JP2000328027A - Lid material - Google Patents
Lid materialInfo
- Publication number
- JP2000328027A JP2000328027A JP11137929A JP13792999A JP2000328027A JP 2000328027 A JP2000328027 A JP 2000328027A JP 11137929 A JP11137929 A JP 11137929A JP 13792999 A JP13792999 A JP 13792999A JP 2000328027 A JP2000328027 A JP 2000328027A
- Authority
- JP
- Japan
- Prior art keywords
- heat
- sensitive adhesive
- adhesive layer
- container
- lid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】
【課題】 容器に熱接着された蓋材を部分的に剥離し後
に、再び蓋材を容器の口部に圧着することにより接着さ
せて容器の開口を塞ぐことができる蓋材を提供すること
である。
【解決手段】 外面から順に紙層と接着層とアルミニウ
ム箔層と加熱により粘着性が発現する感熱粘着剤層から
なり、感熱粘着剤層をアルミニウム箔層の全面ないしは
蓋材が容器に熱接着される際の熱接着部の全体を覆うよ
うに環状に形成された蓋材であって、感熱粘着剤層が水
溶性樹脂からなる海とラジカル重合性単量体の乳化重合
により得られたガラス転移温度が−２０℃以下の樹脂か
らなる島との海島構造を有し、加熱することにより海と
島が逆転して粘着性が発現する構成からなる蓋材であ
る。
PROBLEM TO BE SOLVED: To provide a lid capable of closing an opening of a container by partially peeling off a lid material thermally bonded to a container and then bonding the lid material to a mouth portion of the container again by pressure bonding. To provide materials. SOLUTION: From the outer surface, a paper layer, an adhesive layer, an aluminum foil layer and a heat-sensitive adhesive layer exhibiting tackiness by heating are formed, and the heat-sensitive adhesive layer is heat-bonded to the entire surface of the aluminum foil layer or a lid to a container. Cover material formed in an annular shape so as to cover the entire heat-bonded portion when the heat-sensitive adhesive layer is formed of a water-soluble resin, and a glass transition obtained by emulsion polymerization of a radical polymerizable monomer and the sea. A cover material having a sea-island structure with islands made of a resin having a temperature of -20 ° C or lower, and the sea and the islands are reversed by heating to exhibit adhesiveness.
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、容器の口部に熱接
着して使用される蓋材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lid material which is used by being thermally bonded to a mouth of a container.
【０００２】[0002]
【従来の技術】従来、カップラーメン等の容器の口部に
熱接着により取り付けて容器を密封するための蓋材とし
ては、紙／ポリエチレン／アルミニウム箔／熱接着性樹
脂層からなり、熱接着性樹脂層はエチレン−酢酸ビニル
共重合体を主成分とする熱接着性樹脂を熱溶融押出しに
より積層した構成のものが一般的に使用されている。し
かしながら、カップラーメン容器等の場合には、使用時
に蓋材を容器から一部剥離させて容器に収納されている
小袋をとり出し熱湯を注いだ後に再び蓋をして数分経っ
てから食するのが一般的であるが、上記構成の蓋材で
は、蓋材を容器から一部剥離させて再び蓋をする際に、
蓋材が容器と接着しないため蓋材が開いてしまい容器の
開口を塞ぐことができず、熱湯を容器に注入して数分待
っている間に蓋材が上向きに反って大きく開口し、熱が
外部に逃げてしまい麺を十分に調理できないという欠点
があり、カップ焼きそばのように、熱湯を注ぎ数分間放
置してめんを蒸らした後に湯切りする必要のある用途で
は、湯切りする際に剥離した蓋材と容器の間に隙間がで
きて湯が溢れて湯切りがやりにくい上に、漏れだした湯
で火傷をするおそれがあるという欠点があった。また、
蓋材を部分的に剥離した状態で内容物を取り出して少量
づつ使用する容器の場合には、剥離した蓋材で再び口部
を封止することができないために、使用し始めた容器を
保管するのに不適当であるという欠点があった。2. Description of the Related Art Conventionally, a lid material for sealing a container by attaching it to a mouth portion of a container such as a cup ramen by heat bonding is made of paper / polyethylene / aluminum foil / heat-adhesive resin layer. The resin layer generally has a configuration in which a heat-adhesive resin mainly composed of an ethylene-vinyl acetate copolymer is laminated by hot-melt extrusion. However, in the case of a cup ramen container or the like, the lid material is partially peeled off from the container at the time of use, a small bag stored in the container is taken out, poured with hot water, closed again, and eaten after a few minutes. Although it is common, in the lid material of the above configuration, when the lid material is partially peeled off from the container and re-covered,
Since the lid material does not adhere to the container, the lid material opens and cannot close the opening of the container, and while the hot water is poured into the container and waits for several minutes, the lid material warps upward and opens greatly, However, there is a drawback that noodles escape to the outside and noodles can not be cooked enough.For applications where it is necessary to pour boiling water, leave it for a few minutes, steam the noodles, and then drain it like a cup yakisoba There is a defect that a gap is formed between the peeled lid member and the container, the hot water overflows, it is difficult to drain the hot water, and there is a risk that the leaked hot water may cause a burn. Also,
In the case of a container that is used after removing the contents with the lid partly removed and using it little by little, store the container that has been used since the mouth cannot be sealed again with the peeled lid. There was a drawback that it was unsuitable for doing so.
【０００３】[0003]
【発明が解決しようとする課題】本発明の目的は、容器
に熱接着された蓋材を部分的に剥離した後に、再び蓋材
を容器の口部に圧着することにより接着させて容器の口
部を封止することができる蓋材を提供することである。SUMMARY OF THE INVENTION It is an object of the present invention to provide an object of the present invention, in which after a lid material which has been thermally bonded to a container is partially peeled off, the lid material is again adhered to the opening of the container by pressure bonding. An object of the present invention is to provide a lid member capable of sealing a portion.
