JP2680133B2 - Embroidery lace and its manufacturing method - Google Patents
Embroidery lace and its manufacturing methodInfo
- Publication number
- JP2680133B2 JP2680133B2 JP1173994A JP17399489A JP2680133B2 JP 2680133 B2 JP2680133 B2 JP 2680133B2 JP 1173994 A JP1173994 A JP 1173994A JP 17399489 A JP17399489 A JP 17399489A JP 2680133 B2 JP2680133 B2 JP 2680133B2
- Authority
- JP
- Japan
- Prior art keywords
- embroidery
- fabric
- thread
- lace
- modified polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は、婦人服等に用いられるエンブロイダリー・
レース、特に基布、刺しゅう糸及び裏糸の全てに改質ポ
リエステル・フィラメント糸を用い、柔軟性、染色性並
びにヒートセット性に優れたエンブロイダリー・レース
及びその製法に関する。DETAILED DESCRIPTION OF THE INVENTION (Industrial field of application) The present invention relates to an embroidered product for use in women's clothing and the like.
TECHNICAL FIELD The present invention relates to an embroidery lace excellent in flexibility, dyeability and heat setting by using a modified polyester filament yarn for all of lace, particularly base cloth, embroidery thread and back thread, and a method for producing the same.
（従来の技術） 従来から、エンブロイダリー・レースはチュール、オ
ーガンジー、ローン、ジョーゼット、羽二重など薄地の
基布にレーヨン糸や錦糸などで透し模様の刺しゅうを施
した高級レース地として婦人服等に用いられている。(Prior Art) Traditionally, embroidery lace has been used as a high-class lace fabric with a thin base fabric such as tulle, organdy, lawn, georgette, and habutae, which is embroidered in a transparent pattern with rayon thread or brocade thread. Used in women's clothing.
近年、合成繊維及びその加工技術の進歩に伴い、エン
ブロイダリー・レースの基布や刺しゅう糸に合成繊維を
使用する場合も多くなりつつあり、例えば薄地の基布に
よる形態安定性不良に対してはナイロンのように細くて
強度の大きな合成繊維を用いることによってこれをカバ
ーし、一方剛性の大きいポリエステル繊維についても、
アルカリ処理による減量加工によって剛性を減らし、こ
れを刺しゅう部分や基布部分に使用してしなやかさを付
与させることが可能となる。In recent years, with the progress of synthetic fibers and their processing technology, it is becoming more common to use synthetic fibers for embroidery lace base fabrics and embroidery threads. Covers this by using thin and strong synthetic fibers such as nylon, while polyester fibers with high rigidity
It becomes possible to reduce the rigidity by weight reduction processing by alkali treatment and use it for embroidering or base cloth to give it flexibility.
この様に、各種繊維との組合せが可能となることによ
り、エンブロイダリー・レースも目的に応じて各種素材
を使ったものの提供が可能となり、それだけ用途も広く
且つ大きくなりつつある。As described above, since it is possible to combine with various fibers, it is possible to provide embroidery lace using various materials according to the purpose, and its use is widening and expanding.
（発明が解決しようとする課題） しかし、エンブロイダリー・レースは基布部分、刺し
ゅう部分、裏糸共に同一色相とするのが製品としての基
本であり、しかも最近の用途の拡大に伴い付型加工等ヒ
ートセット性が重要なファクターとなってきている。(Problems to be solved by the invention) However, it is a basic product as for the embroidery lace that the base fabric portion, the embroidery portion, and the back yarn have the same hue. The heat setting property such as processing has become an important factor.
従来のエンブロイダリー・レースの主力となっている
ナイロン糸を基布に用い、レイヨン糸や綿糸を刺しゅう
糸に用いたものは、染色を二回施す必要があり、しかも
その際の色合せがむずかしく、付型性も不十分である等
問題が多い。Nylon threads, which have been the mainstay of conventional embroidery lace, are used as the base cloth, and rayon threads and cotton threads are used as embroidery threads. There are many problems such as difficulty and poor moldability.
