JP2016199432A - Piezoelectric ceramic and piezoelectric element - Google Patents

Abstract

An object of the present invention is to provide a piezoelectric ceramic capable of using a piezoelectric element with a high driving voltage without deteriorating piezoelectric characteristics, and a piezoelectric element using the piezoelectric ceramic. A piezoelectric ceramic according to the present invention is a composite oxide piezoelectric ceramic mainly composed of lead zirconate titanate, wherein crystal grains mainly composed of lead zirconate titanate are disposed between the crystal grains. And containing heterogeneous particles mainly composed of ZnO and containing Cr (0.1% by weight or less (excluding 0) in terms of Cr2O3 with respect to the total weight part of the piezoelectric ceramic). It is characterized by. [Selection] Figure 4

Description

The present invention relates to a piezoelectric ceramic mainly composed of lead zirconate titanate and a piezoelectric element using the same.

Piezoelectric ceramics mainly composed of lead zirconate titanate (hereinafter referred to as PZT) have excellent piezoelectric characteristics and are widely used for piezoelectric actuators, piezoelectric ultrasonic motors, piezoelectric sensors, piezoelectric sounders, and the like. Yes.

A piezoelectric element comprising: a piezoelectric body having first and second main surfaces facing each other; a first external electrode disposed on the first main surface; and a second external electrode disposed on the second main surface. A piezoelectric actuator including a piezoelectric element and a support member that supports the piezoelectric element is known (see, for example, Patent Document 1). In the piezoelectric actuator described in Patent Document 1, the actuator base of a suspension for a hard disk drive (HDD) corresponds to the support member, and the piezoelectric element transmits the displacement to the actuator base.

JP 2002-184140 A

In recent years, electronic devices have been reduced in size or thickness. Accordingly, miniaturization or thinning is also required for piezoelectric elements mounted on electronic devices. However, even when the piezoelectric element is reduced in size or thickness, it is necessary to obtain the same characteristics as in the past. That is, when the size is reduced or the thickness is reduced, a higher driving voltage must be applied to the piezoelectric element in order to make the displacement of the piezoelectric element equivalent to the conventional one.

However, the piezoelectric element mounted on the actuator base of the hard disk drive (HDD) suspension applies an electric field having a polarity opposite to the electric field direction at the time of polarization of the piezoelectric element as a driving voltage. In this case, there has been a problem that the piezoelectric characteristics, that is, the displacement of the element is remarkably lowered.

The present invention has been made in view of such circumstances, and an object of the present invention is to provide a piezoelectric ceramic that can use a piezoelectric element at a high driving voltage without deteriorating piezoelectric characteristics, and a piezoelectric element using the piezoelectric ceramic. And

In order to achieve the above object, a piezoelectric ceramic according to the present invention is a composite oxide piezoelectric ceramic containing PZT as a main component, and ZnO that is unevenly distributed between crystal particles containing PZT as a main component and the crystal particles. And Cr (contains 0.1% by weight or less (excluding 0) in terms of Cr2O3 with respect to the total weight part of the piezoelectric ceramic). .

In such a piezoelectric ceramic, a piezoelectric element that maintains high piezoelectric characteristics and has less deterioration in piezoelectric characteristics due to driving than in the past, especially when a voltage having a polarity opposite to the polarization direction is applied, is produced. it can.

The piezoelectric ceramic of the present invention is a composite oxide (0.85 ≦ x ≦ 1.005, y ≦ 0.13, 0.4) whose main component is represented by (Pbx Me1y) (Tiz Zr1-z) O3. ≦ z ≦ 0.65 is satisfied, and Me1 is at least one selected from the group consisting of Ba, Sr, Ca, and La). The piezoelectric characteristics can be enhanced by replacing a part of Pb with at least one selected from the group consisting of Ba, Sr, Ca, and La.