【０００４】[0004]
【課題を解決するための手段】内面の少なくとも容器と
熱接着される熱接着部に感熱粘着剤層を有し、前記感熱
粘着剤層が水性エマルジョン樹脂からなる感熱粘着剤組
成物により形成された構成からなる蓋材とすることによ
り、この蓋材を容器に熱接着する際の加熱により感熱粘
着剤層に粘着性が発現した状態となるので、とくにカッ
プラーメン等の容器においては、蓋材を容器から一部剥
離させて容器内に熱湯を注いだ後に、再び蓋材を容器の
口部に圧着することにより蓋材を容器に接着させて口部
を塞ぐことができるとともに、口部を塞いだ状態を維持
できるので熱が外部に逃げることがなく内容物を十分に
調理することができる。Means for Solving the Problems A heat-sensitive adhesive layer is provided at least on a heat-bonded portion of the inner surface which is heat-bonded to a container, and the heat-sensitive adhesive layer is formed of a heat-sensitive adhesive composition comprising an aqueous emulsion resin. By making the lid material having the configuration, the lid material becomes in a state in which the heat-sensitive adhesive layer becomes tacky by heating when the lid material is thermally bonded to the container.In particular, in a container such as a cup ramen, the lid material is used. After pouring hot water into the container after peeling it partly from the container, the lid can be adhered to the container by pressing the lid again to the opening of the container, thereby closing the opening and closing the opening. Since the state can be maintained, the heat can be prevented from escaping to the outside, and the contents can be cooked sufficiently.
【０００５】上記の蓋材において、感熱粘着剤層が、蓋
材が容器に熱接着される際に環状に形成される熱接着部
の全体を覆うように周端縁に環状に形成された構成とす
ることにより、感熱粘着剤層を形成する面積を狭くでき
るので感熱粘着剤組成物の使用量を減らすことができる
とともに、絵柄の印刷工程と感熱粘着剤組成物を使用し
て印刷により感熱粘着剤層を形成する工程をインライン
で行うことができるので、蓋材のコストダウンが可能と
なる。[0005] In the above-mentioned lid material, the heat-sensitive adhesive layer is formed in an annular shape on the peripheral edge so as to cover the entire heat-bonded portion formed in an annular shape when the lid material is thermally bonded to the container. By doing so, the area for forming the heat-sensitive adhesive layer can be reduced, so that the amount of the heat-sensitive adhesive composition used can be reduced. Since the step of forming the agent layer can be performed in-line, the cost of the lid material can be reduced.
【０００６】上記の蓋材において、外面から順に紙層と
接着層とアルミニウム箔層と感熱粘着剤層が積層された
構成とすることにより、遮光性が優れるとともに、カー
ルが発生しにくくなるので蓋材製造時の作業性および蓋
材を容器に熱接着する際の作業性に優れた再封可能な蓋
材とすることができる。[0006] In the above-mentioned lid material, a paper layer, an adhesive layer, an aluminum foil layer and a heat-sensitive adhesive layer are laminated in order from the outer surface, so that the light-shielding property is excellent and curling hardly occurs. A resealable lid material excellent in workability at the time of material production and workability when the lid material is thermally bonded to the container can be obtained.
【０００７】上記の蓋材において、感熱粘着剤層が水溶
性樹脂からなる海と、ラジカル重合性単量体の乳化重合
により得られたガラス転移温度が−２０℃以下の樹脂か
らなる島との海島構造を有し、感熱粘着剤層を加熱する
ことにより海と島が逆転して粘着性が発現する構成とす
ることにより、感熱粘着剤層を形成した状態では非粘着
性であり蓋材の製造および充填工程にて支障をきたすこ
となく、蓋材を容器に熱接着する際の加熱により感熱粘
着剤層に粘着性が発現した状態とすることができるの
で、蓋材を容器から一部剥離した後に再び容器に接着さ
せて開口を封止することが可能となる。[0007] In the above-mentioned lid material, the heat-sensitive adhesive layer is composed of a sea composed of a water-soluble resin and an island composed of a resin having a glass transition temperature of -20 ° C or lower obtained by emulsion polymerization of a radical polymerizable monomer. It has a sea-island structure, and the sea and islands are reversed by heating the heat-sensitive adhesive layer so that the adhesive is developed. The lid can be partially peeled off from the container because the heat-sensitive adhesive layer can be made tacky by heating when the lid is heat-bonded to the container without hindering the production and filling processes. After that, the opening can be sealed by adhering to the container again.
【０００８】[0008]
【発明の実施の形態】以下、図面を引用して本発明の実
施の形態を説明する。図１は本発明の第１実施形態を示
す底面図、図２は図１のＩ−Ｉ断面図、図３は第１実施
形態の蓋材を容器に熱接着した状態を示す断面図、図４
は本発明の第２実施形態を示す底面図、図５は図４のII
−II断面図、図６は第２実施形態の蓋材を容器に熱接着
した状態を示す断面図であって、１，1'は蓋材、２は摘
み部、３は容器、４は熱接着部、11は紙層、12は接着
層、13はアルミニウム箔層、14は感熱粘着剤層、14a は
粘着性発現部、15は絵柄層をそれぞれ表す。Embodiments of the present invention will be described below with reference to the drawings. 1 is a bottom view showing a first embodiment of the present invention, FIG. 2 is a cross-sectional view taken along the line II of FIG. 1, and FIG. 3 is a cross-sectional view showing a state where the lid member of the first embodiment is thermally bonded to a container. 4
FIG. 5 is a bottom view showing the second embodiment of the present invention, and FIG.
FIG. 6 is a cross-sectional view showing a state in which the lid material of the second embodiment is thermally bonded to the container, wherein 1 and 1 ′ are the lid material, 2 is the knob, 3 is the container, and 4 is the heat. An adhesive portion, 11 is a paper layer, 12 is an adhesive layer, 13 is an aluminum foil layer, 14 is a heat-sensitive adhesive layer, 14a is an adhesive expression portion, and 15 is a picture layer.
