JP3473993B2 - Anti-fog film - Google Patents
Anti-fog filmInfo
- Publication number
- JP3473993B2 JP3473993B2 JP17094494A JP17094494A JP3473993B2 JP 3473993 B2 JP3473993 B2 JP 3473993B2 JP 17094494 A JP17094494 A JP 17094494A JP 17094494 A JP17094494 A JP 17094494A JP 3473993 B2 JP3473993 B2 JP 3473993B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- parts
- film
- density polyethylene
- antifogging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】Detailed Description of the Invention
【０００１】[0001]
【産業上の利用分野】本発明は、青果物の包装等に使用
され、透明性、柔軟性および伸展性に優れ、低温保存時
にも防曇性を保持することができる防曇性フイルムに関
する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an anti-fog film which is used for packaging fruits and vegetables, has excellent transparency, flexibility and extensibility and can retain anti-fog properties even when stored at low temperatures.
【０００２】[0002]
【従来の技術】青果物の包装用フイルムとしては、透明
性、柔軟性、伸展性等に優れた可塑化ポリ塩化ビニル、
エチレン−酢酸ビニル共重合物、１，２−ポリブタジエ
ン等からなるフイルムが用いられ、青果物のプリパック
（トレイパック）、ノートレイ包装（直接包装）などの
用途に多用されている。（例えば、特開昭５１−８７５
５４号公報、特開昭５２−９６６５４号公報、特開昭５
２−１０９５４８号公報、特開昭５２−７１５５７号公
報、特開昭５２−１３９５９５号公報等参照）。一方、
密度が０．９２０ｇｒ／ｃｍ3以下、好ましくは密度
０．９１０ｇｒ／ｃｍ3程度の直鎖状低密度ポリエチレ
ンは、透明性、柔軟性、伸展性等に優れた性質を有しな
がら上記の青果物包装用フィルムとして用いられていな
かった。その理由としては、青果物の包装用フィルムに
は高レベルの防曇性が要求され、特に低温保存時に曇り
が発生せず、フイルムを透かして内容物が鮮明に見える
ことという要求に対して、直鎖状低密度ポリエチレンフ
イルムは好適には対応できなかったからである。つま
り、直鎖状低密度ポリエチレンは防曇剤との相溶性が高
すぎるため、通常はオレフィン系フイルムの防曇剤とし
て好適であると言われているジグリセリンオレート、ソ
ルビタンモノオレート、ジグリセリンラウレート、ジグ
リセリンモノオレート等を添加しても、それらがフイル
ム表面には十分にブリードアウトしてこないのである。2. Description of the Related Art As a film for packaging fruits and vegetables, plasticized polyvinyl chloride excellent in transparency, flexibility and extensibility,
A film made of an ethylene-vinyl acetate copolymer, 1,2-polybutadiene, etc. is used, and it is often used for prepacks (tray packs) of fruits and vegetables, note ray packaging (direct packaging) and the like. (For example, JP-A-51-875
54, JP-A-52-96654, JP-A-5
2-109548, JP-A-52-71557 and JP-A-52-139595). on the other hand,
The linear low-density polyethylene having a density of 0.920 gr / cm 3 or less, preferably about 0.910 gr / cm 3, is the above-mentioned fruit and vegetable package while having excellent properties such as transparency, flexibility and extensibility. It was not used as a film for use. The reason for this is that the packaging film for fruits and vegetables is required to have a high level of anti-fogging property, and in particular, there is no fogging during storage at low temperature, and the content can be seen clearly through the film. This is because the chain low-density polyethylene film could not be suitable. That is, since the linear low-density polyethylene has too high compatibility with the antifogging agent, diglycerin oleate, sorbitan monooleate, diglycerin laurate, which is generally said to be suitable as an antifogging agent for olefin-based films, is used. Even if rate, diglycerin monooleate, etc. are added, they do not sufficiently bleed out to the film surface.
