JPH01186708A - 難燃性電気絶縁組成物 - Google Patents
難燃性電気絶縁組成物Info
- Publication number
- JPH01186708A JPH01186708A JP63007482A JP748288A JPH01186708A JP H01186708 A JPH01186708 A JP H01186708A JP 63007482 A JP63007482 A JP 63007482A JP 748288 A JP748288 A JP 748288A JP H01186708 A JPH01186708 A JP H01186708A
- Authority
- JP
- Japan
- Prior art keywords
- hydroxide
- polyolefin
- additive
- imidazol
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
［産業上の利用分野］
この発明は、燃焼時に有毒なガスを発生しない難燃性電
気絶縁組成物、特に電線・ケーブルの絶縁材料やシース
材料への適用に好適な難燃性電気絶縁組成物に関する。
気絶縁組成物、特に電線・ケーブルの絶縁材料やシース
材料への適用に好適な難燃性電気絶縁組成物に関する。
［従来の技術］
最近、ビルディング等の高層建築物１発電所。
各種プラント等に３いて、火災が発生した場合を考慮し
て、人体に対する影響や機器腐蝕の原因となるハロゲン
系ガスを発生しない難燃性電気絶縁ケーブルが強く要望
されるようになってきた。
て、人体に対する影響や機器腐蝕の原因となるハロゲン
系ガスを発生しない難燃性電気絶縁ケーブルが強く要望
されるようになってきた。
このような要求に対応するため、従来の塩化ビニル樹脂
やクロロプレンゴムに代り、ポリオレフィンに難燃剤と
して金属水酸化物を混和した絶縁材料が検討されている
。
やクロロプレンゴムに代り、ポリオレフィンに難燃剤と
して金属水酸化物を混和した絶縁材料が検討されている
。
［発明が解決しようとする問題点］
ところで、これらの電気絶縁材料は洞道内や地中埋設等
の微生物の成育し易い環境にさらされた場合、ポリエチ
レン等に比ベカビの発育し易いことが最近明らかになっ
てきた。
の微生物の成育し易い環境にさらされた場合、ポリエチ
レン等に比ベカビの発育し易いことが最近明らかになっ
てきた。
この発明は、このような点に鑑みてなされたもので、カ
ビに対する抵抗性が高く、しかも発煙量が少ないととも
に有毒なハロゲン系ガス等を発生しない難燃性電気絶縁
組成物を提供することを目的とする。
ビに対する抵抗性が高く、しかも発煙量が少ないととも
に有毒なハロゲン系ガス等を発生しない難燃性電気絶縁
組成物を提供することを目的とする。
［問題点を解決するための手段］
この発明の難燃性電気絶縁組成物は、ポリオレフィン１
００重量部に対し金属水酸化物を５０〜３００重量部お
よびイミダゾール系添加剤を０゜２重量部以上含有させ
たものである。
００重量部に対し金属水酸化物を５０〜３００重量部お
よびイミダゾール系添加剤を０゜２重量部以上含有させ
たものである。
［実 施 例］
この発明におけるポリオレフィンとしては、ポリエチレ
ン、ポリプロピレン、エチレン酢酸ビニルコポリマー、
エチレンエチルアクリレートコポリマー、エチレンプロ
ピレンゴム、エチレンブテンコポリマー等を挙げること
ができる。
ン、ポリプロピレン、エチレン酢酸ビニルコポリマー、
エチレンエチルアクリレートコポリマー、エチレンプロ
ピレンゴム、エチレンブテンコポリマー等を挙げること
ができる。
金属水酸化物としては、水酸化アルミニウム。