【０００９】本発明の第１実施形態の蓋材１は図１、図
２に示すとおりである。蓋材１の形状は、図１に示すよ
うに、円形状であって周端縁に外方に突出する摘み部２
が設けられており、内面の全面に感熱粘着剤層14が形成
されている。蓋材１の積層構成は、図２に示すように、
内面から順に感熱粘着剤層14とアルミニウム箔層13と接
着層12と紙層11と絵柄層15が積層された構成である。積
層構成に関しては内面に感熱粘着剤層14を有しておれば
よく外面側の構成は任意である。第１実施形態では蓋材
１の形状を円形状としているが、使用する容器の口部の
形状により楕円形状、４角形状、多角形状等任意の形状
とすることができる。A cover 1 according to a first embodiment of the present invention is as shown in FIGS. As shown in FIG. 1, the shape of the lid member 1 is a circular shape, and the knob portion 2 protruding outward at the peripheral edge.
Is provided, and a heat-sensitive adhesive layer 14 is formed on the entire inner surface. As shown in FIG. 2, the lamination structure of the lid material 1 is as follows.
The heat-sensitive adhesive layer 14, the aluminum foil layer 13, the adhesive layer 12, the paper layer 11, and the picture layer 15 are laminated in this order from the inner surface. Regarding the lamination structure, it is only necessary to have the heat-sensitive adhesive layer 14 on the inner surface, and the structure on the outer surface side is arbitrary. In the first embodiment, the shape of the lid member 1 is circular, but may be any shape such as an elliptical shape, a quadrangular shape, or a polygonal shape depending on the shape of the mouth of the container to be used.
【００１０】第１実施形態の蓋材１を円形状の開口部を
有する容器３の口部に熱接着により取り付けた状態の断
面形状は図３に示すとおりである。蓋材１は内面に形成
された感熱粘着剤層14により容器３の口部に熱接着部４
にて熱接着されて取り付けられている。蓋材１を容器３
に熱接着して取り付ける際の加熱により熱接着部４に対
応した部分の感熱粘着剤層14に粘着性が発現した粘着性
発現部14a となり、粘着性が発現した状態で容器３に接
着されている。したがって、蓋材１を摘み部２を掴んで
容器３から一部引き剥がすと剥がした部分に粘着性が発
現しているので、容器３に熱湯を注入した後に、蓋材１
の剥がした部分を容器３の口部に押しつけることによ
り、容器３の口部に接着させて開口部を被覆することが
できるので熱気が逃げず保温性をよくすることが可能と
なる。FIG. 3 shows a sectional view of the state in which the lid 1 of the first embodiment is attached to the mouth of the container 3 having a circular opening by thermal bonding. The lid material 1 is attached to the mouth of the container 3 by the heat-sensitive adhesive layer 14 formed on the inner surface.
It is attached by heat bonding. Lid 1 into container 3
The heat-adhesive portion 14a, in which the heat-sensitive adhesive layer 14 at the portion corresponding to the heat-bonded portion 4 has developed tackiness due to the heating at the time of attachment, is adhered to the container 3 with the tackiness developed. I have. Therefore, when the lid 1 is gripped by the grip portion 2 and partially peeled off from the container 3, tackiness is developed in the peeled portion.
By pressing the peeled portion against the opening of the container 3, the opening can be covered by adhering to the opening of the container 3, so that hot air does not escape and heat insulation can be improved.
【００１１】本発明の第２実施形態の蓋材1'は図４、図
５に示すとおりである。蓋材1'の形状は、図４に示すよ
うに、円形状であって周端縁に外方に突出する摘み部２
が設けられており、内面の摘み部２を除く周縁部に一定
巾の環状に感熱粘着剤層14が形成されている。感熱粘着
剤層14は蓋材1'が容器３の口部に熱接着される熱接着部
４の全体を覆うように環状に形成されており、環状に形
成された感熱粘着剤層14の内側の領域にはアルミニウム
箔層13が露出した状態である。環状に形成された感熱粘
着剤層14の巾は容器の口部の熱接着部４の巾よりも広く
されている。第２実施形態の蓋材1'の形状を円形状とし
ているが、蓋材1'の形状は容器の開口部の形状に合わせ
て任意に変えればよい。なお、第２実施形態の蓋材1'に
おいてアルミニウム箔層13の感熱粘着剤層14を形成する
面にアンカー材層ないしはアルミニウム箔の保護層を形
成してもよい。A cover 1 'according to a second embodiment of the present invention is as shown in FIGS. As shown in FIG. 4, the shape of the lid member 1 ′ is a circular shape, and the knob portion 2 protruding outward at the peripheral edge.
The heat-sensitive adhesive layer 14 is formed in an annular shape of a fixed width around the inner surface except for the knob 2. The heat-sensitive adhesive layer 14 is formed in a ring shape so as to cover the entire heat-bonded portion 4 in which the lid 1 ′ is heat-bonded to the mouth of the container 3, and the heat-sensitive adhesive layer 14 is formed inside the ring-shaped heat-sensitive adhesive layer 14. In this region, the aluminum foil layer 13 is exposed. The width of the heat-sensitive adhesive layer 14 formed in an annular shape is wider than the width of the heat bonding portion 4 at the mouth of the container. Although the shape of the lid 1 ′ in the second embodiment is circular, the shape of the lid 1 ′ may be arbitrarily changed according to the shape of the opening of the container. In the lid 1 'of the second embodiment, an anchor material layer or a protective layer of aluminum foil may be formed on the surface of the aluminum foil layer 13 on which the heat-sensitive adhesive layer 14 is formed.
【００１２】第２実施形態の蓋材1'の断面形状は、図５
に示すように、内面から順に感熱粘着剤層14とアルミニ
ウム箔層13と接着層12と紙層11と絵柄層15が積層され、
アルミニウム箔層13面に環状に感熱粘着剤層14が形成さ
れた構成である。感熱粘着剤層14は蓋材1'のアルミニウ
ム箔13面の摘み部２を除いた周縁部に一定巾で環状に形
成されており、第１実施形態のようにアルミニウム箔13
の全面に感熱粘着剤層14を形成するのと比較して、感熱
粘着剤層14を形成するための感熱粘着剤組成物の使用量
を減らすことができ、また、環状に感熱粘着剤層14を形
成する工程を紙層11に絵柄層15を形成する印刷工程とイ
ンラインで実施して工程を削減できるので、蓋材のコス
トダウンが可能となる。The cross-sectional shape of the lid 1 'of the second embodiment is shown in FIG.
