FR2842469A1 - Product for protecting automobile bodywork components comprises a sheet of hot-molded polymer foam with a grainy skin covered with a pressure-sensitive adhesive of low adhesive power - Google Patents
Product for protecting automobile bodywork components comprises a sheet of hot-molded polymer foam with a grainy skin covered with a pressure-sensitive adhesive of low adhesive power Download PDFInfo
- Publication number
- FR2842469A1 FR2842469A1 FR0209032A FR0209032A FR2842469A1 FR 2842469 A1 FR2842469 A1 FR 2842469A1 FR 0209032 A FR0209032 A FR 0209032A FR 0209032 A FR0209032 A FR 0209032A FR 2842469 A1 FR2842469 A1 FR 2842469A1
- Authority
- FR
- France
- Prior art keywords
- sheet
- adhesive
- protective part
- part according
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
La présente invention concerne une feuille de protection auto adhésiveThe present invention relates to a self-adhesive protective sheet.
destinée à protéger la carrosserie des véhicules automobiles, notamment pendant les transferts de sorties d'usine, de livraison ou au moment des interventions de maintenance ou de intended to protect the bodywork of motor vehicles, in particular during transfers from the factory, delivery or at the time of maintenance or
réparation dans les garages.repair in garages.
De l'art antérieur, on connaît déjà des films en matière plastique que l'on peut fixer sur les carrosseries des véhicules afin de les protéger des intempéries, de la lumière ou de petits chocs. Il s'agit généralement de films plats, imperméables à l'eau, From the prior art, plastic films are already known which can be fixed to the bodywork of vehicles in order to protect them from bad weather, light or small impacts. These are generally flat, waterproof films,
plus ou moins étirables.more or less stretchable.
Cependant, lorsqu'ils sont utilisés pour la protection des voitures qui sortent de la chaîne de fabrication et qui viennent d'être peintes, ces films peuvent rendre imparfait le However, when used for the protection of cars which have just left the production line and which have just been painted, these films can make the
séchage de la peinture et entraîner des défauts d'aspects très difficiles à éliminer. drying of the paint and causing appearance defects which are very difficult to remove.
Obiet de l'invention La présente invention a pour but de remédier aux inconvénients des films de l'art antérieur en proposant de nouvelles pièces de protection pour éléments de carrosserie qui sont autoadhésives, thermoformées, adaptables aux formes de ladite carrosserie de façon à la protéger des chocs et intempéries, et garantissent l'intégrité de la surface Object of the invention The object of the present invention is to remedy the drawbacks of films of the prior art by proposing new protective parts for bodywork elements which are self-adhesive, thermoformed, adaptable to the shapes of said bodywork so as to protect it. shocks and bad weather, and guarantee the integrity of the surface
protégée en permettant un échange entre celle-ci et l'air ambiant. protected by allowing an exchange between it and the ambient air.
Selon l'invention, cette pièce de protection est essentiellement caractérisée en ce qu'il s'agit d'une feuille de matière plastique alvéolée thermoformable, dont l'une des faces présente un aspect de peau grainée et est enduite sur au moins une partie de sa surface d'une couche de masse adhésive sensible à la pression, faiblement adhésive et According to the invention, this protective part is essentially characterized in that it is a thermoformable cellular plastic sheet, one of the faces of which has the appearance of grainy skin and is coated on at least part on its surface a layer of pressure-sensitive, weakly adhesive and
fortement cohésive.strongly cohesive.
L'invention concerne également l'utilisation de cette pièce de protection pour protéger les parties de carrosserie exposées aux chocs ou aux intempéries, notamment pendant les phases de finition en usine, de transport en concession, ou d'interventions The invention also relates to the use of this protective part to protect the body parts exposed to shocks or bad weather, in particular during the finishing phases in the factory, in concession transport, or in interventions.
(maintenance, réparations) dans les garages. (maintenance, repairs) in garages.
DescriptionDescription
La pièce de protection adhésive selon l'invention est constituée d'une feuille de matière plastique alvéolée, en matière thermoformable, recouverte au moins en partie, sur l'une de ses faces, laquelle présente un aspect de peau grainée, d'une couche de The adhesive protective part according to the invention consists of a sheet of cellular plastic material, of thermoformable material, covered at least in part, on one of its faces, which has an appearance of grainy skin, a layer of
masse adhésive sensible à la pression. pressure-sensitive adhesive mass.
