JP2673628B2 - Method for producing woven fabric having surface wrinkle effect - Google Patents
Method for producing woven fabric having surface wrinkle effectInfo
- Publication number
- JP2673628B2 JP2673628B2 JP4072178A JP7217892A JP2673628B2 JP 2673628 B2 JP2673628 B2 JP 2673628B2 JP 4072178 A JP4072178 A JP 4072178A JP 7217892 A JP7217892 A JP 7217892A JP 2673628 B2 JP2673628 B2 JP 2673628B2
- Authority
- JP
- Japan
- Prior art keywords
- woven fabric
- fabric
- wrinkles
- polyamide
- wrinkle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、布帛の表面変化の一つ
である皺の耐久性が永久に持続する織物の製造方法に関
する。ここで、皺とは凹凸の皺というよりは、比較的平
坦でありながら織物表面の開繊度の違いや繊維配置の差
などにより皺に見えるという表面効果を主に意図してい
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a woven fabric in which the durability of wrinkles, which is one of the surface changes of the fabric, lasts forever. Here, the wrinkle is not intended to be a wrinkle having unevenness, and is mainly intended to have a relatively flat surface effect such that the wrinkle looks like a wrinkle due to a difference in the opening degree of the woven fabric surface or a difference in fiber arrangement.
【０００２】[0002]
【従来の技術】従来、布帛の表面変化の一つである皺を
得る方法としては、最終加工段階にて機械的な圧力を用
いて、皺を得る方法がある。2. Description of the Related Art Conventionally, as a method for obtaining wrinkles, which is one of the surface changes of a fabric, there is a method for obtaining wrinkles by using mechanical pressure in the final processing stage.
【０００３】しかし、かかる方法により、皺を得た場合
には皺の耐久性に欠け、特に着用中や洗濯時に皺が消失
しやすいという欠点があった。However, when wrinkles are obtained by such a method, the wrinkles lack durability, and there is a drawback that wrinkles tend to disappear particularly during wearing or washing.
【０００４】[0004]
【発明が解決しようとする課題】本発明はこのような問
題点に鑑みてなされたものであって、耐久性のある皺を
有する織物の製造方法を提供するものである。SUMMARY OF THE INVENTION The present invention has been made in view of these problems, and provides a method for producing a durable woven fabric having wrinkles.
【０００５】[0005]
【課題を解決するための手段】本発明者らは、上記課題
を解決すべく鋭意、研究を重ねた結果、ポリアミドとポ
リエステルからなるフィブリル化型複合繊維からなる織
物をロープ状として機械的な圧力を加えて皺を生じさ
せ、次に該織物を開繊フィブリル化し、続いて１７０〜
１９０℃で熱セットを実施することを特徴とする表面皺
効果を有する織物の製造方法からなる本発明を完成し
た。Means for Solving the Problems The inventors of the present invention have earnestly studied to solve the above problems, and as a result, as a result, a woven fabric made of fibrillated composite fibers made of polyamide and polyester is formed into a rope and mechanical pressure is applied. Is added to form wrinkles, and then the fabric is opened and fibrillated, followed by 170-
The present invention has been completed which comprises a method for producing a fabric having a surface wrinkle effect, which is characterized by carrying out heat setting at 190 ° C.
【０００６】即ち、本発明は、ポリアミドとポリエステ
ルからなるフィブリル化型複合繊維からなる織物に機械
的に作った皺部と他部との開繊度の違いにより視覚的に
皺が強調されること、つまりかかる表面効果により皺が
見えることに着目して研究を進めた結果、完成するに至
ったものである。That is, according to the present invention, the wrinkles are visually emphasized due to the difference in the degree of opening between the wrinkle portion mechanically formed on the woven fabric made of the fibrillated composite fiber made of polyamide and polyester and the other portion, In other words, as a result of conducting research focusing on the fact that wrinkles can be seen due to such surface effects, they were completed.
【０００７】本発明の方法でいうポリアミドとポリエス
テルのフィブリル化型複合繊維からなる織物とは、ポリ
アミド及びポリエステルが、単一フィラメントの横断面
において一方の成分が他方の成分を完全に包囲しない形
状で、単一フィラメントの長手方向に沿って接合されて
いる複合繊維から織った布帛をいう。The woven fabric composed of fibrillated composite fibers of polyamide and polyester in the method of the present invention means that polyamide and polyester have a shape in which one component does not completely surround the other in the cross section of a single filament. , A fabric woven from composite fibers that are joined along the length of a single filament.
【０００８】ここで、織物としては、平織物、綾織物等
があげられるが、平織物は表面の凹凸が少ないので表面
効果がでやすく好ましい。Examples of the woven fabric include a plain woven fabric and a twill woven fabric. The plain woven fabric is preferable because it has less surface irregularities and thus has a good surface effect.