この問題を解決するには、使用する素材の全てを同一
素材とすることが良いと考えられるが、天然繊維では形
態安定性及び付型性に難点があり、ナイロン繊維を用い
た場合は変色等、衣料としての適性上の問題に加え、付
型性が不十分であり、上記問題点の解決には到っていな
い。In order to solve this problem, it is considered good to use all the same materials, but natural fibers have problems in shape stability and moldability, and when nylon fibers are used, discoloration, etc. In addition to the problem of suitability for clothing, the moldability is insufficient, and the above problems have not been solved.
また、付型性の良いポリエステル繊維で、全ての素材
を形成することも考えられるが、この場合、ポリエステ
ル繊維特有の剛性については、既述した如くアルカリ処
理による減量加工により解決できるとしても、着色には
高温・高圧染色を必要とし、特に高圧処理により刺しゅ
う部分のへたりが大きくなり、商品性能を損なう虞れが
大きい。It is also possible to form all materials with polyester fibers having good moldability, but in this case, the rigidity peculiar to polyester fibers can be colored even if it can be solved by weight reduction processing by alkali treatment as described above. Requires high-temperature and high-pressure dyeing, and in particular, high-pressure treatment causes large embroidery on the embroidery area, which may impair product performance.
こうした点から、従来のエンブロイダリー・レースで
は全てに同一素材を使うことは殆んどなく、上記問題点
を敢えて受け入れざるを得なかったのが現状である。From this point of view, in the conventional embroidery race, the same material is rarely used for all of them, and it is the current situation that the above problems have been compelled to be accepted.
本発明は前述のような問題点を解決したものであり、
同一色相を得べき染色における難点がなく、しかも付型
性の良好なエンブロイダリー・レース及びその製法を提
供するとを目的とするものである。The present invention has solved the above-mentioned problems,
It is an object of the present invention to provide an embroidery lace which has no difficulty in dyeing to obtain the same hue and has good moldability, and a method for producing the same.
（課題を解決するための手段及び作用） 上記目的を達成するため、本発明は、第１に、基布、
刺しゅう糸及び裏糸が共に金属スルホネート基を含有す
る二塩基酸成分とポリエチレンテレフタレート成分とを
共重合して得られる改質ポリエステル・フィラメント糸
を構成糸とし、基布、刺しゅう糸及び裏糸が共に、減量
率３〜20％でアルカリ減量処理が施され、且つ、基布、
刺しゅう糸及び裏糸が同一色相で染色されてなるエンブ
ロイダリー・レースをその要旨とし、また第２に、金属
スルホネート基を含有する二塩基酸成分とポリエチレン
テレフタレート成分とを共重合して得られる改質ポリエ
ステル・フィラメント糸からなる薄地と水溶性繊維から
なる織物を合わせて、基布とし、金属スルホネート基を
含有する二塩基酸成分とポリエチレンテレフタレート成
分とを共重合して得られる改質ポリエステル・フィラメ
ント糸の刺しゅう糸、裏糸によって、レース地を作成
し、その後、水溶液中で水溶性織物を溶解除去し、さら
に、アルカリ減量、染色することを特徴とするエンブロ
イダリー・レースの製法をもその要旨とするものであ
る。(Means and Actions for Solving the Problems) In order to achieve the above object, the present invention firstly provides a base cloth,
A modified polyester filament yarn obtained by copolymerizing a dibasic acid component having a metal sulfonate group in both the embroidery thread and the back thread is used as a constituent thread, and the base cloth, the embroidery thread and the back thread are both , The alkali weight loss treatment is applied at a weight loss rate of 3 to 20%, and the base cloth,
The gist is an embroidery lace in which the embroidery thread and the back thread are dyed in the same hue, and secondly, it is obtained by copolymerizing a dibasic acid component containing a metal sulfonate group and a polyethylene terephthalate component. Modified polyester ・ Modified polyester obtained by copolymerizing a dibasic acid component containing a metal sulfonate group and a polyethylene terephthalate component by combining a thin fabric made of filament yarn and a woven fabric made of water-soluble fiber as a base fabric. An embroidery lace manufacturing method is also characterized in that a lace fabric is created by using embroidery threads and back threads of filament threads, and then water-soluble fabrics are dissolved and removed in an aqueous solution, and further alkali weight reduction and dyeing are performed. This is the summary.