Pour réaliser l'invention, on choisit de préférence une feuille de mousse de polyoléfine, préférentiellement en polypropylène non réticulé, dont l'une au moins de ses faces présente une surface continue irrégulière, formée par des parois de cellules fermées. De telles feuilles de mousse peuvent être obtenues à partir d'une mousse qui n'a pas subit de "postexpansion", et présente un aspect de peau " grainée " continue. Si la feuille de mousse ne présente pas un relief suffisant, on peut accentuer le relief au moyen d'un traitement thermique ou d'un traitement mécanique, tel que par exemple un calandrage. A titre d'exemple, on peut utiliser des feuilles de mousse de polypropylène non réticulé commercialisées par la société PACTIV Sentinel, par exemple sous la référence P 515, dont la surface de l'une de ses faces présente des " grains " irréguliers ayant une amplitude de quelques dixièmes de mm et séparés entre eux de quelques mm (par exemple 1 à 3 mm). L'épaisseur de la feuille est de l'ordre de 1 à 4 mm et la seconde face peut être lisse ou grainée. On préfère généralement utiliser une feuille dont les deux faces sont grainées de façon à réduire les surfaces de contact entre deux feuilles consécutives dans les piles de stockage et pouvoir empiler ainsi les feuilles adhésivées To carry out the invention, a polyolefin foam sheet, preferably made of non-crosslinked polypropylene, is preferably chosen, at least one of its faces having an irregular continuous surface, formed by walls of closed cells. Such foam sheets can be obtained from a foam which has not undergone "post expansion", and has a continuous "grainy" skin appearance. If the foam sheet does not have sufficient relief, the relief can be accentuated by means of a heat treatment or a mechanical treatment, such as for example calendering. By way of example, it is possible to use sheets of uncrosslinked polypropylene foam sold by the company PACTIV Sentinel, for example under the reference P 515, the surface of one of its faces having irregular "grains" having a amplitude of a few tenths of mm and separated from them by a few mm (for example 1 to 3 mm). The thickness of the sheet is of the order of 1 to 4 mm and the second face can be smooth or grained. It is generally preferred to use a sheet whose two faces are grained so as to reduce the contact surfaces between two consecutive sheets in the storage stacks and thus be able to stack the adhesive sheets.
sans qu'il soit nécessaire d'interposer un protecteur antiadhérent entre ces deux feuilles. without the need to interpose a non-stick protector between these two sheets.
Selon l'invention, la feuille de mousse de polyoléfine est recouverte sur au moins une partie de sa face présentant l'aspect d'une peau grainée, d'une couche de masse adhésive sensible à la pression. Cette masse adhésive doit être capable de conférer à la feuille un pouvoir adhésif assez faible, généralement inférieur à 1 N/cm, par exemple de According to the invention, the polyolefin foam sheet is covered on at least part of its face having the appearance of grainy skin, with a layer of pressure-sensitive adhesive mass. This adhesive mass must be capable of giving the sheet a fairly low adhesive power, generally less than 1 N / cm, for example
l'ordre de 0,5 à 1 N/cm (mesuré par traction sous un angle de 900). of the order of 0.5 to 1 N / cm (measured by traction at an angle of 900).
La masse adhésive doit également présenter une bonne cohésion afin de ne pas se séparer de la feuille de mousse lors du retrait de la pièce de protection, ainsi qu'une excellente inertie chimique vis-à-vis des peintures et vernis. Avantageusement, la masse adhésive présente ainsi une cohésion (tenue au fluage) supérieure à 100 heures, lorsque The adhesive mass must also have good cohesion so as not to separate from the foam sheet when the protective part is removed, as well as excellent chemical inertness with regard to paints and varnishes. Advantageously, the adhesive mass thus has a cohesion (resistance to creep) greater than 100 hours, when
mesurée à 90'C et sous une contrainte de 1,5 kg pour 5 cm2. measured at 90 ° C and under a stress of 1.5 kg per 5 cm2.
