IN2015DN00705A - - Google Patents

Download PDF

Info

Publication number
IN2015DN00705A
IN2015DN00705A IN705DEN2015A IN2015DN00705A IN 2015DN00705 A IN2015DN00705 A IN 2015DN00705A IN 705DEN2015 A IN705DEN2015 A IN 705DEN2015A IN 2015DN00705 A IN2015DN00705 A IN 2015DN00705A
Authority
IN
India
Prior art keywords
content
steel sheet
bainite
pearlite
martensite
Prior art date
Application number
Other languages
English (en)
Inventor
Akari Tamaki
Kazuo Hikida
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of IN2015DN00705A publication Critical patent/IN2015DN00705A/en

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/001—Heat treatment of ferrous alloys containing Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D7/00—Modifying the physical properties of iron or steel by deformation
    • C21D7/13—Modifying the physical properties of iron or steel by deformation by hot working
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Coating With Molten Metal (AREA)
IN705DEN2015 2012-08-15 2013-08-15 IN2015DN00705A (2)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012180186 2012-08-15
PCT/JP2013/071971 WO2014027682A1 (ja) 2012-08-15 2013-08-15 熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材

Publications (1)

Publication Number Publication Date
IN2015DN00705A true IN2015DN00705A (2) 2015-06-26

Family

ID=50101304

Family Applications (1)

Application Number Title Priority Date Filing Date
IN705DEN2015 IN2015DN00705A (2) 2012-08-15 2013-08-15

Country Status (12)

Country Link
US (1) US10570470B2 (2)
EP (1) EP2886674B1 (2)
JP (1) JP5505574B1 (2)
KR (1) KR101674331B1 (2)
CN (2) CN104583437A (2)
CA (1) CA2880946C (2)
IN (1) IN2015DN00705A (2)
MX (1) MX2015001772A (2)
RU (1) RU2599934C2 (2)
TW (1) TWI481729B (2)
WO (1) WO2014027682A1 (2)
ZA (1) ZA201501490B (2)