As shown in the figure, the heat-sensitive adhesive layer 14, the aluminum foil layer 13, the adhesive layer 12, the paper layer 11, and the picture layer 15 are laminated in order from the inner surface,
This is a configuration in which a heat-sensitive adhesive layer 14 is formed annularly on the aluminum foil layer 13 surface. The heat-sensitive adhesive layer 14 is formed in an annular shape with a fixed width around the periphery of the lid material 1 ′ except for the knob 2 on the surface of the aluminum foil 13.
Compared to forming the heat-sensitive adhesive layer 14 over the entire surface, the amount of the heat-sensitive adhesive composition used to form the heat-sensitive adhesive layer 14 can be reduced. Is formed in-line with the printing step of forming the picture layer 15 on the paper layer 11, and the number of steps can be reduced, so that the cost of the cover material can be reduced.
【００１３】第２実施形態の蓋材1'を円形状の開口部を
有する容器３の口部のフランジに熱接着して取り付けた
状態の断面形状は図６に示すとおりである。熱接着部４
よりも広い巾で蓋材の周縁部に環状に形成された感熱粘
着剤層14が、蓋材が容器に熱接着される際の加熱により
熱接着部４に対応する感熱粘着剤層14が粘着性が発現し
た粘着性発現部14a となった状態で容器３の口部に接着
されている。したがって、蓋材1'を容器３から一部剥離
させると剥離した熱接着部４に粘着性が発現しているの
で、容器３に熱湯を注入した後に、蓋材1'の剥離した部
分を容器３の口部に押しつけることにより、容器３の口
部に接着させて開口部を封止することができる。FIG. 6 shows a sectional shape of the second embodiment in which the lid 1 ′ is attached to the flange of the opening of the container 3 having a circular opening by heat bonding. Thermal bonding part 4
A heat-sensitive adhesive layer 14 having a wider width and formed annularly on the peripheral edge of the lid material adheres to the heat-sensitive adhesive layer 14 corresponding to the heat bonding portion 4 by heating when the lid material is thermally bonded to the container. It is adhered to the mouth of the container 3 in a state where the adhesiveness has been exhibited in the adhesiveness expressing portion 14a. Therefore, when the lid 1 ′ is partially peeled off from the container 3, the heat-bonded portion 4 that has been peeled off exhibits adhesiveness. After the hot water is poured into the container 3, the peeled portion of the lid 1 ′ is removed from the container 3. By pressing against the opening of the container 3, the opening can be sealed by adhering to the opening of the container 3.
【００１４】本発明において使用する感熱粘着剤層を構
成する感熱粘着剤組成物としては、例えば、特開平８−
２６９４２０号公報、ないしは特開平１１−５９５９号
公報に記載されているような、初期状態では非粘着性か
または粘着性がきわめてひくく、一定温度以上に加熱す
ることにより粘着性を発現する感熱粘着剤組成物を使用
することができる。As the heat-sensitive adhesive composition constituting the heat-sensitive adhesive layer used in the present invention, for example, JP-A-8-
No. 269420 or JP-A-11-5959, a heat-sensitive adhesive which is non-adhesive or extremely poor in its initial state and develops adhesiveness when heated to a certain temperature or higher. The composition can be used.
【００１５】特開平８−２６９４２０号公報に記載され
ているディレードタック型粘着剤組成物は、 (Ａ) カル
ボキシル基を有する不飽和単量体３〜６０重量％、疎水
性単量体４０〜９７重量％、その他の単量体０〜５０重
量％を共重合させて得られるガラス転移温度が２０℃以
上の樹脂であり、その５重量％以上が可溶化された樹脂
を含有する樹脂含有溶液、及び、 (Ｂ) ガラス転移温度
が−３０℃以下の樹脂からなるアクリル系樹脂水性エマ
ルジョンからなり、前記各成分の不揮発分の重量比
(Ａ) ／ (Ｂ) が１５／８５〜５０／５０であるディレ
ードタック型粘着剤組成物である。The delayed tack-type pressure-sensitive adhesive composition described in Japanese Patent Application Laid-Open No. 8-269420 comprises (A) 3 to 60% by weight of an unsaturated monomer having a carboxyl group and 40 to 97% of a hydrophobic monomer. A resin having a glass transition temperature of not less than 20 ° C. obtained by copolymerizing 0 to 50% by weight of another monomer, and a resin containing at least 5% by weight of a solubilized resin; And (B) an aqueous acrylic resin emulsion comprising a resin having a glass transition temperature of −30 ° C. or lower, and a weight ratio of the nonvolatile components of the respective components.
(A) / (B) is a delayed tack type pressure-sensitive adhesive composition having a ratio of 15/85 to 50/50.
【００１６】上記のディレードタック型粘着剤組成物に
おいて、カルボキシル基を有する不飽和単量体としては
アクリル酸、メタクリル酸、イタコン酸等であり、疎水
性単量体としてはメチルメタクリレート、エチルアクリ
レート、ブチルアクリレート、エチルヘキシルアクリレ
ート、塩化ビニル、酢酸ビニル、エチレン、ブタジエン
等であり、その他の単量体としてはアクリルアミド、２
−ヒドロキシエチルアクリレート、ジアセトンアクリル
アミド等である。また、ガラス転移温度が−３０℃以下
の樹脂からなるアクリル系樹脂水性エマルジョンとして
はブチルアクリレート、２−エチルヘキシルアクリレー
ト、ラウリルアクリレート等の単独重合体が使用され
る。In the above delayed tack type pressure-sensitive adhesive composition, the unsaturated monomer having a carboxyl group is acrylic acid, methacrylic acid, itaconic acid or the like, and the hydrophobic monomer is methyl methacrylate, ethyl acrylate or the like. Butyl acrylate, ethylhexyl acrylate, vinyl chloride, vinyl acetate, ethylene, butadiene, and the like.
-Hydroxyethyl acrylate, diacetone acrylamide and the like. Further, as an aqueous acrylic resin emulsion comprising a resin having a glass transition temperature of -30 ° C or lower, a homopolymer such as butyl acrylate, 2-ethylhexyl acrylate, or lauryl acrylate is used.