Parmi les masses adhésives sensibles à la pression convenant dans le cadre de la présente invention, on préfère les masses adhésives de type acrylique en phase solvant et plus particulièrement les masses acryliques réticulées. La masse adhésive est déposée sur la feuille de mousse de polyoléfine soit directement par enduction, soit selon la technique du transfert o l'on enduit en premier lieu la masse adhésive sur une feuille de papier traité antiadhérent, puis l'ensemble ainsi obtenu est déposé sur une face de la feuille de mousse en permettant d'obtenir la feuille adhésivée après retrait du protecteur antiadhérent. De préférence, la face de la feuille recevant la couche adhésive subit préalablement un traitement CORONA, dans le but Among the pressure-sensitive adhesive masses which are suitable in the context of the present invention, the acrylic-type adhesive masses in the solvent phase and more particularly the crosslinked acrylic masses are preferred. The adhesive mass is deposited on the polyolefin foam sheet either directly by coating, or by the transfer technique where the adhesive mass is first coated on a sheet of non-treated treated paper, then the assembly thus obtained is deposited on one side of the foam sheet, making it possible to obtain the adhesive sheet after removal of the non-stick protector. Preferably, the face of the sheet receiving the adhesive layer undergoes a CORONA treatment beforehand, with the aim of
d'obtenir une liaison plus forte entre la surface de la feuille et la couche adhésive. to obtain a stronger bond between the surface of the sheet and the adhesive layer.
Après enduction et retrait du papier protecteur antiadhérent (qui peut être recyclé), la feuille adhésivée peut être thermoformée sur un moule à dépression de façon After coating and removing the release liner (which can be recycled), the adhesive sheet can be thermoformed on a vacuum mold so
à obtenir des protecteurs s'adaptant parfaitement aux formes de la carrosserie. to obtain protectors that adapt perfectly to the shapes of the bodywork.
En variante, la feuille de mousse peut être thermoformée puis adhésivée partiellement au moyen d'un robot qui dépose soit des points de matière adhésive, soit Alternatively, the foam sheet can be thermoformed and then partially adhesive-coated by means of a robot which deposits either dots of adhesive material or
un cordon fibérisé.a fiberized cord.
D'une façon générale, la feuille de mousse est recouverte d'une couche de masse Generally, the foam sheet is covered with a layer of mass
adhésive représentant de l'ordre de 20 à 60 g/m2. adhesive representative of the order of 20 to 60 g / m2.
Le choix particulier d'une feuille de mousse présentant une surface grainée permet d'obtenir une surface adhésive irrégulière qui n'adhère à la surface de la carrosserie que par des points de contact et laisse par conséquent des circuits de circulation d'air entre la majeure partie de la surface de la carrosserie et la couche The particular choice of a foam sheet having a grained surface makes it possible to obtain an irregular adhesive surface which adheres to the surface of the bodywork only through contact points and consequently leaves air circulation circuits between the major part of the body surface and the layer
adhésive.adhesive.
Cette caractéristique permet d'obtenir une protection non occlusive de la carrosserie qui évite par exemple une détérioration de la surface peinte, même dans le cas d'une peinture récente dont la phase de séchage n'est pas encore totalement terminée. De plus, l'utilisation d'une feuille de mousse en remplacement des films habituels, garantit une meilleure protection contre les chocs et facilite la mise en place, notamment dans le cas des protections thermoformées destinées à la protection de parties complexes des véhicules, telles que par exemple des pare-chocs peints ou des This characteristic makes it possible to obtain non-occlusive protection of the bodywork which, for example, prevents deterioration of the painted surface, even in the case of a recent paint whose drying phase is not yet completely finished. In addition, the use of a foam sheet to replace the usual films, guarantees better protection against impact and facilitates the installation, in particular in the case of thermoformed protections intended for the protection of complex parts of vehicles, such as such as painted bumpers or
ailes de la carrosserie.body fenders.
Selon une variante de réalisation, on utilise une feuille de mousse de polypropylène traitée à l'aide d'agents anti-UV, donnant ainsi une meilleure longévité aux pièces de protection lorsque ces dernières sont exposées longuement à la lumière naturelle. Ces pièces, dont le pouvoir adhésif n'est pas affecté après retrait, peuvent être ainsi réutilisées, plusieurs fois, réduisant ainsi les rejets industriels, ce qui constitue un According to an alternative embodiment, a polypropylene foam sheet treated with anti-UV agents is used, thus giving better durability to the protective parts when the latter are exposed for a long time to natural light. These parts, whose adhesive power is not affected after removal, can be reused several times, thus reducing industrial waste, which constitutes a
avantage additionnel de l'invention. additional advantage of the invention.