【０００３】また、ポリオキシエチレンアルキルエーテ
ル、ポリオキシエチレンソルビタントリオレート等の防
曇助剤を並用しても、防曇効果を十分に高めることがで
きなかった。フイルム表面に防曇剤をブリードアウトさ
せるべく、必要以上に多量に防曇剤を添加することも考
えられるが、防曇剤を多量に添加すると押出成膜時にス
クリュー内でスリップ現象が発生して押出変動し、成膜
できないといった問題が生じる。Further, even if an antifogging auxiliary agent such as polyoxyethylene alkyl ether or polyoxyethylene sorbitan triolate is used together, the antifogging effect cannot be sufficiently enhanced. It is possible to add more antifogging agent than necessary in order to bleed out the antifogging agent on the film surface, but if a large amount of antifogging agent is added, a slip phenomenon occurs in the screw during extrusion film formation. There is a problem that the extrusion is fluctuated and the film cannot be formed.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、上記の実情
に鑑みてなされたものであり、密度０．９２０ｇｒ／ｃ
ｍ3以下の直鎖状低密度ポリエチレンに、好適な防曇剤
およびその他の成分を配合することにより、低温保存時
にも良好な防曇性を保持することができる防曇性フイル
ムを提供することを目的とする。The present invention has been made in view of the above circumstances and has a density of 0.920 gr / c.
To provide an anti-fog film capable of maintaining good anti-fog property even at low temperature storage by blending a linear low-density polyethylene of m 3 or less with a suitable anti-fog agent and other components. With the goal.
【０００５】[0005]
【課題を解決するための手段】請求項１記載の発明の防
曇性フイルムは、密度が０．９２０ｇｒ／ｃｍ３以下の
直鎖状低密度ポリエチレン１００重量部に対し、ジグリ
セリンラウレート１〜５重量部、高圧法低密度ポリエチ
レン１０〜３０重量部を含有する樹脂組成物からなり、
そのことにより上記目的が達成される。The anti-fogging film of the invention according to claim 1 has diglycerin laurate 1 to 100 parts by weight of linear low-density polyethylene having a density of 0.920 gr / cm 3 or less. A resin composition containing 5 parts by weight and 10 to 30 parts by weight of high-pressure low-density polyethylene,
Thereby, the above object is achieved.
【０００６】また、請求項２記載の発明の防曇性フイル
ムは、密度が０．９２０ｇｒ／ｃｍ３以下の直鎖状低密
度ポリエチレン１００重量部に対し、ジグリセリンラウ
レート１〜５重量部、グリセリンモノオレート０．１〜
１重量部、ポリオキシエチレンソルビタントリオレート
０．１〜１重量部、ポリオキシエチレンアルキルエーテ
ル０．１〜１重量部、高圧法低密度ポリエチレン１０〜
３０重量部を含有する樹脂組成物からなり、そのことに
より上記目的が達成される。The antifogging film according to the second aspect of the invention has 1 to 5 parts by weight of diglycerin laurate to 100 parts by weight of linear low-density polyethylene having a density of 0.920 gr / cm 3 or less. Glycerin monooleate 0.1
1 part by weight, polyoxyethylene sorbitan trioleate 0.1 to 1 part by weight, polyoxyethylene alkyl ether 0.1 to 1 part by weight, high pressure low density polyethylene 10
It is composed of a resin composition containing 30 parts by weight, whereby the above object is achieved.
【０００７】本発明に使用される直鎖状低密度ポリエチ
レンの密度は、０．９２０ｇｒ／ｃｍ3以下であり、特
に０．９１０ｇｒ／ｃｍ3以下が好ましい。直鎖状低密
度ポリエチレンのメルトフローレート（ＭＦＲ）は、２
〜３が好ましい。その市販品としては、例えば、ウルゼ
ックス１０３０Ｆ（三井石油化学社製ＭＦＲ ３．０、
密度０．９１０ｇｒ／ｃｍ3）があげられる。The linear low density polyethylene used in the present invention has a density of 0.920 gr / cm 3 or less, and particularly preferably 0.910 gr / cm 3 or less. The linear low density polyethylene has a melt flow rate (MFR) of 2
~ 3 are preferred. Examples of commercially available products include Ulzex 1030F (MFR 3.0 manufactured by Mitsui Petrochemical Co., Ltd.,
The density is 0.910 gr / cm 3 ).