【００１７】特開平１１−５９５９号公報に記載されて
いる感熱粘着剤組成物は、 (Ａ) 酸価１ｍｅｑ／ｇ以上
の樹脂が塩基により中和された水溶性樹脂と、 (Ｂ) ラ
ジカル重合性単量体の乳化重合により得られたガラス転
移温度が−２０℃以下の重合体、からなる水性エマルジ
ョン型粘着剤組成物であって、６０℃未満の乾燥によっ
て成分 (Ａ) が海となり成分 (Ｂ) が島となる海島構造
を備え、６０℃以上の加熱処理により上記の海島構造が
逆転して、 (Ａ) 成分が島となり (Ｂ) 成分が海となっ
て粘着性が発現する感熱粘着剤組成物である。なお、上
記の海島構造としては、海（連続層）が完全に連続して
おり島（不連続層）の全てが海中に独立して分散してい
る構造に限らず、海が部分的に途切れている状態及び島
の一部が互いに融合している状態等をも含むものであ
る。The heat-sensitive adhesive composition described in JP-A-11-5959 comprises (A) a water-soluble resin obtained by neutralizing a resin having an acid value of 1 meq / g or more with a base, and (B) radical polymerization. An aqueous emulsion-type pressure-sensitive adhesive composition comprising a polymer having a glass transition temperature of −20 ° C. or lower obtained by emulsion polymerization of a water-soluble monomer, wherein component (A) becomes a sea by drying at less than 60 ° C. (B) has an islands-in-the-sea structure in which islands are formed, and the above-mentioned islands-in-a-sea structure is reversed by heat treatment at 60 ° C. or more, and the component (A) becomes an island, and the component (B) becomes a sea, and heat sensitivity is exhibited. It is an adhesive composition. The above-mentioned sea-island structure is not limited to a structure in which the sea (continuous layer) is completely continuous and all islands (discontinuous layers) are independently dispersed in the sea. This includes a state in which the islands are in contact with each other and a state in which some of the islands are fused with each other.
【００１８】上記の感熱粘着剤組成物において、 (Ａ)
成分としてはα，β−エチレン性不飽和カルボン酸単位
及び疎水性のラジカル重合性単量体単位を主構成単位と
する共重合体が好ましく使用され、α，β−エチレン性
不飽和カルボン酸としてはアクリル酸，メタクリル酸、
クロトン酸、マレイン酸、フマル酸、イタコン酸、シト
ラコン酸、無水マレイン酸等の１種又は２種以上が使用
される。ラジカル重合性単量体としては（メタ）メタク
リル酸メチル、（メタ）アクリル酸メチル、（メタ）ア
クリル酸イソプロピル、（メタ）アクリル酸ｎ−プロピ
ル、（メタ）アクリル酸ｎ−ブチル、（メタ）アクリル
酸イソブチル、（メタ）アクリル酸ヘキシル、（メタ）
アクリル酸２−エチルヘキシル、α−メチルスチレン、
ビニルトルエン等が使用される。 (Ｂ) 成分のラジカル
重合性単量体の乳化重合により得られたガラス転移温度
が−２０℃以下の重合体としては、アクリル系単量体の
乳化重合物、エチレン−ビニルエステル系単量体の乳化
重合物、共役ジエン系単量体の乳化重合物を使用でき
る。アクリル系単量体としては（メタ）メタクリル酸メ
チル、（メタ）アクリル酸メチル、（メタ）アクリル酸
イソプロピル、（メタ）アクリル酸ｎ−プロピル、（メ
タ）アクリル酸ｎ−ブチル、（メタ）アクリル酸イソブ
チル、（メタ）アクリル酸ヘキシル、（メタ）アクリル
酸２−エチルヘキシル等であり、エチレン−ビニルエス
テル系単量体におけるビニルエステル系単量体としては
酢酸ビニル、ピロピオン酸ビニル、酪酸ビニル、ラウリ
ン酸ビニル等であり、共役ジエン系単量体としてはブタ
ジエン、イソプレン、クロロプレン、イソブチレン等で
ある。In the above heat-sensitive adhesive composition, (A)
As the component, a copolymer having an α, β-ethylenically unsaturated carboxylic acid unit and a hydrophobic radically polymerizable monomer unit as main constituent units is preferably used. As the α, β-ethylenically unsaturated carboxylic acid, Is acrylic acid, methacrylic acid,
One or more of crotonic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, maleic anhydride and the like are used. Examples of the radical polymerizable monomer include methyl (meth) methacrylate, methyl (meth) acrylate, isopropyl (meth) acrylate, n-propyl (meth) acrylate, n-butyl (meth) acrylate, and (meth). Isobutyl acrylate, hexyl (meth) acrylate, (meth)
2-ethylhexyl acrylate, α-methylstyrene,
Vinyl toluene or the like is used. As the polymer having a glass transition temperature of -20 ° C or lower obtained by emulsion polymerization of the radical polymerizable monomer (B), an emulsion polymer of an acrylic monomer, an ethylene-vinyl ester monomer And a conjugated diene monomer emulsion polymer. Examples of the acrylic monomer include methyl (meth) methacrylate, methyl (meth) acrylate, isopropyl (meth) acrylate, n-propyl (meth) acrylate, n-butyl (meth) acrylate, and (meth) acryl. Isobutyl acid, hexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, etc. Examples of the vinyl ester monomer in the ethylene-vinyl ester monomer include vinyl acetate, vinyl pyropionate, vinyl butyrate, and laurin. And conjugated diene-based monomers such as butadiene, isoprene, chloroprene, and isobutylene.