In the piezoelectric ceramic according to the present invention, a complex oxide represented by Pb (Zna Me2b Me3c) O3 as the first subcomponent (the first subcomponent satisfies a + b + c ≦ 1; Me2 is Ni , Co, Mg, Bi, and Me3 is at least one selected from the group consisting of Nb, Ta, Sb, and W). Yes. By including such a first subcomponent, the piezoelectric characteristics can be further enhanced as compared with the case where Zn is simply added to PZT.

In the piezoelectric ceramic according to the present invention, Cr is contained as a second subcomponent (0.1% by weight or less (excluding 0) in terms of Cr2O3 with respect to the total weight part of the piezoelectric ceramic). As a feature, Cr may be replaced with a part of Zn or Me2 in the first subcomponent in addition to addition alone.

The piezoelectric ceramic according to the present invention is characterized in that the average particle size of the heterophasic particles mainly composed of ZnO is smaller than the average particle size of particles mainly composed of PZT. This feature enables a piezoelectric ceramic that does not impair the piezoelectric characteristics and the strength of the piezoelectric element.

In addition, a piezoelectric element according to the present invention is characterized by including a piezoelectric body made of the above-described piezoelectric ceramic and a pair of external electrodes facing each other so as to sandwich the piezoelectric body.

According to another aspect of the present invention, there is provided a piezoelectric element including a plurality of piezoelectric layers made of the above-described piezoelectric ceramic, at least one internal electrode layer, and an external electrode formed outside the piezoelectric layer. . Thereby, a large displacement of the piezoelectric element can be realized.

ADVANTAGE OF THE INVENTION According to this invention, the piezoelectric ceramic which can manufacture a piezoelectric element which maintains a high piezoelectric characteristic and there is little deterioration of the piezoelectric characteristic by a drive compared with the past can be provided.

It is a figure for demonstrating the structure of the piezoelectric ceramic of this invention. It is a figure for demonstrating the cross-sectional structure of the piezoelectric element of this invention. It is a figure for demonstrating the cross-sectional structure of the lamination type piezoelectric element of this invention. It is a figure for demonstrating the preparation conditions and characteristics of a sample.

Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the description, the same reference numerals are used for the same elements or elements having the same function, and redundant description is omitted.

The piezoelectric ceramic of the present invention has PZT as a main component and is widely used for piezoelectric actuators, piezoelectric ultrasonic motors, piezoelectric sensors, piezoelectric sounders, and the like. A piezoelectric ceramic mainly composed of PZT is usually a polycrystalline body composed of a plurality of crystal grains and grain boundaries.

The crystal grains constituting the polycrystal are complex oxides (0.85 ≦ x ≦ 1.005, y ≦ 0.13, 0.35) represented by (Pbx Me1y) (Tiz Zr1-z) O3. ≦ z ≦ 0.65 is satisfied, and Me1 is at least one selected from the group consisting of Ba, Sr, Ca, and La). Note that the values of x, y, and z are preferably within the above ranges since the desired piezoelectric ceramic characteristics cannot be obtained if the values are out of the ranges.

With respect to the polycrystalline body composed of such crystal particles, heterogeneous particles mainly composed of ZnO are unevenly distributed between the crystal particles, and further Cr (converted to Cr2O3 with respect to the total weight part of the piezoelectric ceramic) By including 0.1 wt% or less (excluding 0)), a piezoelectric that maintains high piezoelectric characteristics and has little deterioration in piezoelectric characteristics when a voltage having a polarity opposite to the polarization direction is applied when the element is driven. An element can be manufactured.

The crystal particles constituting the piezoelectric ceramic have a complex oxide represented by Pb (Zna Me2b Me3c) O3 as the first subcomponent (the first subcomponent satisfies a + b + c ≦ 1, and Me2 is , Ni, Co, Mg, Bi, and Me3 is at least one selected from the group consisting of Nb, Ta, Sb, and W). preferable. The main component and the first subcomponent are adjusted to be 1 mol in total. In order to make the Curie temperature of the piezoelectric ceramic appropriate, the first subcomponent is preferably 0.3 mol or less.

By including such a complex oxide, the piezoelectric characteristics can be further enhanced as compared with the case where Zn is simply added.