【０００９】ここで、ポリアミドとしては、例えばナイ
ロン４、ナイロン６、ナイロン７、ナイロン１１、ナイ
ロン１２、ナイロン６６、ナイロン６，１０、ポリメタ
キシレンアジバミド、ポリパラキシリレンデカンアミ
ド、ポリビスシクロヘキシルメタンデカンアミド及びそ
れらを成分とするコポリアミド等があげられる。Here, as the polyamide, for example, nylon 4, nylon 6, nylon 7, nylon 11, nylon 12, nylon 66, nylon 6,10, polymeta-xylene adipamide, polyparaxylylene decanamide, polybiscyclohexyl can be used. Examples include methanedecanamide and copolyamides containing them.
【００１０】また、ポリエステルとしては、例えばポリ
エチレンテレフタレート、ポリテトラメチレンテレフタ
レート、ポリエチレンオキシベンゾエート、ポリ１，４
‐ジメチルシクロヘキサンテレフタレート、ポリピバロ
ラクトン及びこれらを成分とするコポリエステル等があ
げられる。As the polyester, for example, polyethylene terephthalate, polytetramethylene terephthalate, polyethylene oxybenzoate, poly 1,4
-Dimethylcyclohexane terephthalate, polypivalolactone and copolyesters containing these as components.
【００１１】ポリアミド／ポリエステル両成分の比率は
通常、０．０５〜０．９５の範囲である。The ratio of both polyamide / polyester components is usually in the range of 0.05 to 0.95.
【００１２】機械的な圧力を利用する皺加工は、例えば
ニップ式皺加工機のような二本一組以上のローラーによ
り機械的に圧力を加えることにより行う。タンブラーに
よる皺加工では織物に与える機械的圧力が小さく十分な
効果を得ることができない。即ち、ニップ式皺加工機等
によって加えられる機械的圧力は、３０〜５０ｋｇ／ｃ
ｍ程度が好ましく、機械的圧力が小さ過ぎれば、後記す
るように皺部と他部との開繊度の差がでないので適当で
ない。Wrinkling using mechanical pressure is performed by mechanically applying pressure with two or more pairs of rollers such as a nip wrinkling machine. Wrinkling with a tumbler does not provide a sufficient effect because the mechanical pressure applied to the fabric is small. That is, the mechanical pressure applied by a nip wrinkle processing machine or the like is 30 to 50 kg / c.
m is preferable, and if the mechanical pressure is too low, there is no difference in the degree of opening between the wrinkle portion and the other portion, which will be described later.
【００１３】皺加工の方法は、上記布帛をロープ状とし
て、皺加工機のローラーに通し、エンドレスにて布帛を
循環させ皺を得る。この際、ローラーを通過する時にの
み、ロープ状とし、次にローラーを通過する時までは拡
布の状態が好ましい。更に、該布帛が、１０〜３０重量
％程度の水分を含有していることが、皺付け効果を上げ
るためには好ましい。なお、皺付けの程度は上記循環回
数により、容易にコントロールすることが可能である
が、例えば、従来の加工方法と同程度の皺を得るために
は、３０秒で１回の循環により約２０分で達成すること
ができる。In the method of wrinkling, the above cloth is formed into a rope shape, passed through a roller of a wrinkling machine, and the cloth is circulated endlessly to obtain wrinkles. At this time, it is preferable that the rope is formed only when passing through the roller and the spread state is obtained until the time when the roller is passed next time. Further, it is preferable that the cloth contains about 10 to 30% by weight of water in order to improve the wrinkling effect. The degree of wrinkling can be easily controlled by the number of times of circulation, but for example, in order to obtain wrinkles of the same degree as in the conventional processing method, it is possible to perform about 20 times by circulating once in 30 seconds. Can be achieved in minutes.
【００１４】この機械的な圧力を利用する皺加工によ
り、皺の屈曲部のフィブリル化複合繊維が一部開繊す
る。また、下記のフィブリル化の際に皺部分と他の部分
との開繊の差がより大きくなる。By the wrinkling process utilizing this mechanical pressure, a part of the fibrillated composite fiber in the bent portion of the wrinkle is opened. In addition, the difference in opening between the wrinkled portion and the other portion becomes larger during the following fibrillation.
【００１５】ここで、フィブリル化とは、フィブリル化
型複合繊維が各成分の接合部に分割され、一方の成分の
セグメント糸と他方の成分のセグメント糸からなるフィ
ブリルになることをいう。具体的には、ポリアミドとポ
リエステルからなるフィブリル化型複合繊維からなる布
帛を、ポリアミド膨潤処理のためのポリアミドを膨潤せ
しめる薬剤（以下、フィブリル化剤という。）により処
理して収縮緻密化させることにより行う。Here, fibrillation means that the fibrillated composite fiber is divided into joints of each component, and becomes a fibril composed of a segment yarn of one component and a segment yarn of the other component. Specifically, a cloth made of fibrillated composite fibers made of polyamide and polyester is treated with an agent for swelling polyamide for polyamide swelling treatment (hereinafter, referred to as fibrillating agent) to shrink and densify it. To do.
