ES2195214T3 - Materias moldeables abs con muy alta resiliencia fabricadas sin emulsion. - Google Patents

Materias moldeables abs con muy alta resiliencia fabricadas sin emulsion.

Info

Publication number
ES2195214T3
ES2195214T3 ES98106020T ES98106020T ES2195214T3 ES 2195214 T3 ES2195214 T3 ES 2195214T3 ES 98106020 T ES98106020 T ES 98106020T ES 98106020 T ES98106020 T ES 98106020T ES 2195214 T3 ES2195214 T3 ES 2195214T3
Authority
ES
Spain
Prior art keywords
weight
proportional
special preference
preferred
proportional weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES98106020T
Other languages
English (en)
Inventor
Herbert Dr Eichenauer
Peter Dr Kruger
Edgar Dr Leitz
Gisbert Dr Michels
Ralph Dr Ostarek
Richard Dr Weider
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bayer AG
Original Assignee
Bayer AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bayer AG filed Critical Bayer AG
Application granted granted Critical
Publication of ES2195214T3 publication Critical patent/ES2195214T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

MASAS MOLDEADAS DE POLIMEROS DE INJERTO DEL TIPO ABS QUE CONTIENEN: A) DE UN 30 A UN 80 EN PESO PROPORCIONAL, PREFERENTEMENTE DE UN 35 A UN 75 EN PESO PROPORCIONAL Y CON ESPECIAL PREFERENCIA DE UN 40 A UN 70 EN PESO PROPORCIONAL, DE UN POLIMERO DE INJERTO PRODUCIDO POR POLIMERIZACION EN SOLUCION, CON UN CONTENIDO DE CAUCHO DE UN 20 A UN 50 % EN PESO, PREFERENTEMENTE DE UN 22,5 A UN 45 % EN PESO Y CON ESPECIAL PREFERENCIA DE UN 25 A UN 40 % EN PESO, Y UN DIAMETRO MEDIO DE PARTICULA DE LA FASE DE CAUCHO DE ENTRE 80 Y 600 NM, PREFERENTEMENTE DE 150 A 400 NM Y CON ESPECIAL PREFERENCIA ENTRE 200 Y 350 NM; B) DE UN 5 A UN 50 EN PESO PROPORCIONAL, PREFERENTEMENTE DE UN 7,5 A UN 45 EN PESO PROPORCIONAL Y CON ESPECIAL PREFERENCIA DE UN 10 A UN 40 EN PESO PROPORCIONAL, DE UN POLIMERO DE ABS PRODUCIDO POR POLIMERIZACION EN MASA, SOLUCION O SUSPENSION, CON UN CONTENIDO DE CAUCHO DE UN 3 A UN 18 % EN PESO, PREFERENTEMENTE DE UN 5 A UN 16,5 % EN PESO Y CON ESPECIAL PREFERENCIA DE UN 7,5 A UN 15 % EN PESO, Y UN DIAMETRO MEDIO DE PARTICULA DE LA FASE DE CAUCHO DE ENTRE 700 Y 15.000 NM, PREFERENTEMENTE DE 800 A 10.000 NM Y CON ESPECIAL PREFERENCIA ENTRE 1.000 Y 5.000 NM; C) DE UN 5 A UN 70 EN PESO PROPORCIONAL, PREFERENTEMENTE DE UN 7,5 A UN 65 EN PESO PROPORCIONAL Y CON ESPECIAL PREFERENCIA DE UN 10 A UN 60 EN PESO PROPORCIONAL, AL MENOS DE UNA RESINA TERMOPLASTICA, CONSTRUIDA A PARTIR DE UNIDADES DE MONOMEROS DE VINILO Y PRODUCIDA SIN CAUCHO AL MENOS POR POLIMERIZACION EN MASA, SOLUCION O SUSPENSION.
ES98106020T 1997-04-15 1998-04-02 Materias moldeables abs con muy alta resiliencia fabricadas sin emulsion. Expired - Lifetime ES2195214T3 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
DE19715595A DE19715595A1 (de) 1997-04-15 1997-04-15 Emulsionsfrei hergestellte ABS-Formmassen mit sehr hohrer Kerbschlagzähigkeit

Publications (1)

Publication Number Publication Date
ES2195214T3 true ES2195214T3 (es) 2003-12-01

Family

ID=7826505

Family Applications (1)

Application Number Title Priority Date Filing Date
ES98106020T Expired - Lifetime ES2195214T3 (es) 1997-04-15 1998-04-02 Materias moldeables abs con muy alta resiliencia fabricadas sin emulsion.