In addition, Cr contained in the crystal particles constituting the piezoelectric ceramic as the second subcomponent is Cr2O3 with respect to the total weight of the piezoelectric ceramic in order to improve the desired piezoelectric ceramic characteristics and durability during driving. It is preferably contained in 0.1% by weight or less (excluding 0).

FIG. 1 is a diagram for explaining the configuration of a piezoelectric ceramic according to the present invention. In addition, all the crystal particles other than the heterophasic particle 102 which has ZnO as a main component in FIG. The heterophasic particles containing ZnO as the main component are surrounded by crystal particles 101 of the main component of the piezoelectric ceramic and are unevenly distributed in the piezoelectric ceramic.

The average particle size of the heterophasic particles mainly composed of ZnO that is unevenly distributed in the piezoelectric ceramic is preferably smaller than the crystal particle size of the piezoelectric ceramic main component. For example, when the crystal grain size of the piezoelectric ceramic main component is 1, the average particle size of the heterophasic particles containing ZnO as the main component is preferably 0.8 or less. More preferably, the average particle size of the heterophasic particles mainly composed of ZnO is 0.1 or more and 0.8 or less. By thus forming ZnO heterogeneous particles in the piezoelectric ceramic, a piezoelectric ceramic that does not impair the piezoelectric characteristics and the strength of the piezoelectric element can be obtained. Note that the average particle size and content of the heterophasic particles mainly composed of ZnO are the piezoelectric ceramic powder adjustment conditions before the piezoelectric element firing, the piezoelectric element firing conditions such as temperature, The temperature can be controlled by setting conditions such as the temperature rise rate, the temperature fall rate, and the atmosphere up to the firing temperature. The number of heterophasic particles containing ZnO as the main component is preferably in the range of 0.01 to 1% with respect to the number of piezoelectric ceramic main components.

A piezoelectric element can be formed using the piezoelectric ceramic as described above. The configuration of the piezoelectric element according to this embodiment will be described with reference to FIGS. FIG. 2 is a diagram for explaining a cross-sectional configuration of a piezoelectric element not including an internal electrode. FIG. 3 is a view for explaining a cross-sectional configuration of a multilayer piezoelectric element including internal electrodes. In the piezoelectric element 200, external electrodes 202 a and 202 b are formed on the main surface of the piezoelectric body 201 and the piezoelectric body 201. The piezoelectric layer 201 is made of a piezoelectric ceramic. The external electrodes 202a and 202b are made of, for example, a metal layer such as Au, Cu, Cr, or Ni or a composite metal layer combining them. Accordingly, it is possible to realize a piezoelectric element having high piezoelectric characteristics and little deterioration in piezoelectric characteristics when a voltage having a polarity opposite to the polarization direction is applied when the element is driven.

The multilayer piezoelectric element 300 includes a piezoelectric layer 301, internal electrode layers 302a and 302b, and external electrodes 303a and 303b. The piezoelectric layer 201 is made of a piezoelectric ceramic. The internal electrode layers 302a and 302b are made of a metal such as Ag, Pd, Pt, Au, or Cu or an alloy thereof, and the external electrodes 202a and 202b are metal layers such as Au, Cu, Cr, or Ni, or a combination thereof. Consisting of a composite metal layer. The internal electrode layers 302a and 302b are connected to the external electrodes 303a and 303b every other layer.

(Piezoelectric Ceramic and Piezoelectric Element Manufacturing Method) As a raw material constituting the piezoelectric ceramic, an oxide and / or a compound that becomes an oxide by firing is used. In addition, as a compound which becomes an oxide by baking, carbonate, nitrate, oxalate, an organometallic compound, etc. are illustrated, for example. Of course, you may use together an oxide and the compound which becomes an oxide by baking. What is necessary is just to determine content of each compound in a piezoelectric ceramic raw material so that it may become a composition of an above-described piezoelectric ceramic composition after baking. As these raw material powders, those having an average particle diameter of about 0.1 to 10 μm are usually used.