【００１９】感熱粘着剤層14の厚さは５〜１０μが好ま
しく、４０〜６０μ深さのグラビア印刷版を使用して２
回刷りすることにより形成することができる。第１、第
２実施形態のようにアルミニウム箔面に５〜１０μの厚
さに感熱粘着剤層を形成することにより、発泡ポリスチ
レン製容器、内面にポリエチレンが積層された紙製容器
の口部に熱接着することにより、感熱粘着剤層に粘着性
が発現した状態で容器に接着されて、６００〜８００ｇ
／１５ｍｍ巾の接着強度が得られるので、実用的な蓋材
の接着強度としては問題がなく且つ蓋材を容器から剥離
する際に蓋材のアルミニウム箔が破れて剥離したり、紙
製容器の内面のポリエチレンが剥離してくることはな
い。また、蓋材を容器から剥離した際に蓋材の感熱粘着
剤層の熱接着部において粘着性が発現しているので、蓋
を閉めることにより蓋材が容器に再び接着して口部を封
止することが可能となる。The thickness of the heat-sensitive adhesive layer 14 is preferably 5 to 10 μm, and is preferably 2 to 40 μm using a gravure printing plate having a depth of 60 to 60 μm.
It can be formed by reprinting. By forming a heat-sensitive adhesive layer to a thickness of 5 to 10 μm on the aluminum foil surface as in the first and second embodiments, a foamed polystyrene container and a paper container in which polyethylene is laminated on the inner surface can be used at the mouth. By heat bonding, the heat-sensitive adhesive layer is adhered to the container in a state in which tackiness is developed, and 600 to 800 g
/ 15mm width adhesive strength, there is no problem in practical adhesive strength of the lid material, and when the lid material is peeled from the container, the aluminum foil of the lid material is torn and peeled, The polyethylene on the inner surface does not come off. Also, when the lid material is peeled off from the container, the heat-sensitive adhesive layer of the lid material exhibits adhesiveness in the heat-bonded portion, so when the lid is closed, the lid material adheres to the container again and the mouth is sealed. It is possible to stop.
【００２０】蓋材の構成としては第１、第２実施形態の
ように紙層と接着層とアルミニウム箔層と感熱粘着剤層
からなり、接着層をポリエチレンの熱溶融押出し層とし
た構成が最も好ましいが、紙層を合成紙、又は紙とプラ
スチックフィルムの積層体とすることもできる。また、
アルミニウム箔層を使用せずに、紙層と合成樹脂層と感
熱粘着剤層からなる構成とすることも可能であり、積層
構成は必要とする物性により任意に決めればよいもので
ある。As the structure of the lid material, as in the first and second embodiments, it is most preferable that the cover layer is composed of a paper layer, an adhesive layer, an aluminum foil layer, and a heat-sensitive adhesive layer, and the adhesive layer is a hot-melt extruded layer of polyethylene. Although preferred, the paper layer can also be a synthetic paper or a laminate of paper and a plastic film. Also,
Instead of using the aluminum foil layer, it is also possible to adopt a configuration comprising a paper layer, a synthetic resin layer, and a heat-sensitive adhesive layer, and the lamination configuration may be arbitrarily determined according to the required physical properties.
【００２１】実施形態の蓋材の製造方法は、ロール状の
紙とアルミニウム箔を接着層となるポリエチレンを使用
した押出ラミネーションにより積層した後に、積層した
紙面にグラビア印刷等により所定の印刷絵柄を印刷する
とともに、反対側のアルミニウム箔面に水性エマルジョ
ン樹脂からなる感熱粘着剤組成物をベタ印刷するか、な
いしは、アルミニウム箔面に紙面に印刷された絵柄層に
見当を合わせて、水性エマルジョン樹脂からなる感熱粘
着剤組成物を所定巾を有する環状に印刷して、６０℃以
下の温度で乾燥して感熱粘着剤層を形成する。その後、
シート状に断裁し、所定の位置にて打ち抜くことにより
第１、第２実施形態の蓋材を作製することができる。上
記の方法で製造することにより、紙とアルミニウム箔を
ポリエチレンにて押出しラミネーションし、積層した紙
面への絵柄層の印刷工程と、反対側のアルミニウム箔面
へ感熱粘着剤組成物を印刷して感熱粘着剤層を形成する
工程とをインラインで行うことができるので、感熱粘着
剤層を形成する工程を別に設ける必要がなく、工程を削
減してコストダウンを図ることができる。In the method of manufacturing the lid material according to the embodiment, a roll-shaped paper and aluminum foil are laminated by extrusion lamination using polyethylene as an adhesive layer, and then a predetermined printing pattern is printed on the laminated paper surface by gravure printing or the like. Along with the above, the heat-sensitive adhesive composition composed of the aqueous emulsion resin is solid-printed on the aluminum foil surface on the opposite side, or the aluminum foil surface is registered with the pattern layer printed on the paper surface, and is made of the aqueous emulsion resin. The heat-sensitive adhesive composition is printed in a ring having a predetermined width and dried at a temperature of 60 ° C. or less to form a heat-sensitive adhesive layer. afterwards,
By cutting the sheet into a sheet and punching it out at a predetermined position, the lid members of the first and second embodiments can be manufactured. By manufacturing according to the above method, paper and aluminum foil are extruded and laminated with polyethylene, a printing step of a pattern layer on the laminated paper surface, and a heat-sensitive adhesive composition is printed on the opposite aluminum foil surface by printing. Since the step of forming the pressure-sensitive adhesive layer and the step of forming the pressure-sensitive adhesive layer can be performed in-line, there is no need to separately provide a step of forming the heat-sensitive pressure-sensitive adhesive layer, and the cost can be reduced by reducing the number of steps.