Families Citing this family (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101417260B1 (ko) * 2012-04-10 2014-07-08 주식회사 포스코 재질 균일성이 우수한 고탄소 열연강판 및 이의 제조방법
JP2015196890A (ja) * 2014-04-02 2015-11-09 本田技研工業株式会社 ホットスタンプ成形体
WO2016157896A1 (ja) * 2015-04-01 2016-10-06 Ｊｆｅスチール株式会社 熱延鋼板およびその製造方法
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
CN105316601B (zh) * 2015-10-28 2017-03-22 安徽省三方新材料科技有限公司 一种顽石破碎机用衬板及其制备方法
KR20170075046A (ko) 2015-12-22 2017-07-03 주식회사 포스코 내식성이 우수한 열간 프레스 성형품 및 그 제조방법
CN107127238B (zh) * 2016-02-26 2019-12-27 宝山钢铁股份有限公司 一种锌系镀覆钢板或钢带的热冲压成型方法
KR101819345B1 (ko) 2016-07-07 2018-01-17 주식회사 포스코 균열전파 저항성 및 연성이 우수한 열간성형 부재 및 이의 제조방법
KR101963936B1 (ko) 2016-11-08 2019-07-31 한국과학기술원 전자파 신호 송수신 안테나 및 em-터널이 내장된 구조를 갖는 인쇄회로기판 및 그 제작 방법
WO2018220430A1 (en) 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
KR101977474B1 (ko) * 2017-08-09 2019-05-10 주식회사 포스코 표면 품질, 강도 및 연성이 우수한 도금강판
RU2738130C1 (ru) 2017-10-24 2020-12-08 Арселормиттал Способ изготовления гальванизированной и отожженной листовой стали
KR102206929B1 (ko) * 2017-10-24 2021-01-25 아르셀러미탈 코팅된 강 시트의 제조 방법
CN107604266A (zh) * 2017-10-31 2018-01-19 桂林加宏汽车修理有限公司 一种高韧性钢合金
MX2020005026A (es) 2017-11-17 2020-08-13 Arcelormittal Un metodo para la fabricacion de hoja de acero recubierta con zinc resistente a la fragilizacion por metal liquido.
CN109365606A (zh) * 2018-11-30 2019-02-22 宝山钢铁股份有限公司 一种耐腐蚀性优良的锌系镀层钢板或钢带的成形方法
EP3929314A4 (en) * 2019-02-22 2022-01-12 JFE Steel Corporation HOT PRESSED ELEMENT AND METHOD FOR ITS MANUFACTURE AND METHOD FOR PRODUCTION OF STEEL SHEET FOR HOT PRESSED ELEMENTS
EP4065736A1 (en) * 2019-11-27 2022-10-05 Tata Steel IJmuiden B.V. Method of hot press forming a steel article and steel article
JP7648620B2 (ja) * 2019-12-20 2025-03-18 ポスコホールディングス インコーポレーティッド 熱間成形用鋼材、熱間成形部材及びこれらの製造方法
CN111676417A (zh) * 2020-05-07 2020-09-18 天津英利模具制造有限公司 一种轻量化汽车用高强钢板及其热冲压成型工艺
KR102790648B1 (ko) * 2020-05-13 2025-04-04 닛폰세이테츠 가부시키가이샤 핫 스탬프용 강판 및 핫 스탬프 성형체
KR102790645B1 (ko) 2020-05-13 2025-04-04 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형체
JP7553837B2 (ja) * 2020-10-16 2024-09-19 日本製鉄株式会社 ホットスタンプ用鋼板及びその製造方法、並びに、ホットスタンプ部材及びその製造方法
WO2022195024A1 (en) * 2021-03-17 2022-09-22 Tata Steel Ijmuiden B.V. Steel strip, sheet or blank and method for producing a hot-formed part or a heat-treated pre-formed part
WO2023008670A1 (ko) * 2021-07-30 2023-02-02 현대제철 주식회사 열간 프레스용 강판 및 이를 이용하여 제조된 알루미늄계 도금 블랭크
JP7512987B2 (ja) * 2021-09-22 2024-07-09 Ｊｆｅスチール株式会社 熱間プレス用鋼板、その製造方法、熱間プレス部材およびその製造方法
WO2023079344A1 (en) * 2021-11-05 2023-05-11 Arcelormittal Method for producing a steel sheet having excellent processability before hot forming, steel sheet, process to manufacture a hot stamped part and hot stamped part
TWI876779B (zh) * 2023-12-18 2025-03-11 中國鋼鐵股份有限公司 高平坦度及超高強度鋼材及其製造方法