First, a chemically pure starting material is weighed so that the composition after firing has a desired blending ratio. Next, the starting material is wet-mixed by a ball mill for 24 to 48 hours and then calcined at 800 to 900 ° C. Next, it grind | pulverizes for 5 to 24 hours using a ball mill, and it is set as the calcined material as a piezoelectric ceramic raw material. These manufacturing conditions are adjusted so that heterogeneous particles mainly composed of desired ZnO are easily formed in the piezoelectric ceramic.

Polyvinyl alcohol as a binder is added to the obtained calcined powder and press-molded into a predetermined square plate shape. This press-molded product is subjected to a binder removal treatment at 450 ° C. for 1 hour in the air, and is subsequently fired at 1050 to 1150 ° C. to obtain a sintered body. In addition, the temperature increase rate, the temperature decrease rate, the firing atmosphere, and the like up to the firing temperature at the time of firing are adjusted so that the desired out-of-phase particles mainly composed of ZnO are formed in the piezoelectric ceramic.

The obtained sintered body is processed to have a predetermined thickness, and, for example, Ni—Cr / Au layer electrodes are formed on both main surfaces by sputtering, and then subjected to polarization treatment by applying an electric field. Thereafter, dicing is performed so as to obtain a predetermined size, thereby obtaining a piezoelectric element.

Moreover, a dispersing agent, an organic binder, an organic solvent, etc. are added and mixed with the powder of the said calcined material, and it shape | molds by sheet | seat shaping | molding etc. An internal electrode layer is printed on the molded sheet using an alloy paste having an Ag / Pd ratio of 70/30, and laminated pressure bonding and pressing are performed to produce a laminated molded body. A laminate-type sintered body can be obtained by performing a binder removal treatment at 450 ° C. for 3 hours in the air and firing at 1000 to 1100 ° C. continuously. In addition, by adjusting the temperature raising rate, the temperature lowering rate, the firing atmosphere, and the like up to the firing temperature at the time of firing, the heterophasic particles containing the desired ZnO as a main component are formed in the piezoelectric ceramic.

After processing this sintered body to a desired size, an external electrode is formed by sputtering with a Ni—Cr / Au layer electrode, and then polarized by applying an electric field to obtain a laminated piezoelectric element. Can do.

(Examples and Comparative Examples) Each chemically pure raw material PbO, TiO2, ZrO2, ZnO, Nb2O5, Sb2O3 so as to be a perovskite complex oxide (see FIG. 4) containing a predetermined amount of main components and subcomponents. , WO3, NiO, MgCO3, Bi2O3, CoO, BaCO3, SrCO3, CaCO3, La2O3, Cr2O3 were weighed and wet-mixed by a ball mill for 24-48 hours, and then calcined at 800-900 ° C. Next, it grind | pulverized for 5 to 24 hours using the ball mill, and it was set as the calcined material as a piezoelectric ceramic raw material.
These production conditions were adjusted so that different phase particles mainly composed of desired ZnO were easily formed in the piezoelectric ceramic.

Polyvinyl alcohol as a binder was added to the obtained calcined powder and press-molded into a predetermined square plate shape. This press-molded product was subjected to a binder removal treatment at 450 ° C. for 1 hour in the air, and was subsequently fired at 1050 to 1150 ° C. to obtain a sintered body. In addition, the temperature increase rate, the temperature decrease rate, the firing atmosphere, and the like up to the firing temperature at the time of firing were adjusted so that the desired out-of-phase particles mainly composed of ZnO were formed in the piezoelectric ceramic.

The obtained sintered body was processed to a thickness of 0.1 mm, and Ni—Cr / Au layer electrodes were formed on both main surfaces by sputtering so that the film thickness was about 300 nm, and then heated to 120 ° C., Polarization treatment was performed by applying an electric field of 2 kV / mm for 3 minutes. Thereafter, dicing was performed so as to obtain a size of 4.5 mm in length and 1.5 mm in width to obtain a sample of a piezoelectric element.