【０００８】本発明に使用される低密度ポリエチレンと
しては高圧法により製造されるポリエチレンが使用で
き、そのメルトフローレート（ＭＦＲ）は、５〜１０が
好ましい。その市販品としては、例えば、ペトロセン２
０７（東ソー社製ＭＦＲ８．０、密度０．９２５ｇｒ／
ｃｍ３）があげられる。[0008] and the low density polyethylene used in the present invention
Polyethylene produced by high pressure method can be used
Come, its melt flow rate (MFR), 5 to 10 is preferred. The commercially available product is, for example, petrosene 2
07 (MFR 8.0 manufactured by Tosoh Corporation, density 0.925 gr /
cm 3 ).
【０００９】上記樹脂組成物は、直鎖状低密度ポリエチ
レンの１００重量部に対し、防曇剤としてジグリセリン
ラウレート１〜５重量部、より好適には２〜３重量部、
高圧法低密度ポリエチレン１０〜３０重量部、より好適
には１５〜２５重量部を混合して得られる。混合は通常
の混合機を用いて行うことができる。The above resin composition contains 1 to 5 parts by weight of diglycerin laurate as an antifogging agent, and more preferably 2 to 3 parts by weight, based on 100 parts by weight of linear low-density polyethylene.
It is obtained by mixing 10 to 30 parts by weight, more preferably 15 to 25 parts by weight of high-pressure low density polyethylene. Mixing can be performed using an ordinary mixer.
【００１０】ジグリセリンラウレートの含有割合が１重
量部未満の場合には、得られるフィルムの防曇性を高め
る効果が小さく、５重量部を超えると押出変動が起き
る。When the content of diglycerin laurate is less than 1 part by weight, the effect of improving the antifogging property of the obtained film is small, and when it exceeds 5 parts by weight, extrusion fluctuation occurs.
【００１１】高圧法低密度ポリエチレンは上記ジグリセ
リンラウレートの直鎖状低密度ポリエチレンに対する相
溶性を低下させる働きを有し、ジグリセリンラウレート
が成膜されたフィルム表面にブリードアウトし易くする
効果を有する。高圧法低密度ポリエチレンの含有割合が
１０重量部未満の場合には、防曇剤のフィルム表面への
ブリードアウトに時間がかかり防曇性を高める効果が不
十分であり、３０重量部を超えるとフィルムの透明性、
光沢が低下してくる。また、フィルム物性も低下し柔軟
性等が損なわれる。The high-pressure method low-density polyethylene has a function of reducing the compatibility of the above-mentioned diglycerin laurate with linear low-density polyethylene, and has an effect of making it easy to bleed out on the film surface on which diglycerin laurate is formed. Have. When the content of the high-pressure low-density polyethylene is less than 10 parts by weight, it takes time to bleed out the antifogging agent to the film surface, and the effect of increasing the antifogging property is insufficient, and when it exceeds 30 parts by weight. Film transparency,
The gloss decreases. In addition, the physical properties of the film are deteriorated and the flexibility and the like are impaired.