水酸化マグネシウム、塩基性炭酸マグネシウム。
水酸化カルシウム、ハイドロタルサイト類等が挙げられ
る。これらの金属水酸化物はポリオレフィン１００重量
部に対して５０〜３００重量部の範囲で含有させる必要
があり、５０重量部未満では目的とする難燃性を付与で
きず、３００重量部を越えると引張特性等の機械的強度
が不十分となる。
る。これらの金属水酸化物はポリオレフィン１００重量
部に対して５０〜３００重量部の範囲で含有させる必要
があり、５０重量部未満では目的とする難燃性を付与で
きず、３００重量部を越えると引張特性等の機械的強度
が不十分となる。
このような配合系にイミダゾール系添加物を加えること
により、カビ抵抗性が著しく向上することを見出し、こ
の発明に至った。
により、カビ抵抗性が著しく向上することを見出し、こ
の発明に至った。
−を有する化合物を言い、具体的には２−メルカプトベ
ンズイミダゾール、２−メルカプトメチル・ベンズイミ
ダゾール、２−メルカプトベンズイミダゾールの亜鉛塩
、パラバン酸、ヒダントイン酸、アラントイン、グリコ
シアミジン、ヒスタミン、ヒスチジン、ピロカルピン等
が挙げられる。
ンズイミダゾール、２−メルカプトメチル・ベンズイミ
ダゾール、２−メルカプトベンズイミダゾールの亜鉛塩
、パラバン酸、ヒダントイン酸、アラントイン、グリコ
シアミジン、ヒスタミン、ヒスチジン、ピロカルピン等
が挙げられる。
このようなイミダゾール系添加物は、ポリオレフィン１
００重量部に対して０．２重量部以上含有せしめる必要
があり、０．２重量部未満では十分なカビ抵抗性が得ら
れない。
００重量部に対して０．２重量部以上含有せしめる必要
があり、０．２重量部未満では十分なカビ抵抗性が得ら
れない。
この発明においては、上記成分に加えて架橋剤、酸化防
止剤、滑剤、軟化剤１分散剤等を適宜添加してもよい。
止剤、滑剤、軟化剤１分散剤等を適宜添加してもよい。
架橋剤としては、ジクミルパーオキサイド、３−ビス（
ｔ−ブチルパーオキシイソプロピル）ベンゼンに代表さ
れる有機過酸化物が適切であり、これに架橋助剤として
、ｔｊ、Ｓ、エチレンジメタアクリレート、ジアリルフ
タレート、ｐ−キノンジオキシム等を併用してもよい。
ｔ−ブチルパーオキシイソプロピル）ベンゼンに代表さ
れる有機過酸化物が適切であり、これに架橋助剤として
、ｔｊ、Ｓ、エチレンジメタアクリレート、ジアリルフ
タレート、ｐ−キノンジオキシム等を併用してもよい。
また、電子線等の電離性放射線による架橋の場合には、
架橋助剤としてトリメチロールプロパントリメリテート
、トリアリルイソシアヌレート等の反応性のモノマーを
添加するのが一般的である。
架橋助剤としてトリメチロールプロパントリメリテート
、トリアリルイソシアヌレート等の反応性のモノマーを
添加するのが一般的である。
さらに、ビニルトリメトキシシランに代表されるシリコ
ーン化合物をポリオレフィンにグラフトあるいは共重合
させ、水分の存在下で架橋することも可能である。
ーン化合物をポリオレフィンにグラフトあるいは共重合
させ、水分の存在下で架橋することも可能である。
以下、具体的な実施例について説明する。
第１表に示すような配合割合に従って各種成分を温度１
００〜１２０℃に一保持した６インチロールに投入して
混線を行い、その後この組成物を用い電線およびシート
を作成し、実施例１〜実施例７および比較例１〜比較例
３の試料とした。電線は４０ ｍ／ｍ押出機（１，／Ｄ
−２５）を用い、外径２．０層−の銅線上に厚さ１．０
１に押出し被覆を行い、架橋を施すものは、その後圧力
１３ ｋｇ／ｍ■２の水蒸気雰囲気中に３分間保持して
架橋し電線を作製して試料とした。また、シートは８０
トンの熱プレスを用い圧力１００ ｋｇ／ｃｍ”、温度
