calcio y sulfato de calcio a fin de activar dicho clinker. En dicha molienda deberá observarse una temperatura de aproximadamente 100 a 125oC y un tiempo suficiente para convertir el yeso en hemidrato con lo que se logrará que el sulfato de calcio presente en el producto obtenido se encuentre en condiciones y reaccionar rápidamente durante la hidratación del cemento, dando lugar a la formación de la entringita, requiriéndose para ello la precensia de un pHsuperior a 12. Por supuesto, también reclama como novedad el cemento activado, resultante del método de calcinación y de molienda de la invención.The invention consists of a method for the manufacture of calcium sulfoaluminate-based cements, which consists of the formation of a clinker by calcining the raw materials at temperatures above 1200oC in such a way that the clinker produced has a contained content. of calcium sulfoaluminate, tricalcium silicate and dicalcium silicate and, during or prior to the grinding stage, add to the clinker thus produced and with the aforementioned basic components optimum amounts of calcium oxide or hydroxide and calcium sulfate in order to activate said clinker. In said grinding, a temperature of approximately 100 to 125oC must be observed and a time sufficient to convert the gypsum into hemidrate, thereby achieving that the calcium sulfate present in the product obtained is in good condition and reacts quickly during the hydration of the cement, giving rise to the formation of the entringite, requiring for it the precensia of a pH higher than 12. Of course, it also claims as a novelty the activated cement, resulting from the calcination and grinding method of the invention.
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| ECSP972073 ECSP972073A (en) | 1997-04-04 | 1997-04-04 | HYDRAULIC CEMENT WITH HIGH STRENGTH ACCELERATED DEVELOPMENT |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| ECSP972073 ECSP972073A (en) | 1997-04-04 | 1997-04-04 | HYDRAULIC CEMENT WITH HIGH STRENGTH ACCELERATED DEVELOPMENT |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| ECSP972073A true ECSP972073A (en) | 1998-04-07 |
Family
ID=42042906
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| ECSP972073 ECSP972073A (en) | 1997-04-04 | 1997-04-04 | HYDRAULIC CEMENT WITH HIGH STRENGTH ACCELERATED DEVELOPMENT |
Country Status (1)
| Country | Link |
|---|---|
| EC (1) | ECSP972073A (en) |
-
1997
- 1997-04-04 EC ECSP972073 patent/ECSP972073A/en unknown
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| CO4560452A1 (en) | HYDRAULIX CEMENT WITH HIGH RESISTANCE ACCELERATED DEVELOPMENT | |
| Costa et al. | Hydration of sustainable ternary cements containing phosphogypsum | |
| US10752545B2 (en) | Steam-assisted production of metal silicate cements, compositions and methods thereof | |
| US8715411B2 (en) | Method for producing a clinker for hydraulic cement with low CO2 emission and high resistance | |
| MX2011011989A (en) | Portland limestone calcined clay cement. | |
| Hua et al. | Preparation and properties of II-anhydrite calcined from phosphogypsum | |
| EA200501487A1 (en) | COMPOSITIONS BASED ON CALCIUM SULPHATE AND METHODS FOR THEIR PRODUCTION | |
| GB938765A (en) | Sulfoaluminate cement | |
| NZ600745A (en) | Lightweight gypsum products having enhanced water resistance | |
| Marroccoli et al. | Early hydration of calcium sulfoaluminate-based cements for structural applications | |
| CN102557719A (en) | Production method of gypsum board | |
| ECSP972073A (en) | HYDRAULIC CEMENT WITH HIGH STRENGTH ACCELERATED DEVELOPMENT | |
| BR9808558A (en) | Processes for producing crystalline tetrahydrate calcium hexaborate and for dehydration of the crystalline tetrahydrate calcium hexaborate composition, crystalline tetrahydrate calcium hexaborate, and, amorphous calcium hexaborate composition. | |
| Siziakova et al. | Hydrocarboaliminate calcium application in aluminum processing for production of special cement brands | |
| CA1138903A (en) | Hydraulic binders based on portland cement clinkers and their process of obtention | |
| GB253929A (en) | Building cement or plaster | |
| CN107117838B (en) | A kind of sulfoaluminate cement clinker containing tricalcium silicate and preparation method thereof | |
| KR101129393B1 (en) | Blast furnace slag cement synthetic method and blast furnace slag cement produced by this method | |
| SU950691A1 (en) | Raw mix for producing portland cement clinker | |
| SU1006403A1 (en) | Raw mix for producing quick-hardening portland cement clinker | |
| Chen et al. | Manufacturing properties of γ-dicalcium silicate with synthetic method | |
| SU771044A1 (en) | Expanding additive to cement | |
| UA36147A (en) | Process for the preparation of aluminium dihydroxy sulphate | |
| SU368198A1 (en) | EXPANDING CEMENT | |
| ES2187340B1 (en) | PROCEDURE FOR OBTAINING CALCIUM VANADATES BY MIX OF COCO3-V2O5. |