本発明のエンブロイダリー・レースは、金属スルホネ
ート基を含有する二塩基酸成分とポリエチレンテレフタ
レート成分とを共重合して得られる改質ポリエステル・
フィラメント糸からなる薄地と水溶性繊維からなる織物
を合わせて、基布とし、金属スルホネート基を含有する
二塩基酸成分とポリエチレンテレフタレート成分とを共
重合して得られる改質ポリエステル・フィラメント糸の
刺しゅう糸、裏糸によってレース地を作成し、その後、
水溶液中で水溶性織物を溶解除去し、さらに、アルカリ
減量と染色を施すことにより製造できる。なお、このア
ルカリ減量と染色とは、耐アルカリ性の染料を用いるこ
とにより同時に行うことが可能であり、勿論それぞれ別
個に行うこともできる。また、基布として水溶性繊維か
らなる織物を合わせ用いる必要は必ずしもなく、金属ス
ルホネート基を含有する二塩基酸成分とポリエチレンテ
レフタレート成分とを共重合して得られる改質ポリエス
テル・フィラメント糸で製した布のみで基布を構成して
もよい。The embroidery lace of the present invention is a modified polyester obtained by copolymerizing a dibasic acid component containing a metal sulfonate group and a polyethylene terephthalate component.
Embroidery of modified polyester filament yarn obtained by copolymerizing a dibasic acid component containing a metal sulfonate group and a polyethylene terephthalate component by combining a thin fabric made of filament yarn and a woven fabric made of water-soluble fiber as a base fabric. Create lace with thread and back thread, then
It can be produced by dissolving and removing the water-soluble fabric in an aqueous solution, and further subjecting it to alkali reduction and dyeing. The alkali weight loss and the dyeing can be performed at the same time by using an alkali-resistant dye, and can of course be performed separately. Further, it is not always necessary to use a woven fabric composed of water-soluble fibers as the base fabric, and it is made of a modified polyester filament yarn obtained by copolymerizing a dibasic acid component containing a metal sulfonate group and a polyethylene terephthalate component. The base fabric may be composed of only the fabric.
以下、本発明をその作用と共に詳細に説明する。 Hereinafter, the present invention will be described in detail together with its operation.
本発明のエンブロイダリー・レースは、基布部分、刺
しゅう部分及び裏糸部分の全てが改質ポリエステル繊維
から成るフィラメント糸で形成されている。In the embroidery lace of the present invention, the base fabric portion, the embroidery portion and the back yarn portion are all formed of filament yarn made of modified polyester fiber.
本発明に使用する改質ポリエステル・フィラメント糸
は、金属スルホネート基を有する二塩基酸成分とポリエ
チレンテレフタレート成分とを共重合して得られるもの
であり、カチオン可染型ポリエステル繊維として公知の
ものである。必要に応じ、他の成分を混用して共重合し
たものを用いても良く、具体的な製造方法等については
特開昭58−136826号公報等に詳しく記載されている。The modified polyester filament yarn used in the present invention is obtained by copolymerizing a dibasic acid component having a metal sulfonate group and a polyethylene terephthalate component, and is known as a cationic dyeable polyester fiber. . If desired, other components may be mixed and copolymerized, and specific production methods and the like are described in detail in JP-A-58-136826.