In addition, the piezoelectric strain constant d31, which is one of the piezoelectric characteristics, was measured for these samples with reference to EM-4501 of the Japan Electronics and Information Technology Industries Association. The electrical characteristics necessary for calculating the piezoelectric strain constant d31 were measured with an impedance analyzer, and the sintered body density was calculated by the Archimedes method. Regarding the driving durability of the piezoelectric characteristics when an electric field opposite to the polarization direction is applied, a voltage of ± 70 V is applied to the above sample with a sine wave of 3 KHz in an environment of 120 ° C. for 168 hours. The determination was made by comparing the value of the piezoelectric strain constant d31.

FIG. 4 is a view for explaining sample preparation conditions and characteristics. The examples shown in FIG. 4 are all samples in which a different phase mainly composed of desired ZnO is present in the piezoelectric ceramic. In addition, ○ and × of driving durability indicate good and bad driving durability. When the rate of change of the piezoelectric strain constant before and after the test is within 10%, it is judged as good. It is shown. As shown in FIG. 4, it was found that in the example, a high piezoelectric strain constant d31 was obtained and good driving durability was obtained.

It has been found that a piezoelectric element to which Cr2O3 is not added does not have good driving durability, and when Cr2O3 is excessively added, the piezoelectric strain constant d31 is lowered and the driving durability is not good. A sample for comparison was produced under the same composition as sample 2 in the example, under different production conditions from those in the example, so that the heterophasic particles mainly composed of ZnO were less than 0.01% in the piezoelectric ceramic. . When the same driving durability test was performed on the comparative sample, it was found that the rate of change of the piezoelectric strain constant d31 after the test greatly exceeded 10%.

DESCRIPTION OF SYMBOLS 101 ... Crystal particle | grains of a piezoelectric ceramic main component, 102 ... Different phase particle | grains which have ZnO as a main component, 200 ... Piezoelectric element, 300 ... Multilayer piezoelectric element, 201, 301 ... Piezoelectric layer 202a, 202b, 302a, 302b ... internal electrode layer, 203a, 203b, 303a, 303b ... external electrode

Claims (6)

A composite oxide piezoelectric ceramic mainly composed of lead zirconate titanate, wherein heterophase particles mainly composed of ZnO are unevenly distributed between the piezoelectric ceramic crystal particles, and Cr element is contained in the piezoelectric ceramic. A piezoelectric ceramic characterized in that it is included. The piezoelectric ceramic is a composite oxide (0.85 ≦ x ≦ 1.005, y ≦ 0.13, 0.35 ≦ z ≦ 0.65) represented by (Pbx Me1y) (Tiz Zr1-z) O3. 2. The piezoelectric ceramic according to claim 1, wherein Me1 is at least one selected from the group consisting of Ba, Sr, Ca, and La). The piezoelectric ceramic has a composite oxide represented by Pb (Zna Me2b Me3c) O3 as an auxiliary component (the auxiliary component satisfies a + b + c ≦ 1, and Me2 is made of Ni, Co, Mg, and Bi. The at least one selected from the group, and Me3 is at least one selected from the group consisting of Nb, Ta, Sb, and W). Piezoelectric ceramic. The Cr contained in the piezoelectric ceramic is 0.1 wt% or less (excluding 0) in terms of Cr2O3 with respect to the total weight part of the piezoelectric ceramic. The piezoelectric ceramic according to item. A piezoelectric element comprising two electrodes opposed to each other and a piezoelectric body arranged between the electrodes, wherein the piezoelectric body is constituted by the piezoelectric ceramic according to any one of claims 1 to 4. A piezoelectric element characterized by comprising: A laminated piezoelectric element comprising an internal electrode, a piezoelectric layer, and an external electrode, wherein the internal electrode and the piezoelectric layer are alternately stacked, and the internal electrode is connected to the external electrode, wherein the piezoelectric body The layer is a multilayer piezoelectric element comprising the piezoelectric ceramic according to any one of claims 1 to 4.