【００１６】フィブリル化剤としては、具体的には、ベ
ンジルアルコール、β‐フェニルエチルアルコール、フ
ェノール、ｍ‐クレゾール、蟻酸、酢酸等があげられ
る。また、その水溶液又は水性エマルジョンとして用い
るのが適している。特に、以上の中でもベンジルアルコ
ールの水性エマルジョンを用いる方法が織物の収縮性や
フィブリル化効果の点で、また取扱いが比較的容易な点
で本発明の方法に最適である。Specific examples of the fibrillating agent include benzyl alcohol, β-phenylethyl alcohol, phenol, m-cresol, formic acid, acetic acid and the like. It is also suitable to use as an aqueous solution or emulsion thereof. In particular, the method using an aqueous emulsion of benzyl alcohol is most suitable for the method of the present invention in terms of the shrinkage and fibrillation effect of the fabric and the relatively easy handling.
【００１７】上記フィブリル化剤の水性エマルジョンを
作るには、フィブリル化剤に界面活性剤を添加して乳化
分散させればよく、該界面活性剤としては、ノニオン系
活性剤、カチオン系活性剤、アニオン系活性剤、両性活
性剤またはそれらの混合型等いずれでもよい。In order to prepare an aqueous emulsion of the above fibrillating agent, a surfactant may be added to the fibrillating agent and emulsified and dispersed. As the surfactant, a nonionic surfactant, a cationic surfactant, It may be an anionic activator, an amphoteric activator or a mixture thereof.
【００１８】フィブリル化剤の濃度は、十分な収縮とフ
ィブリル化効果を得るためには１．５重量％以上が好ま
しい。５０重量％を越えると水性エマルジョンの場合は
不安定となり、後のフィブリル化剤の除去が非常に困難
になり、またポリアミド成分以外の成分に影響を与える
恐れがある。かかる観点から該濃度は３〜３０重量％で
あるのが特に好ましい。The concentration of the fibrillating agent is preferably 1.5% by weight or more in order to obtain sufficient shrinkage and fibrillation effect. If the content exceeds 50% by weight, the aqueous emulsion becomes unstable, making it extremely difficult to remove the fibrillating agent later, and may affect components other than the polyamide component. From such a viewpoint, the concentration is particularly preferably 3 to 30% by weight.
【００１９】本発明の方法では、上記のようなフィブリ
ル化剤を含む処理液中に非処理物を浸漬放置するか、浸
漬後マングル等により絞液するのが好適である。In the method of the present invention, it is preferable that the untreated product is left in the treatment liquid containing the fibrillating agent as described above, or is squeezed by mangle after the immersion.
【００２０】該処理液の温度は、５〜８０℃、特に１０
〜５０℃が望ましく、浸漬絞液する場合、該布帛が保持
するフィブリル化剤の量は、１〜５０重量％（対布帛重
量）が好ましい。The temperature of the treatment liquid is 5 to 80 ° C., especially 10
When the immersion and squeezing solution is used, the amount of the fibrillating agent held by the fabric is preferably 1 to 50% by weight (based on the weight of the fabric).
【００２１】熱セットは、通常使用される１７０〜１９
０℃の温度で実施される。The heat set is generally used 170 to 19
It is performed at a temperature of 0 ° C.
【００２２】上述したような機械的皺加工の効果は比較
的弱いものであるから、該効果を十分に発揮させるため
には、上記開繊条件を余り強くしないことが好ましい。Since the effect of the mechanical wrinkle processing as described above is relatively weak, it is preferable that the opening condition is not so strong in order to sufficiently bring out the effect.
【００２３】以上述べたように、本発明の方法では、フ
ィブリル化剤による開繊フィブリル化前に、ローラーに
よる機械的圧力を加え、適度にフィブリル化剤による開
繊フィブリル化を実施して皺加工を施す。即ち、機械的
圧力により予め皺を付与しフィブリル化繊維の一部を軽
度に開繊して、皺部分と他の部分のフィブリル化度の差
を大きくすることにより皺を形成せしめ、続くフィブリ
ル化後の収縮過程での高収縮時の収縮差を利用して耐久
性のある皺を得る。As described above, in the method of the present invention, before the fiber-opening fibrillation by the fibrillating agent, mechanical pressure is applied by the roller, and the fiber-opening fibrillation is appropriately performed by the fibrillating agent to perform the wrinkle processing. Give. That is, wrinkles are applied in advance by mechanical pressure to lightly open a part of the fibrillated fiber, and wrinkles are formed by increasing the difference in the degree of fibrillation between the wrinkled portion and the other portion, followed by fibrillation. A durable wrinkle is obtained by utilizing the difference in shrinkage at the time of high shrinkage in the subsequent shrinking process.