本発明に用いる改質ポリエステル・フィラメント糸と
しては、金属スルホネート基を有しており、カチオン染
料による常圧染色が可能であることが肝要であって、通
常のポリエステル繊維に必要な高温・高圧染色を必要と
しないものであれば良い。The modified polyester filament yarn used in the present invention has a metal sulfonate group, and it is essential that it can be dyed under atmospheric pressure with a cationic dye, and high-temperature / high-pressure dyeing required for ordinary polyester fibers. Anything that does not require
本発明のエンブロイダリー・レースに用いる基布の組
織は、編物、織物、不織布のいずれでも良いが、取り扱
いの容易さからは平織組織の織物が好ましい。また、フ
ィラメント糸としては、マルチフィラメント糸、モノフ
ィラメント糸のいずれでも良く、スプリット・ファイバ
ーやテープ状の糸を用いることも可能である。そして、
エンブロイダリー・レースの基布の構造としては、改質
ポリエステル・フィラメント糸からなる薄地と水溶性繊
維からなる織物とを合わせて基布としてもよいし、改質
ポリエステル・フィラメント糸からなる布のみにより基
布を構成してもよいが、簡単、効率的に薄いエンブロイ
ダリー・レースを製造することができるため、水溶性繊
維からなる織物を合わせて基布とするのが好ましい。The design of the base fabric used for the embroidery lace of the present invention may be any of knitted fabric, woven fabric and non-woven fabric, but a plain woven fabric is preferred from the viewpoint of easy handling. Further, the filament yarn may be either a multifilament yarn or a monofilament yarn, and it is also possible to use a split fiber or a tape-shaped yarn. And
The structure of the embroidery lace base fabric may be a combination of a thin fabric made of modified polyester filament yarn and a woven fabric made of water-soluble fiber, or only a fabric made of modified polyester filament yarn. Although the base fabric may be formed by the above method, it is preferable to use a woven fabric made of water-soluble fibers together as the base fabric because a thin embroidery lace can be easily and efficiently manufactured.
次に本発明に係るエンブロイダリー・レースの製造法
について説明する。Next, a method for manufacturing the embroidery lace according to the present invention will be described.
本発明に用いる改質ポリエステル・フィラメント糸
は、金属スルホネート基を含有する二塩基酸成分とポリ
エチレンテレフタレート成分を共重合し、溶融紡糸して
得られるものであり、この様な繊維の製法は特開昭58−
136826号等で公知である。The modified polyester filament yarn used in the present invention is obtained by copolymerizing a dibasic acid component containing a metal sulfonate group and a polyethylene terephthalate component, and melt-spinning the fiber. 58-
It is known from No. 136826.
本発明においては、この改質ポリエステル繊維による
フィラメント糸を用いて、基布部分、刺しゅう部分及び
裏糸部分の全てを同一素材で形成する。In the present invention, the base fabric portion, the embroidery portion and the back yarn portion are all formed of the same material by using the filament yarn made of the modified polyester fiber.
基布への刺しゅうの仕方等については、従来エンブロ
イダリー・レースにおいて用いられる手法をそのまま利
用することが出来る。基布に刺しゅうを施した後、次い
でアルカリ水溶液にて改質ポリエステル繊維に減量処理
を施す。Regarding the method of embroidering the base cloth, the method used in the conventional embroidery race can be used as it is. After embroidering the base cloth, the modified polyester fiber is then weight-reduced with an alkaline aqueous solution.
減量処理はポリエステル繊維の剛さを除去すると同時
に美麗な表面光沢としなやかさを付与させるためのもの
である。またこの減量処理で基布の構成糸条間に間隙が
生じるため、同基布の透視性が向上し、より高級感が高
められる。更には、後の染色工程における染色性並びに
発色性が向上される。この減量処理の程度は、減量率が
３〜20％が好ましい。３％以下では柔軟性に乏しく、20
％以上では柔軟に過ぎてへたりやすく、いずれにしても
高級感が失われる。The weight reduction treatment is for removing the stiffness of the polyester fiber and at the same time imparting a beautiful surface gloss and suppleness. In addition, since a gap is formed between the constituent yarns of the base cloth by this weight reduction treatment, the see-through property of the base cloth is improved and a higher-grade feeling is enhanced. Furthermore, the dyeability and color developability in the subsequent dyeing step are improved. The degree of this weight reduction treatment is preferably such that the weight reduction rate is 3 to 20%. Less than 3% has poor flexibility, 20
If it is more than%, it is too flexible and easily tired, and in any case, the high-class feeling is lost.