【００２２】[0022]
【実施例】実施例１ 坪量７９ｇ／ｍ2 の片アート紙と７μのアルミニウム箔
とを２０μのポリエチレンの押出ラミネーションにより
積層した後、積層した片アート紙面にグラビア印刷によ
り絵柄を形成するとともに、絵柄の印刷とインライン
で、積層したアルミニウム箔面に、下記の感熱粘着剤組
成物を、深さ５０μのグラビア印刷版にて２回刷りを行
い６０℃以下の温度で乾燥することにより８μの厚さ
の、（Ａ）成分が海となり（Ｂ）成分が島となった海島
構造を有する感熱粘着剤層を、感熱粘着剤層の巾が蓋材
が完成した状態で７ｍｍの環状となるように形成した蓋
材用の積層体を作製した。 〔感熱粘着剤組成物〕固形分比で下記（Ａ）成分２０重
量部と下記（Ｂ）成分８０重量部からなる水性エマルジ
ョン（固形分含有量が約５０％）。 （Ａ）成分：メタクリル酸メチル９０重量部とアクリル
酸１０重量部の共重合体（酸価１．４ｍｅｑ／ｇ） （Ｂ）成分：アクリル酸ブチル９９重量部とメタクリル
酸２−ヒドロキシエチル１重量部の共重合体 上記で得られた積層体を断裁し所定位置にて打ち抜き、
内面の周縁部に７ｍｍ巾の環状に感熱粘着剤層が形成さ
れた蓋材を作製した。得られた蓋材を口径が１００ｍｍ
で口部フランジ巾が３ｍｍの内面にポリエチレンが積層
された紙製容器の口部フランジに熱接着して取り付け、
蓋材と容器の接着強度を測定した結果、６８０ｇ／１５
ｍｍ巾の強度が得られ、熱接着した蓋材を容器から一部
剥離した際に紙製容器の内面のポリエチレンが剥離して
くることがなく、且つ容器から剥離した蓋材の熱接着部
は粘着性を有しており、再び容器の口部を接着させて容
器を封止することができた。蓋材を容器に熱接着する条
件は、温度１６０℃、圧力５ｋｇ／ｃｍ2 、加圧時間
１．０秒とした。Example 1 A piece of art paper having a basis weight of 79 g / m 2 and an aluminum foil of 7μ were laminated by extrusion lamination of 20μ polyethylene, and a pattern was formed on the laminated piece of art paper by gravure printing. Inline with the printing of the pattern, the following heat-sensitive adhesive composition was printed twice on a laminated aluminum foil surface with a gravure printing plate having a depth of 50μ and dried at a temperature of 60 ° C or less to obtain a thickness of 8μ. The heat-sensitive adhesive layer having a sea-island structure in which the component (A) becomes the sea and the component (B) becomes the island is formed such that the width of the heat-sensitive adhesive layer becomes a 7 mm ring in a state where the lid material is completed. A laminated body for the formed lid material was produced. [Thermosensitive adhesive composition] An aqueous emulsion (solid content: about 50%) consisting of 20 parts by weight of the following component (A) and 80 parts by weight of the following component (B) in terms of solid content. (A) Component: Copolymer of 90 parts by weight of methyl methacrylate and 10 parts by weight of acrylic acid (acid value 1.4 meq / g) (B) Component: 99 parts by weight of butyl acrylate and 1 part by weight of 2-hydroxyethyl methacrylate Part of copolymer The laminate obtained above was cut and punched at a predetermined position,
A lid member having a 7 mm-width annular heat-sensitive adhesive layer formed on the inner peripheral portion was produced. The obtained lid material is 100 mm in diameter.
Attach and attach to the mouth flange of the paper container where the mouth flange width is 3mm and polyethylene is laminated on the inner surface,
As a result of measuring the adhesive strength between the lid member and the container, 680 g / 15
mm of strength is obtained, the polyethylene on the inner surface of the paper container does not come off when the thermally bonded lid material is partially peeled from the container, and the thermally bonded portion of the lid material peeled from the container is It was sticky, and the container was sealed again by bonding the mouth of the container again. The conditions for thermally bonding the lid material to the container were a temperature of 160 ° C., a pressure of 5 kg / cm 2 , and a pressing time of 1.0 second.
【００２３】[0023]
【発明の効果】内面の少なくとも容器と熱接着される熱
接着部に感熱粘着剤層を有し、前記感熱粘着剤層が水性
エマルジョン樹脂からなる感熱粘着剤組成物により形成
された構成からなる蓋材とすることにより、この蓋材を
容器に熱接着する際の加熱により感熱粘着剤層に粘着性
が発現した状態となるので、とくにカップラーメン等の
容器においては、蓋材を容器から一部剥離させて容器内
に熱湯を注いだ後に、再び蓋材を容器の口部に押しつけ
ることにより蓋材を容器に接着させて口部を塞ぐことが
できるとともに、口部を塞いだ状態を維持できるので熱
が外部に逃げることがなく内容物を十分に加熱すことが
できる。また、感熱粘着剤層が、蓋材が容器に熱接着さ
れる際に環状に形成される熱接着部の全体を覆うように
周端縁に環状に形成された構成とすることにより、感熱
粘着剤層を形成する面積が狭くなり感熱粘着剤組成物の
使用量を減らすことができるとともに、絵柄の印刷工程
と感熱粘着剤組成物を使用して印刷により感熱粘着剤層
を形成する工程をインラインで行うことができるので、
蓋材のコストダウンが可能となる。上記の蓋材の構成
を、外面から順に紙層と接着層とアルミニウム箔層と感
熱粘着剤層が積層された構成とすることにより、遮光性
が優れるとともに、カールが発生しにくくなり製造時の
作業性および内容物充填時の作業性に優れた、再封可能
な蓋材とすることができる。感熱粘着剤層を、水溶性樹
脂からなる海とガラス転移温度が−２０℃以下のラジカ
ル重合性単量体の乳化重合により得られた樹脂からなる
島との海島構造を有し、感熱粘着剤層を加熱することに
より海と島が逆転して粘着性が発現する構成とすること
により、感熱粘着剤層を形成した状態では非粘着性であ
り、蓋材を容器に熱接着する際の加熱により粘着性が発
現した状態となるので、製造時および内容物充填時の作
業性に優れた再封可能な蓋材とすることができる。According to the present invention, there is provided a lid having a structure in which a heat-sensitive adhesive layer is formed at least on a heat-bonded portion of the inner surface which is heat-bonded to a container, and the heat-sensitive adhesive layer is formed of a heat-sensitive adhesive composition comprising an aqueous emulsion resin. By making the cover material heat-adhesive to the container, the heat-sensitive adhesive layer becomes in a state in which the heat-sensitive adhesive layer becomes tacky.In particular, in a container such as a cup ramen, the cover material is partially removed from the container. After peeling and pouring hot water into the container, the lid can be adhered to the container by pressing the lid against the opening of the container again to close the opening, and the state in which the opening is closed can be maintained. Therefore, the contents can be sufficiently heated without heat escaping to the outside. Further, the heat-sensitive adhesive layer is formed in a ring shape on the peripheral edge so as to cover the entire heat-bonded portion formed in a ring shape when the lid member is heat-bonded to the container, so that the heat-sensitive adhesive layer is formed. The area for forming the pressure-sensitive adhesive layer is reduced, and the amount of the heat-sensitive adhesive composition used can be reduced. In addition, the process of printing a pattern and the step of forming the heat-sensitive adhesive layer by printing using the heat-sensitive adhesive composition are performed in-line. So you can do
The cost of the lid material can be reduced. The above-mentioned lid material has a configuration in which a paper layer, an adhesive layer, an aluminum foil layer, and a heat-sensitive adhesive layer are laminated in order from the outer surface. A resealable lid material excellent in workability and workability when filling contents can be obtained. The heat-sensitive adhesive layer has a sea-island structure of a sea made of a water-soluble resin and an island made of a resin obtained by emulsion polymerization of a radical polymerizable monomer having a glass transition temperature of −20 ° C. or less. By heating the layer, the sea and islands are reversed and the adhesive is developed, so it is non-adhesive when the heat-sensitive adhesive layer is formed, and is heated when the lid material is thermally bonded to the container. As a result, a state in which tackiness is developed can be obtained, so that a resealable lid material excellent in workability at the time of production and filling of contents can be obtained.