【００１２】本発明で使用される樹脂組成物は、さら
に、防曇剤として、グリセリンモノオレート、ポリオキ
シエチレンソルビタントリオレートおよびポリオキシエ
チレンアルキルエーテルを含有することができる。この
場合、該樹脂組成物は、直鎖状低密度ポリエチレン１０
０重量部に対し、ジグリセリンラウレートを１〜５重量
部、より好適には２〜３重量部、グリセリンモノオレー
トを０．１〜１重量部、より好適には０．２〜０．３重
量部、ポリオキシエチレンソルビタントリオレートを
０．１〜１重量部、より好適には０．２〜０．３重量
部、ポリオキシエチレンアルキルエーテルを０．１〜１
重量部、より好適には０．２〜０．３重量部、および、
高圧法低密度ポリエチレンを１０〜３０重量部、より好
適には１５〜２５重量部を混合して得られる。The resin composition used in the present invention may further contain glycerin monooleate, polyoxyethylene sorbitan trioleate and polyoxyethylene alkyl ether as an antifogging agent. In this case, the resin composition is a linear low-density polyethylene 10
With respect to 0 parts by weight, 1 to 5 parts by weight of diglycerin laurate, more preferably 2 to 3 parts by weight, 0.1 to 1 part by weight of glycerin monooleate, and more preferably 0.2 to 0.3 parts by weight. Parts by weight, 0.1 to 1 parts by weight of polyoxyethylene sorbitan trioleate, more preferably 0.2 to 0.3 parts by weight, 0.1 to 1 of polyoxyethylene alkyl ether.
Parts by weight, more preferably 0.2 to 0.3 parts by weight, and
It is obtained by mixing 10 to 30 parts by weight, more preferably 15 to 25 parts by weight, of high-pressure low density polyethylene.
【００１３】グリセリンモノオレートの含有割合が０．
１重量部未満の場合には、防曇剤のフィルム表面へのブ
リードアウト効果が小さくなり、防曇効果が不十分とな
る。逆に、１重量部を超えるとフィルム表面がべたつ
き、滑り不良等の不具合が生じる。The content ratio of glycerin monooleate is 0.
If the amount is less than 1 part by weight, the bleed-out effect of the antifogging agent on the film surface becomes small and the antifogging effect becomes insufficient. On the other hand, if the amount exceeds 1 part by weight, the film surface becomes sticky and defects such as slippage occur.
【００１４】ポリオキシエチレンソルビタントリオレー
トの含有割合が、０．１重量部未満の場合には、フィル
ムの製造初期の防曇効果が乏しく、１重量部を超えると
押出変動が大きく良好な成膜ができない。When the content of the polyoxyethylene sorbitan trioleate is less than 0.1 part by weight, the antifogging effect at the initial stage of film production is poor, and when it exceeds 1 part by weight, the extrusion fluctuation is large and a good film formation is achieved. I can't.
【００１５】ポリオキシエチレンアルキルエーテルの含
有割合が０．１重量部未満の場合には、フィルムの製造
初期の防曇効果が乏しく、１重量部を超えると押出変動
が大きく良好な成膜ができない。When the content of the polyoxyethylene alkyl ether is less than 0.1 part by weight, the antifogging effect at the initial production of the film is poor, and when it exceeds 1 part by weight, the extrusion variation is large and a good film cannot be formed. .
【００１６】該樹脂組成物には、各種添加剤、例えば、
着色剤、安定剤等を添加することができる。樹脂組成物
から公知の押出成膜機を使用して本発明の防曇性フィル
ムが得られる。フィルムの厚さは限定するものではない
が、１５〜３０μｍが好ましい。Various additives such as, for example,
Colorants, stabilizers and the like can be added. The antifogging film of the present invention can be obtained from the resin composition using a known extrusion film forming machine. Although the thickness of the film is not limited, it is preferably 15 to 30 μm.
【００１７】[0017]
【作用】樹脂組成物にジグリセリンラウレートと高圧法
低密度ポリエチレンとを含有させることにより、ジグリ
セリンラウレートの直鎖状低密度ポリエチレンに対する
相溶性が低下し、防曇性フイルムの表面に適量のジグリ
セリンラウレートをブリードアウトさせることができ
る。得られる樹脂組成物は高圧法低密度ポリエチレンを
含有するので押出変動を起こすことがない。By incorporating diglycerin laurate and high-pressure low-density polyethylene in the resin composition, the compatibility of diglycerin laurate with linear low-density polyethylene is reduced, and an anti-fogging film is obtained. An appropriate amount of diglycerin laurate can be bleed out on the surface of the. The obtained resin composition does not cause extrusion fluctuation because it contains high-pressure low-density polyethylene.