ここで本発明のエンブロイダリー・レースに使用され
る改質ポリエステル繊維は、一般のポリエステル繊維に
比較して減量されやすく、処理時間を短くすることが可
能である。そのため、厚みが少なく繊維の密度の小さい
刺しゅうの施されていない基布部分は所望のしなやかさ
を付与するのに十分な減量がなされていても、厚みが大
きく繊維の密度の大きい刺しゅうの施された部分はその
減量が表層に止まることが多く、刺しゅう部分のへたり
が少ない。また、処理液のアルカリ濃度も低くすること
ができるため、コストも削減される。Here, the modified polyester fiber used in the embroidery lace of the present invention is more likely to be reduced in weight than the general polyester fiber, and the treatment time can be shortened. Therefore, the embroidery with a large thickness and a high fiber density is applied even if the base cloth part with a small thickness and a low fiber density is not embroidered, even if the weight is reduced enough to give the desired suppleness. The weight loss of the embroidered part often stops on the surface layer, and the embroidery part has less squat. Further, since the alkali concentration of the treatment liquid can be lowered, the cost can be reduced.
次いで染色処理を施す。 Then, a dyeing process is performed.
本発明に用いる改質ポリエステル・フィラメント糸
は、繊維成分に金属スルホネート基を含有している常圧
カチオン可染タイプであり、沸騰水での通常の染色条件
で一浴染色が可能となる。使用する染料はカチオン染
料、分散染料のいずれのタイプを用いても良い。The modified polyester filament yarn used in the present invention is a normal pressure cation dyeable type containing a metal sulfonate group in the fiber component, and enables one-bath dyeing under normal dyeing conditions with boiling water. The dye used may be either a cationic dye or a disperse dye.
本発明においては、アルカリ減量処理により染色性及
び発色性が向上されるため、このアルカリ減量処理は染
色前又は染色と同時に行う必要がある。アルカリ減量処
理と染色とを同時に施す場合には、使用染料は耐アルカ
リ性の染料に限定され、分散染料が使用される。この分
散染料の使用にあたっては、減量処理を同時に施すこと
による染色性の向上の結果、低温（沸騰温度）常圧条件
下での染色が可能となった。In the present invention, since the dyeability and color developability are improved by the alkali weight reduction treatment, the alkali weight reduction treatment needs to be performed before or simultaneously with the dyeing. When the alkali reduction treatment and the dyeing are simultaneously performed, the dyes used are limited to alkali-resistant dyes, and disperse dyes are used. When this disperse dye was used, the dyeing property was improved by simultaneously performing the weight reduction treatment, and as a result, dyeing under low temperature (boiling temperature) and normal pressure conditions became possible.
また、アルカリ減量処理と染色とを同時に施すことに
より、工程が合理化されコストが低減されると共に、ア
ルカリ浴で染色することにより、染色中の布地の移動が
柔軟に行なわれ、刺しゅう糸等の損傷を防止することが
出来る。In addition, the alkali reduction treatment and dyeing are performed simultaneously to streamline the process and reduce costs, and dyeing in an alkaline bath allows the fabric to be moved flexibly during dyeing, resulting in damage to embroidery threads. Can be prevented.
（実施例） 以下、本発明を実施例により具体的に説明する。(Examples) Hereinafter, the present invention will be described specifically with reference to examples.
実施例１ ５−ソジウムスルホイソフタル酸をポリエチレンテレ
フタレートに5.3モル％共重合した改質ポリエステル・
フィラメント糸40d/12fで編成したチュールに、水溶性
ビニール繊維（ソルブロン（ニチビ製））製平織物を合
せて基布とし、同一素材の改質ポリエステル・フィラメ
ント糸100d/48fの二本合撚で得られた刺しゅう糸と、15
0d/48fにエアー交絡加工を施した改質ポリエステル・フ
ィラメント糸を裏糸としてレース地を作成した。Example 1 Modified polyester prepared by copolymerizing 5-sodium sulfoisophthalic acid with polyethylene terephthalate in an amount of 5.3 mol%.