Family Cites Families (37)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001226741A (ja) 2000-02-15 2001-08-21 Kawasaki Steel Corp 伸びフランジ加工性に優れた高強度冷延鋼板およびその製造方法
JP3389562B2 (ja) 2000-07-28 2003-03-24 アイシン高丘株式会社 車輌用衝突補強材の製造方法
JP3879459B2 (ja) 2001-08-31 2007-02-14 Ｊｆｅスチール株式会社 高焼入れ性高炭素熱延鋼板の製造方法
JP3468239B2 (ja) * 2001-10-01 2003-11-17 住友金属工業株式会社 機械構造用鋼及びその製造方法
CA2511661C (en) * 2002-12-24 2010-01-26 Nippon Steel Corporation High burring, high strength steel sheet excellent in softening resistance of weld heat affected zone and method of production of same
JP4160840B2 (ja) * 2003-02-19 2008-10-08 新日本製鐵株式会社 形状凍結性に優れた高加工性高強度熱延鋼板とその製造方法
JP4292986B2 (ja) * 2003-04-16 2009-07-08 Ｊｆｅスチール株式会社 高張力冷延鋼板およびその製造方法
JP3885763B2 (ja) 2003-04-25 2007-02-28 住友金属工業株式会社 焼入用溶融亜鉛系めっき鋼板とその製造方法及び用途
JP2005126733A (ja) 2003-10-21 2005-05-19 Nippon Steel Corp 高温加工性にすぐれた熱間プレス用鋼板及び自動車用部材
KR20080082015A (ko) * 2003-12-19 2008-09-10 신닛뽄세이테쯔 카부시키카이샤 초고강도 라인파이프용 강판 및 우수한 저온 인성을 갖는 초고강도 라인파이프, 및 그 제조 방법
JP4288216B2 (ja) * 2004-09-06 2009-07-01 新日本製鐵株式会社 耐水素脆化特性に優れたホットプレス用鋼板、自動車用部材及びその製造方法
JP4575799B2 (ja) 2005-02-02 2010-11-04 新日本製鐵株式会社 成形性に優れたホットプレス高強度鋼製部材の製造方法
RU2277594C1 (ru) * 2005-03-30 2006-06-10 Открытое акционерное общество "Северсталь" Способ производства холоднокатаных листов для глубокой вытяжки
CN101120114B (zh) * 2005-03-31 2013-11-06 株式会社神户制钢所 涂膜附着性、加工性及耐氢脆化特性优异的高强度冷轧钢板和机动车用钢零件
CN101218362B (zh) 2005-07-07 2010-05-12 住友金属工业株式会社 无方向性电磁钢板及其制造方法
JP4967360B2 (ja) * 2006-02-08 2012-07-04 住友金属工業株式会社 熱間プレス用めっき鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
EP1832667A1 (fr) * 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
JP5008173B2 (ja) * 2006-05-17 2012-08-22 日産自動車株式会社 抵抗溶接用高張力鋼板及びその接合方法
KR101399741B1 (ko) * 2007-10-25 2014-05-27 제이에프이 스틸 가부시키가이샤 가공성이 우수한 고강도 용융 아연 도금 강판 및 그 제조 방법
JP5167487B2 (ja) * 2008-02-19 2013-03-21 Ｊｆｅスチール株式会社 延性に優れる高強度鋼板およびその製造方法
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5347392B2 (ja) 2008-09-12 2013-11-20 Ｊｆｅスチール株式会社 延性に優れたホットプレス部材、そのホットプレス部材用鋼板、およびそのホットプレス部材の製造方法
JP2010174301A (ja) * 2009-01-28 2010-08-12 Jfe Steel Corp ダイクエンチ用鋼板
JP4811528B2 (ja) * 2009-07-28 2011-11-09 Ｊｆｅスチール株式会社 高強度冷延鋼板およびその製造方法
JP5786317B2 (ja) * 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 材質安定性と加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
MX356054B (es) * 2010-01-26 2018-05-11 Nippon Steel & Sumitomo Metal Corp Lámina de acero laminada en frío, de alta resistencia y método para la fabricación de la misma.
EA022687B1 (ru) 2010-02-26 2016-02-29 Сумитомо Метал Индастриз, Лтд. Термообработанный стальной материал, способ его получения и базовый стальной материал для него
EP2374910A1 (de) 2010-04-01 2011-10-12 ThyssenKrupp Steel Europe AG Stahl, Stahlflachprodukt, Stahlbauteil und Verfahren zur Herstellung eines Stahlbauteils
JP5440371B2 (ja) 2010-05-12 2014-03-12 新日鐵住金株式会社 熱処理用鋼板およびその製造方法
CN102409235A (zh) * 2010-09-21 2012-04-11 鞍钢股份有限公司 高强度冷轧相变诱导塑性钢板及其制备方法
MX359051B (es) * 2010-10-22 2018-09-13 Nippon Steel & Sumitomo Metal Corp Proceso para producir un artículo moldeado por estampación en caliente, y artículo moldeado por estampación en caliente.
RU2562654C2 (ru) 2011-05-13 2015-09-10 Ниппон Стил Энд Сумитомо Метал Корпорейшн Горячештампованное изделие, способ изготовления горячештампованного изделия, энергопоглощающий элемент и способ изготовления энергопоглощающего элемента
CA2862810C (en) 2012-01-13 2017-07-11 Nippon Steel & Sumitomo Metal Corporation Cold rolled steel sheet and manufacturing method thereof
JP5382278B1 (ja) 2012-01-13 2014-01-08 新日鐵住金株式会社 ホットスタンプ成形体及びその製造方法
BR112014017020B1 (pt) 2012-01-13 2020-04-14 Nippon Steel & Sumitomo Metal Corp chapa de aço laminada a frio e método para produzir chapa de aço laminada a frio
EP2881484B1 (en) 2012-08-06 2017-10-25 Nippon Steel & Sumitomo Metal Corporation Cold-rolled steel sheet, method for producing same, and hot-stamp-molded article
BR112015001774B1 (pt) 2012-08-07 2020-11-10 Nippon Steel Corporation chapa de aço galvanizada para conformação a quente