Selon une autre variante de réalisation, le thermoformage est assorti d'une découpe particulière de la feuille de mousse afin d'obtenir, après le thermoformage, un profil en forme de métal déployé qui augmente ainsi considérablement le caractère respirant du protecteur, tout en assurant une bonne protection contre les chocs et les intempéries. Les exemples de réalisation suivants, qui ne doivent pas être considérés comme According to another alternative embodiment, the thermoforming is accompanied by a particular cut out of the foam sheet in order to obtain, after the thermoforming, a profile in the form of expanded metal which thus considerably increases the breathability of the protector, while ensuring good protection against shocks and bad weather. The following exemplary embodiments, which should not be considered as
limitatifs, permettent de mieux comprendre l'invention. limiting, allow a better understanding of the invention.
Exemple 1:Example 1:
On prépare dans un malaxeur une masse adhésive à partir d'une base (réf. BPS 5231 fournie par la société TOYO) titrant 40% d'extrait sec et on ajoute 4% en poids d'un agent réticulant (BXX 5134 fournie par la société TOYO). Cette masse adhésive est enduite sur une feuille anti-adhérente (réf. R1610 ou R1615 de chez SOPAL) de façon à obtenir, après séchage des solvants, environ 30g/m de masse adhésive sensible à la pression. Cette couche adhésive est ensuite transférée sur une feuille de mousse de polypropylène non réticulé à surfaces grainées (obtenue de la société PAKTIV Sentinel), et d'épaisseur d'environ 2 mm. La surface recevant la couche adhésive a été préalablement traitée selon le procédé CORONA. Après transfert, la feuille antiadhérente est retirée et la feuille de mousse peut être encerclée sur elle-même sans protecteur. Cette feuille adhésivée est ensuite découpée et thermoformée par dépression pour obtenir des coques adhésivées sur leur face interne et utilisables pour protéger les parties exposées aux chocs des pare-chocs d'automobile. Ces coques adhésivées sont An adhesive mass is prepared in a mixer from a base (ref. BPS 5231 supplied by the company TOYO) titrating 40% of dry extract and 4% by weight of a crosslinking agent (BXX 5134 supplied by the TOYO company). This adhesive mass is coated on a non-stick sheet (ref. R1610 or R1615 from SOPAL) so as to obtain, after drying of the solvents, about 30 g / m of pressure-sensitive adhesive mass. This adhesive layer is then transferred to a sheet of non-crosslinked polypropylene foam with grained surfaces (obtained from the company PAKTIV Sentinel), and of thickness of approximately 2 mm. The surface receiving the adhesive layer was previously treated according to the CORONA process. After transfer, the non-stick sheet is removed and the foam sheet can be encircled on itself without a protector. This adhesive sheet is then cut and thermoformed by vacuum to obtain adhesive shells on their internal face and usable to protect the parts exposed to shocks of automobile bumpers. These adhesive shells are
repositionnables et peuvent être utilisées plusieurs fois. repositionable and can be used multiple times.
Selon une variante de cet exemple, on utilise une feuille de mousse en polypropylène non réticulé traité à l'aide d'un additif anti-UV. Ce traitement du support augmente la résistance à la lumière du jour et permet un recyclage plus long des coques According to a variant of this example, use is made of a non-crosslinked polypropylene foam sheet treated with an anti-UV additive. This treatment of the support increases the resistance to daylight and allows a longer recycling of the hulls
de protection.protection.
Exemple 2:Example 2:
On procède pour cet exemple de façon analogue à l'exemple 1, à l'exception de la masse adhésive qui est ici formulée à partir d'un produit de référence Acris 663 (fourni par la société ICAP), auquel est ajouté 0,25% d'un agent réticulant (ICAPLINK The procedure for this example is analogous to Example 1, with the exception of the adhesive mass which is here formulated from a reference product Acris 663 (supplied by the company ICAP), to which is added 0.25 % of a crosslinking agent (ICAPLINK
664).664).
