ES2118791T3 - Procedimiento para reducir la corrosion de componentes expuestos a agua a alta temperatura. - Google Patents

Procedimiento para reducir la corrosion de componentes expuestos a agua a alta temperatura.

Info

Publication number
ES2118791T3
ES2118791T3 ES92304148T ES92304148T ES2118791T3 ES 2118791 T3 ES2118791 T3 ES 2118791T3 ES 92304148 T ES92304148 T ES 92304148T ES 92304148 T ES92304148 T ES 92304148T ES 2118791 T3 ES2118791 T3 ES 2118791T3
Authority
ES
Spain
Prior art keywords
high temperature
corrosion
water
procedure
reduce
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES92304148T
Other languages
English (en)
Inventor
Peter Louis Andresen
Leonard William Niedrach
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
General Electric Co
Original Assignee
General Electric Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Electric Co filed Critical General Electric Co
Application granted granted Critical
Publication of ES2118791T3 publication Critical patent/ES2118791T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

SE MUESTRA UN METODO PARA REDUCIR EL POTENCIAL DE CORROSION DE COMPONENTES FORMADOS POR ACERO AL CARBONO, ACERO ALEADO, ACERO INOXIDABLE, ALEACIONES BASADAS EN NIQUEL, O ALEACIONES BASADAS EN COBALTO, Y EXPUESTOS A AGUA CON ALTA TEMPERATURA QUE COMPRENDE: SUMINISTRAR ESPECIES REDUCTORAS EN AGUA CON ALTA TEMPERATURA QUE PUEDEN COMBINARSE CON ESPECIES OXIDANTES, Y FORMAR EL COMPONENTE PARA DISPONER DE UNA CAPA CATALITICA DE UN METAL DEL GRUPO PLATINO.
ES92304148T 1991-05-13 1992-05-08 Procedimiento para reducir la corrosion de componentes expuestos a agua a alta temperatura. Expired - Lifetime ES2118791T3 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US07/698,885 US5135709A (en) 1991-05-13 1991-05-13 Method for reducing corrosion of components exposed to high-temperature water

Publications (1)

Publication Number Publication Date
ES2118791T3 true ES2118791T3 (es) 1998-10-01

Family

ID=24807065

Family Applications (1)

Application Number Title Priority Date Filing Date
ES92304148T Expired - Lifetime ES2118791T3 (es) 1991-05-13 1992-05-08 Procedimiento para reducir la corrosion de componentes expuestos a agua a alta temperatura.

Country Status (6)

Country Link
US (1) US5135709A (es)
EP (1) EP0514089B1 (es)
JP (1) JP2766422B2 (es)
DE (2) DE514089T1 (es)
ES (1) ES2118791T3 (es)
MX (1) MX9202218A (es)