【図１】本発明の第１実施形態を示す底面図。FIG. 1 is a bottom view showing a first embodiment of the present invention.
【図２】図１におけるＩ−Ｉ断面図。FIG. 2 is a sectional view taken along line II in FIG.
【図３】第１実施形態の蓋材を容器に熱接着した状態を
示す断面図。FIG. 3 is a cross-sectional view illustrating a state in which the lid member according to the first embodiment is thermally bonded to a container.
【図４】本発明の第２実施形態を示す底面図。FIG. 4 is a bottom view showing a second embodiment of the present invention.
【図５】図４におけるII−II断面図。FIG. 5 is a sectional view taken along line II-II in FIG.
【図６】第２実施形態の蓋材を容器に熱接着した状態を
示す断面図。FIG. 6 is a cross-sectional view illustrating a state in which the lid member according to the second embodiment is thermally bonded to a container.
１，1' 蓋材 ２ 摘み部 ３ 容器 ４ 熱接着部 11 紙層 12 接着層 13 アルミニウム箔層 14 感熱粘着剤層 14a 粘着性発現部 15 絵柄層 1, 1 'Lid material 2 Knob part 3 Container 4 Thermal bonding part 11 Paper layer 12 Adhesive layer 13 Aluminum foil layer 14 Heat-sensitive adhesive layer 14a Adhesion exhibiting part 15 Picture layer
───────────────────────────────────────────────────── フロントページの続き (72)発明者 安藤 雅之 東京都新宿区市谷加賀町一丁目１番１号 大日本印刷株式会社内 Ｆターム(参考） 3E067 AA11 AB01 BB01A BB12A BB25A BC07A CA12 CA24 EA05 EB17 EE02 4J040 CA061 CA062 DA071 DA072 DC061 DC062 DE021 DE022 DF011 DF012 DF041 DF042 DF051 DF052 DF061 DF062 DF101 DF102 DG001 DG002 GA07 JA02 JA03 JA09 JB09 JB11 LA02 MA02 MA09 NA06 PA18 ────────────────────────────────────────────────── ─── Continuing on the front page (72) Inventor Masayuki Ando 1-1-1 Ichigaya Kagacho, Shinjuku-ku, Tokyo Dai Nippon Printing Co., Ltd. F-term (reference) 3E067 AA11 AB01 BB01A BB12A BB25A BC07A CA12 CA24 EA05 EB17 EE02 4J040 CA061 CA062 DA071 DA072 DC061 DC062 DE021 DE022 DF011 DF012 DF041 DF042 DF051 DF052 DF061 DF062 DF101 DF102 DG001 DG002 GA07 JA02 JA03 JA09 JB09 JB11 LA02 MA02 MA09 NA06 PA18
Claims (4)
接着部に感熱粘着剤層を有し、前記感熱粘着剤層が水性
エマルジョン樹脂からなる感熱粘着剤組成物により形成
された構成からなることを特徴とする蓋材。1. A heat-sensitive adhesive layer at least on a heat-bonded portion of an inner surface of a container which is heat-bonded to a container, wherein the heat-sensitive adhesive layer is formed of a heat-sensitive adhesive composition comprising an aqueous emulsion resin. A lid material characterized by the following.
着される際に環状に形成される熱接着部の全体を覆うよ
うに周端縁に環状に形成された構成からなることを特徴
とする請求項１記載の蓋材。2. The heat-sensitive adhesive layer has a configuration in which a peripheral edge is formed in a ring shape so as to cover the entire heat-bonded portion formed in a ring shape when the lid member is heat-bonded to the container. The lid material according to claim 1, wherein:
ム箔層と前記感熱粘着剤層が積層された構成からなるこ
とを特徴とする請求項１または２に記載の蓋材。3. The lid material according to claim 1, wherein the lid material has a configuration in which a paper layer, an adhesive layer, an aluminum foil layer, and the heat-sensitive adhesive layer are laminated in order from the outer surface.
る海とラジカル重合性単量体の乳化重合により得られた
ガラス転移温度が−２０℃以下の樹脂からなる島との海
島構造を有し、前記感熱粘着剤層を加熱することにより
海と島が逆転して粘着性が発現する構成からなることを
特徴とする請求項１〜３のいずれかに記載の蓋材。4. The heat-sensitive adhesive layer has a sea-island structure comprising a sea of a water-soluble resin and an island of a resin having a glass transition temperature of −20 ° C. or lower obtained by emulsion polymerization of a radical polymerizable monomer. The lid material according to any one of claims 1 to 3, wherein the heat-sensitive adhesive layer has a configuration in which the sea and the island are reversed by heating the heat-sensitive adhesive layer to exhibit adhesiveness.