１７０℃でｌａｍ厚に成形した。なお、架橋を施すもの
は１２０°Ｃで予備成・形後、温度１８０℃、１０分の
条件でシートを作製し試料とした。
００〜１２０℃に一保持した６インチロールに投入して
混線を行い、その後この組成物を用い電線およびシート
を作成し、実施例１〜実施例７および比較例１〜比較例
３の試料とした。電線は４０ ｍ／ｍ押出機（１，／Ｄ
−２５）を用い、外径２．０層−の銅線上に厚さ１．０
１に押出し被覆を行い、架橋を施すものは、その後圧力
１３ ｋｇ／ｍ■２の水蒸気雰囲気中に３分間保持して
架橋し電線を作製して試料とした。また、シートは８０
トンの熱プレスを用い圧力１００ ｋｇ／ｃｍ”、温度
１７０℃でｌａｍ厚に成形した。なお、架橋を施すもの
は１２０°Ｃで予備成・形後、温度１８０℃、１０分の
条件でシートを作製し試料とした。
６例についての評価結果を第１表に纒めて示す、なお、
この評価は次に記載した点に基づいて行った。
この評価は次に記載した点に基づいて行った。
難燃性：ＪＩＳ Ｃ３００４に基づき、水平に保持し
た電線をバーナで燃焼後バーナを取り去り、１分以内に
消えれば合格であり、１分以上燃えるものは不合格とし
た。
た電線をバーナで燃焼後バーナを取り去り、１分以内に
消えれば合格であり、１分以上燃えるものは不合格とし
た。
引張特性：架橋後に銅線を引き抜き、温度２０°Ｃの恒
温室に１日放置した後、ショパ型引張試験機により引張
速度５００園臘／■ｉｎで測定した。
温室に１日放置した後、ショパ型引張試験機により引張
速度５００園臘／■ｉｎで測定した。
カビ抵抗性試験：ＪＩＳ Ｚ ２９１１の繊維製品
の湿式法に準拠して５０ｘ５０■−角のシートを用い、
２週間培養後判定した。
の湿式法に準拠して５０ｘ５０■−角のシートを用い、
２週間培養後判定した。
第１表からも明らかなように、この発明に係る実施例１
〜実施例７のものは、難燃性および引張特性に優れ、培
養期間が２週間経過後もカビの発育は認められなかった
。
〜実施例７のものは、難燃性および引張特性に優れ、培
養期間が２週間経過後もカビの発育は認められなかった
。
これに対し、比較例１は金属水酸化物の含有量が規定値
未満のものであり、難燃性が不十分である。また、比較
例２は金属水酸化物の含有量が規定値を越えるものであ
り、引張特性が著しく悪化している。さらに、比較例３
はイミダゾール系添加剤の含有量が規定値未満のもので
あり、カビ抵抗性が著しく劣り、カビの発育が認められ
る。
未満のものであり、難燃性が不十分である。また、比較
例２は金属水酸化物の含有量が規定値を越えるものであ
り、引張特性が著しく悪化している。さらに、比較例３
はイミダゾール系添加剤の含有量が規定値未満のもので
あり、カビ抵抗性が著しく劣り、カビの発育が認められ
る。
［発明の効果］
以上説明したように、この発明の難燃性電気絶縁組成物
はポリオレフィンに金属水酸化物を混和するに当り、イ
ミダゾール系添加剤を加えるものであり、難燃性、引張
特性Ｓよびカビ抵抗性に優れ、しかも燃焼時に有毒なハ
ロゲン系ガスの発生を抑制できるようになり、洞道内や
地中埋設等の用途に適用できる優れた電線・ケーブルを
形成することができる。
はポリオレフィンに金属水酸化物を混和するに当り、イ
ミダゾール系添加剤を加えるものであり、難燃性、引張
特性Ｓよびカビ抵抗性に優れ、しかも燃焼時に有毒なハ
ロゲン系ガスの発生を抑制できるようになり、洞道内や
地中埋設等の用途に適用できる優れた電線・ケーブルを
形成することができる。
Claims (1)
- ポリオレフィン１００重量部に対し、金属水酸化物を５
０〜３００重量部およびイミダゾール系添加剤を０．２
重量部以上含有することを特徴とする難燃性電気絶縁組
成物。