Also Published As

Publication number Publication date
JPWO2014027682A1 (ja) 2016-07-28
CN109023051A (zh) 2018-12-18
JP5505574B1 (ja) 2014-05-28
WO2014027682A1 (ja) 2014-02-20
CA2880946A1 (en) 2014-02-20
MX2015001772A (es) 2015-05-08
KR101674331B1 (ko) 2016-11-08
US20150284819A1 (en) 2015-10-08
EP2886674A1 (en) 2015-06-24
ZA201501490B (en) 2016-01-27
EP2886674B1 (en) 2020-09-30
RU2015108067A (ru) 2016-10-10
KR20150029742A (ko) 2015-03-18
TW201410878A (zh) 2014-03-16
EP2886674A4 (en) 2016-11-30
US10570470B2 (en) 2020-02-25
RU2599934C2 (ru) 2016-10-20
TWI481729B (zh) 2015-04-21
CA2880946C (en) 2018-06-12
CN104583437A (zh) 2015-04-29

Similar Documents

Publication Publication Date Title
IN2015DN00705A (2)
MX2016007664A (es) Acero de elevada resistencia y procedimiento de fabricacion.
IN2014DN08590A (2)
MX375031B (es) Hoja de acero laminada en caliente.
GB201315448D0 (en) High-strength steel sheet exerting excellent deep drawability at room temperature and warm temperatures and method for warm working same
MX378469B (es) Artìculo moldeado por estampado en caliente, làmina de acero enrollada en frio, y mètodo para manufacturar el artìculo moldeado por estampado en caliente.
MX2020003923A (es) Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma.
MX368564B (es) Lamina de acero laminada en frio, metodo para producir la misma y articulo moldeado mediante estampado en caliente.
MX364430B (es) Hoja de acero laminado en caliente con excelente formabilidad de prensa y metodo de produccion del mismo.
MX2017010537A (es) Chapa de acero laminada en caliente.
MX356131B (es) Artículo moldeado por estampado en caliente, método para producir artículo moldeado por estampado en caliente, miembro absorbedor de energía, y método para producir miembro absorbedor de energía.
MX356054B (es) Lámina de acero laminada en frío, de alta resistencia y método para la fabricación de la misma.
MX2014009994A (es) Lamina de acero laminada en frio y proceso para fabricar la misma.
TW201612331A (en) Hot-rolled steel sheet
MX395449B (es) Lámina de acero galvanizada de alta resistencia y método para producir la misma.
MX2016011437A (es) Lamina de acero con contenido de carbono medio/alto y metodo para la fabricacion de la misma.
MX373607B (es) Artículo moldeado estampado en caliente y método para la producción del mismo.
MX2010008622A (es) Lamina de acero galvanizada por inmersion en caliente, de alta tenacidad, con excelente procesabilidad y procedimiento para la produccion de la misma.
MX2018012680A (es) Lamina de acero galvanizada por inmersion en caliente.
MX357255B (es) Lamina de acero laminada en frio de alta resistencia que tiene excelente capacidad de conformacion en formas complejas y capacidad de perforacion de precision y metodo de fabricacion de la misma.
MX390392B (es) Hoja de acero laminada en caliente.
MX350227B (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia con excelente estirabilidad profunda y susceptibilidad a rebordeado por extendido, y proceso para producir la msima.
MX2016012797A (es) Chapa de acero laminada en frio de alta resistencia, chapa de acero galvanizada en baño caliente de alta resistencia y chapa de acero galvanofusionado en baño caliente de alta resistencia que tiene excelente ductilidad, abocardabilidad por estiramiento y soldabilidad.
IN2015DN00826A (2)
MX2018011606A (es) Chapa de acero galvanizada de alta resistencia y metodo para producir la misma.