Tulle knitted with filament yarn 40d / 12f, plain fabric made of water-soluble vinyl fiber (Solvlon (Nichibi)) was used as the base fabric, and doubled twist of 100d / 48f modified polyester filament yarn of the same material The resulting embroidery thread, 15
A lace fabric was prepared using a modified polyester filament yarn, which was air-entangled at 0d / 48f, as the back yarn.
この原布をヒート・セッターで170℃で熱処理し、巾
出しを行った後、沸騰水中で30分間処理をして水溶性ビ
ニール製平織物を溶解除去して、所定のエンブロイダリ
ー・レース生地を得た。This raw fabric is heat-treated at 170 ° C with a heat setter, tentering, and then treated in boiling water for 30 minutes to dissolve and remove the water-soluble vinyl plain weave, and then to the specified embroidery lace fabric. Got
この生地を分散型カチオン染料を用いて、次の様な処
理浴で沸騰水中で30分間処理した。This fabric was treated with a dispersion type cationic dye in boiling water for 30 minutes in the following treatment bath.
得られたエンブロイダリー・レース地は、基布、刺しゅ
う糸、裏糸共に同一色相に染色された良好な外観を有す
るものであった。 The embroidered lace obtained had a good appearance in which the base cloth, the embroidery thread and the back thread were dyed in the same hue.
実施例２ 実施例１と同様にして得られたエンブロイダリー・レ
ース地を苛性ソーダ10g/l、浴比1:30で沸騰水中で30分
間処理し、10.7％減量された生地を得た。Example 2 The embroidery lace obtained in the same manner as in Example 1 was treated with caustic soda at 10 g / l and a bath ratio of 1:30 in boiling water for 30 minutes to obtain a dough having a weight loss of 10.7%.
次いで分散型カチオン染料を用いて、実施例１と同様
の染色を行った。Then, the same dyeing as in Example 1 was performed using a dispersion type cationic dye.
得られたエンブロイダリー・レース地は、基布、刺し
ゅう糸、裏糸共に同一色相に染色された良好な外観を有
すると共に、ドレープ性に富むものであった。The obtained embroidery lace fabric had a good appearance in which the base fabric, the embroidery thread and the back thread were dyed in the same hue, and had a good drape property.
この生地を100℃の蒸熱で20分間の加工条件でプリー
ツ加工を実施し、洗濯処理した結果、良好なプリーツ保
持性を示した。対照的にナイロン・チュールにレーヨン
刺しゅうをしたものは洗濯によりプリーツが消失した。The fabric was pleated under steaming conditions of 100 ° C. for 20 minutes, and subjected to washing treatment, and as a result, good pleating retention was exhibited. In contrast, nylon tulle with rayon embroidery lost its pleats upon washing.
実施例３ 実施例１と同様にして得られたエンブロイダリー・レ
ース地を耐アルカリ性の分散染料とアルカリ剤で染色し
た。Example 3 The embroidered lace obtained in the same manner as in Example 1 was dyed with an alkali-resistant disperse dye and an alkali agent.
なお、対照として通常の分散染料の染色条件で染色し
たものを作成し、比較した。 As a control, a dye dyed under the usual dyeing conditions of a disperse dye was prepared and compared.
従来の条件で染色したものに比較して風合が柔軟であ
り、良好な同色性の生地が得られた。The texture was softer than that dyed under the conventional conditions, and a fabric having the same color was obtained.
アルカリ浴での染色による減量率は5.2％であった。 The weight loss rate due to dyeing in an alkaline bath was 5.2%.
（発明の効果） 本発明は基布、刺しゅう糸及び裏糸が共に常圧可染型
の改質ポリエステル・フィラメント糸で形成されている
ために、常圧による一浴染色が可能であり、アルカリに
よる減量処理を併せ施すことにより、柔軟で発色性が良
い、しかも基布、刺しゅう糸及び裏糸が同一色相のエン
ブロイダリー・レースが容易に得られる。 (Effect of the invention) Since the base fabric, the embroidery thread and the back thread are both formed of the atmospheric pressure dyeable modified polyester filament yarn in the present invention, one-bath dyeing under atmospheric pressure is possible, and An embroidery lace having the same hue as the base cloth, the embroidery thread and the back thread can be easily obtained by performing the weight reduction treatment together with.