Families Citing this family (52)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH05280687A (ja) * 1991-03-26 1993-10-26 Mitsubishi Heavy Ind Ltd 火力、原子力発電プラント用機器
US5164152A (en) * 1991-08-02 1992-11-17 General Electric Company Method for reducing flow assisted corrosion of carbon steel components
JP2982517B2 (ja) * 1992-10-20 1999-11-22 株式会社日立製作所 沸騰水型原子力プラントの運転方法及び沸騰水型原子力プラント
US5287392A (en) * 1992-11-25 1994-02-15 General Electric Company Internal passive water recombiner/hydrogen peroxide decomposer for a boiling water reactor
US5285486A (en) * 1992-11-25 1994-02-08 General Electric Company Internal passive hydrogen peroxide decomposer for a boiling water reactor
US5392325A (en) * 1993-05-21 1995-02-21 General Electric Company Method and apparatus for local protection of piping systems from stress corrosion cracking
US5625656A (en) * 1993-10-29 1997-04-29 General Electric Company Method for monitoring noble metal distribution in reactor circuit during plant application
US5448605A (en) * 1993-10-29 1995-09-05 General Electric Company Palladium acetylacetonate solution and related method of manufacture
US5608766A (en) * 1993-10-29 1997-03-04 General Electric Company Co-deposition of palladium during oxide film growth in high-temperature water to mitigate stress corrosion cracking
US5818893A (en) * 1993-10-29 1998-10-06 General Electric Company In-situ palladium doping or coating of stainless steel surfaces
US5773096A (en) * 1993-10-29 1998-06-30 General Electric Company Method of catalyst preparation by high-temperature hydrothermal incorporation of noble metals onto surfaces and matrices
US5600691A (en) * 1993-10-29 1997-02-04 General Electric Company Noble metal doping or coating of crack interior for stress corrosion cracking protection of metals
US5774516A (en) * 1993-10-29 1998-06-30 General Electric Company Modification of oxide film electrical conductivity to maintain low corrosion potential in high-temperature water
TW241314B (en) * 1993-10-29 1995-02-21 Gen Electric In-situ palladium doping or coating of stainless steel surfaces
US5602888A (en) * 1993-10-29 1997-02-11 General Electric Company Radiation-induced palladium doping of metals to protect against stress corrosion cracking
US5600692A (en) * 1993-10-29 1997-02-04 General Electric Company Method for improving tenacity and loading of palladium on palladium-doped metal surfaces
JP3053325B2 (ja) * 1993-12-20 2000-06-19 株式会社日立製作所 腐食電位のシミュレーション方法および原子炉プラントの運転監視装置
TW253058B (en) * 1994-03-10 1995-08-01 Gen Electric Method of doping or coating metal surfaces with metallic elements to improve oxide film insulating characteristics
US5465281A (en) * 1994-04-11 1995-11-07 General Electric Company Insulated protective coating for mitigation of stress corrosion cracking of metal components in high-temperature water
US5465278A (en) * 1994-05-23 1995-11-07 General Electric Company Shroud electrochemical potential monitor
US5461648A (en) * 1994-10-27 1995-10-24 The United States Of America As Represented By The Secretary Of The Navy Supercritical water oxidation reactor with a corrosion-resistant lining
US5527471A (en) * 1995-02-02 1996-06-18 Modar, Inc. Iridium material for hydrothermal oxidation environments
US5581588A (en) * 1995-06-23 1996-12-03 General Electric Company Insulated protective coating doped with a noble metal for mitigation of stress corrosion cracking
US5793830A (en) * 1995-07-03 1998-08-11 General Electric Company Metal alloy coating for mitigation of stress corrosion cracking of metal components in high-temperature water
DE19610977C1 (de) * 1996-03-20 1997-04-10 Siemens Ag Kernreaktor mit Katalysatormaterial zum Beseitigen von Oxidationsmitteln
US6128361A (en) * 1996-03-26 2000-10-03 General Electric Company Coating for reducing corrosion of zirconium-based alloys induced by . .beta-particle irradiation
US6024805A (en) * 1997-11-12 2000-02-15 General Electric Company Metal hydride addition for reducing corrosion potential of structural steel
US6714618B1 (en) * 1997-11-28 2004-03-30 General Electric Company Temperature-based method for controlling the amount of metal applied to metal oxide surfaces to reduce corrosion and stress corrosion cracking
JP3550544B2 (ja) * 1997-11-28 2004-08-04 ゼネラル・エレクトリック・カンパニイ 腐食及び応力腐食割れを減少するために金属酸化物表面に加える金属の量を制御する温度に基づく方法
US5991352A (en) * 1998-03-30 1999-11-23 General Electric Company Method for determining corrosion susceptibility of nuclear fuel cladding to nodular corrosion
DE19818772C2 (de) * 1998-04-27 2000-05-31 Siemens Ag Verfahren zum Abbau der Radioaktivität eines Metallteiles
US6473480B1 (en) * 1999-12-30 2002-10-29 General Electric Company Method and apparatus for maintaining proper noble metal loading for a noble metal application process for water-cooled nuclear reactors
DE10013865A1 (de) 2000-03-21 2001-10-04 Siemens Ag Verfahren zur Verminderung der Korrosion eines Bauteils einer kerntechnischen Anlage und Bauteil einer kerntechnischen Anlage
US20040057549A1 (en) * 2000-08-08 2004-03-25 Hitachi, Ltd. Method of operating nuclear reactor
US20020080906A1 (en) * 2000-12-21 2002-06-27 Andresen Peter L. Noble metal catalysis for mitigation of corrosion, erosion and stress corrosion cracking in pressurized water reactor and related high temperature water environments
US6488782B2 (en) * 2001-01-29 2002-12-03 General Electric Company Method of reducing corrosion potential and stress corrosion cracking susceptibility in nickel-based alloys
DE10123690A1 (de) * 2001-05-15 2002-12-05 Framatome Anp Gmbh Verfahren zum Schutz der Bauteile des Primärsystems eines Siedewasserreaktors insbesondere vor Spannungsrisskorrosion
US20040022346A1 (en) * 2002-07-31 2004-02-05 General Electric Company Method for forming coatings on structural components with corrosion-mitigating materials
US6888908B1 (en) * 2002-11-18 2005-05-03 Babcock & Wilcox Canada, Ltd. Reactor head with integral nozzles
US6724854B1 (en) 2003-06-16 2004-04-20 General Electric Company Process to mitigate stress corrosion cracking of structural materials in high temperature water
US20040258192A1 (en) * 2003-06-16 2004-12-23 General Electric Company Mitigation of steam turbine stress corrosion cracking
JP4105052B2 (ja) * 2003-07-22 2008-06-18 日立Ｇｅニュークリア・エナジー株式会社 原子力プラント構造材料の応力腐食割れを緩和する方法
US7287756B2 (en) * 2004-03-08 2007-10-30 Westinghouse Electric Co Llc Film riding shaft seal
US20060203952A1 (en) * 2005-03-14 2006-09-14 General Electric Company Methods of reducing hydrogen absorption in zirconium alloys of nuclear fuel assemblies
DE102006009502B3 (de) * 2006-02-27 2007-08-30 Framatome Anp Gmbh Verfahren zur Prüfung eines Brennstabhüllrohres sowie zugehörige Vorrichtung
US7430902B2 (en) * 2006-06-16 2008-10-07 General Electric Company Method of monitoring deposition of a noble metal in a nuclear reactor and deposition monitor therefor
US20100246745A1 (en) * 2006-12-29 2010-09-30 Samson Hettiarachchi Methods for operating and methods for reducing post-shutdown radiation levels of nuclear reactors
US11469006B2 (en) 2016-08-04 2022-10-11 Dominion Engineering, Inc. Suppression of radionuclide deposition on nuclear power plant components
JP6620081B2 (ja) * 2016-09-20 2019-12-11 日立Ｇｅニュークリア・エナジー株式会社 原子力プラントの炭素鋼部材への貴金属の付着方法及び原子力プラントの炭素鋼部材への放射性核種の付着抑制方法
JP6751044B2 (ja) * 2017-03-28 2020-09-02 日立Ｇｅニュークリア・エナジー株式会社 原子力プラントの炭素鋼部材への貴金属の付着方法、及び原子力プラントの炭素鋼部材への放射性核種の付着抑制方法
JP2020186453A (ja) * 2019-05-16 2020-11-19 三菱重工業株式会社 炭素鋼、放射性物質収納容器、遮蔽性能の解析方法及び遮蔽構造の設計方法
KR102549737B1 (ko) * 2021-08-04 2023-06-29 포항공과대학교 산학협력단 산소환원촉매를 이용한 금속기재 표면의 내부식성 강화 방법