Exemple 3:Example 3:
Selon cet exemple, on utilise une feuille de mousse de polypropylène à cellules According to this example, a sheet of polypropylene foam with cells is used.
fermées de 3 mm d'épaisseur, dont la surface présente une structure à peau grainée. closed 3 mm thick, the surface of which has a grainy skin structure.
L'adhésif utilisé est une masse acrylique hot melt (fusible sans solvant) de référence ACRESIN 258 UV (obtenu de la société BASF). L'enduction est faite directement sur la surface de la feuille de mousse au moyen d'une buse, de façon à déposer environ g/m2 de masse adhésive chauffée à 140'C1450C. La couche adhésive est réticulée par passage sous lampe UV (lampe HONLE UVA Print 740), puissance 240W/cm, puis le complexe adhésivé est ensuite refroidi par passage sur un cylindre réfrigéré. La feuille de mousse ainsi adhésivée, qui peut être thermoformée sur moule à dépression, The adhesive used is an acrylic hot melt (solvent-free fuse) reference ACRESIN 258 UV (obtained from the company BASF). The coating is made directly on the surface of the foam sheet by means of a nozzle, so as to deposit approximately g / m2 of adhesive mass heated to 140'C1450C. The adhesive layer is crosslinked by passage under a UV lamp (HONLE UVA Print 740 lamp), power 240W / cm, then the adhesive complex is then cooled by passage over a refrigerated cylinder. The foam sheet thus adhered, which can be thermoformed on a vacuum mold,
est utilisée pour fabriquer des protecteurs auto-adhésifs de pare-chocs. is used to make self-adhesive bumper protectors.
Les adhésifs ci-dessus ont été formulés et sélectionnés particulièrement pour obtenir des éléments de protection repositionnables, c'est-à-dire présentant un pouvoir adhésif suffisant pour maintenir la protection en place dans des conditions climatiques et d'environnement difficiles, mais faciles à retirer, sans laisser de traces d'adhésif sur le support à protéger et capables d'être repositionnés soit sur le même véhicule, soit sur The above adhesives have been specially formulated and selected to obtain repositionable protective elements, that is to say having sufficient adhesive power to keep the protection in place in difficult climatic and environmental conditions, but easy to remove, without leaving traces of adhesive on the support to be protected and capable of being repositioned either on the same vehicle or on
un véhicule différent.a different vehicle.
Les mesures effectuées sur ces masses adhésives montrent une tenue au fluage supérieure à 100 heures à une température de 90'C et sous une charge de 1,5 kg pour The measurements carried out on these adhesive masses show a creep resistance greater than 100 hours at a temperature of 90 ° C. and under a load of 1.5 kg for
une surface de 5 cm2 (lx5 cm).an area of 5 cm2 (lx5 cm).
Les pouvoirs adhésifs de ces masses adhésives, mesurés sur plaque de tôle peinte et sous un angle de traction de 900, à une vitesse de traction de 100 mm/mn, sont The adhesive powers of these adhesive masses, measured on a painted sheet metal plate and at a traction angle of 900, at a traction speed of 100 mm / min, are
compris entre 0,5 et 1N/cm.between 0.5 and 1N / cm.
L'aspect de surface en " grains " de la feuille support en mousse a pour effet de limiter la surface de contact entre l'adhésif et la carrosserie et ménager ainsi des espaces libres communiquants dans lesquels l'air peut circuler et évacuer les vapeurs résiduelles de solvant des peintures en permettant d'achever complètement la réticulation. Par la combinaison de la feuille de mousse et de l'adhésif, on obtient une protection qui est à The "grain" surface appearance of the foam support sheet has the effect of limiting the contact surface between the adhesive and the body and thus providing communicating free spaces in which air can circulate and evacuate residual vapors. solvent paint allowing complete crosslinking. By the combination of the foam sheet and the adhesive, a protection is obtained which is
la fois imperméable aux intempéries et respirante sur sa face adhésivée. both weatherproof and breathable on its adhesive side.
L'invention trouve notamment application pour la protection d'éléments de carrosserie peints. Elle s'applique aussi à la protection d'éléments non peints comme par The invention finds particular application for the protection of painted bodywork elements. It also applies to the protection of unpainted elements such as
exemple des plastiques injectés.example of injected plastics.
Claims (8)