Country Status (9)

Country Link
EP (1) EP0872520B1 (es)
JP (1) JPH10292087A (es)
CN (1) CN1137205C (es)
AR (1) AR012416A1 (es)
AU (1) AU741719B2 (es)
BR (1) BR9801051A (es)
CA (1) CA2234542A1 (es)
DE (2) DE19715595A1 (es)
ES (1) ES2195214T3 (es)

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10127748A1 (de) * 2001-06-07 2002-12-12 Bayer Ag Verbund enthaltend ABS
CN102108165B (zh) * 2009-12-23 2012-10-10 中国石油天然气股份有限公司 一种高光泽和高刚性abs树脂组合物
CN103059560B (zh) * 2012-12-14 2015-03-04 上海金山锦湖日丽塑料有限公司 一种高性能尼龙类合金树脂及其制备方法
KR102065685B1 (ko) 2016-12-28 2020-01-13 주식회사 엘지화학 열가소성 수지 조성물, 이의 제조방법 및 이를 포함하는 사출 성형품
CN111004470B (zh) * 2019-12-20 2022-08-23 上海锦湖日丽塑料有限公司 一种高尺寸稳定性abs树脂及其制备方法

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3928494A (en) * 1973-01-09 1975-12-23 Monsanto Co Polyblend of two types of ABS graft polymers and a copolymer matrix
DE3926273A1 (de) * 1989-08-09 1991-02-14 Bayer Ag Abs-formmassen mit verbesserter streckspannung
US5210135A (en) * 1989-08-09 1993-05-11 Bayer Aktiengesellschaft ABS moulding compounds with improved yield stress
DE4110459A1 (de) * 1991-03-30 1992-10-01 Basf Ag Abs-formmassen mit bimodaler kautschukpartikelgroessenverteilung
DE19507749A1 (de) * 1995-03-06 1996-09-12 Bayer Ag Thermoplastische Formmassen vom ABS-Typ
DE19518025A1 (de) * 1995-05-17 1996-11-21 Bayer Ag Thermoplastische ABS-Formmassen

Also Published As

Publication number Publication date
AR012416A1 (es) 2000-10-18
AU6061198A (en) 1998-10-22
DE19715595A1 (de) 1998-10-22
EP0872520A1 (de) 1998-10-21
DE59807924D1 (de) 2003-05-22
BR9801051A (pt) 1999-12-14
JPH10292087A (ja) 1998-11-04
CN1197816A (zh) 1998-11-04
CN1137205C (zh) 2004-02-04
CA2234542A1 (en) 1998-10-15
EP0872520B1 (de) 2003-04-16
AU741719B2 (en) 2001-12-06

Similar Documents

Publication Publication Date Title
ES2153388T3 (es) Procedimientos de polimerizacion y composiciones de toner preparadas mediante los mismos.
ES2106575T3 (es) Composiciones de polimeros abs con superficie mate uniforme.
ES2185613T3 (es) Compuestos de resina termoplastica.
NO931759L (no) Slagmodifisert podingskopolymer inneholdende propylen medbred molekylvektsfordeling
KR910018481A (ko) 무광 표면 외관을 갖는, 방향족 폴리카보네이트 수지, abs 중합체 및 san 공중합체의 성형 조성물
BR9906970A (pt) "massas de moldagem abs de policarbonato antichamas""
AR010665A1 (es) Composiciones de moldeo termoplasticas del tipo abs, y empleo de las mismas para la fabricacion de piezas moldeadas
ES2195214T3 (es) Materias moldeables abs con muy alta resiliencia fabricadas sin emulsion.
KR920000863A (ko) 열가소성 성형 재료
ATE133988T1 (de) Thermoplastische polymere zusammensetzungen, welche modifikatoren der schmelz-rheologie enthalten
KR960014217A (ko) 재순환한 물질을 함유하고 있는 발포성의 스티렌 중합체
KR910014451A (ko) 열처리-밀봉 가능한 열가소성 성형 재료
KR960034306A (ko) 무광택 열가소성 성형재료
ES2172621T3 (es) Masas termoplasticas con contraste frente a rayos x mejorado.
KR900014514A (ko) 열가소성 수지 조성물
ES2059026T3 (es) Masas de moldeo termoplasticas ignifugas.
ES2145947T3 (es) Masas de moldeo termoplasticas del tipo-abs.
BR9916171A (pt) Massas de moldagem abs de alta resistência ao choque
KR920002693A (ko) 할로겐없이 방염처리된 abs성형재료
ES2070251T3 (es) Composiciones de resinas de policarbonato aromatico y san o resinas san y abs.
ES2109743T3 (es) Composiciones mate de polimeros abs.
ATE202126T1 (de) Film aus polymer
ES2040921T3 (es) Mezclas de polimeros termoplasticos pulverulentos.
BR9813822A (pt) Composição de moldagem termoplástica que é opaca ao raio-x
EP0953604A3 (en) Thermoplastic resin composition