更に基布、刺しゅう糸及び裏糸が共に同一の改質ポリ
エステル・フィラメント糸であるが故に、ヒートセット
性が極めて良く、従来むづかしいとされていたエンブロ
イダリー・レースのプリーツ加工等による付型性能を飛
躍的に向上させ得るものであり、用途の拡大等、その効
果は大きい。Furthermore, since the base cloth, embroidery thread and back thread are all the same modified polyester filament thread, the heat setting property is extremely good, and the embossing / lace pleating process, which was previously considered difficult, has a good moldability. Can be dramatically improved, and the effect is large, such as expansion of applications.
また改質ポリエステル・フィラメント糸からなる薄地
と水溶性繊維からなる織物を合わせて基布とし、レース
地を作成した後、水溶液中で水溶性織物を溶解除去し、
さらに、アルカリ減量、染色することにより、簡単、効
率的に薄いエンブロイダリー・レースを製造することも
できる。In addition, a thin fabric made of modified polyester filament yarn and a woven fabric made of water-soluble fiber are combined to form a base fabric, and after creating a lace fabric, the water-soluble woven fabric is dissolved and removed in an aqueous solution,
Further, by thinning with alkali and dyeing, it is possible to easily and efficiently produce a thin embroidery lace.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭61−152888（ＪＰ，Ａ) 特開 昭54−59463（ＪＰ，Ａ) 特開 昭54−106672（ＪＰ，Ａ) ─────────────────────────────────────────────────── ─── Continuation of front page (56) References JP-A-61-152888 (JP, A) JP-A-54-59463 (JP, A) JP-A-54-106672 (JP, A)
Claims (2)
ルホネート基を含有する二塩基酸成分とポリエチレンテ
レフタレート成分とを共重合して得られる改質ポリエス
テル・フィラメント糸を構成糸とし、基布、刺しゅう糸
及び裏糸が共に、減量率３〜20％でアルカリ減量処理が
施され、且つ、基布、刺しゅう糸及び裏糸が同一色相で
染色されてなることを特徴とするエンブロイダリー・レ
ース。1. A modified polyester filament yarn obtained by copolymerizing a dibasic acid component containing a metal sulfonate group and a polyethylene terephthalate component as the base fabric, the embroidery yarn and the back yarn. An embroidery characterized in that the cloth, the embroidery thread and the back thread are both subjected to an alkali weight loss treatment at a weight loss rate of 3 to 20%, and the base cloth, the embroidery thread and the back thread are dyed in the same hue. ·race.
分とポリエチレンテレフタレート成分とを共重合して得
られる改質ポリエステル・フィラメント糸からなる薄地
と水溶性繊維からなる織物を合わせて、基布とし、金属
スルホネート基を含有する二塩基酸成分とポリエチレン
テレフタレート成分とを共重合して得られる改質ポリエ
ステル・フィラメント糸の刺しゅう糸、裏糸によって、
レース地を作成し、その後、水溶液中で水溶性織物を溶
解除去し、さらに、アルカリ減量、染色することを特徴
とするエンブロイダリー・レースの製法。2. A base fabric is made by combining a thin fabric made of modified polyester filament yarn obtained by copolymerizing a dibasic acid component having a metal sulfonate group and a polyethylene terephthalate component with a woven fabric made of water-soluble fibers. A modified polyester filament yarn obtained by copolymerizing a dibasic acid component containing a metal sulfonate group and a polyethylene terephthalate component, by an embroidery yarn and a back yarn,
A method for producing embroidery lace, which comprises forming a lace fabric, then dissolving and removing the water-soluble fabric in an aqueous solution, and further reducing the alkali and dyeing.