【００２４】以下、実施例により本発明を更に詳しく説
明するが、本発明はこの実施例に限定されるものではな
い。Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples.
【００２５】[0025]
【実施例】経糸（ポリエチレンテレフタレートフィラメ
ント７５デニール／フィラメント本数７２／撚回数１２
００）及び緯糸（ポリアミドとポリエステルからなるフ
ィブリル化型複合繊維５０デニール／フィラメント本数
２５／撚回数２１００）を用いた平織生機（密度；９９
×８２）を、ニップ式皺加工機を使用してロープ状で圧
力ローラーを通して４０ｋｇ／ｃｍの機械的圧力をか
け、皺加工を実施した。この際、該布帛はエンドレスと
して３０秒以内に１回の割合で循環させ、圧力ローラー
を通過して皺付けされる時にのみロープ状とし、次に圧
力ローラーを通過する時までは拡布の状態を保つように
した。尚、皺付けの効果を増大させるため布帛の水分を
１５重量％とした。この条件下で、約２０分間の皺付け
加工を実施した。Example: Warp (polyethylene terephthalate filament 75 denier / filament number 72 / twist number 12
00) and wefts (50 denier fibrillated composite fibers composed of polyamide and polyester / 25 filaments / twist number 2100) using a plain weaving machine (density: 99)
The wrinkle processing was carried out by applying a mechanical pressure of 40 kg / cm through a pressure roller to the 82 ×) through a pressure roller using a nip wrinkling machine. At this time, the fabric is circulated once within 30 seconds as endless, and is formed into a rope shape only when it is wrinkled after passing through the pressure roller, and the spread state is maintained until the time when it is next passed through the pressure roller. I tried to keep it. The water content of the cloth was set to 15% by weight in order to increase the effect of wrinkling. Under this condition, wrinkling was performed for about 20 minutes.
【００２６】その後、拡布の状態としてベンジルアルコ
ール１８％のエマルジョン（乳化剤：日華化学サンモー
ルＢＫ２０Ｃｏｎｃ．１．８％使用）でピックアップ４
８％でパッドした後、巻き取って１０分間空回転させな
がら放置し、開繊を促進させ、更に、マングルにより機
械的圧力を加え開繊を完了してから、湯洗（８０〜９５
℃）を行った。この結果、該布帛は幅方向で約７０％に
まで高収縮した。Then, as a spread state, picked up with an emulsion of 18% benzyl alcohol (emulsifier: used Nichika Kagaku Sanmor BK20Conc. 1.8%) 4
After padding with 8%, it is wound up and left for 10 minutes while idly rotating to accelerate the opening, and further, mechanical pressure is applied by the mangle to complete the opening, and then washing with hot water (80 to 95
C) was performed. As a result, the fabric was highly shrunk to about 70% in the width direction.
【００２７】続いて、１９０℃で２分間熱セットを実施
した。Subsequently, heat setting was carried out at 190 ° C. for 2 minutes.
【００２８】この結果として、耐久性のある皺を有する
織物が製造された。As a result of this, a durable wrinkled fabric was produced.
【００２９】[0029]
【発明の効果】以上のように本発明の方法を使用するこ
とにより、ポリアミドとポリエステルのフィブリル化型
複合繊維からなる織物の表面に耐久性のある皺を持たせ
ることができる。As described above, by using the method of the present invention, it is possible to impart a durable wrinkle to the surface of the woven fabric made of the fibrillated composite fiber of polyamide and polyester.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ０６Ｃ 23/04 Ｄ０６Ｃ 23/04 Ａ Ｄ０６Ｊ 1/12 Ｄ０６Ｊ 1/12 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display location D06C 23/04 D06C 23/04 A D06J 1/12 D06J 1/12
Claims (1)
ブリル化型複合繊維からなる織物をロープ状として機械
的な圧力を加えて皺を生じさせ、次に該織物を開繊フィ
ブリル化し、続いて１７０〜１９０℃で熱セットを実施
することを特徴とする表面皺効果を有する織物の製造方
法。1. A woven fabric made of a fibrillated type composite fiber made of polyamide and polyester is formed into a rope shape and mechanical pressure is applied to generate wrinkles, and then the woven fabric is opened and fibrillated, and then 170 to 190 ° C. A method for producing a woven fabric having a surface wrinkle effect, which comprises performing heat setting in