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1210496B (de) * 1964-10-30 1966-02-10 Keller & Knappich Gmbh Ausfuetterung fuer einen Mantel eines Kernreaktor-Behaelters
SE300994B (es) * 1964-12-22 1968-05-20 Svenska Metallverken Ab
US3343979A (en) * 1965-10-22 1967-09-26 Jr Charles E Hamrin Method for depositing a tungsten-rhenium metal alloy on a substrate
US3783005A (en) * 1972-02-04 1974-01-01 Western Electric Co Method of depositing a metal on a surface of a nonconductive substrate
US4097402A (en) * 1976-06-29 1978-06-27 General Electric Company Nuclear fuel assembly and process
JPS548357A (en) * 1977-06-22 1979-01-22 Mitsubishi Heavy Ind Ltd Simple bucket device of fork lift
US4123594A (en) * 1977-09-22 1978-10-31 General Electric Company Metallic coated article of improved environmental resistance
JPS57596A (en) * 1980-06-02 1982-01-05 Tokyo Shibaura Electric Co Oxygen concentration control devece of nuclear reactor
JPS573086A (en) * 1980-06-06 1982-01-08 Tokyo Shibaura Electric Co Method of operating nuclear reactor
US4477538A (en) * 1981-02-17 1984-10-16 The United States Of America As Represented By The Secretary Of The Navy Platinum underlayers and overlayers for coatings
GB2149391B (en) * 1983-11-10 1987-10-07 Westinghouse Electric Corp Method for removing dissolved oxygen from aqueous media
US4842811A (en) * 1985-02-05 1989-06-27 Westinghouse Electric Corp. Method for preventing oxygen corrosion in a boiling water nuclear reactor and improved boiling water reactor system
JPS629696A (ja) * 1985-07-06 1987-01-17 株式会社リコー 可撓性印刷配線基板と印刷配線基板との導体パタ−ンの接続方法
JPS629296A (ja) * 1985-07-08 1987-01-17 株式会社東芝 原子炉一次冷却系の構造材
US4849082A (en) * 1986-02-03 1989-07-18 The Babcock & Wilcox Company Ion implantation of zirconium alloys with hafnium
US4917968A (en) * 1988-04-15 1990-04-17 Ultramet High temperature corrosion resistant composite structure
US5130081A (en) * 1990-04-02 1992-07-14 General Electric Company Operation life of on-life boiling water reactors
US5130080A (en) * 1990-04-02 1992-07-14 General Electric Company Method of providing extended life expectancy for components of boiling water reactors