【００１８】特に、防曇剤としてジグリセリンラウレー
トに加えて、グリセリンモノオレート、ポリオキシエチ
レンソルビタントリオレートおよびポリオキシエチレン
アルキルエーテルを添加すると、防曇剤の直鎖状低密度
ポリエチレンに対する相溶性がさらに低下し、防曇性フ
ィルム表面への防曇剤のブリードアウトが、樹脂組成物
の押出変動を伴うことなく、短時間で行われる。Particularly, when glycerin monooleate, polyoxyethylene sorbitan trioleate and polyoxyethylene alkyl ether are added in addition to diglycerin laurate as an antifogging agent, the compatibility of the antifogging agent with linear low density polyethylene is improved. Is further reduced, and the bleed-out of the antifogging agent on the surface of the antifogging film is carried out in a short time without the fluctuation of extrusion of the resin composition.
【００１９】[0019]
【実施例】以下に、本発明を実施例に基づいて説明す
る。EXAMPLES The present invention will be described below based on examples.
【００２０】（実施例１）
直鎖状低密度ポリエチレン（三井石油化学社製、ウルト
ゼックス１０３０Ｆ、ＭＦＲ３．０、密度０．９１０ｇ
ｒ／ｃｍ３）１００重量部と、ジグリセリンラウレート
（理研ビタミン社製、リケマールＬ−７１−Ｄ）２．０
重量部と、高圧法低密度ポリエチレン（東ソー社製、ペ
トロセン２０７、ＭＦＲ８．０、密度０．９２５ｇｒ／
ｃｍ３）２０重量部とをミキサーで充分混合し樹脂組成
物を得た。この樹脂組成物から、５０ｍｍインフレーシ
ョン押出成膜機を使用し、厚さ１５μｍのフイルムを得
た。(Example 1) Linear low density polyethylene (Mitsui Petrochemical Co., Ltd., Ultzex 1030F, MFR 3.0, density 0.910 g)
r / cm 3 ) 100 parts by weight and diglycerin laurate (Rikenal L-71-D, manufactured by Riken Vitamin Co.) 2.0
Parts by weight and high-pressure low-density polyethylene (manufactured by Tosoh Corporation, Petrosene 207, MFR 8.0, density 0.925 gr /
cm 3 ) 20 parts by weight was thoroughly mixed with a mixer to obtain a resin composition. A film having a thickness of 15 μm was obtained from this resin composition using a 50 mm inflation extrusion film forming machine.
【００２１】（実施例２）
直鎖状低密度ポリエチレン（三井石油化学社製、ウルト
ゼックス１０３０Ｆ、ＭＦＲ３．０、密度０．９１０ｇ
ｒ／ｃｍ３）１００重量部と、ジグリセリンラウレート
（理研ビタミン社製、リケマールＬ−７１−Ｄ）２．０
重量部と、グリセリンモノオレート（理研ビタミン社
製、リケマールＯＬ−１００）０．２重量部と、ポリオ
キシエチレンソルビタントリオレート（理研ビタミン社
製、リケマールＯ−８５２）０．２重量部と、ポリオキ
シエチレンアルキルエーテル（理研ビタミン社製、リケ
マールＢ−２０５）０．２重量部と、高圧法低密度ポリ
エチレン（東ソー社製、ペトロセン２０７、ＭＦＲ８．
０、密度０．９２５ｇｒ／ｃｍ３）２０重量部とをミキ
サーで充分混合し樹脂組成物を得た。この樹脂組成物か
ら、５０ｍｍインフレーション押出成膜機を使用し、厚
さ１５μｍのフイルムを得た。(Example 2) Linear low-density polyethylene (Mitsui Petrochemical Co., Ltd., Ultzex 1030F, MFR 3.0, density 0.910 g)
r / cm 3 ) 100 parts by weight and diglycerin laurate (Rikenal L-71-D, manufactured by Riken Vitamin Co.) 2.0
Parts by weight, 0.2 part by weight of glycerin monooleate (manufactured by Riken Vitamin Co., Likemar OL-100), 0.2 part by weight of polyoxyethylene sorbitan trioleate (manufactured by Riken Vitamin Co., Likemar O-852), and poly Oxyethylene alkyl ether (Riken Vitamin Co., Riquemal B-205) 0.2 parts by weight, and high-pressure low density polyethylene (Tosoh Corp., Petrosene 207, MFR8.