Also Published As

Publication number Publication date
EP0514089B1 (en) 1998-08-12
US5135709A (en) 1992-08-04
JPH05148674A (ja) 1993-06-15
DE69226558T2 (de) 1999-02-11
EP0514089A1 (en) 1992-11-19
DE514089T1 (de) 1996-10-10
JP2766422B2 (ja) 1998-06-18
DE69226558D1 (de) 1998-09-17
MX9202218A (es) 1992-11-01

Similar Documents

Publication Publication Date Title
ES2195144T3 (es) Dopado o revestimiento in situ con paladio de superficies de acero inoxidable.
ES2132074T3 (es) Procedimiento para proporcionar una esperanza de vida extendida a los componentes de los reactores de agua en ebullicion.
JPS5431062A (en) Manufacture of structure superior in stress corrosion cracking resistivity
ES471061A1 (es) Metodo para controlar la composicion de una solucion de de- capado
IT1302202B1 (it) Processo di decapaggio elettrolitico con soluzioni esenti da acidonitrico.
ES556779A0 (es) Procedimiento para producir un articulo de acero inoxidable que tiene una estructura metalurgica duplex de aproximadamente 20-80% ferrita y el resto austenita
ES2027850A6 (es) Metodo para aplicar superficies resistentes a la erosion a componentesde turbinas de vapor.
SE8802186L (sv) Metod foer ytbehandling av metallegeringar
MX166288B (es) Tratamiento para inhibir el agrietamiento por corrosion debida a esfuerzo inducido por irradacion en acero inoxdable austenitico
GB1490694A (en) Ductile corrosion resistant alloy
DE1621204B1 (de) Verfahren zur verbesserung der haltbarkeit von chrom schutzschichten auf metallen bei hohen temperaturen in stickstoffhaltiger atomsphäre
JPS6428349A (en) Manufacture of aluminum-plated steel sheet and steel foil using stainless steel as base material
MX167671B (es) Tratamiento para contrarrestar el agrietamiento, poducido por la corrosion debida a los esfuerzos inucidos por irradiacion, el aleaciones austeniticas, tales como acero inoxidable
JPS5397941A (en) Surface treating method for high temperature corrosion resistance and ion plating diffusion treatment furnace
GB1396898A (en) Method for making ferrous metal having highly improved resistances to corrosion at elevated temperatures and to oxidization
JPS5525782A (en) Multi-tube heat exchanger
JPS5629680A (en) Surface treatment in annealing line
KR860000912A (ko) 톱날의 제조방법
Laycock et al. Prediction of pitting potentials and critical pitting temperatures
Drodten et al. Stress Corrosion Cracking of Molybdenum-Free and Molybdenum-Containing Steels in Calcium Nitrate and Sodium Hydroxide Solutions
Eckstein et al. Testing of the susceptibility to pitting corrosion of austenitic steels of the type 18. 10 with a modified electrochemical method.
SE7607593L (sv) Laglegerat stal med forbettrat korrisionsforhallande, serskilt mot havsvatten
SU834463A1 (ru) Среда дл испытани металлов напиТТиНгОВую КОРРОзию
Herbsleb et al. Electrochemical Study of the Pitting Corrosion of Austenitic Cr-Ni Steels Containing Mo Between 0 and 4 per cent With Special Reference to the Measuring Procedure and Method
JPS5461981A (en) Embrittlement judgement method of austenite base stainless steel welding metal

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 514089

Country of ref document: ES