0 and a density of 0.925 gr / cm 3 ) 20 parts by weight were thoroughly mixed with a mixer to obtain a resin composition. A film having a thickness of 15 μm was obtained from this resin composition using a 50 mm inflation extrusion film forming machine.
【００２２】（比較例１）高圧法
低密度ポリエチレンを除いたこと以外は、実施例
１と同様の方法でフイルムを得た。(Comparative Example 1) High pressure method A film was obtained in the same manner as in Example 1 except that low density polyethylene was removed.
【００２３】（比較例２）ジグリセリンラウレートをジ
グリセリンオレート（理研ビタミン社製、リケマールＯ
−７１−Ｄ）に変更したこと以外は、実施例１と同様に
してフイルムを得た。(Comparative Example 2) Diglycerin laurate was replaced with diglycerin oleate (Rikemar O manufactured by Riken Vitamin Co., Ltd.).
A film was obtained in the same manner as in Example 1, except that the film was changed to -71-D).
【００２４】（比較例３）ジグリセリンラウレートをソ
ルビタンモノオレート（理研ビタミン社製、リケマール
Ｏ−８０）に変更したこと以外は、実施例１と同様にし
てフイルムを得た。(Comparative Example 3) A film was obtained in the same manner as in Example 1, except that sorbitan monooleate (Rikemar O-80, manufactured by Riken Vitamin Co.) was used instead of diglycerin laurate.
【００２５】（比較例４）ジグリセリンラウレートをジ
グリセリンモノオレート（理研ビタミン社製、リケマー
ルＤＯ−１００）に変更したこと以外は、実施例１と同
様にしてフイルムを得た。(Comparative Example 4) A film was obtained in the same manner as in Example 1 except that diglycerin laurate was changed to diglycerin monooleate (Rikemar DO-100, manufactured by Riken Vitamin Co., Ltd.).
【００２６】（比較例５）高圧法
低密度ポリエチレンを除いたこと以外は、実施例
２と同様の方法でフイルムを得た。Comparative Example 5 High Pressure Method A film was obtained in the same manner as in Example 2 except that the low density polyethylene was removed.
【００２７】（比較例６）ジグリセリンラウレートをジ
グリセリンオレート（理研ビタミン社製、リケマールＯ
−７１−Ｄ）に変更したこと以外は、実施例２と同様に
してフイルムを得た。Comparative Example 6 Diglycerin laurate was replaced with diglycerin oleate (Rikemar O manufactured by Riken Vitamin Co., Ltd.).
A film was obtained in the same manner as in Example 2, except that the film was changed to -71-D).
【００２８】（比較例７）ジグリセリンラウレートをソ
ルビタンモノオレート（理研ビタミン社製、リケマール
Ｏ−８０）に変更したこと以外は、実施例２と同様にし
てフイルムを得た。(Comparative Example 7) A film was obtained in the same manner as in Example 2, except that sorbitan monooleate (Rikemar O-80, manufactured by Riken Vitamin Co.) was used instead of diglycerin laurate.
【００２９】（比較例８）ジグリセリンラウレートをジ
グリセリンモノオレート（理研ビタミン社製、リケマー
ルＤＯ−１００）に変更したこと以外は、実施例２と同
様にしてフイルムを得た。Comparative Example 8 A film was obtained in the same manner as in Example 2 except that diglycerin laurate was changed to diglycerin monooleate (Rikemar DO-100 manufactured by Riken Vitamin Co., Ltd.).
【００３０】上記実施例１、２および比較例１〜８にお
けるフィルムの成形性および得られたフィルムの低温防
曇性を以下の方法で評価した。The moldability of the films in Examples 1 and 2 and Comparative Examples 1 to 8 and the low temperature antifogging property of the obtained films were evaluated by the following methods.
【００３１】成形性：樹脂組成物を用いて押出機にて
成形を行い、押出変動の有無を確認した。結果を表１に
示す。Moldability: The resin composition was molded by an extruder, and the presence or absence of extrusion fluctuation was confirmed. The results are shown in Table 1.
【００３２】低温防曇性：水を含ませた布をフイルム
にてトレー包装し、−１５℃の冷凍庫内に２４時間保管
後、２４℃の室温に取り出し、２分、５分、１０分、１
５分、３０分、４５分、６０分、９０分、１２０分およ
び１８０分後のフィルムの防曇状態を目視にて評価し
た。Low-temperature anti-fogging property: A cloth moistened with water is tray-wrapped in a film, stored in a freezer at -15 ° C for 24 hours, and then taken out at room temperature at 24 ° C for 2 minutes, 5 minutes, 10 minutes, 1
The antifogging state of the film after 5 minutes, 30 minutes, 45 minutes, 60 minutes, 90 minutes, 120 minutes and 180 minutes was visually evaluated.
【００３３】防曇性評価基準は、以下の通りとした。そ
れらの結果を表１に示す。The evaluation criteria for the antifogging property are as follows. The results are shown in Table 1.
【００３４】◎…水滴がない、○+…ごくわずかに水滴
がある、○…一部に水滴がある、△…小水滴が目立つ、
×…全面が曇る。∘: No water droplets, ○ + : Very slight water droplets, ○: Partially water droplets, △: Small water droplets are conspicuous,
×: The entire surface becomes cloudy.
【００３５】[0035]
【表１】 [Table 1]
【００３６】[0036]
【発明の効果】本発明によれば、従来の直鎖状低密度ポ
リエチレンの長所である透明性、柔軟性、伸展性を保持
し、かつ押出成膜時のスクリュー内でのスリップ現象を
生じることなく、低温保存時にも優れた防曇性を有する
防曇性フイルムを提供することができる。According to the present invention, the advantages of the conventional linear low-density polyethylene, such as transparency, flexibility, and extensibility, are maintained, and a slip phenomenon occurs in the screw during extrusion film formation. It is possible to provide an antifogging film having excellent antifogging properties even when stored at low temperature.
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) C08L 23/00 - 23/36 C08K 3/00 - 13/08 C08J 5/18 ─────────────────────────────────────────────────── ─── Continuation of front page (58) Fields investigated (Int.Cl. 7 , DB name) C08L 23/00-23/36 C08K 3/00-13/08 C08J 5/18
Claims (2)
鎖状低密度ポリエチレン１００重量部に対し、ジグリセ
リンラウレート１〜５重量部、高圧法低密度ポリエチレ
ン１０〜３０重量部を含有する樹脂組成物からなる防曇
性フイルム。1. Containing 1 to 5 parts by weight of diglycerin laurate and 10 to 30 parts by weight of high-pressure low-density polyethylene to 100 parts by weight of linear low-density polyethylene having a density of 0.920 gr / cm 3 or less. An anti-fog film made of a resin composition.
鎖状低密度ポリエチレン１００重量部に対し、ジグリセ
リンラウレート１〜５重量部、グリセリンモノオレート
０．１〜１重量部、ポリオキシエチレンソルビタントリ
オレート０．１〜１重量部、ポリオキシエチレンアルキ
ルエーテル０．１〜１重量部、高圧法低密度ポリエチレ
ン１０〜３０重量部を含有する樹脂組成物からなる防曇
性フイルム。2. 1 to 5 parts by weight of diglycerin laurate, 0.1 to 1 part by weight of glycerin monooleate, and polyoxy for 100 parts by weight of linear low-density polyethylene having a density of 0.920 gr / cm 3 or less. An antifogging film comprising a resin composition containing 0.1 to 1 part by weight of ethylene sorbitan trioleate, 0.1 to 1 part by weight of polyoxyethylene alkyl ether, and 10 to 30 parts by weight of low-density polyethylene of high pressure method .